Magnetodielectric Ni ferrite ceramics with Bi2O3 additive for potential antenna miniaturizations

2009 ◽  
Vol 24 (2) ◽  
pp. 324-332 ◽  
Author(s):  
X.T. Liew ◽  
K.C. Chan ◽  
L.B. Kong
Keyword(s):  
Magnetic Properties ◽  
Dielectric Loss ◽  
Grain Growth ◽  
Sintering Temperature ◽  
Magnetic Loss ◽  
Liquid Phase Sintering ◽  
X Ray Diffraction ◽  
Low Dielectric ◽  
High Concentrations

This paper reports on the preparation and characterization of nickel ferrite (NiFe1.98O4) ceramics doped with Bi2O3 as sintering aid. Focus has been on the effects of concentration of Bi2O3 and sintering temperature on the densification, grain growth, dielectric, and magnetic properties of the NiFe1.98O4 ceramics, with an aim at developing magnetodielectric properties, with almost equal real permeability and permittivity, as well as sufficiently low magnetic and dielectric loss tangents, over 3 to 30 MHz (high frequency or HF band). X-ray diffraction results indicated that there is no obvious reaction between NiFe1.98O4 and Bi2O3, at Bi2O3 levels of up to 7 wt% and temperatures up to 1150 °C. The addition of Bi2O3 facilitated a liquid phase sintering mechanism for the densification of NiFe1.98O4 ceramics. The addition of Bi2O3 not only improved the densification but also promoted the grain growth of NiFe1.98O4 ceramics. To achieve sufficiently low dielectric loss tangent, the concentration of Bi2O3 should not be less than 5 wt%. The low dielectric loss tangents of the samples doped with high concentrations of Bi2O3 can be attributed to the full densification of the ceramics. Magnetic properties of the NiFe1.98O4 ceramics, as a function of sintering temperature and Bi2O3 concentration, can be qualitatively explained by the Globus model. Promising magnetodielectric properties have been obtained in the sample doped with 5% Bi2O3 and sintered at 1050 °C for 2 h. The sample has almost equal values of permeability and permittivity of ∼12, together with low dielectric and magnetic loss tangents, over 3 to 30 MHz. This material might be useful for the miniaturization of HF (3 to 30 MHz) antennas.

scholarly journals Synthesis And Characterization of Cobalt-Zinc Spinel Ferrites For High Frequency Applications

2021 ◽  
Author(s):  
Salma Aman ◽  
Tahani I. Al-Muhimeed ◽  
Zaki Ismail Zaki ◽  
Zeinhom M. El-Bahy ◽  
Abeer A. AlObaid ◽  
...  
Keyword(s):  
Dielectric Loss ◽  
High Frequency ◽  
Sol Gel ◽  
Secondary Phase ◽  
Spinel Ferrites ◽  
Dc Resistivity ◽  
X Ray Diffraction ◽  
X Ray ◽  
Low Dielectric

Abstract Spinel ferrites are attractive for high frequency applications due to their larger direct current (dc) resistivity and low dielectric loss. In the present work, Co0.6Zn0.4HoxFe2-xO4 (x = 0.00 and 0.1) spinel ferrites were prepared by sol-gel method. The X-ray diffraction pattern showed that both samples had cubic spinel structure, while in sample (x = 0.1), the secondary phase (HoFeO3) was also observed. The dc resistivity was increased with the addition of holmium ions. As the temperature increased, the dc resistivity was decreased by proving their semiconducting nature. The dielectric properties were also measured as a function of temperature and frequency. The sample which was composed by the substitution of holmium ions contained low value of dielectric loss. The magnetic properties were also experimentally measured by applying the field up to 2000 oersted. The small area covered by hysteresis loop proved that both samples possessed soft nature of magnetic materials.

scholarly journals Synthesis, growth and characterization of NaAl(SO4)·H2O triangular prism single crystal for inorganic NLO application

2019 ◽  
Vol 37 (2) ◽  
pp. 142-148
Author(s):  
P. Sakthi ◽  
R. Rajasekaran ◽  
A. Arun
Keyword(s):  
Dielectric Loss ◽  
Single Crystal ◽  
Grown Crystal ◽  
Triangular Prism ◽  
X Ray Diffraction ◽  
Low Dielectric ◽  
Different Temperatures ◽  
Evaporation Technique ◽  
Ft Ir

