Synthesis of highly active Cu(I)-Y(III)-Y zeolite and its selective adsorption desulfurization performance in presence of xylene isomers

Abstract Abstract A bimetal-exchanged NaY zeolite (Cu(I)-Y(III)-Y) with a desirable adsorptive desulfurization (ADS) performance was prepared and characterized by means of X-ray diffraction, specific surface area measurements, X-ray fluorescence spectrometer, X-ray photoelectron spectroscopy, thermal gravity analysis and Fourier transform infrared spectroscopy. The effect of Y(III) ions on ADS in the presence of the xylenes was investigated. Results indicated that the ADS performance of Y(III)-Y is higher than that of most reported CeY. The Y(III)-based Cu(I)-Y(III)-Y demonstrated the higher breakthrough loading than those of reported Ce(III)/Ce(IV)-based transition metal Y zeolites, showing that Y(III) ions play a promoting role in improving the ADS selectivity. For Cu(I)-Y(III)-Y, a new strong S-M interaction (S stands for sulfur, while M stands for metal) active site was formed, which might be caused by the synergistic effect between Cu(I) and Y(III). The Cu(I)-Y(III)-Y, which combined the advantages of Cu(I)-Y and Y(III)-Y, is a kind of promising adsorbent. The breakthrough loading decreased in the order of Cu(I)-Y(III)-Y > Y(III)-Y > Cu(I)-Y, and the effect of xylene isomers on the sulfur removal was in the order of ortho-xylene > meta-xylene > para-xylene, which exhibited the same trend with the bond order of xylenes.

Download Full-text

Fe-Containing MOFs as Seeds for the Preparation of Highly Active Fe/Al-SBA-15 Catalysts in the NAlkylation of Aniline

Molecules ◽

10.3390/molecules24152695 ◽

2019 ◽

Vol 24 (15) ◽

pp. 2695 ◽

Cited By ~ 1

Author(s):

Mhadmhan ◽

Marquez-Medina ◽

Romero ◽

Reubroycharoen ◽

Luque

Keyword(s):

Photoelectron Spectroscopy ◽

Inductively Coupled Plasma ◽

Catalytic Performance ◽

Alkylation Reaction ◽

X Ray Diffraction ◽

X Ray ◽

Inductively Coupled ◽

Highly Active ◽

Milling Method ◽

Plasma Mass Spectrometry

We have successfully incorporated iron species into mesoporous aluminosilicates (AlSBA15) using a simple mechanochemical milling method. The catalysts were characterized by nitrogen physisorption, inductively coupled plasma mass spectrometry (ICP-MS), pyridine (PY) and 2,6-dimethylpyridine (DMPY) pulse chromatography titration, powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM-EDX). The catalysts were tested in the N-alkylation reaction of aniline with benzyl alcohol for imine production. According to the results, the iron sources, acidity of catalyst and reaction conditions were important factors influencing the reaction. The catalyst showed excellent catalytic performance, achieving 97% of aniline conversion and 96% of imine selectivity under optimized conditions.

Download Full-text

Selective adsorption of PHC and regeneration of washing effluents by modified diatomite

Water Science & Technology ◽

10.2166/wst.2020.262 ◽

2020 ◽

Vol 81 (10) ◽

pp. 2066-2077

Author(s):

Zhuoqi Xu ◽

Gengbo Ren ◽

Yanying Zhu ◽

Xiaodong Ma ◽

Hongrui Li ◽

...

