scholarly journals DETERMINATION OF ATMOSPHERIC CORROSION RATE OF METALS IN 12 VIETNAMESE AREAS

2018 ◽  
Vol 55 (5B) ◽  
pp. 272
Author(s):  
Pham Duy Nam
Keyword(s):  
Carbon Steel ◽  
Corrosion Rate ◽  
Rural Areas ◽  
Atmospheric Corrosion ◽  
Climatic Factors ◽  
Air Pollutant ◽  
Climatic Data ◽  
Corrosion Rates ◽  
Copper Aluminum

The corrosion of materials is a result of complex impact from many climatic factors such as temperature, humidity, air pollutant content in the air, rainfall etc. In addition, the corrosion rate of metals can be measured. Each climatic zone is characterized by its corrosion rate. This article presents the testing results to determine the corrosion rate of carbon steel, copper, aluminum and zinc in 12 districts characterizing different climate zones of Vietnam. Testing, evaluation, and classification of atmospheric corrosion were conducted in accordance with the standard ISO 9223. The results show that for all types of studied metals, their corrosion rates which are determined from climatic data are higher than the corrosion rates in reality, especially for carbon steel and aluminum. This difference is more visible in the rural areas.

scholarly journals AEROSOL SALINITY AND CORROSION RATE OF CARBON STEEL IN NHA TRANG CITY ATMOSPHERE

2010 ◽  
Vol 13 (1) ◽  
pp. 26-34
Author(s):  
Thao Van Bui ◽  
De Vo ◽  
Tan Quang Nguyen ◽  
Tan Huu Nguyen ◽  
Tru Nhi Nguyen
Keyword(s):  
Carbon Steel ◽  
Wind Speed ◽  
Corrosion Rate ◽  
Atmospheric Corrosion ◽  
Meteorological Parameters ◽  
First Year ◽  
Exposure Test ◽  
Sea Levels ◽  
Coastal City ◽  
Corrosion Rates

Aerosol salinity and atmospheric corrosion rate of carbon steel were determined at six sites in Nhatrang coastal city. The sites have been selected with different distances from the sea and various heights above sea levels. Results show that the aerosol salinity was strongly influenced by salt collecting positions and by various meteorological parameters, especially by wind speed and directions. Corrosion rates of carbon steel were dependent with the aerosol salinity values at all exposure sites. Besides, atmospheric corrosivities for above mentioned sites of Nhatrang city have been classified according to ISO 9223:1992. Nhatrang atmosphere is considered to be in S1 class by aerosol salinity and C3 class by corrosion rate of carbon steel after first year exposure test.

Research on Prediction of Carbon Steel in SO2 Atmospheric Corrosion Using Grey Model

2014 ◽  
Vol 507 ◽  
pp. 258-262
Author(s):  
Ping Wang ◽  
Zhao Hui Yin ◽  
Han Tao Ren ◽  
Song Xu
Keyword(s):  
Carbon Steel ◽  
Corrosion Rate ◽  
Prediction Model ◽  
Relative Error ◽  
Atmospheric Corrosion ◽  
Grey Model ◽  
Fitting Accuracy

The rate of carbon steel in SO2 Atmospheric Corrosion was modeled by grey model GM (1, 1). The accuracy and rationality of prediction model have been evaluated. The result indicated that the model had a better fitting accuracy. By comparing the calculated values with a predicted atmospheric corrosion rate of carbon steel after 264h, it showed that its relative error has been just 0.5619% which had higher forecast reliability.

The Corrosion of Carbon Steel and Stainless Steel in Simulated Geothermal Media

1985 ◽  
Vol 38 (8) ◽  
pp. 1133 ◽  
Author(s):  
BG Pound ◽  
MH Abdurrahman ◽  
MP Glucina ◽  
GA Wright ◽  
RM Sharp
Keyword(s):  
Carbon Steel ◽  
Corrosion Rate ◽  
Stainless Steels ◽  
Polarization Resistance ◽  
Iron Sulfide ◽  
Low Carbon Steel ◽  
Passive Films ◽  
Low Carbon ◽  
Corrosion Rates ◽  
Good Agreement

The corrosion rates of low-carbon steel, and 304, 316 and 410/420 stainless steels in simulated geothermal media containing hydrogen sulfide have been measured by means of the polarization resistance technique. Good agreement was found between weight-loss and polarization resistance measurements of the corrosion rate for all the metals tested. Carbon steel formed a non-adherent film of mackinawite (Fe1 + xS). The lack of protection afforded to the steel by the film resulted in an approximately constant corrosion rate. The stainless steels also exhibited corrosion rates that were independent of time. However, the 410 and 420 alloys formed an adherent film consisting mainly of troilite ( FeS ) which provided only limited passivity. In contrast, the 304 and 316 alloys appeared to be essentially protected by a passive film which did not seem to involve an iron sulfide phase. However, all the stainless steels, particularly the 410 and 420 alloys, showed pitting, which indicated that some breakdown of the passive films occurred.

