Preparation and CO2 Gas Sensitive Properties of CuO-SrTiO3-Based Semiconductor Thin Films

2007 ◽  
Vol 280-283 ◽  
pp. 311-314 ◽  
Author(s):  
Yan Fei Gu ◽  
Hui Ming Ji ◽  
Bin Zhang ◽  
Ting Xian Xu
Keyword(s):  
Thin Films ◽  
Chelating Agents ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
Good Resistance ◽  
Gas Sensitivity ◽  
X Ray ◽  
Semiconductor Thin Films ◽  
Wide Range ◽  
Ft Ir

CuO-SrTiO3-based thin films were prepared by novel sol-gel technology on Al2O3 substrates using Cu(NO3)2, SrCl2 and TiCl4 as the starting materials, critic acid and ethylene glycol as chelating agents. CO2 sensing properties of the films were investigated. Structure characteristics of the sol and asgrown thin films were analyzed by FT-IR spectrum, X-ray diffraction and SEM. The results reveal that the films consisted of CuO phase and SrTiO3 phase have nanocrystalline microstructure at 750°C for 40 min. The modified CuO-SrTiO3 thin films exhibit good resistance-temperature and gas sensitivity properties in a wide range of temperature. The films exposed to 6% CO2 show that sensitivity are 32, and response and recover time are within 2 s at 250 °C operating temperature.

scholarly journals Structural and magnetic studies on Co-Zn nanoferrite synthesized via sol-gel and combustion methods

2019 ◽  
Vol 37 (1) ◽  
pp. 39-54 ◽  
Author(s):  
B.B.V.S. Vara Prasad ◽  
K.V. Ramesh ◽  
A. Srinivas
Keyword(s):  
Citric Acid ◽  
Chelating Agents ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
Gel Method ◽  
X Ray ◽  
Sol Gel Method ◽  
Three Samples ◽  
Crystallite Sizes ◽  
Ft Ir

AbstractCo–Zn nanocrystalline ferrites with chemical composition Co0:5Zn0:5Fe2O4 were synthesized by sol-gel and combustion methods. The sol-gel method was carried out in two ways, i.e. based on chelating agents PVA and PEG of high and low molecular weights. In auto-combustion method, the ratio of citric acid to metal nitrate was taken as 1:1, while in sol-gel method the chelating agents were taken based on oxygen balance. All the three samples were studied by thermogravimetric and differential thermal analysis for the identification of phase formation and ferritization temperature. The synthesized samples were characterized by powder X-ray diffraction and FT-IR spectroscopy without any thermal treatment. The measured lattice constants and observed characteristic IR absorption bands of the three samples are in good agreement with the reported values showing the formation of a cubic spinel structure. The crystallite sizes of all samples were determined using high intensity peaks and W-H plot. Size-Strain Plot method was also implemented since two of the samples showed low crystallite sizes. The least crystallite size (5.5 nm) was observed for the sample CZVP while the highest (23.8 nm) was observed for the sample CZCA. Cation distribution was proposed based on calculated and observed intensity ratios of selected planes from X ray diffraction data. All structural parameters were presented using experimental lattice constant and oxygen positional parameter, and they correlated with FT-IR results. Magnetic measurements were carried out using vibrating sample magnetometer at room temperature to obtain the characteristic parameters such as saturation magnetization, coercivity, remanence, squareness ratio and Bohr magnetons. Among all, the sample synthesized via citric acid autocombustion method displayed a remarkably higher magnetization of 53 emu/g and the remaining two samples displayed low magnetization values owing to their smaller crystallite sizes.

scholarly journals Multidimensional Ln-Aminophthalate Photoluminescent Coordination Polymers

Materials ◽  
2021 ◽  
Vol 14 (7) ◽  
pp. 1786
Author(s):  
Carla Queirós ◽  
Chen Sun ◽  
Ana M. G. Silva ◽  
Baltazar de Castro ◽  
Juan Cabanillas-Gonzalez ◽  
...  
Keyword(s):  
Water Content ◽  
Coordination Polymers ◽  
Metal Ion ◽  
Low Cost ◽  
Microwave Assisted Synthesis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Wide Range ◽  
Ft Ir ◽  
Ft Ir Spectroscopy

