Influence of Duplex Treatment on Structural and Tribological Properties of Commercially Pure Titanium

2017 ◽  
Vol 36 (1) ◽  
pp. 63-68 ◽  
Author(s):  
Ilhan Çelik
Keyword(s):  
Wear Resistance ◽  
Tribological Properties ◽  
Physical Vapor Deposition ◽  
Plasma Nitriding ◽  
Pure Titanium ◽  
Surface Hardness ◽  
Compound Layer ◽  
Commercially Pure Titanium ◽  
Wear Properties ◽  
Commercially Pure

AbstractTitanium and its alloys are widely used in many fields, including aerospace and the chemical and biomedical industries. This is due to their mechanical properties, excellent corrosion resistance, and biocompatibility although they do have poor wear resistance. In this study, a duplex layer was successfully formed on the commercially pure titanium surface by duplex treatments (plasma nitriding and physical vapor deposition (PVD)). In the initial treatment, plasma nitriding was performed on the pure titanium samples and in the second treatment, the nitrided samples were coated with CrN by PVD. The friction and wear properties of the duplex-treated samples were investigated for tribological applications. Surface morphology and microstructure of the duplex-treated samples were analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). In addition, the tribological properties were investigated using pin-on-disc tribometer. A compound layer composed of ε-Ti2N and δ-TiN phases and a diffusion layer formed under the compound layer were obtained on the surface of pure titanium after the nitriding treatments. CrN coated on the nitrided surface provided an increase in the surface hardness and in the wear resistance.

Structure and Phase Composition of a Ti Film–Al Substrate System Irradiated with an Intense Pulsed Electron Beam

2018 ◽  
Vol 781 ◽  
pp. 101-107
Author(s):  
Yurii Ivanov ◽  
Olga V. Krysina ◽  
Pavel Moskvin ◽  
Elizaveta A. Petrikova ◽  
Olga V. Ivanova ◽  
...  
Keyword(s):  
Wear Resistance ◽  
Electron Beam ◽  
High Surface ◽  
Pure Titanium ◽  
Surface Hardness ◽  
Vacuum Arc ◽  
High Wear Resistance ◽  
Commercially Pure Titanium ◽  
Plasma Cathode ◽  
Commercially Pure

Commercially pure A7 aluminum was exposed to surface modification in a single vacuum cycle which included vacuum arc evaporation and deposition of commercially pure titanium and intense electron beam irradiation and melting of the film–substrate system using a plasma-cathode pulsed electron source. The deposited Ti film thickness was 0.5 and 1 μm. The irradiated Ti–Al system revealed a multilayer multiphase structure consisting of submicro-and nanosized elements with intermetallic inclusions Al3Ti, Al2Ti, and TiAl3. The Ti film during irradiation broke up into fragments with their immersion in the molten Al surface layer to a depth of 20 μm. The modified material surpassed the initial aluminum in wear resistance by a factor of 2.4 and in microhardness by a factor larger than 4. The main cause for the high surface hardness and high wear resistance of the modified aluminum was likely the formation of both the intermetallic particles and the Ti-hardened transition layer.

Effects of Plasma Nitriding and TiN Coating Duplex Treatment on Wear Resistance of Commercially Pure Titanium

2011 ◽  
Vol 217-218 ◽  
pp. 1050-1055 ◽  
Author(s):  
Yu Tong ◽  
Tian Wen Guo ◽  
Jing Wang ◽  
Hai Feng Liang ◽  
Mi Qian
Keyword(s):  
Wear Resistance ◽  
Plasma Nitriding ◽  
Pure Titanium ◽  
Surface Characteristics ◽  
Film Deposition ◽  
Commercially Pure Titanium ◽  
Tin Film ◽  
Commercially Pure ◽  
Duplex Treatment ◽  
Ball On Disc

The commercially pure(CP) titanium specimens were modified with Direct current(DC) plasma nitriding and arc ion plating of TiN film. The duplex treated titanium samples were characterized by scanning electron microscopy(SEM), microhardness tester and ball-on-disc tribotester. The results showed that the duplex treated CP titanium appeared uniform and bright golden, microhardness and wear resistance improved substantially and were superior to that of only TiN coated ones. All these results indicate plasma nitriding and TiN film deposition duplex treatment can improve surface characteristics of CP titanium significantly. The method can be applied to the titanium denture to improve the tribological properties and color.

