Corrosion Behavior of Electroless Deposited Fe-Zn Coating

2011 ◽  
Vol 117-119 ◽  
pp. 81-84
Author(s):  
Xi Ran Wang ◽  
Jing Wu ◽  
Xin Gang Hu
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Behavior ◽  
Open Circuit Potential ◽  
Corrosion Current ◽  
Open Circuit ◽  
Nacl Solution ◽  
Positive Direction ◽  
Heat Treated ◽  
Heat Treated Temperature ◽  
Electronic Microscope

In this work, Fe-Zn coating on copper is obtained by electroless plating. The surface mor -phologies and composition of the coatings has been investigated using scanning electronic microscope (SEM) and energy dispersive spectroscopy(EDS). Corrosion behavior of Fe-Zn coating in3.5% NaCl solution is gaved a further insight. The impedance diagram indicates that corrosion resistance of coating is better. The open circuit potential of Fe-Zn coating is at about -1V. Self-corrosion potential of Fe-Zn coating in 3.5%NaCl solution shifts in the positive direction first and then shifts from -0.622V to -0.603V with increasing heat-treated temperature, while corresponding self-corrosion current decreases at first and then. increases Corrosion resistance of coating is the best when heat-treated temperature is 300°C.

scholarly journals The Corrosion Behavior of Sputter?deposited W?xTa Alloys in 0.5 M NaCl Solution

2013 ◽  
Vol 14 (1) ◽  
pp. 103-108
Author(s):  
Jagadeesh Bhattarai ◽  
Susil Baral
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Open Circuit Potential ◽  
Corrosion Potential ◽  
Open Circuit ◽  
Nacl Solution ◽  
High Corrosion Resistance ◽  
Positive Direction ◽  
Sputter Deposited

The corrosion behavior of the sputter–deposited amorphous and nanocrystalline W–xTa (x = 8–77) alloys was studied in 0.5 M NaCl solution open to air at 25°C using corrosion tests and electrochemical measurements. Tungsten and tantalum metals act synergistically in enhancing the corrosion resistance of the sputter–deposited W–xTa alloys and hence additions of 23 at. % of tantalum or more to the sputter–deposited W–xTa alloys were found to be effective to achieve significantly high corrosion resistance properties of the alloys than those of alloy– constituting elements. In particular, the corrosion rate of the W–60Ta alloy showed the lowest corrosion rate (that is, 2.0×10-3). The open circuit potential of the alloys shifted noble (positive) direction with immersion time. Addition of tantalum metal in W–xTa alloys is effective for ennoblement of the open circuit corrosion potential of the tungsten metal in 0.5 M NaCl solution open to air at 25°C. Nepal Journal of Science and Technology Vol. 14, No. 1 (2013) 103-108 DOI: http://dx.doi.org/10.3126/njst.v14i1.8929

scholarly journals Effect of Fluid Flow on the Corrosion Performance of as-Cast and Heat-Treated Nickel Aluminum Bronze Alloy (UNS C95800) in Saline Solution

2021 ◽  
Vol 2 (1) ◽  
pp. 61-77
Author(s):  
Hamid Reza Jafari ◽  
Ali Davoodi ◽  
Saman Hosseinpour
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Behavior ◽  
Flow Rate ◽  
Solution Temperature ◽  
Aluminum Bronze ◽  
Nickel Aluminum ◽  
Nacl Solution ◽  
Flow Conditions ◽  
Heat Treated ◽  
Nickel Aluminum Bronze

In this work, the corrosion behavior and surface reactivity of as-cast and heat-treated nickel aluminum bronze casting alloy (UNS C95800) in 3.5 wt% NaCl solution is investigated under stagnant and flow conditions. Increasing flow rate conditions are simulated using a rotating disk electrode from 0 to 9000 revolutions per minute (rpm). Optical micrographs confirm the decrease in the phase fraction of corrosion-sensitive β phase in the microstructure of C95800 after annealing, which, in turn, enhances the corrosion resistance of the alloy. Electrochemical studies including open circuit potentiometry, potentiodynamic polarization, and electrochemical impedance spectroscopy are performed to assess the effect of flow rate and heat treatment on the corrosion of samples at 25 and 40 °C in 3.5 wt% NaCl solution. For both as-cast and heat-treated samples, increasing the flow rate (i.e., electrode rotating rate) linearly reduces the corrosion resistance, indicating that the metal dissolution rate is significantly affected by hydrodynamic flow. Increasing the solution temperature negatively impacts the corrosion behavior of the as-cast and heat-treated samples at all flow conditions.

scholarly journals The Corrosion Behavior of Sputter-Deposited Nanocrystalline W-Cr Alloys in Nacl and NaohaSolutions

