scholarly journals Development of Polyvinylidene Fluoride Membrane by Incorporating Bio-Based Ginger Extract as Additive

Polymers ◽  
2020 ◽  
Vol 12 (9) ◽  
pp. 2003
Author(s):  
Afrillia Fahrina ◽  
Nasrul Arahman ◽  
Sri Mulyati ◽  
Sri Aprilia ◽  
Normi Izati Mat Nawi ◽  
...  
Keyword(s):  
Polyvinylidene Fluoride ◽  
Membrane Filtration ◽  
Membrane Surface ◽  
Pure Water ◽  
Water Flux ◽  
Inhibition Zone ◽  
Diffusion Method ◽  
Ginger Extract ◽  
Dimethyl Acetamide ◽  
Antibiotic Property

Biofouling on the membrane surface leads to performance deficiencies in membrane filtration. In this study, the application of ginger extract as a bio-based additive to enhance membrane antibiofouling properties was investigated. The extract was dispersed in a dimethyl acetamide (DMAc) solvent together with polyvinylidene fluoride (PVDF) to enhance biofouling resistance of the resulting membrane due to its antibiotic property. The concentrations of the ginger extract in the dope solution were varied in the range of 0–0.1 wt %. The antibacterial property of the resulting membranes was assessed using the Kirby Bauer disc diffusion method. The results show an inhibition zone formed around the PVDF/ginger membrane against Escherichia coli and Staphylococcus aureus demonstrating the efficacy of the residual ginger extract in the membrane matrix to impose the antibiofouling property. The addition of the ginger extract also enhanced the hydrophilicity in the membrane surface by lowering the contact angle from 93° to 85°, which was in good agreement with the increase in the pure water flux of up to 62%.

Fabrication and Properties of the PVDF/PVDF-g-PMMA Blend Hydrophilic Membrane

2011 ◽  
Vol 418-420 ◽  
pp. 639-642
Author(s):  
Tao Yuan ◽  
Jian Qiang Meng ◽  
Guo Rong Cai ◽  
Yu Feng Zhang
Keyword(s):  
Contact Angle ◽  
Water Contact Angle ◽  
Polyvinylidene Fluoride ◽  
Membrane Surface ◽  
Pure Water ◽  
Water Flux ◽  
Water Contact ◽  
H Nmr ◽  
Membrane Surfaces ◽  
Static Water

An amphiphilic graft copolymer was obtained via atom transfer radical polymerization (ATRP) of methacrylate (MMA) initiated directly by polyvinylidene fluoride (PVDF). Hydrophilic PVDF membranes were prepared by immersion precipitation of PVDF-g-PMMA and PVDF blend solutions. The chemical structure and the molecular weight were characterized by 1H-NMR and GPC. The hydrophilicity of membrane surfaces were characterized by static water contact angle. Top surface and cross-section of membranes were observed by Field Emission Scanning Electron Microscope (FESEM). The results demonstrated the water contact angle of the membrane surface decreased from 89°to 67°, indicating enhanced hydrophilicity; the pure water flux water firstly decreased and then increased up to 1.7 times of the PVDF membrane. The retention of PEG (Mn=6000) could be maintained at 93%-95%.

Preparation and Characterization of PVDF-TiO2 Composite Membranes Blended with Different Mw of PVP for Oily Wastewater Treatment using Submerged Membrane System

2014 ◽  
Vol 69 (9) ◽  
Author(s):  
C. S. Ong ◽  
W. J. Lau ◽  
P. S. Goh ◽  
A. F. Ismail Ismail
Keyword(s):  
Polyvinylidene Fluoride ◽  
Membrane Surface ◽  
Pure Water ◽  
Water Flux ◽  
Composite Membranes ◽  
Membrane System ◽  
Morphological Properties ◽  
Oily Wastewater ◽  
Permeate Flux ◽  
Oily Wastewater Treatment

Polyvinylidene fluoride (PVDF) hollow fiber ultrafiltration (UF) membranes consisted of TiO2 and different molecular weight (Mw) of polyvinylpyrrolidone (PVP) (i.e. 10, 24, 40 and 360 kDa) were prepared to treat synthesized oily wastewater. The membrane performances were characterized in terms of pure water flux, permeate flux and oil rejection while the membrane morphological properties were studied using SEM and AFM. PVDF-TiO2 composite membrane prepared from PVP40k was found as the optimum membrane due to its high flux and high rejection during filtration process, recording      45 L/m2.h and 80% respectively, when tested using 250 ppm oily solution under submerged condition. The experimental results demonstrated that with increasing Mw of PVP, PVDF-TiO2 membrane had higher protein rejection, smaller porosity and smoother surface layer. With increasing oil concentration from 250 to 1000 ppm, the permeate flux of the PVDF-PVP40k was obviously decreased while the oil rejection was gradually increased due to the additional selective layer formed on the membrane surface.  Based on the findings, the PVDF-TiO2 membrane with PVP40k can be considered as a potential membrane for oily wastewater industry due to the high permeate flux and oil rejection. 

