scholarly journals Post-cracking tensile behaviour of steel-fibre-reinforced roller-compacted-concrete for FE modelling and design purposes

2017 ◽  
Vol 67 (326) ◽  
pp. 122 ◽  
Author(s):  
N. Jafarifar ◽  
K. Pilakoutas ◽  
H. Angelakopoulos ◽  
T. Bennett
Keyword(s):  
Reinforced Concrete ◽  
Steel Fibre ◽  
Bending Test ◽  
Tensile Behaviour ◽  
Fibre Reinforced Concrete ◽  
Test Results ◽  
Fe Modelling ◽  
Steel Fibres ◽  
Roller Compacted Concrete ◽  
Crack Band

Fracture of steel-fibre-reinforced-concrete occurs mostly in the form of a smeared crack band undergoing progressive microcracking. For FE modelling and design purposes, this crack band could be characterised by a stress-strain (σ-ε) relationship. For industrially-produced steel fibres, existing methodologies such as RILEM TC 162-TDF (2003) propose empirical equations to predict a trilinear σ-ε relationship directly from bending test results. This paper evaluates the accuracy of these methodologies and their applicability for roller-compacted-concrete and concrete incorporating steel fibres recycled from post-consumer tyres. It is shown that the energy absorption capacity is generally overestimated by these methodologies, sometimes up to 60%, for both conventional and roller-compacted concrete. Tensile behaviour of fibre-reinforced-concrete is estimated in this paper by inverse analysis of bending test results, examining a variety of concrete mixes and steel fibres. A multilinear relationship is proposed which largely eliminates the overestimation problem and can lead to safer designs.

Adding an expansive agent to increase the toughness of steel fibre reinforced concrete

2019 ◽  
Vol 26 (4) ◽  
pp. 197-208
Author(s):  
Leo Gu Li ◽  
Albert Kwok Hung Kwan
Keyword(s):  
Reinforced Concrete ◽  
Steel Fibre ◽  
The Other ◽  
Fibre Reinforced Concrete ◽  
Test Results ◽  
Compressive Properties ◽  
Shrinkage Cracking ◽  
Steel Fibre Reinforced Concrete ◽  
Expansive Agent ◽  
Concrete Matrix

Previous research studies have indicated that using fibres to improve crack resistance and applying expansive agent (EA) to compensate shrinkage are both effective methods to mitigate shrinkage cracking of concrete, and the additions of both fibres and EA can enhance the other performance attributes of concrete. In this study, an EA was added to fibre reinforced concrete (FRC) to produce concrete mixes with various water/binder (W/B) ratios, steel fibre (SF) contents and EA contents for testing of their workability and compressive properties. The test results showed that adding EA would slightly increase the superplasticiser (SP) demand and decrease the compressive strength, Young’s modulus and Poisson’s ratio, but significantly improve the toughness and specific toughness of the steel FRC produced. Such improvement in toughness may be attributed to the pre-stress of the concrete matrix and the confinement effect of the SFs due to the expansion of the concrete and the restraint of the SFs against such expansion.

scholarly journals Experimental Investigation of Shear Strength for Steel Fibre Reinforced Concrete Beams

2021 ◽  
Vol 15 (1) ◽  
pp. 81-92
Author(s):  
Constantinos B. Demakos ◽  
Constantinos C. Repapis ◽  
Dimitros P. Drivas
Keyword(s):  
Tensile Strength ◽  
Compressive Strength ◽  
Shear Strength ◽  
Reinforced Concrete ◽  
Steel Fibre ◽  
Concrete Beams ◽  
Reinforced Concrete Beams ◽  
Fibre Reinforced Concrete ◽  
Steel Fibres ◽  
Steel Fibre Reinforced Concrete

Aims: The aim of this paper is to investigate the influence of the volume fraction of fibres, the depth of the beam and the shear span-to-depth ratio on the shear strength of steel fibre reinforced concrete beams. Background: Concrete is a material widely used in structures, as it has high compressive strength and stiffness with low cost manufacturing. However, it presents low tensile strength and ductility. Therefore, through years various materials have been embedded inside it to improve its properties, one of which is steel fibres. Steel fibre reinforced concrete presents improved flexural, tensile, shear and torsional strength and post-cracking ductility. Objective: A better understanding of the shear performance of SFRC could lead to improved behaviour and higher safety of structures subject to high shear forces. Therefore, the influence of steel fibres on shear strength of reinforced concrete beams without transverse reinforcement is experimentally investigated. Methods: Eighteen concrete beams were constructed for this purpose and tested under monotonic four-point bending, six of which were made of plain concrete and twelve of SFRC. Two different aspect ratios of beams, steel fibres volume fractions and shear span-to-depth ratios were selected. Results: During the experimental tests, the ultimate loading, deformation at the mid-span, propagation of cracks and failure mode were detected. From the tests, it was shown that SFRC beams with high volume fractions of fibres exhibited an increased shear capacity. Conclusion: The addition of steel fibres resulted in a slight increase of the compressive strength and a significant increase in the tensile strength of concrete and shear resistance capacity of the beam. Moreover, these beams exhibit a more ductile behaviour. Empirical relations predicting the shear strength capacity of fibre reinforced concrete beams were revised and applied successfully to verify the experimental results obtained in this study.