Keyword(s):

Photoelectron Spectroscopy ◽

Selective Adsorption ◽

Low Cost ◽

Soil Washing ◽

X Ray Diffraction ◽

X Ray ◽

Monolayer Adsorption ◽

Pseudo Second Order ◽

Adsorption Desorption ◽

Modified Diatomite

Abstract Selective removal of petroleum hydrocarbons (PHCs) from soil washing effluents is the key to the surfactant-enhanced soil washing technology. In this study, the diatomite was modified by nonionic surfactant TX-100 and applied in the selective adsorption of PHCs in the soil washing effluents. The modified diatomites were characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, N2 adsorption/desorption and X-ray photoelectron spectroscopy respectively. The adsorption process followed the pseudo-second-order model and the adsorption isotherms indicated that the interaction between PHCs and modified diatomite was monolayer adsorption. The important operating factors such as TX-100 dosage, adsorbent dosage, time and temperature were optimized. With the participation of the low-cost adsorbent TX3-Db with high adsorption capacity, the recovery efficiency of the washing effluents was still up to 78.9% after three cycles. A selective adsorption mechanism, based on steric hindrance and electrostatic repulsion, was proposed to explain the removal of PHCs from washing effluents.

Download Full-text

Investigation of the Effect of Uv-Assisted Oxidation and Nitridation of Hafnium Metal Films

MRS Proceedings ◽

10.1557/proc-780-y5.5 ◽

2003 ◽

Vol 780 ◽

Author(s):

C. Essary ◽

V. Craciun ◽

J. M. Howard ◽

R. K. Singh

Keyword(s):

Uv Radiation ◽

Photoelectron Spectroscopy ◽

Grazing Angle ◽

X Ray Diffraction ◽

Metal Thin Films ◽

X Ray ◽

Force Microscopy ◽

Si Substrates ◽

Atomic Force ◽

Silicon Interface

AbstractHf metal thin films were deposited on Si substrates using a pulsed laser deposition technique in vacuum and in ammonia ambients. The films were then oxidized at 400 °C in 300 Torr of O2. Half the samples were oxidized in the presence of ultraviolet (UV) radiation from a Hg lamp array. X-ray photoelectron spectroscopy, atomic force microscopy, and grazing angle X-ray diffraction were used to compare the crystallinity, roughness, and composition of the films. It has been found that UV radiation causes roughening of the films and also promotes crystallization at lower temperatures.Furthermore, increased silicon oxidation at the interface was noted with the UVirradiated samples and was shown to be in the form of a mixed layer using angle-resolved X-ray photoelectron spectroscopy. Incorporation of nitrogen into the film reduces the oxidation of the silicon interface.

Download Full-text

α-Cellulose Fibers of Paper-Waste Origin Surface-Modified with Fe3O4 and Thiolated-Chitosan for Efficacious Immobilization of Laccase

Polymers ◽

10.3390/polym13040581 ◽

2021 ◽

Vol 13 (4) ◽

pp. 581

Author(s):

Gajanan S. Ghodake ◽

Surendra K. Shinde ◽

Ganesh D. Saratale ◽

Rijuta G. Saratale ◽

Min Kim ◽

...

Keyword(s):

Enzyme Immobilization ◽

Photoelectron Spectroscopy ◽

Cellulose Fibers ◽

Relative Activity ◽

Significant Activity ◽

X Ray Diffraction ◽

X Ray ◽

Transmission Electron ◽

Laccase Immobilization ◽

Surface Modified

The utilization of waste-paper-biomass for extraction of important α-cellulose biopolymer, and modification of extracted α-cellulose for application in enzyme immobilization can be extremely vital for green circular bio-economy. Thus, in this study, α-cellulose fibers were super-magnetized (Fe3O4), grafted with chitosan (CTNs), and thiol (-SH) modified for laccase immobilization. The developed material was characterized by high-resolution transmission electron microscopy (HR-TEM), HR-TEM energy dispersive X-ray spectroscopy (HR-TEM-EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy (FT-IR) analyses. Laccase immobilized on α-Cellulose-Fe3O4-CTNs (α-Cellulose-Fe3O4-CTNs-Laccase) gave significant activity recovery (99.16%) and laccase loading potential (169.36 mg/g). The α-Cellulose-Fe3O4-CTNs-Laccase displayed excellent stabilities for temperature, pH, and storage time. The α-Cellulose-Fe3O4-CTNs-Laccase applied in repeated cycles shown remarkable consistency of activity retention for 10 cycles. After the 10th cycle, α-Cellulose-Fe3O4-CTNs possessed 80.65% relative activity. Furthermore, α-Cellulose-Fe3O4-CTNs-Laccase shown excellent degradation of pharmaceutical contaminant sulfamethoxazole (SMX). The SMX degradation by α-Cellulose-Fe3O4-CTNs-Laccase was found optimum at incubation time (20 h), pH (3), temperatures (30 °C), and shaking conditions (200 rpm). Finally, α-Cellulose-Fe3O4-CTNs-Laccase gave repeated degradation of SMX. Thus, this study presents a novel, waste-derived, highly capable, and super-magnetic nanocomposite for enzyme immobilization applications.

