Effect of Y on Microstructure and Mechanical Properties of Mg-6Al-1Zn-1.8Gd Magnesium Alloy

2014 ◽  
Vol 1035 ◽  
pp. 303-306
Author(s):  
Xiao Ya Chen ◽  
Quan An Li ◽  
Qing Zhang ◽  
Jun Chen ◽  
Hui Zhen Jiang
Keyword(s):  
Mechanical Properties ◽  
Mechanical Property ◽  
Tensile Strength ◽  
High Temperature ◽  
Room Temperature ◽  
Tensile Tests ◽  
High Mechanical Property ◽  
Microstructure And Mechanical Properties ◽  
Micro Analysis ◽  
Very High

The microstructure and mechanical properties of Mg-6Al-1Zn-0.9Y-1.8Gd alloy have been studied by micro-analysis and tensile tests. The results showed that the alloy mainly consists of Mg matrix, Al2Y, Mg17Al12and Al2Gd. The best tensile strength of the alloy was 255 Mpa at room temperature, and the alloy still had the very high mechanical property at high temperature.

Microstructure and Mechanical Properties of a Novel Ti-6.5Al-2Sn-4Zr-1.5Mo-2Nb-0.25Fe-0.2Si High-Temperature Titanium Alloy

2020 ◽  
Vol 993 ◽  
pp. 351-357
Author(s):  
Ming Yu Zhao ◽  
Xiao Yun Song ◽  
Wen Jing Zhang ◽  
Yu Wei Diao ◽  
Wen Jun Ye ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
Room Temperature ◽  
Annealing Treatment ◽  
Tensile Tests ◽  
Electron Backscattered Diffraction ◽  
Two Phase ◽  
Bimodal Structure ◽  
Α Phase ◽  
Microstructure And Mechanical Properties

The Ti-6.5Al-2Sn-4Zr-1.5Mo-2Nb-0.25Fe-0.2Si (wt%) alloy is a novel two-phase high temperature alloy for short-term application. The effects of different heat treatments on the microstructure and mechanical properties were investigated through electron probe microanalysis (EPMA), optical microcopy (OM), scanning electron microscope (SEM), electron backscattered diffraction (EBSD) and tensile tests at room temperature and 650°C. Subjected to the annealing treatment at α+β region (1010 °C/2 h, FC to 990 °C+990 °C/2 h, AC), the microstructure was composed of bimodal structure, which consists of equiaxed primary α (αp) phase and lamellar transformed β (βt) structure. As a strong β stabilizer, the content of Fe in α phase is much less than that in β phase. Annealing at β region (1040 °C/2 h, AC) resulted in the formation of widmannstatten structure, consisting of coarse raw β grain and secondary α phase precipitated on the β grain. With respect to the tensile property, different heat-treated alloys obtained similar strength. However, widmannstatten structure was characterized by lower plasticity, with the elongation only half that of bimodal structure. The fracture characteristics at room temperature for the alloy with bimodal structure and widmannstatten structure are dominated by ductile fracture and cleavage fracture, respectively.

Microstructure and Mechanical Properties of Mg-9Gd-2Y-1Sm-0.5Zr Alloy

2014 ◽  
Vol 488-489 ◽  
pp. 205-208
Author(s):  
Xiao Ya Chen ◽  
Quan An Li ◽  
Hui Zhen Jiang ◽  
Lei Lei Chen
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Tensile Tests ◽  
Microstructure And Mechanical Properties ◽  
Micro Analysis

The microstructure and mechanical properties of Mg-9Gd-2Y-1Sm-0.5Zr alloy have been studied by micro-analysis and tensile tests. The results showed that the alloy mainly consists of α-Mg matrix, Mg5Gd and Mg24Y5. With the increase of temperature, the tensile strength of the alloy increases at first and then decreases, and the peak appears at 250°C.

Microstructure and Mechanical Properties of AZ81 Magnesium Alloy after Unequal Channel Angular Pressing

2013 ◽  
Vol 749 ◽  
pp. 343-348
Author(s):  
Xiao Ping Luo ◽  
Ming Gang Zhang ◽  
Jun Qi Zhou
Keyword(s):  
Mechanical Properties ◽  
Mechanical Property ◽  
Plastic Deformation ◽  
Tensile Strength ◽  
High Temperature ◽  
Magnesium Alloy ◽  
Pressing Temperature ◽  
Angular Pressing ◽  
Microstructure And Mechanical Properties ◽  
Tensile Fractures