scholarly journals Experimental study of flexural behaviour of layered steel fibre reinforced concrete beams

2017 ◽  
Vol 23 (6) ◽  
pp. 806-813 ◽  
Author(s):  
Inmaculada MARTÍNEZ-PÉREZ ◽  
Juozas VALIVONIS ◽  
Remigijus ŠALNA ◽  
Alfonso COBO-ESCAMILLA
Keyword(s):  
Reinforced Concrete ◽  
Steel Fibre ◽  
Load Capacity ◽  
Reinforced Concrete Beams ◽  
Internal Layer ◽  
Fibre Reinforced Concrete ◽  
Test Results ◽  
Flexural Behaviour ◽  
Steel Fibre Reinforced Concrete ◽  
Layered Beams

The building of structures from steel fibre reinforced concrete (SFRC) in the external and conventional rein­forced concrete (RC) in the internal layer represents an economical alternative of structures effectively using SFRC. The paper presents test results of flexural behaviour of layered beams with SFRC external layers and RC internal layer. The behaviour of these beams is compared to test results of SFRC and conventional RC beams. The test results show, that the flexural load capacity for all series of beams is nearly similar, but the deflections of layered beams are less comparing to monolithic ones. It also been shown that the equations indicated in the Eurocode 2 can be used to design the flexural reinforcement in layered SFRC beams.

scholarly journals Failure mode in shear of steel fiber reinforced concrete beams

2018 ◽  
Vol 163 ◽  
pp. 02003 ◽  
Author(s):  
Julita Krassowska ◽  
Marta Kosior-Kazberuk
Keyword(s):  
Reinforced Concrete ◽  
Steel Fiber ◽  
Concrete Beams ◽  
Fiber Reinforced Concrete ◽  
Reinforced Concrete Beams ◽  
Bending Test ◽  
Fibre Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Steel Fibres

Experimental tests were carried out to assess the failure model of steel fiber reinforced concrete beams. Experimental research was focused on observing changes in the behavior of the tested elements depending on the amount of shear reinforcement and the fiber. Model two-span beams with a cross-section of 80x180 mm and a length of 2000 mm were tested. The beams had varied stirrup spacing. The following amounts of steel fibres in concrete were used: 78.5 kg/m3 (1.0%) i 118 kg/m3 (1.5%). Concrete beams without fibres were examined at the same time. The beams were loaded in a five-point bending test until they were destroyed. Shear or bending capacity of the element was observed. Fibre reinforced concrete beams were not destroyed rapidly, but they kept their shape consistent under load. Larger number of diagonal cracks with a smaller width were observed in fibre reinforced concrete beams. Failure of concrete beams without fibres was rapid, with a characteristic brittle cracking. Steel fibres revealed the ability to transfer significant shear stress after cracking in comparison to plain concrete.

Complementary Use of Inductive Test and Bending Test for the Characterization of SFRC

2014 ◽  
Vol 580-583 ◽  
pp. 2213-2219 ◽  
Author(s):  
Lin Liao ◽  
Sergio Cavalaro ◽  
Albert de la Fuente ◽  
Antonio Aguado
Keyword(s):  
Steel Fibre ◽  
Fibre Orientation ◽  
Bending Test ◽  
Fibre Reinforced Concrete ◽  
Test Results ◽  
Flexural Behaviour ◽  
Steel Fibre Reinforced Concrete ◽  
Three Point Bending ◽  
Experimental Campaign

Many researches have been conducted in past decades for promoting the application of steel fibre reinforced concrete (SFRC), either conventional or self-compacting. However, the differences of post-crack behaviour and the properties of these two types of concrete remains unclear. The objective of this paper is to analyse such differences in terms of flexural behaviour, fibre orientation and contribution as well as the fibre content. For that, an extensive experimental campaign was carried out. In total 3 mixes of self-compacting and 3 mixes with traditional concrete were produced with the nominal fibre contents of 30kg/m3, 45kg/m3 and 60kg/m3. In each series, specimens were produces and characterized by three point bending test (code EN 14651) and inductive test. The results illustrate how fibre orientation and distribution justify the differences in the mechanical behaviour of the materials and the scatter of the bending test results.