1970 ◽  
Vol 25 ◽  
pp. 53-61
Author(s):  
Minu Basnet ◽  
Jagadeesh Bhattarai
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Chromium Content ◽  
Open Circuit ◽  
Nacl Solution ◽  
Corrosion Rates ◽  
Naoh Solution ◽  
Order Of Magnitude ◽  
Sputter Deposited

The corrosion behavior of the sputter-deposited nanocrystalline W-Cr alloys wasstudied in 0.5 M NaCl and alkaline 1 M NaOH solutions at 25°C, open to air usingimmersion tests and electrochemical measurements. Chromium metal acts synergisticallywith tungsten in enhancing the corrosion resistance of the sputter-deposited W-Cr alloys soas to show higher corrosion resistance than those of alloy-constituting elements in both 0.5M NaCl and 1 M NaOH solutions. In particular, the nanocrystalline W-Cr alloys containing25-91 at% chromium showed about one order of magnitude lower corrosion rates (that is,about 1-2 × 10-3 mm.y-1) than those of tungsten and chromium metals even for prolongedimmersion in 0.5 M NaCl solution at 25°C. On the other hand, the corrosion rate of thesputter-deposited W-Cr alloys containing 25-75 at % chromium was decreased significantlywith increasing chromium content and showed lowest corrosion rates (that is, 1.5-2.0 × 10-3 mm.y-1) after immersed for prolonged immersion in 1 M NaOH solution. The corrosion ratesof these nanocrystalline W-(25-75)Cr alloys are nearly two orders of magnitude lower thanthat of tungsten and more than one order of magnitude lower corrosion rate than that ofsputter-deposited chromium metal in 1 M NaOH solution. The corrosion-resistant of all theexamined sputter-deposited W-Cr alloys in 0.5 M NaCl solution is higher than in alkaline 1M NaOH solution at 25°C. Open circuit potentials of all the examined W-Cr alloys areshifted to more noble direction with increasing the chromium content in the alloys afterimmersion for 72 h in both 0.5 M NaCl and 1 M NaOH solutions at 25°C, open to air.Keywords: Sputter deposition, nanocrystalline W-Cr alloys, corrosion test, electrochemicalmeasurement, NaCl and NaOH solutions.DOI:  10.3126/jncs.v25i0.3300Journal of Nepal Chemical Society Volume 25, 2010 pp 53-61

Corrosion Behavior of Zr53.5Cu26.5Ni5Al12Ag3 Bulk Amorphous Alloy in 3.5% NaCl Solution

2011 ◽  
Vol 299-300 ◽  
pp. 427-431
Author(s):  
Yun Li ◽  
Shi Zhi Shang ◽  
Ming Cheng ◽  
Liang Xu ◽  
Shi Hong Zhang
Keyword(s):  
Corrosion Resistance ◽  
Amorphous Alloy ◽  
Passive Film ◽  
Corrosion Behavior ◽  
Electrochemical Impedance ◽  
Corrosion Current ◽  
Bulk Amorphous Alloy ◽  
Nacl Solution ◽  
Current Densities ◽  
Resistance Decrease

The corrosion behavior of Zr53.5Cu26.5Ni5Al12Ag3 bulk amorphous alloy in 3.5% NaCl solution was investigated by using potentiodynamic polarization experiments and electrochemical impedance spectroscopy (EIS). The results show that Zr53.5Cu26.5Ni5Al12Ag3 bulk amorphous alloy has the better corrosion resistance than its corresponding crystal alloy. During the bath in the 3.5% NaCl solution at 25°C, Zr53.5Cu26.5Ni5Al12Ag3 alloy has the lower corrosion current density than the corresponding crystal alloy. After 100h, the corrosion current densities of Zr53.5Cu26.5Ni5Al12Ag3 and the corresponding crystal alloy are 3.8415×10-8A/cm2 and 5.2827×10-7A/cm2, respectively. The results of EIS test indicate that Zr53.5Cu26.5Ni5Al12Ag3 bulk amorphous alloy has the excellent corrosion resistance because passive film with stable structure formed on the surface in 3.5% NaCl solution. With an increase in the immersion time, the passive film becomes thicker. It leads to impedance resistance and corrosion resistance decrease. The surface of Zr53.5Cu26.5Ni5Al12Ag3 bulk amorphous alloy in 3.5% NaCl solution for 100h was analyzed by SEM and EDS. The results show that the corrosive pitting can be found at both the amorphous alloy and the corresponding crystal alloy. However, the amorphous alloy has the better corrosive pitting resistance than the crystal one because the corrosion products formed by selective dissolving of Zr and Al elements. Moreover, the addition of Ag element helps to improve the corrosion resistance of the amorphous alloy greatly.