The development of straightforward reproducible methods for the preparation of new photoluminescent coordination polymers (CPs) is an important goal in luminescence and chemical sensing fields. Isophthalic acid derivatives have been reported for a wide range of applications, and in addition to their relatively low cost, have encouraged its use in the preparation of novel lanthanide-based coordination polymers (LnCPs). Considering that the photoluminescent properties of these CPs are highly dependent on the existence of water molecules in the crystal structure, our research efforts are now focused on the preparation of CP with the lowest water content possible, while considering a green chemistry approach. One- and two-dimensional (1D and 2D) LnCPs were prepared from 5-aminoisophthalic acid and Sm3+/Tb3+ using hydrothermal and/or microwave-assisted synthesis. The unprecedented LnCPs were characterized by single-crystal X-ray diffraction (SCRXD), powder X-ray diffraction (PXRD), Fourier transform infrared (FT-IR) spectroscopy and scanning electron microscopy (SEM), and their photoluminescence (PL) properties were studied in the solid state, at room temperature, using the CPs as powders and encapsulated in poly(methyl methacrylate (PMMA) films, envisaging the potential preparation of devices for sensing. The materials revealed interesting PL properties that depend on the dimensionality, metal ion, co-ligand used and water content.

Luminescent Properties of Zn2SiO4:Eu3+,Dy3+ Phosphors via Sol-Gel Process

2012 ◽  
Vol 217-219 ◽  
pp. 733-736
Author(s):  
Xiu Mei Han ◽  
Shu Ai Hao ◽  
Ying Ling Wang ◽  
Gui Fang Sun ◽  
Xi Wei Qi
Keyword(s):  
Thermal Analysis ◽  
Ir Spectra ◽  
Sol Gel ◽  
Luminescent Properties ◽  
Photoluminescence Spectra ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process ◽  
Ft Ir

Zn2SiO4:Eu3+, Dy3+ phosphors have been prepared through the sol-gel process. X-ray diffraction (XRD), thermogravimetric and ddifferential thermal analysis (TG-DTA), FT-IR spectra and photoluminescence spectra were used to characterize the resulting phosphors. The results of XRD indicated that the phosphors crystallized completely at 1000oC. In Zn2SiO4:Eu3+,Dy3+ phosphors, the Eu3+ and Dy3+ show their characteristic red(613nm, 5D0-7F2), blue (481nm, 4F9/2–6H15/2) and yellow (577nm, 4F9/2–6H13/2) emissions.

ITO Thin Films on Silicon Buffer by Sol Gel Method

2006 ◽  
Vol 514-516 ◽  
pp. 1155-1160 ◽  
Author(s):  
Talaat Moussa Hammad
Keyword(s):  
Thin Films ◽  
Indium Tin Oxide ◽  
Optical Transmission ◽  
Sol Gel ◽  
Precursor Solution ◽  
Charge Carriers ◽  
X Ray Diffraction ◽  
X Ray ◽  
Ito Thin Films ◽  
Uv Visible

Sol gel indium tin oxide thin films (In: Sn = 90:10) were prepared by the sol-gel dipcoating process on silicon buffer substrate. The precursor solution was prepared by mixing SnCl2.2H2O and InCl3 dissolved in ethanol and acetic acid. The crystalline structure and grain orientation of ITO films were determined by X-ray diffraction. The surface morphology of the films was characterized by scanning electron microscope (SEM). Optical transmission and reflectance spectra of the films were analyzed by using a UV-visible spectrophotometer. The transport properties of majority charge carriers for these films were studied by Hall measurement. ITO thin film with electrical resistivity of 7.6 ×10-3 3.cm, Hall mobility of approximately 2 cm2(Vs)-1 and free carrier concentration of approximately 4.2 ×1020 cm-3 are obtained for films 100 nm thick films. The I-V curve measurement showed typical I-V characteristic behavior of sol gel ITO thin films.