Preparation and Characterization of Hydrophilic PVDF Hollow Fiber Ultrafiltration Membrane

2011 ◽  
Vol 480-481 ◽  
pp. 201-206
Author(s):  
Li Guo Wang ◽  
Xiu Ju Wang ◽  
Ai Min Wang ◽  
Wen Juan Liu ◽  
Shi Qi Guo ◽  
...  
Keyword(s):  
Acrylic Acid ◽  
Hollow Fiber ◽  
Polyvinylidene Fluoride ◽  
Breaking Strength ◽  
Pure Water ◽  
Water Flux ◽  
Technical Parameters ◽  
Rupture Pressure ◽  
Pure Water Flux

Hydrophilic Polyvinylidene fluoride (PVDF) hollow fiber ultrafiltration membranes were prepared by wet-spinning method. The effects of technical parameters of acrylic acid grafted onto PVDF on the performance of hydrophilic PVDF membranes were investigated via orthogonal test, the technical parameters of preparation of hydrophilic PVDF membranes were determined, and hydrophilic PVDF membranes were prepared. Then hydrophilic PVDF membranes were characterized in terms of breaking strength, breaking elongation, rupture pressure, pure water flux and rejection. The fouling properties and the conditions of acrylic acid grafted onto PVDF were also examined. The results showed that acrylic acid had been grafted onto PVDF, the breaking strength and rupture pressure improved greatly, and the fouling properties were better than PS hollow fiber UF membrane.

scholarly journals Preparation, characterization and dyeing wastewater treatment of a new PVDF/PMMA five-bore UF membrane with β-cyclodextrin and additive combinations

2021 ◽  
Author(s):  
Xiaozheng Bian ◽  
Jianping Huang ◽  
Lin Qiu ◽  
Chunyan Ma ◽  
Danli Xi
Keyword(s):  
Wastewater Treatment ◽  
Bovine Serum Albumin ◽  
Serum Albumin ◽  
Membrane Fouling ◽  
Bovine Serum ◽  
Polyvinylidene Fluoride ◽  
Hollow Fiber Membrane ◽  
Pure Water ◽  
Water Flux ◽  
Dyeing Wastewater

Abstract A new type of polyvinylidene fluoride (PVDF)/polymethyl methacrylate (PMMA) hollow fiber membrane (HFM) with five bores was prepared. The effects of Polyvinylpyrrolidone (PVP), β-cyclodextrine (β-CD), Polyethylene Glycol (PEG) and Polysorbate 80 (Tween 80) and their combinations on the PVDF/PMMA five-bore HFMs were investigated. The performance and fouling characteristics of five-bore HFMs for dyeing wastewater treatment were evaluated. Results indicated that adding 5wt.% PVP could increase the porosity and water flux of the membrane but decrease the bovine serum albumin (BSA) rejection rate. Adding 5wt.% β-CD significantly improved the tensile and rejection of the HFMs without showing effect on the increase of water flux. The characteristic of the HFMs with different additives combinations proved that the mixture of 5wt.% PVP and 1wt.% β-CD obtained the best membrane performance, with a pure water flux of 427.9 L/ m2·h, a contact angle of 25°, and a rejection to bovine serum albumin (BSA) of 89.7%. The CODcr and UV254 removal rates of dyeing wastewater treatment were 61.10% and 50.41%, respectively. No breakage or leakage points were found after 120d operation showing the reliable mechanical properties. We set the operating flux to 55 L/m2·h and cross flow rate to 10% which can effectively control membrane fouling.

scholarly journals The Modification of PVDF Membrane via Crosslinking with Chitosan and Glutaraldehyde as the Crosslinking Agent

2018 ◽  
Vol 18 (1) ◽  
pp. 1
Author(s):  
Romaya Sitha Silitonga ◽  
Nurul Widiastuti ◽  
Juhana Jaafar ◽  
Ahmad Fauzi Ismail ◽  
Muhammad Nidzhom Zainol Abidin ◽  
...  
Keyword(s):  
Contact Angle ◽  
Vinylidene Fluoride ◽  
Membrane Surface ◽  
Pure Water ◽  
Water Flux ◽  
Crosslinking Agent ◽  
Hydrophobic Properties ◽  
Pvdf Membrane ◽  
Pure Water Flux ◽  
Modified Membrane