scholarly journals Experimental evaluation of corrosion resistance of the alloys used in the fixed dental prosthesis

2015 ◽  
Vol 61 (2) ◽  
pp. 117-120
Author(s):  
Costin Coman ◽  
◽  
Raluca Monica Comăneanu ◽  
Violeta Hâncu ◽  
Horia Mihail Barbu ◽  
...  
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Current Density ◽  
Applied Research ◽  
Open Circuit Potential ◽  
Corrosion Potential ◽  
Artificial Saliva ◽  
Corrosion Current ◽  
Open Circuit ◽  
Metal Alloys ◽  
Fixed Dental Prosthesis

Objectives. In this study we evaluated corrosion resistance of three types of metal alloys (two NiCr and one CoCr). Methods. Samples (coded A, B, C) of circular shape, with dimensions 13 x 1.5 mm, sanded and polished, were introduced in Fusayama Meyer artificial saliva at pH 5.2 and 37 ± 0.5°C and tested in terms of corrosion resistance with a potentiostat/galvanostat (model 4000 PARSTAT, Princeton Applied Research). Results. Open circuit potential EOC [mV] ranged between 21.316 and 5.75. Corrosion potential Ecor [mV] was between -73.536 and -395.662, and the corrosion current density icor [A/cm2] was between 1.237 x 10-6 and 905.13 x 10-9. Conclusion. The best corrosion behavior in Fusayama Meyer artificial saliva at pH 5.2 and at a temperature of 37 ± 0.5°C is the alloy A, followed by the alloy C.

scholarly journals Influence of Ultrasonic Excitation Sealing on the Corrosion Resistance of HVOF-Sprayed Nanostructured WC-CoCr Coatings under Different Corrosive Environments

Coatings ◽  
2019 ◽  
Vol 9 (11) ◽  
pp. 724 ◽  
Author(s):  
Zhang ◽  
Hong ◽  
Lin ◽  
Zheng
Keyword(s):  
Corrosion Resistance ◽  
Atmospheric Pressure ◽  
Room Temperature ◽  
Open Circuit Potential ◽  
Electrochemical Impedance ◽  
Corrosion Current ◽  
Aluminum Phosphate ◽  
Open Circuit ◽  
Corrosive Environments ◽  
Oxygen Fuel

The corrosion behavior of unsealed and sealed high-velocity oxygen-fuel (HVOF)-sprayed nanostructured WC-CoCr cermet coatings under different corrosive environments was investigated using scanning electron microscopy (SEM), open circuit potential (OCP), potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). Ultrasonic excitation sealing with aluminum phosphate was performed in an external ultrasonic bath with the frequency of 40 kHz at atmospheric pressure and room temperature. SEM micrographs revealed that the exposed area of the coating was effectively reduced by the coverage of aluminum phosphate sealant on the majority of pores. Electrochemical measurements demonstrated that the sealant with the help of ultrasonic energy could shift the corrosion potential to a more noble direction, reduce the corrosion current density, increase the resistance of charge transfer, and effectively improve the corrosion resistance of the coating in both 3.5 wt % NaCl and 1 mol·L−1 HCl solutions.

Effect of High-Intensity Pulsed Ion Beam Irradiation on the Electrochemical Corrosion Behavior of AZ31 Magnesium Alloy

2011 ◽  
Vol 189-193 ◽  
pp. 571-574
Author(s):  
Peng Li
Keyword(s):  
Corrosion Resistance ◽  
Magnesium Alloy ◽  
Corrosion Behavior ◽  
Current Density ◽  
Ion Beam ◽  
Electrochemical Corrosion ◽  
Corrosion Current ◽  
Open Circuit ◽  
Electrochemical Corrosion Behavior ◽  
Shot Number

HIPIB irradiation experiment is carried out at a specific ion current density of 1.1 J/cm2 with shot number from one to ten in order to explore the effect of shot number on electrochemical corrosion behavior of magnesium alloy. Surface morphologies, microstructure and corrosion resistance of the irradiated samples are examined by scanning electron microscopy (SEM), transmission electron microscope (TEM) and potentiodynamic polarization technique, respectively. It is found that HIPIB irradiation leads to the increase in open circuit potential, corrosion potential and breakdown potential, and the decrease in the corrosion current density and the corrosion rate as compared to the original sample. The improved corrosion resistance is mainly attributed to the grain refinement and surface purification induced by HIPIB irradiation.

scholarly journals The Corrosion Behavior of Sputter-deposited W-Ti Alloys in 0.5 M NaCl Solution