The Influence of Laser Irradiation Parameters on Tribological Behaviour of Commercially Pure Titanium for Dental Prostheses

2016 ◽  
Author(s):  
Karibeeran Shanmuga Sundaram ◽  
Gurusami Kiliyappan ◽  
Senthil Kumaran Selvadurai
Keyword(s):  
Surface Roughness ◽  
Wear Resistance ◽  
Pure Titanium ◽  
Laser Surface ◽  
Commercially Pure Titanium ◽  
Laser Shock ◽  
Micro Hardness ◽  
Dental Prostheses ◽  
Commercially Pure ◽  
Cp Ti

Laser shock peening (LSP) is one of the innovative technique that produces a compressive residual stress on the surface of metallic materials, thereby significantly increasing its fatigue life in applications where failure is caused by surface-initiated cracks. The specimens were treated with laser shock waves with different processing parameters, and characterization studies were made on treated specimens. The purpose of the present study was to investigate the influence of Nd:YAG laser on commercially pure titanium (CP-Ti) used in prosthetic dental restorations. The treatment influenced change in microstructure, micro hardness, surface roughness, and wear resistance characteristics. Though CP-Ti is considered as an excellent material for dental applications due to its outstanding biocompatibility, it is not suitable when high mastication forces are applied. In the present study, pulsed Nd:YAG laser surface treatment technique was adopted to improve the wear resistance of CP-Ti. The wear test pin specimens of CP-Ti were investment cast with centrifugal titanium casting machine. The wear properties of specimens were evaluated after LSP on a “pin-on-disc” wear testing tribometer, as per ASTM G99-05 standards. The results of the wear experiment showed that the treated laser surface has higher wear resistance, micro hardness, and surface roughness compared to as-cast samples. The improvement of wear resistance may be attributed due to grain refinement imparted by LSP processes. The microstructure, wear surfaces, wear debris, and morphology of the specimen were analyzed by using optical electron microscope, scanning electron microscope, and X-ray diffraction (XRD). The data were compared using ANOVA and post-hoc Tukey tests. The characteristic change resulted in increase in wear resistance and decrease in wear rate. Hence, it is evident that the more reliable and removable partial denture metal frameworks for dental prostheses may find its applications.

EFFECT OF NITROGEN AMOUNT ON TRIBOLOGICAL BEHAVIOR OF PLASMA NITRIDED 31CrMoV9 STEEL

2019 ◽  
Vol 26 (07) ◽  
pp. 1850217 ◽  
Author(s):  
O. ÇOMAKLI ◽  
A. F. YETIM ◽  
B. KARACA ◽  
A. ÇELIK
Keyword(s):  
Wear Resistance ◽  
Tribological Behavior ◽  
Wear Behavior ◽  
Plasma Nitriding ◽  
Surface Hardness ◽  
Compound Layer ◽  
Gas Mixture ◽  
X Ray Diffraction ◽  
X Ray ◽  
Pin On Disk

The 31CrMoV9 steels were plasma nitrided under different gas mixture ratios to investigate an influence of nitrogen amount on wear behavior. The structure, mechanical and tribological behavior of untreated and nitrided 31CrMoV9 steels were analyzed with X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), microhardness device, 3D profilometer and pin-on-disk wear tester. The analysis outcomes displayed that the compound layer consists of nitride phases (Fe2N, Fe3N, Fe4N and CrN). Additionally, the thickness of the compound layers, surface hardness and roughness increased with increasing nitrogen amount in the gas mixture. The highest friction coefficient value was obtained at nitrogen amount of 50%, but the lowest value was seen at nitrogen amount of 6%. It was observed that wear resistance of 31CrMoV9 steel improved after plasma nitriding, and the best wear resistance was also obtained from plasma nitrided sample at the gas mixture of 94% H[Formula: see text]% N2.

Ti6Al4V Surface Hardness Improvement by Duplex Coating

2013 ◽  
Vol 701 ◽  
pp. 370-374
Author(s):  
Yusliza Yusuf ◽  
Zulkifli Mohd Rosli ◽  
Jariah Mohamad Juoi ◽  
Zainab Mahamud ◽  
Kwan Wai Loon
Keyword(s):  
Microwave Plasma ◽  
Plasma Nitriding ◽  
Microstructural Analysis ◽  
Surface Hardness ◽  
Hardness Measurement ◽  
Compound Layer ◽  
Ti6al4v Alloy ◽  
Process Time ◽  
Wear Properties ◽  
Duplex Coating

Ti6Al4V alloy are among the most widely used materials in engineering applications. This is because their relatively beneficial properties. However, inadequate wear properties of Ti6Al4V alloy have largely constrained the application for this material. In this study, Plasma nitriding of the Ti6Al4V was performed using microwave plasma technique at 600°C for 1hour, 3 hours and 5 hours then followed with deposition of CrN on plasma nitrided samples for duplex coating purposes. Microstructural analysis and hardness measurement revealed that formation of Ti2N and TiN phases indicating the formation of compound layer is observed for substrate nitrided at temperature as low as 600°C 1 hour and a substantial increase on the surface hardness of plasma nitrided Ti6Al4V is observed with an increase of process time. The duplex coating obtained in this study has significant surface hardness property and superior as compared with CrN coatings deposited on as received Ti6Al4V.