Download Full-text

Photocatalytic Reduction of CO2 to Methanol Using a Copper-Zirconia Imidazolate Framework

Catalysts ◽

10.3390/catal11030346 ◽

2021 ◽

Vol 11 (3) ◽

pp. 346

Author(s):

Sonam Goyal ◽

Maizatul Shima Shaharun ◽

Ganaga Suriya Jayabal ◽

Chong Fai Kait ◽

Bawadi Abdullah ◽

...

Keyword(s):

Photoelectron Spectroscopy ◽

Catalyst Support ◽

Oxidation Potential ◽

Molar Ratio ◽

X Ray Diffraction ◽

X Ray ◽

Molar Ratios ◽

Optimum Parameters ◽

Reduction Of Co2 ◽

Enhanced Yield

A set of novel photocatalysts, i.e., copper-zirconia imidazolate (CuZrIm) frameworks, were synthesized using different zirconia molar ratios (i.e., 0.5, 1, and 1.5 mmol). The photoreduction process of CO2 to methanol in a continuous-flow stirred photoreactor at pressure and temperature of 1 atm and 25 °C, respectively, was studied. The physicochemical properties of the synthesized catalysts were studied using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and photoluminescence (PL) spectroscopy. The highest methanol activity of 818.59 µmol/L.g was recorded when the CuZrIm1 catalyst with Cu/Zr/Im/NH4OH molar ratio of 2:1:4:2 (mmol/mmol/mmol/M) was employed. The enhanced yield is attributed to the presence of Cu2+ oxidation state and the uniformly dispersed active metals. The response surface methodology (RSM) was used to optimize the reaction parameters. The predicted results agreed well with the experimental ones with the correlation coefficient (R2) of 0.99. The optimization results showed that the highest methanol activity of 1054 µmol/L.g was recorded when the optimum parameters were employed, i.e., stirring rate (540 rpm), intensity of light (275 W/m2) and photocatalyst loading (1.3 g/L). The redox potential value for the CuZrIm1 shows that the reduction potential is −1.70 V and the oxidation potential is +1.28 V for the photoreduction of CO2 to methanol. The current work has established the potential utilization of the imidazolate framework as catalyst support for the photoreduction of CO2 to methanol.

Download Full-text

Highly active carbon nanotube–promoted Rh-Mn-Li/SiO2 catalysts for the synthesis of C2+ oxygenates from syngas

Journal of Chemical Research ◽

10.1177/1747519820984728 ◽

2021 ◽

pp. 174751982098472

Author(s):

Jun Yu ◽

Ying Han ◽

Guoqing Chen ◽

Xiuzhen Xiao ◽

Haifang Mao ◽

...

Keyword(s):

Carbon Nanotubes ◽

Photoelectron Spectroscopy ◽

Co Hydrogenation ◽

X Ray ◽

Highly Active ◽

Transmission Electron ◽

Co Insertion ◽

Temperature Programmed Surface Reaction ◽

Temperature Programmed ◽

Oxygenate Synthesis

The effect of carbon nanotubes on the catalytic properties of Rh-Mn-Li/SiO2 catalysts was investigated for CO hydrogenation. The catalysts were comprehensively characterized by means of X-ray power diffraction, N2 sorption, transmission electron microscope, H2–temperature-programmed reduction, CO–temperature-programmed desorption, temperature-programmed surface reaction, and X-ray photoelectron spectroscopy. The results showed that an appropriate amount of carbon nanotubes can be attached to the surface of the SiO2 sphere and can improve the Rh dispersion. Moderate Rh-Mn interaction can be obtained by doping with the appropriate amount of carbon nanotubes, which promotes the formation of strongly adsorbed CO and facilitates the progress of CO insertion, resulting in the increase in the selectivity of C2+ oxygenate synthesis.