The microstructure and mechanical properties of AZ81magnesium alloys after unequal channel angular pressing (UCAP) was investigated using self-made 90° die under different temperature. The results showed that under the same pressing speed, there was a better grain refinement and mechanical property improvement with the decreasing of pressing temperature, however, the tiny cracks on the surface of the processed samples increased. When squeezed at 250 , the average grain was refined from the initial 150um to10um. The tensile strength was changed to 350Mpa, and the elongation was of 10. Tensile fractures presented the increment of dimples structure, which was the result of refined α-Mg matrix and intermetallic compound β-Mg17Al12 phase by severe shear and plastic deformation at high temperature press.

scholarly journals Effects of Different Solid Solution Temperatures on Microstructure and Mechanical Properties of the AA7075 Alloy After T6 Heat Treatment

2019 ◽  
Vol 38 (2019) ◽  
pp. 892-896 ◽  
Author(s):  
Süleyman Tekeli ◽  
Ijlal Simsek ◽  
Dogan Simsek ◽  
Dursun Ozyurek
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Solid Solution ◽  
Tensile Strength ◽  
Tensile Tests ◽  
Solution Temperature ◽  
T6 Heat Treatment ◽  
Microstructure And Mechanical Properties ◽  
Different Temperatures

AbstractIn this study, the effect of solid solution temperature on microstructure and mechanical properties of the AA7075 alloy after T6 heat treatment was investigated. Following solid solution at five different temperatures for 2 hours, the AA7075 alloy was quenched and then artificially aged at 120∘C for 24 hours. Hardness measurements, microstructure examinations (SEM+EDS, XRD) and tensile tests were carried out for the alloys. The results showed that the increased solid solution temperature led to formation of precipitates in the microstructures and thus caused higher hardness and tensile strength.

Influence of Heat Treatment on Microstructure and Mechanical Properties of Selective Laser Melted TiAl6V4 Alloy

2018 ◽  
Vol 284 ◽  
pp. 615-620 ◽  
Author(s):  
R.M. Baitimerov ◽  
P.A. Lykov ◽  
L.V. Radionova
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Selective Laser Melting ◽  
Room Temperature ◽  
Base Alloy ◽  
Tensile Tests ◽  
Heat Treatments ◽  
Laser Melting ◽  
Microstructure And Mechanical Properties ◽  
Treatment Procedures

TiAl6V4 titanium base alloy is widely used in aerospace and medical industries. Specimens for tensile tests from TiAl6V4 with porosity less than 0.5% was fabricated by selective laser melting (SLM). Specimens were treated using two heat treatment procedures, third batch of specimens was tested in as-fabricated statement after machining. Tensile tests were carried out at room temperature. Microstructure and mechanical properties of SLM fabricated TiAl6V4 after different heat treatments were investigated.

Manufacturing and High Temperature Mechanical Properties of Inconel 713C by Using Metal Injection Molding

2012 ◽  
Vol 602-604 ◽  
pp. 627-630 ◽  
Author(s):  
Kyu Sik Kim ◽  
Kee Ahn Lee ◽  
Jong Ha Kim ◽  
Si Woo Park ◽  
Kyu Sang Cho
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
Injection Molding ◽  
Room Temperature ◽  
Tensile Tests ◽  
Metal Injection Molding ◽  
Injection Molding Process ◽  
Molding Process ◽  
High Temperature Mechanical Properties ◽  
Inconel 713C

Inconel 713C alloy was tried to manufacture by using MIM(Metal Injection Molding) process. The high-temperature mechanical properties of MIMed Inconel 713C were also investigated. Processing defects such as pores and binders could be observed near the surface. Tensile tests were conducted from room temperature to 900°C. The result of tensile tests showed that this alloy had similar or somewhat higher strengths (YS: 734 MPa, UTS: 968 MPa, elongation: 7.16 % at room temperature) from RT to 700°C than those of conventional Inconel 713C alloys. Above 800°C, however, ultimate tensile strength decreased rapidly with increasing temperature (lower than casted Inconel 713C). Based on the observation of fractography, initial crack was found to have started near the surface defects and propagated rapidly. The superior mechanical properties of MIMed Inconel 713C could be obtained by optimizing the MIM process parameters.

Effect of Hot Processing on Mircrostructure and Properties of Flat Billets of TA15 Titanium Alloy

2021 ◽  
Vol 1016 ◽  
pp. 906-910
Author(s):  
Xin Hua Min ◽  
Cheng Jin
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Titanium Alloy ◽  
High Temperature ◽  
Room Temperature ◽  
High Strength ◽  
Slow Cooling ◽  
Microstructure And Mechanical Properties ◽  
Ta15 Titanium Alloy ◽  
The Ideal

In this paper,effect of the different forging processes on the microstructure and mechanical properties of the flat flat billets of TA15 titanium alloy was investigated.The flat billiets of 80 mm×150 mm×L sizes of TA15 titanium alloy are produced by four different forging processes.Then the different microstrure and properties of the flat billiets were obtained by heat treatment of 800 °C~850 °C×1 h~4h.The results show that, adopting the first forging temperature at T1 °C、slow cooling and the second forging temperature at T2°C 、quick cooling, the primary αphases content is just 10%, and there are lots of thin aciculate phases on the base. This microstructure has both high strength at room temperature and high temperature, while the properties between the cross and lengthwise directions are just the same. So the hot processing of the first forging temperature at T1 °C、slow cooling and the second forging temperature at T2°C 、quick cooling is choosed as the ideal processing for production of aircraft frame parts.

