Modification of Low ĸ Materials for ULSI Multilevel Interconnects by Ion Implantation

2002 ◽  
Vol 716 ◽  
Author(s):  
Alok Nandini ◽  
U. Roy ◽  
A. Mallikarjunan ◽  
A. Kumar ◽  
J. Fortin ◽  
...  
Keyword(s):  
Dielectric Constant ◽  
Ion Implantation ◽  
Dielectric Materials ◽  
Dramatic Improvement ◽  
Force Microscopy ◽  
Low Dielectric ◽  
Quantitative Measurements ◽  
Hardness Increase ◽  
Xerogel Films ◽  
Ion Species

AbstractThin films of low dielectric constant (κ) materials such as Xerogel (ĸ=1.76) and SilkTM (ĸ=2.65) were implanted with argon, neon, nitrogen, carbon and helium with 2 x 1015 cm -2 and 1 x 1016 cm -2 dose at energies varying from 50 to 150 keV at room temperature. In this work we discuss the improvement of hardness as well as elasticity of low ĸ dielectric materials by ion implantation. Ultrasonic Force Microscopy (UFM) [6] and Nano indentation technique [5] have been used for qualitative and quantitative measurements respectively. The hardness increased with increasing ion energy and dose of implantation. For a given energy and dose, the hardness improvement varied with ion species. Dramatic improvement of hardness is seen for multi-dose implantation. Among all the implanted ion species (Helium, Carbon, Nitrogen, Neon and Argon), Argon implantation resulted in 5x hardness increase in Xerogel films, sacrificing only a slight increase (∼ 15%) in dielectric constant.

Sol–gel deposited xerogel, aerogel and porogen based porous low-k thin films: A comparative investigation

2021 ◽  
pp. 2140019
Author(s):  
Swati Gupta ◽  
Anil Gaikwad ◽  
Ashok Mahajan ◽  
Lin Hongxiao ◽  
He Zhewei
Keyword(s):  
Dielectric Constant ◽  
Sol Gel ◽  
Comparative Investigation ◽  
Crosstalk Noise ◽  
Nanoelectronic Devices ◽  
Low Dielectric ◽  
Interconnect Delay ◽  
Xerogel Films ◽  
Low K ◽  
Porosity Percentage

Low dielectric constant (Low-[Formula: see text]) films are used as inter layer dielectric (ILD) in nanoelectronic devices to reduce interconnect delay, crosstalk noise and power consumption. Tailoring capability of porous low-[Formula: see text] films attracted more attention. Present work investigates comparative study of xerogel, aerogel and porogen based porous low-[Formula: see text] films. Deposition of SiO2 and incorporation of less polar bonds in film matrix is confirmed using Fourier Transform Infra-Red Spectroscopy (FTIR). Refractive indices (RI) of xerogel, aerogel and porogen based low-[Formula: see text] films observed to be as low as 1.25, 1.19 and 1.14, respectively. Higher porosity percentage of 69.46% is observed for porogen-based films while for shrinked xerogel films, it is lowered to 45.47%. Porous structure of low-[Formula: see text] films has been validated by using Field Emission Scanning Electron Microscopy (FE-SEM). The pore diameters of porogen based annealed samples were in the range of 3.53–25.50 nm. The dielectric constant ([Formula: see text]) obtained from RI for xerogel, aerogel and porogen based films are 2.58, 2.20 and 1.88, respectively.

Intrinsic low dielectric behaviour of a highly thermally stable Sr-based metal–organic framework for interlayer dielectric materials

2014 ◽  
Vol 2 (19) ◽  
pp. 3762-3768 ◽  
Author(s):  
Muhammad Usman ◽  
Cheng-Hua Lee ◽  
Dung-Shing Hung ◽  
Shang-Fan Lee ◽  
Chih-Chieh Wang ◽  
...  
Keyword(s):  
Dielectric Constant ◽  
Metal Organic Framework ◽  
Dielectric Materials ◽  
Low Dielectric Constant ◽  
Water Molecules ◽  
Compound A ◽  
Interlayer Dielectric ◽  
Low Dielectric ◽  
Metal Organic ◽  
Organic Framework

A Sr-based metal–organic framework exhibits an intrinsic low dielectric constant after removing the water molecules. A low dielectric constant and high thermal stability make this compound a candidate for use as a low-k material.