Download Full-text

Study on the Electrical, Structural, Chemical and Optical Properties of PVD Ta(N) Films Deposited with Different N2 Flow Rates

Coatings ◽

10.3390/coatings11080937 ◽

2021 ◽

Vol 11 (8) ◽

pp. 937

Author(s):

Yingying Hu ◽

Md Rasadujjaman ◽

Yanrong Wang ◽

Jing Zhang ◽

Jiang Yan ◽

...

Keyword(s):

Crystal Structure ◽

Optical Properties ◽

Photoelectron Spectroscopy ◽

Crystal Size ◽

Silicon Substrates ◽

X Ray Diffraction ◽

Dc Magnetron Sputtering ◽

Flow Rates ◽

X Ray ◽

N2 Flow Rate

By reactive DC magnetron sputtering from a pure Ta target onto silicon substrates, Ta(N) films were prepared with different N2 flow rates of 0, 12, 17, 25, 38, and 58 sccm. The effects of N2 flow rate on the electrical properties, crystal structure, elemental composition, and optical properties of Ta(N) were studied. These properties were characterized by the four-probe method, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and spectroscopic ellipsometry (SE). Results show that the deposition rate decreases with an increase of N2 flows. Furthermore, as resistivity increases, the crystal size decreases, the crystal structure transitions from β-Ta to TaN(111), and finally becomes the N-rich phase Ta3N5(130, 040). Studying the optical properties, it is found that there are differences in the refractive index (n) and extinction coefficient (k) of Ta(N) with different thicknesses and different N2 flow rates, depending on the crystal size and crystal phase structure.

Download Full-text

Optical, XPS and XRD Studies of Semiconducting Copper Sulfide Layers on a Polyamide Film

International Journal of Photoenergy ◽

10.1155/2009/304308 ◽

2009 ◽

Vol 2009 ◽

pp. 1-8 ◽

Cited By ~ 69

Author(s):

Valentina Krylova ◽

Mindaugas Andrulevičius

Keyword(s):

Photoelectron Spectroscopy ◽

Copper Sulfide ◽

Diffusion Method ◽

X Ray Diffraction ◽

Xps Spectra ◽

X Ray ◽

Xrd Studies ◽

Polyamide Film ◽

Indirect Band Gap ◽

Xrd Method

Copper sulfide layers were formed on polyamide PA 6 surface using the sorption-diffusion method. Polymer samples were immersed for 4 and 5 h in 0.15 mol⋅ solutions and acidified with HCl (0.1 mol⋅) at . After washing and drying, the samples were treated with Cu(I) salt solution. The samples were studied by UV/VIS, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) methods. All methods confirmed that on the surface of the polyamide film a layer of copper sulfide was formed. The copper sulfide layers are indirect band-gap semiconductors. The values of are 1.25 and 1.3 eV for 4 h and 5 h sulfured PA 6 respectively. Copper XPS spectra analyses showed Cu(I) bonds only in deeper layers of the formed film, while in sulfur XPS S 2p spectra dominating sulfide bonds were found after cleaning the surface with ions. It has been established by the XRD method that, beside , the layer contains as well. For PA 6 initially sulfured 4 h, grain size forchalcocite, , was nm and fordjurleite, , it was 54.17 nm. The sheet resistance of the obtained layer varies from 6300 to 102 .