Mechanical Properties and Fracture Energy of Concrete Beams Reinforced with Basalt Fibres

2022 ◽  
Author(s):  
Ana Caroline Da Costa Santos ◽  
Paul Archbold
Keyword(s):  
Tensile Strength ◽  
Reinforced Concrete ◽  
Fracture Energy ◽  
Mechanical Performance ◽  
Plain Concrete ◽  
Natural Fibre ◽  
Bending Test ◽  
Natural Material ◽  
Fibre Reinforced Concrete ◽  
Steel Fibres

Fibre-reinforced concrete (FRC) is widely employed in the construction industry, with assorted fibre types being used for different applications. Typically, steel fibres give additional tensile strength to the mixture, while flexible fibres may be used in large sections, such as floor slabs, to control crack width and to improve the handling ability of precast sections. For many reasons, including durability concerns, environmental impact, thermal performance, etc, alternatives to the currently available fibres are being sought. This study examines the potential of using basalt fibres, a mineral and natural material, as reinforcement of concrete sections in comparison to steel fibres and plain concrete mix. Mixes were tested containing 0.5% and 1.0% of basalt fibres measuring 25mm length, 0.5% of the same material with 48mm length and steel fibres measuring 50mm by 0.05%, 0.1%, 0.15% and 0.2% of the concrete volume. For the mechanical performance analysis, the 3-point bending test was led and the fracture energy, Young’s modulus and tensile strength in different moments of the tests were calculated. When compared to the control mixtures and the steel-fibre-reinforced concrete, the mixes containing basalt had a reduction in their elastic modulus, representing a decrease in the concrete brittleness. At the same time, the fracture energy of the mixtures was significantly increased with the basalt fibres in both lengths. Finally, the flexural strength was also higher for the natural fibre reinforced concrete than for the plain concrete and comparable to the results obtained with the addition of steel fibres by 0.15%.

Experimental Study of Steel Fibre Bridging Action on Crack Propagation in Fibre Reinforced Concrete

2006 ◽  
Vol 324-325 ◽  
pp. 1067-1070 ◽  
Author(s):  
Zhi Hong Xu ◽  
Wen Yin Liang ◽  
Yu Jing Liang
Keyword(s):  
Reinforced Concrete ◽  
Crack Propagation ◽  
Steel Fibre ◽  
Fibre Reinforced Concrete ◽  
Interfacial Bond ◽  
Cycle Number ◽  
Steel Fibres ◽  
Steel Fibre Reinforced Concrete ◽  
Fibre Bridging ◽  
The Matrix

In this paper the bridging action of steel fibres on the model I crack propagation has been studied experimentally for steel fibre reinforced concrete (FRC). From the experimental results three main conclusions are obtained. First, the bridging action increases with the number of the steel fibres across the crack surface and the stress intensity factor near the crack tip decreases thereby. Second, bridging action increases with the strength of the matrix because the matrix with higher strength can provide stronger interfacial bond with steel fibres. Third, the interfacial bonding gets damaged when the steel fibres under cyclic loads and the bridging action degrades with the cycle number.

Experimental Tests of Steel Fibre Reinforced Concrete Beams under Drop-Weight Impacts

2014 ◽  
Vol 626 ◽  
pp. 311-316 ◽  
Author(s):  
Yi Fei Hao ◽  
Hong Hao ◽  
Gang Chen
Keyword(s):  
Reinforced Concrete ◽  
Steel Fibre ◽  
Concrete Beams ◽  
Plain Concrete ◽  
Fibre Reinforced Concrete ◽  
Steel Fibres ◽  
Steel Fibre Reinforced Concrete ◽  
Impact Tests ◽  
Drop Weight ◽  
The Impact

Concrete is a brittle material, especially under tension. Intensive researches have been reported to add various types of fibres into concrete mix to increase its ductility. Recently, the authors proposed a new type of steel fibre with spiral shape to reinforce concrete material. Laboratory tests on concrete cylinder specimens demonstrated that compared to other fibre types such as the hooked-end, deformed and corrugated fibres the new fibres have larger displacement capacity and provide better bonding with the concrete. This study performs drop-weight impact tests to investigate the behaviour of concrete beams reinforced by different types of steel fibres. The quasi-static compressive and split tensile tests were also conducted to obtain the static properties of plain concrete and steel fibre reinforced concrete (FRC) materials. The quasi-static tests were carried out using hydraulic testing machine and the impact tests were conducted using an instrumented drop-weight testing system. Plain concrete and concrete reinforced by the commonly used hooked-end steel fibres and the proposed spiral-shaped steel fibres were tested in this study. The volume dosage of 1% fibre was used to prepare all FRC specimens. Repeated drop-weight impacts were applied to the beam specimens until total collapse. A 15.2 kg hard steel was used as the drop-weight impactor. A drop height of 0.5 m was considered in performing the impact tests. The force-displacement relations and the energy absorption capabilities of plain concrete and FRC beams were obtained, compared and discussed. The advantage and effectiveness of the newly proposed spiral-shaped steel fibres in increasing the performance of FRC beam elements under impact loads were examined.