Effect of Fast Annealing on Microstructure and Mechanical Properties of Non-Oriented Al-Si Low C Electrical Steels

2007 ◽  
Vol 560 ◽  
pp. 29-34 ◽  
Author(s):  
Emmanuel Gutiérrez C. ◽  
Armando Salinas-Rodríguez ◽  
Enrique Nava-Vázquez
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Room Temperature ◽  
Tensile Tests ◽  
Rate Of Change ◽  
Uniaxial Tensile ◽  
Electrical Steels ◽  
Offset Yield Strength ◽  
Microstructure And Mechanical Properties ◽  
Increasing Temperature

The effects of heating rate and annealing temperature on the microstructure and mechanical properties of cold rolled Al-Si, low C non-oriented electrical steels are investigated using SEM metallography and uniaxial tensile tests. The experimental results show that short term annealing at temperatures up to 850 °C result in microstructures consisting of recrystallized ferrite grains with sizes similar to those observed in industrial semi-processed strips subjected to long term batch annealing treatments. Within the temperature range investigated, the grain size increases and the 0.2% offset yield strength decreases with increasing temperature. It was observed that the rate of change of grain size with increasing temperature increases when annealing is performed at temperatures greater than Ac1 (~870 °C). This effect is attributed to Fe3C dissolution and rapid C segregation to austenite for annealing temperatures within the ferrite+austenite phase field. This leads to faster ferrite growth and formation of pearlite when the steel is finally cooled to room temperature. The presence of pearlite at room temperature decreases the ductility of samples annealed at T > Ac1.

Microstructure and Mechanical Properties of Mg-Based Composites Reinforced with TiB2 Particles

2014 ◽  
Vol 900 ◽  
pp. 141-145 ◽  
Author(s):  
Can Feng Fang ◽  
Guang Xu Liu ◽  
Ling Gang Meng ◽  
Xing Guo Zhang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Composite Material ◽  
High Temperature ◽  
The Self ◽  
Al Alloy ◽  
Temperature Synthesis ◽  
Microstructure And Mechanical Properties ◽  
High Temperature Synthesis

The effects of in-situ TiB2 particle fabricated from Al-Ti-B system via the self-propagating high-temperature synthesis (SHS) reaction technology on microstructure and mechanical properties of Mg-Sn-Zn-Al alloy were investigated. The results indicate that the size of the Mg2Sn and α-Mg+Mg32(Al,Zn)49 phase becomes coarser with the increasing content of Al-Ti-B preform, meanwhile the amount of eutectic α-Mg+Mg32(Al,Zn)49 phase increases too. The addition of Al-Ti-B is favorable toward promoting the strength of composites, but deteriorates elongation. The resulting as-extruded composite material with 4 wt.% Al-Ti-B preform exhibits good overall mechanical properties with an ultimate tensile strength of 291 MPa and an elongation over 2 %.

Effect of High Temperature Caliber Rolling on Microstructure and Room Temperature Tensile Properties of Mg-3Al-1Zn (AZ31) Alloy

2013 ◽  
Vol 209 ◽  
pp. 6-9 ◽  
Author(s):  
Rajendra Doiphode ◽  
S.V.S. Narayana Murty ◽  
Nityanand Prabhu ◽  
Bhagwati Prasad Kashyap
Keyword(s):  
Tensile Strength ◽  
High Temperature ◽  
Yield Strength ◽  
Strain Rate ◽  
Tensile Properties ◽  
Room Temperature ◽  
Tensile Tests ◽  
Az31 Alloy ◽  
Rolling Temperature ◽  
Grain Sizes

Mg-3Al-1Zn (AZ31) alloy was caliber rolled at 250, 300, 350, 400 and 450 °C. The effects of caliber rolling temperature on the microstructure and tensile properties were investigated. The room temperature tensile tests were carried out to failure at a strain rate of 1 x 10-4s-1. The nature of stress-strain curves obtained was found to vary with the temperature employed in caliber rolling. The yield strength and tensile strength followed a sinusoidal behaviour with increasing caliber rolling temperature but no such trend was noted in ductility. These variations in tensile properties were explained by the varying grain sizes obtained as a function of caliber rolling temperature.

Sign in / Sign up

Export Citation Format

Share Document