AbstractAn inorganic coordination complex of single crystal containing sodium and aluminum (SA) was grown at room temperature by slow evaporation technique. The crystal was characterized using single crystal X-ray diffraction (XRD), FT-IR, UV-Vis, SHG, SEM, EDX and TG/DTA analyses. The size of the grown crystal was around 17 mm × 15 mm × 5 mm. Both optical and SEM photographs confirmed that the crystal is transparent with smooth surface. The XRD data showed that the crystal belongs to the BCC crystal structure. The crystal shows excellent transparency in the entire region of visible light (cut-off value is 339 cm−1). The dielectric constant as well as dielectric loss of the sample was calculated by varying frequencies at different temperatures and the presence of low dielectric loss proved that this crystal can be used for the NLO application.

scholarly journals Synthesis and Na+ Ion Conductivity of Stoichiometric Na3Zr2Si2PO12 by Liquid-Phase Sintering with NaPO3 Glass

Materials ◽  
2021 ◽  
Vol 14 (14) ◽  
pp. 3790
Author(s):  
Yongzheng Ji ◽  
Tsuyoshi Honma ◽  
Takayuki Komatsu
Keyword(s):  
Solid State ◽  
Liquid Phase ◽  
Sintering Temperature ◽  
Liquid Phase Sintering ◽  
Ion Conductivity ◽  
X Ray Diffraction ◽  
Conventional Solid State Reaction ◽  
X Ray ◽  
Sintering Time ◽  
Lower Activation

Sodium super ionic conductor (NASICON)-type Na3Zr2Si2PO12 (NZSP) with the advantages of the high ionic conductivity, stability and safety is one of the most famous solid-state electrolytes. NZSP, however, requires the high sintering temperature about 1200 °C and long sintering time in the conventional solid-state reaction (SSR) method. In this study, the liquid-phase sintering (LPS) method was applied to synthesize NZSP with the use of NaPO3 glass with a low glass transition temperature of 292 °C. The formation of NZSP was confirmed by X-ray diffraction analyses in the samples obtained by the LPS method for the mixture of Na2ZrSi2O7, ZrO2, and NaPO3 glass. The sample sintered at 1000 °C for 10 h exhibited a higher Na+ ion conductivity of 1.81 mS/cm at 100 °C and a lower activation energy of 0.18 eV compared with the samples prepared by the SSR method. It is proposed that a new LPE method is effective for the synthesis of NZSP and the NaPO3 glass has a great contribution to the Na+ diffusion at the grain boundaries.

scholarly journals Green synthesis and characterization of hexaferrite strontium-perovskite strontium photocatalyst nanocomposites

2020 ◽  
Vol 43 (1) ◽  
pp. 26-42 ◽  
Author(s):  
Zahra Hajian Karahroudi ◽  
Kambiz Hedayati ◽  
Mojtaba Goodarzi
Keyword(s):  
Magnetic Properties ◽  
Green Synthesis ◽  
Sol Gel ◽  
Synthesis Method ◽  
Combustion Method ◽  
Lemon Juice ◽  
X Ray Diffraction ◽  
X Ray ◽  
Auto Combustion

AbstractThis study presents a preparation of SrFe12O19– SrTiO3 nanocomposite synthesis via the green auto-combustion method. At first, SrFe12O19 nanoparticles were synthesized as a core and then, SrTiO3 nanoparticles were prepared as a shell for it to manufacture SrFe12O19–SrTiO3 nanocomposite. A novel sol-gel auto-combustion green synthesis method has been used with lemon juice as a capping agent. The prepared SrFe12O19–SrTiO3 nanocomposites were characterized by using several techniques to characterize their structural, morphological and magnetic properties. The crystal structures of the nanocomposite were investigated via X-ray diffraction (XRD). The morphology of SrFe12O19– SrTiO3 nanocomposite was studied by using a scanning electron microscope (SEM). The elemental composition of the materials was analyzed by an energy-dispersive X-ray (EDX). Magnetic properties and hysteresis loop of nanopowder were characterized via vibrating sample magnetometer (VSM) in the room temperature. Fourier transform infrared spectroscopy (FTIR) spectra of the samples showed the molecular bands of nanoparticles. Also, the photocatalytic behavior of nanocomposites has been checked by the degradation of azo dyes under irradiation of ultraviolet light.