Poly(vinylidene fluoride) (PVDF) has outstanding properties such as high thermal stability, resistance to acid solvents and good mechanical strength. Due to its properties, PVDF is widely used as a membrane matrix. However, PVDF membrane is hydrophobic properties, so as for specific applications, the surface of membrane needs to be modified to become hydrophilic. This research aims to modify PVDF membrane surface with chitosan and glutaraldehyde as a crosslinker agent. The FTIR spectra showed that the modified membrane has a peak at 1655 cm-1, indicating the imine group (–N=C)- that was formed due to the crosslink between amine group from chitosan and aldehyde group from glutaraldehyde. Results showed that the contact angle of the modified membrane decreases to 77.22° indicated that the membrane hydrophilic properties (< 90°) were enhanced. Prior to the modification, the contact angle of the PVDF membrane was 90.24°, which shows hydrophobic properties (> 90°). The results of porosity, Ɛ (%) for unmodified PVDF membrane was 55.39%, while the modified PVDF membrane has a porosity of 81.99%. Similarly, by modifying the PVDF membrane, pure water flux increased from 0.9867 L/m2h to 1.1253 L/m2h. The enhancement of porosity and pure water flux for the modified PVDF membrane was due to the improved surface hydrophilicity of PVDF membrane.

Fabrication and Characterization of PVDF/UiO-66(Zr) Mixed Matrix Membrane on Non-Woven PET Support

2020 ◽  
Vol 1005 ◽  
pp. 108-115
Author(s):  
John Rhoel Cementina ◽  
Michael V. Torres ◽  
Dante P. Bernabe ◽  
Stephen Lirio ◽  
Micah Belle Marie Yap Ang ◽  
...  
Keyword(s):  
Mechanical Strength ◽  
Polyvinylidene Fluoride ◽  
Gas Permeability ◽  
Metal Organic Framework ◽  
Pure Water ◽  
Polymer Concentration ◽  
Water Flux ◽  
Mixed Matrix Membrane ◽  
Mixed Matrix ◽  
Metal Organic

Polyvinylidene fluoride (PVDF) membranes, enhanced with metal-organic framework (MOF), were fabricated on a non-woven polyethylene terephthalate (PET) support using the non-solvent induced phase inversion (NIPS) method to produce mixed matrix membrane (MMM). Polymer concentration of 10%, 15%, and 20% were used in the study whereas UiO-66(Zr) was used as a MOF filler. The resulting membranes were characterized in terms of their morphology, porosity, wettability, mechanical strength, pure water flux, and gas permeability. Results show that the presence of UiO-66(Zr) filler improved membrane morphology, mechanical strength, and hydrophobicity of MMM as compared to pristine PVDF.

Preparation and Characterization of Hydrophilic PVDF Membrane via Graft Modification by Maleic Anhydride

2011 ◽  
Vol 295-297 ◽  
pp. 286-291
Author(s):  
Li Guo Wang ◽  
Xiao Guang Zhang ◽  
Shu Fang Hou ◽  
Xiu Ju Wang ◽  
Ai Min Wang ◽  
...  
Keyword(s):  
Maleic Anhydride ◽  
Polyvinylidene Fluoride ◽  
Pure Water ◽  
Water Flux ◽  
Pvdf Membrane ◽  
Technical Parameters ◽  
Pure Water Flux ◽  
Flat Membranes ◽  
Better Than

Hydrophilic polyvinylidene fluoride (PVDF) flat ultrafiltration membranes were prepared by wet-spinning method. The effects of technical parameters of maleic anhydride grafted onto PVDF on the performance of hydrophilic PVDF membranes were investigated, the preparation technical parameters were determined, and the hydrophilic PVDF flat membranes were prepared. Then, hydrophilic PVDF membranes were characterized in terms of pure water flux, contact angle, infrared spectroscopic analysis and scanning electron microscope(SEM). The results showed that maleic anhydride had been grafted onto PVDF, and the hydrophilic performance of the modified membrane was better than the traditional one.

scholarly journals Synthesis, characterization and filtration performance of the polyvinylidene fluoride membrane modified by poly(methyl ethacrylate-co-2-acrylamido-2-methylpropane sulfonic acid)

2018 ◽  
Vol 19 (4) ◽  
pp. 1279-1285
Author(s):  
Q. Y. Zhang ◽  
Q. An ◽  
Y. G. Guo ◽  
J. Zhang ◽  
K. Y. Zhao
Keyword(s):  
Sulfonic Acid ◽  
Polyvinylidene Fluoride ◽  
Phase Inversion ◽  
Pure Water ◽  
Water Flux ◽  
Contact Angles ◽  
Fouling Resistance ◽  
Inversion Process ◽  
Pvdf Membrane ◽  
Pure Water Flux