Download Full-text

Biodiesel Production on Monometallic Pt, Pd, Ru, and Ag Catalysts Supported on Natural Zeolite

Materials ◽

10.3390/ma14010048 ◽

2020 ◽

Vol 14 (1) ◽

pp. 48

Author(s):

Pawel Mierczynski ◽

Magdalena Mosińska ◽

Lukasz Szkudlarek ◽

Karolina Chalupka ◽

Misa Tatsuzawa ◽

...

Keyword(s):

Photoelectron Spectroscopy ◽

Natural Zeolite ◽

Noble Metals ◽

Methyl Esters ◽

Physicochemical Characteristics ◽

Biodiesel Production ◽

X Ray Diffraction ◽

X Ray ◽

Yield Values ◽

Temperature Programmed

Biodiesel production from rapeseed oil and methanol via transesterification reaction facilitated by various monometallic catalyst supported on natural zeolite (NZ) was investigated. The physicochemical characteristics of the synthesized catalysts were studied by X-ray diffraction (XRD), Brunauer–Emmett–Teller method (BET), temperature-programmed-reduction in hydrogen (H2-TPR), temperature-programmed-desorption of ammonia (NH3-TPD), Scanning Electron Microscope equipped with EDX detector (SEM-EDS), and X-ray photoelectron spectroscopy (XPS) methods. The highest activity and methyl ester yields were obtained for the Pt/NZ catalyst. This catalyst showed the highest triglycerides conversion of 98.9% and fatty acids methyl esters yields of 94.6%. The activity results also confirmed the high activity of the carrier material (NZ) itself in the investigated reaction. Support material exhibited 90.5% of TG conversion and the Fatty Acid Methyl Esters yield (FAME) of 67.2%. Introduction of noble metals improves the TG conversion and FAME yield values. Increasing of the metal loading from 0.5 to 2 wt.% improves the reactivity properties of the investigated catalysts.

Download Full-text

Impact of high temperatures on aluminoceladonite studied by Mössbauer, Raman, X-ray diffraction and X-ray photoelectron spectroscopy

Mineralogy and Petrology ◽

10.1007/s00710-021-00753-z ◽

2021 ◽

Author(s):

Mariola Kądziołka-Gaweł ◽

Maria Czaja ◽

Mateusz Dulski ◽

Tomasz Krzykawski ◽

Magdalena Szubka

Keyword(s):

Photoelectron Spectroscopy ◽

Integral Intensity ◽

Photoelectron Spectra ◽

X Ray Diffraction ◽

Structural Reorganization ◽

Oh Groups ◽

X Ray ◽

Al Content ◽

Integral Intensity Ratio ◽

Higher Temperature

AbstractMössbauer, Raman, X-ray diffraction and X-ray photoelectron spectroscopies were used to examine the effects of temperature on the structure of two aluminoceladonite samples. The process of oxidation of Fe2+ to Fe3+ ions started at about 350 °C for the sample richer in Al and at 300 °C for the sample somewhat lower Al-content. Mössbauer results show that this process may be associated with dehydroxylation or even initiate it. The first stage of dehydroxylation takes place at a temperature > 350 °C when the adjacent OH groups are replaced with a single residual oxygen atom. Up to ~500 °C, Fe ions do not migrate from cis-octahedra to trans-octahedra sites, but the coordination number of polyhedra changes from six to five. This temperature can be treated as the second stage of dehydroxylation. The temperature dependence on the integral intensity ratio between bands centered at ~590 and 705 cm−1 (I590/I705) clearly reflects the temperature at which six-coordinated polyhedra are transformed into five-coordinated polyhedra. X-ray photoelectron spectra obtained in the region of the Si2p, Al2p, Fe2p, K2p and O1s core levels, highlighted a route to identify the position of Si, Al, K and Fe cations in a structure of layered silicates with temperature. All the measurements show that the sample with a higher aluminum content and a lower iron content in octahedral sites starts to undergo a structural reorganization at a relatively higher temperature than the less aluminum-rich sample does. This suggests that iron may perform an important role in the initiation of the dehydroxylation of aluminoceladonites.

Download Full-text