scholarly journals The effect of volatile organic acids and CO2 on the corrosion rate of carbon steel from a Top-of-Line-Corrosion (TLC) perspective

2021 ◽  
Vol 1201 (1) ◽  
pp. 012079
Author(s):  
S B Gjertsen ◽  
A Palencsar ◽  
M Seiersten ◽  
T H Hemmingsen
Keyword(s):  
Carbon Steel ◽  
Corrosion Rate ◽  
Organic Acid ◽  
Carbonic Acid ◽  
Acid Corrosion ◽  
Iron Concentration ◽  
Critical Factor ◽  
Steel Corrosion ◽  
Carbon Steels ◽  
Corrosion Rates

Abstract Models for predicting top-of-line corrosion (TLC) rates on carbon steels are important tools for cost-effectively designing and operating natural gas transportation pipelines. The work presented in this paper is aimed to investigate how the corrosion rates on carbon steel is affected by acids typically present in the transported pipeline fluids. This investigation may contribute to the development of improved models. In a series of experiments, the corrosion rate differences for pure CO2 (carbonic acid) corrosion and pure organic acid corrosion (acetic acid and formic acid) on X65 carbon steel were investigated at starting pH values; 4.5, 5.3, or 6.3. The experiments were conducted in deaerated low-salinity aqueous solutions at atmospheric pressure and temperature of 65 °C. The corrosion rates were evaluated from linear polarization resistance data as well as mass loss and released iron concentration. A correlation between lower pH values and increased corrosion rates was found for the organic acid experiments. However, the pH was not the most critical factor for the rates of carbon steel corrosion in these experiments. The experimental results showed that the type of acid species involved and the concentration of the undissociated acid in the solution influenced the corrosion rates considerably.

scholarly journals Maps estimates of atmospheric corrosion of low alloy steel in Costa Rica

2015 ◽  
Vol 7 (2) ◽  
pp. 181-191
Author(s):  
Javier Rodríguez Yáñez ◽  
Luis Garita Arce ◽  
Ericka Saborío Leiva
Keyword(s):  
Costa Rica ◽  
Alloy Steel ◽  
Atmospheric Corrosion ◽  
Climatic Data ◽  
Local Models ◽  
Low Alloy Steel ◽  
Atmospheric Parameters ◽  
Corrosion Rates ◽  
Wetting Time ◽  
Low Levels

The Corrosion maps used are to display quickly the different situations in a country. These maps developed are for low alloy steel in Costa Rica depending on climatic data and pollutant levels, considering the different regulations associated with ISO 9223 and models developed by the Center for Research in Corrosion (CICorr). The atmosphere in Costa Rica has high rates of Brooks, considered very corrosive. The corrosion controlling atmospheric parameters are the relative humidity (RH) and Wetting Time (TWH) associated with low levels of pollution and rural type atmospheres. The corrosion rates are between 25 and 80μm*yr-1 (Class 3 and 4 according to ISO 9223). Local models associated with the controlling parameters are more suitable for estimating the corrosion according to ISO 9223.

scholarly journals Electrochemical Impedance Spectroscopy for the Measurement of the Corrosion Rate of Magnesium Alloys: Brief Review and Challenges

Metals ◽  
2020 ◽  
Vol 10 (6) ◽  
pp. 775 ◽  
Author(s):  
Sebastián Feliu
Keyword(s):  
Electrochemical Impedance Spectroscopy ◽  
Impedance Spectroscopy ◽  
Corrosion Rate ◽  
Electrochemical Impedance ◽  
State Of The Art ◽  
Point Of View ◽  
Reliable Determination ◽  
Corrosion Rates ◽  
Non Destructive

From a technological point of view, measurement of the corrosion rate of magnesium (Mg) and its alloys is critical for lifetime predictions of Mg-based structures and for comparative assessments of their corrosion protection ability. Whilst weight loss, hydrogen evolution, and polarization curves methods are frequently used for measuring the corrosion rate, the determination of values by electrochemical impedance spectroscopy (EIS) is relatively scarce and has only been realized recently. This technique seems to be the most suitable for monitoring corrosion rate values due to its “non-destructive” character, its reproducibility, and its reliable determination of small corrosion rates, much lower than those measured by other techniques. This review aims to picture the state-of-the-art technique of using EIS for measuring the corrosion rate of Mg. This paper starts by introducing some fundamental aspects of the most widely used methods for monitoring the corrosion rate of Mg/Mg alloy and continues by briefly explaining some of the fundamental concepts surrounding EIS, which are essential for the user to be able to understand how to interpret the EIS spectra. Lastly, these concepts are applied, and different approaches that have been proposed to obtain quantitative values of corrosion rate since the 1990s are discussed.