Abstract To enhance the anti-fouling and separating properties of polyvinylidene fluoride (PVDF) membranes, an amphiphilic copolymer of methyl methacrylate and 2-acrylamido-2-methylpropane sulfonic acid, poly(MMA-co-AMPS), was designed and synthesized. Through a phase-inversion process, the poly(MMA-co-AMPS) were fully dispersed in the PVDF membrane. The properties of membrane including the surface and cross-section morphology, surface wettability and fouling resistance under different pH solutions were investigated. Compared to the unmodified PVDF membranes, the contact angles of modified PVDF membranes decreased from 80.6° to 71.6°, and the pure water flux increased from 54 to 71 L·m−2·h−1. In addition, the hybrid PVDF membrane containing 0.5 wt% copolymers demonstrated an larger permeability, better fouling resistance and higher recovery ratio via pure water backlashing, when it was compared with the other blend membranes, and the virgin one in the cyclic test of anti-fouling. The modified membranes with the copolymers possessed an outstanding performance and may be used for further water treatment applications.

Preparation and Characterization of Poly(vinylidene) Fluoride Membranes Reinforced by Modified Nano-SiO2 Particles

2014 ◽  
Vol 789 ◽  
pp. 201-204
Author(s):  
Ai Wen Qin ◽  
Xiang Li ◽  
Bo Mou Ma ◽  
Xin Zhen Zhao ◽  
Chun Yi Liu ◽  
...  
Keyword(s):  
Pore Size ◽  
Vinylidene Fluoride ◽  
Cell Structure ◽  
Membrane Surface ◽  
Pure Water ◽  
Water Flux ◽  
Cross Sectional ◽  
Antifouling Property ◽  
Poly Vinylidene Fluoride ◽  
Mechanical Performances

Poly (vinylidene fluoride) (PVDF) hybrid membranes reinforced by hydrophilic nanoSiO2 particles were fabricated from PVDF/N-dimethylacetamide (DMAc)/γ-butyrolactone (γ-BL) system via thermally induced phase separation (TIPS) process. Surface and cross-sectional morphology of membranes were characterized by scanning electron microscope (SEM). The properties such as permeability, mechanical performances and antifouling property were also determined. The results showed that the pore size of membrane surface became smaller, while cross-sectional morphology was changed from bicontinuous structure to cell structure, the pore size became larger and majorities of closed pores became open with the addition of hydrophilic nanoSiO2 particles in the system. Compared with pure membrane, pure water flux of hybrid membrane increased by 30.3%, i.e. from 290 to 378 L/(m2·h·0.1MPa), antifouling property increased from 63.1% to 80.2%. Meanwhile, tensile strength and elongation at break increased by 70.6% and124%, respectively.

scholarly journals Fabrication and Characterization of Nanofibers Membranes using Electrospinning Technology for Oil Removal

2021 ◽  
Vol 18 (4) ◽  
pp. 1338
Author(s):  
Amer Naji Al-Naemi ◽  
Mohammed Amer Abdul-Majeed ◽  
Mustafa H. Al-Furaiji ◽  
Inmar N Ghazi
Keyword(s):  
Polyvinylidene Fluoride ◽  
Membrane Surface ◽  
Water Flux ◽  
Oil Removal ◽  
Nanofiber Membrane ◽  
Pvdf Membrane ◽  
Electrospinning Method ◽  
Average Water ◽  
Graphene Membranes

Oily wastewater is one of the most challenging streams to deal with especially if the oil exists in emulsified form. In this study, electrospinning method was used to prepare nanofiberous polyvinylidene fluoride (PVDF) membranes and study their performance in oil removal. Graphene particles were embedded in the electrospun PVDF membrane to enhance the efficiency of the membranes. The prepared membranes were characterized using a scanning electron microscopy (SEM) to verify the graphene stabilization on the surface of the membrane homogeneously; while FTIR was used to detect the functional groups on the membrane surface. The membrane wettability was assessed by measuring the contact angle. The PVDF and PVDF / Graphene membranes efficiency was tested in separation of emulsified oil from aqueous solutions. The results showed that PVDF-Graphene nanofiber membrane exhibited better performance than the plain PVDF nanofiber membrane with average water flux of 210 and 180 L.m-2.h-1, respectively. Both membranes showed high oil rejection with more than 98%.

Sign in / Sign up

Export Citation Format

Share Document