Characterization of SrBi2Nb2O9 Thin Films Prepared by Sol Gel Technique

1996 ◽  
Vol 459 ◽  
Author(s):  
E. Ching-Prado ◽  
W. Pérez ◽  
A. Reynés-Figueroa ◽  
R. S. Katiyar ◽  
D. Ravichandran ◽  
...  
Keyword(s):  
Thin Films ◽  
Raman Band ◽  
Sol Gel ◽  
Orthorhombic Symmetry ◽  
X Ray Diffraction ◽  
Ft Ir ◽  
Gel Technique ◽  
High Degree ◽  
First Time

ABSTRACTThin films of SrBi2Nb2O9 (SBN) with thicknesses of 0.1, 0.2, and 0.4 μ were grown by Sol-gel technique on silicon, and annealed at 650°C. The SBN films were investigated by Raman scatering for the first time. Raman spectra in some of the samples present bands around 60, 167, 196, 222, 302, 451, 560, 771, 837, and 863 cm−1, which correspond to the SBN formation. The study indicates that the films are inhomogeneous, and only in samples with thicknesses 0.4 μ the SBN material was found in some places. The prominent Raman band around 870 cm−1, which is the A1g mode of the orthorhombic symmetry, is assigned to the symmetric stretching of the NbO6 octahedrals. The frequency of this band is found to shift in different places in the same sample, as well as from sample to sample. The frequency shifts and the width of the Raman bands are discussed in term of ions in non-equilibrium positions. FT-IR spectra reveal a sharp peak at 1260 cm−1, and two broad bands around 995 and 772 cm−1. The bandwidths of the latter two bands are believed to be associated with the presence of a high degree of defects in the films. The experimental results of the SBN films are compared with those obtained in SBT (T=Ta) films. X-ray diffraction and SEM techniques are also used for the structural characterization.

Sol-Gel derived Bi4-xNdxTi3O12 Thin Films and Their Characterization

2002 ◽  
Vol 737 ◽  
Author(s):  
R.E. Melgarejo ◽  
M.S. Tomar ◽  
A. Hidalgo ◽  
R.S. Katiyar
Keyword(s):  
Thin Films ◽  
Spin Coating ◽  
Bismuth Titanate ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
X Ray ◽  
Complete Solid Solution ◽  
Sol Gel Process ◽  
Ferroelectric Memory ◽  
Initial Results

ABSTRACTNd substituted bismuth titanate Bi4-xNdxTi3O12 were synthesized by sol-gel process and thin films were deposited on Pt substrate (Pt/TiO2/SiO2/Si) by spin coating. Thin films, characterized by X-ray diffraction and Raman spectroscopy, shows complete solid solution up to the composition x < 1. Initial results indicate that the ferroelectric polarization increases with increasing Nd content in the film with 2Pr = 50μC/cm2 for x = 0.46, which may have application in non-volatile ferroelectric memory devices.

Synthesis, Characterization and Optical Properties of PLA / P3HT Blends Thin Films

2021 ◽  
Vol 19 (5) ◽  
pp. 132-138
Author(s):  
Maan Abd-Alameer Salih ◽  
Q.S. Kareem ◽  
Mohammed Hadi Shinen
Keyword(s):  
Thin Films ◽  
Optical Properties ◽  
Spin Coating ◽  
Ring Opening ◽  
Energy Gap ◽  
Ring Opening Polymerization ◽  
X Ray Diffraction ◽  
X Ray ◽  
Conductivity Increase ◽  
Ft Ir

In this exploration Poly lactic corrosive (PLA) was orchestrated the ring-opening polymerization Poly lactic corrosive (PLA) blended with poly(3-hexylthiophene) (P3HT) which prepared by solution. Blends thin films Synthesis by spin coating technique and using Tetrahydrofuran (THF) as solvent. PLA powder was 'characterized by' 'X-ray' 'diffraction', '(FT-IR)'. pure Optical properties (PLA), (PLA)/P3HT blends thin films with different percentage of P3HT (0, 1, 2, and 3) wt% were investigated using UV-VS spectroscopy The results showed that the absorption, absorption coefficient, extinction coefficient and conductivity increase with increasing the rate of deformation P3HT, The energy gap decreases with increasing deformation.