Regularities of the formation and the role of secondary structures in the improvement of the wear resistance of commercially pure titanium VT1-0

2012 ◽  
Vol 33 (3) ◽  
pp. 184-189 ◽  
Author(s):  
B. P. Gritsenko ◽  
Yu. F. Ivanov ◽  
N. N. Koval’ ◽  
K. V. Krukovskii ◽  
N. V. Girsova ◽  
...  
Keyword(s):  
Wear Resistance ◽  
Pure Titanium ◽  
Secondary Structures ◽  
Commercially Pure Titanium ◽  
Commercially Pure

Comparison of Commercially Pure Titanium Surface Hardness Improvement by Plasma Nitrocarburizing and Ion Implantation

2013 ◽  
Vol 789 ◽  
pp. 347-351 ◽  
Author(s):  
Agung Setyo Darmawan ◽  
Waluyo Adi Siswanto ◽  
Tjipto Sujitno
Keyword(s):  
Ion Implantation ◽  
Elevated Temperatures ◽  
Pure Titanium ◽  
Surface Hardness ◽  
Commercially Pure Titanium ◽  
Hardness Tester ◽  
Hardness Number ◽  
Commercially Pure ◽  
Hardness Tests ◽  
Plasma Nitrocarburizing

Commercially pure (cp) titanium has a relative soft hardness property. In particular usage such as sliding, the improvement of the surface hardness will be required. In this study, surface hardness improvement of cp titanium by Plasma Nitrocarburizing and Ion Implantation are compared. Plasma Nitrocarburizing processes are conducted at different elevated temperatures with different duration processes, i.e. at 350 °C for 3, 4, and 5 hours, and at 450 °C for 2, 3, and 4 hours respectively, while Ion Implantation processes are conducted at room temperature and process durations are varied as 2.3 hours, 4.7 hours, and 9.3 hours. Nitrogen ions are used to implant the material. Hardness tests are then performed on each specimen by using Micro Vickers Hardness Tester. The surface hardness number (HV) for specimens of the Plasma Nitrocarburizing processes at temperature of 350 °C for process duration of 3 hours, 4 hours, and 5 hours are 74.16, 92.25 and 94.41, respectively while those at temperature of 450 °C for duration process of 2 hours, 3 hours, and 4 hours are 103.70, 121.31 and 126.17, respectively. The processes of Ion Implantation produce the surface hardness number (HV) of 88.97, 125.51, and 130.2, for duration processes of 2.3 hours, 4.7 hours, and 9.3 hours. The process of Ion Implantation produce higher surface hardness number than the Plasma Nitrocarburizing process at temperature 350 °C but the surface hardness number is lower when compared to the Plasma Nitrocarburizing at a temperature of 450 °C. For the duration processes 4 hours and more, the process of Ion Implantation produces the same surface hardness number with the Plasma Nitrocarburizing at temperature of 450 °C.

L. KLEIN TITAN GRADE 2

Alloy Digest ◽  
2021 ◽  
Vol 70 (4) ◽  
Keyword(s):  
Wear Resistance ◽  
Corrosion Resistance ◽  
Physical Properties ◽  
Pure Titanium ◽  
Heat Treating ◽  
Commercially Pure Titanium ◽  
Commercially Pure ◽  
Continuous Service ◽  
Titanium Grade ◽  
Service Environments

Abstract L. Klein Titan Grade 2 is an unalloyed, commercially pure titanium grade. It is the most widely used commercially pure titanium grade. It offers a combination of moderate strength and good ductility, with outstanding corrosion resistance in many challenging service environments. L. Klein Titan Grade 2 can operate in continuous service up to 425 °C (800 °F) and in intermittent service up to 540 °C (1005 °F). This datasheet provides information on composition, physical properties, and tensile properties. It also includes information on corrosion resistance and wear resistance as well as forming, heat treating, machining, and joining. Filing Code: Ti-177. Producer or source: L. Klein SA.