1970 ◽  
Vol 10 ◽  
pp. 109-113 ◽  
Author(s):  
Jagadeesh Bhattarai
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Behavior ◽  
Open Circuit ◽  
Nacl Solution ◽  
Corrosion Resistant ◽  
Corrosion Rates ◽  
Ti Alloys ◽  
Confocal Scanning ◽  
Confocal Scanning Laser ◽  
Sputter Deposited

The corrosion behavior of the sputter-deposited amorphous or nanocrystalline W-Ti alloys was studied in neutral 0.5 MNaCl solution at 25°C, open to air by immersion tests, electrochemical measurements and confocal scanning laser microscopic(CSLM) techniques. Titanium metal acts synergistically with tungsten in enhancing the corrosion resistance of the sputter-deposited W-Ti alloys so as to show higher corrosion resistance than those of alloy-constituting elements (that is, tungsten and titanium) in neutral 0.5 M NaCl solution. In particular, the amorphous W-Ti alloys containing 30-53 at% titanium showed lowest corrosion rates (that is, about 1 × 10-3 mm.y-1). Open circuit potentials of all the examined W-Ti alloys were shifted to more noble direction than those of the open circuit potentials of alloyconstituting elements in 0.5 M NaCl solution.Key words: Sputter deposition; W-Ti alloys; Corrosion-resistant; CSLM; NaCl solution.DOI: 10.3126/njst.v10i0.2899Nepal Journal of Science and Technology Volume 10, 2009 December Page:109-113 

scholarly journals Corrosion behavior of AH-36 steel in seawater

2020 ◽  
Vol 63 (9) ◽  
pp. 113-118
Author(s):  
Van Chi Nguyen ◽  
◽  
Nhat Linh Cao ◽  
Van Kien Dong ◽  
Hong Quan Le ◽  
...  
Keyword(s):  
Corrosion Behavior ◽  
Open Circuit Potential ◽  
Surface Passivation ◽  
Sample Surface ◽  
Open Circuit ◽  
Corrosion Process ◽  
Anodic Process ◽  
Natural Seawater ◽  
Nacl Solution ◽  
Over Time

In the present work, the corrosion behavior of AH-36 steel in 3% NaCl aqueous solution and natural seawater was studied using a three-electrode cell, Autolab PGSTAT 204N, and Nova 2.0 software by electrochemical methods. It has been established that after contact of the steel with chloride-containing media, the open circuit potential of steel shifts sharply to the negative region, which indicates a decrease in the corrosion resistance of steel in chloride-containing media. In seawater, the stabilization of the open circuit potential is observed within 60 min, and in NaCl solution – 120 min. The constant value of the open circuit potential of steel in seawater is in a more negative range compared to the constant value of the open circuit potential of steel in NaCl solution. In order to study the kinetics of the corrosion process of steel, polarization curves were obtained in the potentiostatic mode. It is shown that the corrosion potentials and currents of the samples decrease over time and tend to constant values. In all cases, the corrosion process in seawater occurs and stabilizes (within 20 min) faster than in NaCl solution. The anode Tafel coefficient takes a value in the range of 0.1-0.2 V, which may indicate the same mechanism of the anodic process. As a result of full-scale tests (Nha Trang, Vietnam), it can be seen that the steel samples are strongly susceptible to corrosion at the initial stage and over time the corrosion rate decreases and tends to a constant value (0.27 g/m2.h). This is due to the sample surface passivation during corrosion tests.

Corrosion Resistance of Modified Silane Films Formed on AZ31 Magnesium Alloys

2011 ◽  
Vol 686 ◽  
pp. 21-25
Author(s):  
Xian Long Cao ◽  
Fu Sheng Pan ◽  
Hong Da Deng ◽  
Wei Cai
Keyword(s):  
Corrosion Resistance ◽  
Magnesium Alloy ◽  
Corrosion Behavior ◽  
Open Circuit Potential ◽  
Electrochemical Impedance ◽  
Open Circuit ◽  
Chloride Ions ◽  
Cerium Nitrate ◽  
Az31 Magnesium Alloy ◽  
Sodium Chloride Solutions

This present work investigated the corrosion behavior of AZ31 magnesium alloy substrates pre-treated with bis-[triethoxysilylpropyl] tetrasulfide silane modified with cerium nitrate. The corrosion behavior of the pre-treated substrates in 0.005M sodium chloride solutions was assessed by potentiodynamic polarization, open circuit potential and electrochemical impedance spectroscopy (EIS). The results showed that the silane pre-treatments improved the corrosion resistance of the AZ31 magnesium alloy substrates in the presence of chloride ions. Especially the addition of cerium nitrate played an important role in reducing the corrosion activity.

Sign in / Sign up

Export Citation Format

Share Document