Siloxane Polymers as Low Dielectric Materials for Microelectronics

1995 ◽  
Vol 390 ◽  
Author(s):  
C. P. Wong
Keyword(s):  
Dielectric Constant ◽  
Three Dimensional ◽  
Signal Propagation ◽  
Dielectric Materials ◽  
Propagation Delay ◽  
Dimensional Structure ◽  
Low Dielectric Constant ◽  
Interlayer Dielectric ◽  
Low Dielectric ◽  
High Dielectric

ABSTRACTA modem VLSI device is a complicated three-dimensional structure that consists of multilayer metallization conductor lines which are separated with interlayer-dielectrics as insulation. This VLSI technology drives the IC device into sub-micron feature size that operates at ultra-fast speed (in excess of > 100 MHz). Passivation and interlayer dielectric materials are critical to the device performance due to the conductor signal propagation delay of the high dielectric constant of the material. Low dielectric constant materials are the preferred choice of materials for this reasons. These materials, such as Teflon® and siloxanes (silicones), are desirable because of their low dielectric constant (∈1) = 2.0, 2.7, respectively. This paper describes the use of a low dielectric constant siloxane polymer (silicone) as IC devices passivation layer material, its chemistry, material processes and reliability testing.

Low-K Porous Spin-On-Glass

1999 ◽  
Vol 565 ◽  
Author(s):  
Paul A. Kohl ◽  
Agnes Padovani ◽  
Michael Wedlake ◽  
Dhananjay Bhusari ◽  
Sue Ann ◽  
...  
Keyword(s):  
Dielectric Constant ◽  
Elevated Temperatures ◽  
Porous Silica ◽  
Dielectric Materials ◽  
Decomposition Products ◽  
Air Gaps ◽  
Low Dielectric ◽  
Polymer Decomposition ◽  
Low K ◽  
By Products

AbstractPreviously, the fabrication of air-gap structures for electrical interconnections was demonstrated using a sacrificial polymer encapsulated in conventional dielectric materials. The air-gaps were formed by thermally decomposing the sacrificial polymer and allowing the by-products to diffuse through the encapsulating dielectric. The diffusivity of the polymer decomposition products is adequate at elevated temperatures to allow the formation of air-gaps. This process was extended to form low dielectric constant, porous silica from commercially available methylsilsesquioxane (MSQ) by the addition of the sacrificial polymer to the MSQ. The porous MSQ film was thermally cured followed by decomposition of the NB at temperatures above 400°C. The dielectric constant of the MSQ was lowered from 2.7 to 2.3 by creating 70 nm pores in the MSQ. The voids created in the MSQ appeared to exhibit a closed-pore structure.

First Pass Study of Surface Modified Porous Low-k by Ion Implantation for Zero Thickness Barrier Requirement of Cu/MSQ/Si Stacks in Copper Metallization Scheme

2005 ◽  
Vol 863 ◽  
Author(s):  
Alok Nandini ◽  
U. Roy ◽  
Zubin P. Patel ◽  
H. Bakhru
Keyword(s):  
Mechanical Properties ◽  
Dielectric Constant ◽  
Ion Implantation ◽  
Porous Silica ◽  
Surface Hardness ◽  
Low Dielectric Constant ◽  
Copper Metallization ◽  
Porous Films ◽  
Critical Dimensions ◽  
Low Dielectric