Annual atmospheric corrosion rate and dose-response function for carbon steel in Bogotá

Atmósfera ◽  
2017 ◽  
Vol 30 (1) ◽  
pp. 53-61 ◽  
Author(s):  
John Fredy Ríos Rojas ◽  
◽  
David Aperador Rodríguez ◽  
Edwin Arbey Hernández García ◽  
Carlos Enrique Arroyave Posada ◽  
...  
Keyword(s):  
Carbon Steel ◽  
Corrosion Rate ◽  
Response Function ◽  
Dose Response ◽  
Atmospheric Corrosion ◽  
Dose Response Function

scholarly journals A Field Study of Atmospheric Corrosion of Carbon Steel after Short Exposure in Pelabuhan Ratu, West Java Province, Indonesia

2021 ◽  
Vol 18 (17) ◽  
Author(s):  
Gadang PRIYOTOMO ◽  
Siska PRIFIHARNI ◽  
Lutviasari NURAINI ◽  
Joko TRIWARDONO ◽  
Ahmad ROYANI ◽  
...  
Keyword(s):  
Carbon Steel ◽  
Relative Humidity ◽  
Air Temperature ◽  
Atmospheric Corrosion ◽  
Short Exposure ◽  
Corrosion Attack ◽  
West Java ◽  
Corrosion Rates ◽  
Magnetite Fe3o4 ◽  
Chloride Deposition

The investigation of atmospheric corrosion of mild carbon steel as representative of offshore infrastructure has been carried out in the marine tropical of Pelabuhan Ratu, West Java, Indonesia. They are exposed up to 76 days of periods, and their corrosion rates are determined according to ASTM G1-03. The surface morphology, the elemental compositions and compounds were observed using a scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), respectively.  The environmental parameters of the test site are monitored during exposure, such as air temperature, relative humidity (RH), airborne salinity and dew temperature. Based on the results, the corrosion rates of steels were 2.79 and 2.8 mpy within the 27 and 76 days exposures, respectively. The presence of chloride deposition on the surface of steel can increase the severity of corrosion. Moreover, the detrimental effect of chloride was observed in rust product, which was covered by an oxygen element. The main phases of rust products present were magnetite (Fe3O4) and hematite (α-Fe2O3.H2O). Several cracks were observed in the rust layer, which tended to exfoliate and lose adherence and protectiveness from further corrosion attack. HIGHLIGHTS The presence of chloride deposition on the surface of steel can increase the severity of corrosion. The severity of corrosion attack mainly depends on the exposure time and some climatic parameters, such as relative humidity (RH), air temperature and chloride airborne. The uniform distribution of the chloride tends to increase the production of ferrous chloride in high RH condition and the aqueous layer deposited on carbon steel. There are two phases on corroded carbon steel such as hematite (α-Fe2O3.H2O) and Magnetite (Fe3O4) after exposure GRAPHICAL ABSTRACT

scholarly journals The Influence of The Marine Bacillus Cereus Mc-1 Over Carbon Steel, Stainless Corrosion And Copper Coupons

2021 ◽  
Author(s):  
Paulo Moreira-Filho ◽  
Paloma de Paula da Silva Figueiredo ◽  
Artur Capão ◽  
Luciano Procópio
Keyword(s):  
Stainless Steel ◽  
Control System ◽  
Carbon Steel ◽  
Corrosion Rate ◽  
Bacillus Cereus ◽  
Copper Alloy ◽  
Culture Medium ◽  
316L Stainless Steel ◽  
Corrosion Rates ◽  
Nitrate Supplementation

Abstract The present study evaluated the influence of the marine bacteria Bacillus cereus Mc-1 on the corrosion of 1020 carbon steel, 316L stainless steel, and copper alloy. The Mc-1 strain was grown in a modified ammoniacal citrate culture medium (CFA.ico-), CFA.ico- with sodium nitrate supplementation (NO3-), and CFA.ico- with sodium chloride supplementation (NaCl). The and mass loss and corrosion rate were evaluated after the periods of seven, 15, and 30 days. The results showed that in CFA.ico- and CFA.ico- medium added NO3- the corrosion rates of carbon steel and copper alloy were high when compared to the control. Whereas the medium was supplemented with NaCl, despite the rates being above the averages of the control system, they were considerably below the previous results. In general, the corrosion rates induced by Mc-1 on 316L coupons were below the results compared to carbon steel and copper alloy. When analyzing the corrosion rate measurements, regardless of the culture medium, the corrosion levels decreased consistently after 15 days, being below the levels evaluated after seven days of the experiment. Our analyzes suggest that B. cereus Mc-1 has different influences on corrosion in different metals and environmental conditions, such as the presence of NO3- and NaCl. These results can help to better understand the influence of this bacteria genus on the corrosion of metals in marine environments.

Sign in / Sign up

Export Citation Format

Share Document