Deposition of TRISO Particles With Superhard SiC Coatings and the Characterization of Anisotropy by Raman Spectroscopy

2009 ◽  
Vol 131 (4) ◽  
Author(s):  
E. López-Honorato ◽  
P. J. Meadows ◽  
J. Tan ◽  
Y. Xiang ◽  
P. Xiao
Keyword(s):  
Solid Solution ◽  
Raman Spectroscopy ◽  
Pyrolytic Carbon ◽  
X Ray Diffraction ◽  
X Ray ◽  
Flat Substrate ◽  
High Concentrations ◽  
Triso Particles ◽  
Sic Coatings

In this work we have deposited silicon carbide (SiC) at 1300°C with the addition of small amounts of propylene. The use of propylene and high concentrations of methyltrichlorosilane (9 vol %) allowed the deposition of superhard SiC coatings (42 GPa). The superhard SiC could result from the presence of a SiC–C solid solution, undetectable by X-ray diffraction but visible by Raman spectroscopy. Another sample obtained by the use of 50 vol % Argon, also showed the formation of SiC with good properties. The use of a flat substrate together with the particles showed the importance of carrying out the analysis on actual particles rather than in flat substrates. We show that it is possible to characterize the anisotropy of pyrolytic carbon by Raman spectroscopy.

PREPARATION AND CHARACTERIZATION OF MECHANICALLY FLEXIBLE RUBBER-CERAMIC COMPOSITE DIELECTRICS

2013 ◽  
Vol 22 ◽  
pp. 148-152
Author(s):  
DHANESH THOMAS ◽  
M. T. SEBASTIAN
Keyword(s):  
Dielectric Loss ◽  
Hot Pressing ◽  
Relative Permittivity ◽  
Ceramic Composite ◽  
Temperature Stability ◽  
Theoretical Models ◽  
Butyl Rubber ◽  
Low Dielectric

Butyl rubber — Ca 4 La 6( SiO 4)4( PO 4)2 O 2 — composites have been prepared by sigma mixing and hot pressing. The relative permittivity of the composites varies from 3 to 5.3 at 1 MHz. All the composites show low dielectric loss of the order of 10−3 at 1 MHz. The experimentally observed values of relative permittivity are correlated with those calculated using various theoretical models. The composites show good temperature stability of relative permittivity.

CHARACTERIZATION OF HYDROXYAPATITE/TI6AL4V COMPOSITE POWDER UNDER VARIOUS SINTERING TEMPERATURE

2015 ◽  
Vol 75 (7) ◽  
Author(s):  
Amir Arifin ◽  
Abu Bakar Sulong ◽  
Norhamidi Muhamad ◽  
Junaidi Syarif
Keyword(s):  
Mechanical Properties ◽  
Composite Powder ◽  
Sintering Temperature ◽  
Physical And Mechanical Properties ◽  
Xrd Analysis ◽  
X Ray Diffraction ◽  
Different Temperatures ◽  
Two Phases ◽  
Work Interaction

Hydroxyapatite (HA) has been widely used in biomedical applications due to its excellent biocompatibility. However, Hydroxyapatite possesses poor mechanical properties and only tolerate limited loads for implants. Titanium is well-known materials applied in implant that has advantage in mechanical properties but poor in biocompatibility. The combination of the Titanium alloy and HA is expected to produce bio-implants with good in term of mechanical properties and biocompatabilty. In this work, interaction and mechanical properties of HA/Ti6Al4V was analyzed. The physical and mechanical properties of HA/Ti6Al4V composite powder obtained from compaction (powder metallurgy) of 60 wt.% Ti6Al4V and 40 wt.% HA and sintering at different temperatures in air were investigated in this study. Interactions of the mixed powders were investigated using X-ray diffraction. The hardness and density of the HA/Ti6Al4V composites were also measured. Based on the results of XRD analysis, the oxidation of Ti began at 700 °C. At 1000 °C, two phases were formed (i.e., TiO2 and CaTiO3). The results showed that the hardness HA/Ti6Al4V composites increased by 221.6% with increasing sintering temperature from 700oC to 1000oC. In contrast, the density of the composites decreased by 1.9% with increasing sintering temperature. 