AbstractLow-κ dielectrics have to meet stringent requirements in material properties in order to be successfully integrated. A particularly difficult challenge for material development is to obtain a combination of low dielectric constant with good thermal and mechanical properties. Incorporation of low dielectric constant materials such as porous silica based materials as a replacement to conventional dielectrics like SiO2 and use of Cu metallization schemes has become a necessity as critical dimensions of devices decrease. This paper is focused on the challenges in developing materials with low dielectric constant but strong thermo mechanical properties. Thin films of Ultra-Low materials such as porous Methyl Silsesquioxane (MSQ) (κ=2.2) were implanted with argon 1 × 1016 cm-2 dose at energies varying from 20 to 50 keV at room temperature. This work shows that the surface hardness of the porous films can be improved five times as compared to the as-deposited porous films by implanting Ar with 1 × 1016 cm-2 doses at 20 keV, sacrificing only a slight increase (∼9%) in dielectric constant (e.g., from 2.2 to 2.4). The hardness persists after 4500C annealing. In this current work, an ion implantation strategy was pursued to create a SiO2-like surface on MSQ. The effects of implantation parameters on the barrier property and bulk stability of MSQ were then studied. The results reveal one possible route to attain the “zero barrier thickness” requirement for interconnects systems.

Novel Materials as Interlayer Low-K Dielectrics for CMOS Interconnect Applications

2011 ◽  
Vol 110-116 ◽  
pp. 5380-5383
Author(s):  
Tejas R. Naik ◽  
Veena R. Naik ◽  
Nisha P. Sarwade
Keyword(s):  
Dielectric Constant ◽  
Integrated Circuits ◽  
Dielectric Materials ◽  
Low Dielectric Constant ◽  
Interlayer Dielectric ◽  
Novel Materials ◽  
Low Dielectric ◽  
Processing Properties ◽  
New Generation ◽  
Low K

Scaling down the integrated circuits has resulted in the arousal of number of problems like interaction between interconnect, crosstalk, time delay etc. These problems can be overcome by new designs and by use of corresponding novel materials, which may be a solution to these problems. In the present paper we try to put forward very recent development in the use of novel materials as interlayer dielectrics (ILDs) having low dielectric constant (k) for CMOS interconnects. The materials presented here are porous and hybrid organo-inorganic new generation interlayer dielectric materials possessing low dielectric constant and better processing properties.

scholarly journals Polyarylene Ether Nitrile-Based High-k Composites for Dielectric Applications

2018 ◽  
Vol 2018 ◽  
pp. 1-15 ◽  
Author(s):  
Yong You ◽  
Chenhao Zhan ◽  
Ling Tu ◽  
Yajie Wang ◽  
Weibin Hu ◽  
...  
Keyword(s):  
Dielectric Constant ◽  
High Dielectric Constant ◽  
Dielectric Materials ◽  
Dielectric Ceramic ◽  
Polyarylene Ether Nitrile ◽  
Effective Strategies ◽  
Low Dielectric ◽  
Flexible Polymer ◽  
Ceramic Fillers ◽  
High Dielectric

Flexible polymer-based composites exhibiting high dielectric constant as well as low dielectric loss have been intensively investigated for their potential utilization in electronics and electricity industry and energy storage. Resulting from the polar -CN on the side chain, polyarylene ether nitrile (PEN) shows relatively high dielectric constant which has been extensively investigated as one of the hot spots as dielectric materials. However, the dielectric constant of PEN is still much lower than the ceramic dielectrics such as BaTiO3, TiO2, and Al2O3. In this review, recent and in-progress advancements in the designing and preparing strategies to obtain high-k PEN-based nanocomposites are summarized. According to the types of the added fillers, the effects of organic fillers, dielectric ceramic fillers, and conductive fillers on electric properties of PEN-based composites are investigated. In addition, other factors including the structures and sizes of the additive, the compatibility between the additive agent and the PEN, and the interface which affects the dielectric properties of the obtained composite materials are investigated. Finally, challenges facing in the design of more effective strategies for the high-k PEN-based dielectric materials are discussed.

Sign in / Sign up

Export Citation Format

Share Document