Synthesis and Characterizations of Strontium Substituted Hydroxyapatite Thin Films

2010 ◽  
Vol 93-94 ◽  
pp. 231-234
Author(s):  
B. Hongthong ◽  
Satreerat K. Hodak ◽  
Sukkaneste Tungasmita
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Composition ◽  
Spin Coating ◽  
Phase Structure ◽  
Sol Gel ◽  
Cross Linking ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process

Strontium substituted hydroxyapatite(SrHAp) were fabricated both in the form of powder as reference and thin film by using inorganic precursor reaction. The sol-gel process has been used for the deposition of SrHAp layer on stainless steal 316L substrate by spin coating technique, after that the films were annealed in air at various temperatures. The chemical composition of SrHAp is represented (SrxCa1-x)5(PO4)3OH, where x is equal to 0, 0.5 and 1.0. Investigations of the phase structure of SrHAp were carried out by using X-ray diffraction technique (XRD). The results showed that strontium is incorporated into hydroxyapatite where its substitution for calcium increases in the lattice parameters, and Sr3(PO4)2 can be detected at 900°C. The SEM micrographs showed that SrHAp films exhibited porous structure before develop to a cross-linking structure.

Preparation and Photocatalytic Properties of Rod-Shaped TiO2 Based on Salix Fiber

2014 ◽  
Vol 609-610 ◽  
pp. 250-254
Author(s):  
Ya Bin Li ◽  
Jin Tian Huang ◽  
Yan Fei Pan
Keyword(s):  
Photocatalytic Performance ◽  
Sol Gel ◽  
Average Diameter ◽  
X Ray Diffraction ◽  
Nanocomposite Structure ◽  
X Ray ◽  
Infrared Spectrometer ◽  
Ft Ir ◽  
Degradation Of Methyl Orange ◽  
Scanning Electron

In the paper, the TiO2nanomaterials adopted the microcrystalline cellulose as the template by the template method and sol-gel method was prepared. Through the infrared spectrometer (FT-IR), scanning electron microscope (SEM), X-ray diffraction (XRD), the surface morphology, composition and the type of the samples were characterized respectively. The influence of the macro morphology of TiO2photocatalytic performance to use the reaction of decolorization and degradation of methyl orange as model was analyzed. The results showed that TiO2which was produced by the template of sallix fiber was Rod-shaped and the average diameter size of nanocomposite structure was 20.592 nm, which can provide a new method of producing other morphology of TiO2.

Preparation of CuS/SiO2 Composite Modified Aerogel and Its Superoleophobic and Photocatalytic Properties

NANO ◽  
2020 ◽  
Vol 15 (02) ◽  
pp. 2050017
Author(s):  
Ke-Cheng Yang ◽  
Li-Hui Xu ◽  
Hong Pan ◽  
Li-Ming Wang ◽  
Yong Shen ◽  
...  
Keyword(s):  
Gas Adsorption ◽  
Ambient Pressure ◽  
Sol Gel ◽  
Photocatalytic Properties ◽  
X Ray Diffraction ◽  
Sliding Angle ◽  
Nitrogen Gas ◽  
Ir Spectrometry ◽  
X Ray ◽  
Ft Ir

In this study, CuS/SiO2 composite modified aerogel was prepared by the incorporation of hollow spherical CuS into methyltrimethoxysilane-based SiO2 sol and modification with hexadecafluorodecyltriethoxysilane via acid-base catalyzed sol–gel reaction and drying under ambient pressure. The CuS/SiO2 composite modified aerogel was characterized by Fourier-transform infrared (FT-IR) spectrometry, scanning electron microscope (SEM), nitrogen gas adsorption and desorption and X-ray diffraction (XRD), respectively. The effects of CuS and fluorosilane concentration on density and porosity of aerogel, oleophobic and photocatalytic properties were evaluated. The results showed that structure and physical properties of aerogel had some effect by introducing CuS and fluorosilane, and the CuS/SiO2 composite modified aerogel with density of 0.146[Formula: see text]g/cm3 and specific surface area of 241[Formula: see text]m2/g achieved super-oleophobicity with oil contact angle of 152.8∘ and sliding angle of 10∘, and good photocatalytic properties for methylene blue.