Effect of Process on the Dielectric Properties of BaTiO3-Based X9R Ceramics

2014 ◽  
Vol 906 ◽  
pp. 18-24 ◽  
Author(s):  
Bao Lin Zhang ◽  
Bin Bin Zhang ◽  
Ning Ning Wang ◽  
Jing Ming Fei
Keyword(s):  
Particle Size ◽  
Dielectric Properties ◽  
Milling Time ◽  
Sintering Temperature ◽  
Sintering Process ◽  
X Ray Diffraction ◽  
Sintered Ceramic ◽  
X Ray ◽  
Particle Size Analyzer

The effect of milling time and sintering process on the dielectric properties of BaTiO3-based X9R ceramics was investigated. The characterization of the raw powders and the sintered ceramic was carried out by X-ray diffraction and scanning electron microscopy. The particle size distribution of the mixed powders was examined by Laser Particle Size Analyzer. The results shown that with the milling time extended, the Cruie Peak was depressed, or even disappeared. Moreover, with the rise of sintering temperature, the dielectric constant of the ceramics increased and the dielectric loss decreased gradually. Eventually, by milling for 11h and sintering at 1090°Cfor 2h, good dielectric properties were obtained, which were ε25°C≥ 2526, εr/εr25°C≤± 12% (–55~200°C), tanδ≤1.12% (25°C).

scholarly journals Effect of TeO2 addition on the dielectric properties of CaCu3Ti4O12 ceramics derived from the oxalate precursor route

2013 ◽  
Vol 03 (04) ◽  
pp. 1350028 ◽  
Author(s):  
P. Thomas ◽  
K. B. R. Varma
Keyword(s):  
Dielectric Properties ◽  
Dielectric Loss ◽  
Room Temperature ◽  
X Ray Diffraction ◽  
Oxalate Precursor ◽  
X Ray ◽  
Practical Applications ◽  
Low Dielectric ◽  
Precursor Route ◽  
Tan Δ

CaCu 3 Ti 4 O 12 (CCTO) ceramics which has perovskite structure gained considerable attention due to its giant permittivity. But it has high tan δ (0.1 at 1 kHz) at room temperature, which needs to be minimized to the level of practical applications. Hence, TeO 2 which is a good glass former has been deliberately added to CCTO nanoceramic (derived from the oxalate precursor route) to explore the possibility of reducing the dielectric loss while maintaining the high permittivity. The structural, morphological and dielectric properties of the pure CCTO and TeO 2 added ceramics were studied using X-ray diffraction, Scanning Electron Microscope along with Energy Dispersive X-ray Analysis (EDX), spectroscopy and Impedance analyzer. For the 2.0 wt.% TeO 2 added ceramics, there is a remarkable difference in the microstructural features as compared to that of pure CCTO ceramics. This sample exhibited permittivity values as high as 7387 at 10 KHz and low dielectric loss value of 0.037 at 10 kHz, which can be exploited for the high frequency capacitors application.

Synthesis and Characterization of BiFeO3 Ceramic by Simple and Novel Methods

2016 ◽  
Vol 35 (6) ◽  
pp. 551-557 ◽  
Author(s):  
Omid Amiri ◽  
Mohammad Reza Mozdianfar ◽  
Mahmoud Vahid ◽  
Masoud Salavati-Niasari ◽  
Sousan Gholamrezaei
Keyword(s):  
Magnetic Properties ◽  
Domain Walls ◽  
Magnetic Domain ◽  
X Ray Diffraction ◽  
X Ray ◽  
Size Dependent ◽  
Magnetic Domain Walls ◽  
Magnetization Orientation ◽  
Thermal Stability Of

AbstractBiFeO3 nanopowders with new morphology have been synthesized by different methods. X-ray diffraction analysis, scanning electron microscopy, Fourier transform infrared and vibrating sample magnetometer were carried out at room temperature to study the structural and magnetic properties of as-synthesized products. VSM was utilized to measure the size-dependent magnetic behaviors of the as-prepared nanoparticles. Results show that the method has strong effect on the purity of the products. BFO synthesized by third method was pure. Crystallite size has a great effect on the magnetic properties. According to these results the nanoparticle diameter is smaller than the critical single-domain diameter, avoiding the configuration of magnetic domain walls decreases the magnetization. Even though the diameter of particle becomes even smaller, the thermal stability of the magnetization orientation decreases.

Sign in / Sign up

Export Citation Format

Share Document