Abrasion Behavior of WC Reinforced Cast Iron Surface Composite Fabricated by Cast-Infiltration Method

2012 ◽  
Vol 476-478 ◽  
pp. 555-559
Author(s):  
Guo Jian Cao ◽  
Er Jun Guo ◽  
Yi Cheng Feng ◽  
Li Ping Wang
Keyword(s):  
Wear Resistance ◽  
Cast Iron ◽  
Sliding Wear ◽  
Room Temperature ◽  
Matrix Alloy ◽  
Volume Fractions ◽  
Heat Treated ◽  
The Matrix ◽  
Infiltration Method ◽  
Better Than

In this paper, WC particles and NH4HCO3 powders were mixed evenly, and then pressed under 150MPa. The WC porous preforms were obtained after the compacts being heat treated to eliminate NH4HCO3. The volume ratios of WC in the preforms were 30%, 40% and 50% respectively. WC/Fe composites were fabricated by infiltrating liquid cast iron into the WC porous preforms. Optic microscope and scanning electron microscope were employed to observe the microstructure of the matrix alloy and the composites. The results showed that matrix alloy without WC addition had pores in the surface. The microstructure of the composites with WC volume fractions of 30%, and 40% were denser than that of 50%. Hardness and wet sliding wear behaviors of the composites were investigated at room temperature. The addition of WC particles could effectively improve the hardness and the wear resistance of the composites. The influence of volume fractions on hardness of the composites was similar to that on wear resistance. The hardness and the wear resistance of the 40vol.%WC/Fe composite was better than those of the 30vol.%WC/Fe composite. And the properties of the 50vol.%WC/Fe composite were the worst.

Microstructure and wear resistance of Cuss-toughened Cr5Si3/CrSi metal silicide alloys

2005 ◽  
Vol 20 (5) ◽  
pp. 1122-1130 ◽  
Author(s):  
Y.X. Yin ◽  
H.M. Wang
Keyword(s):  
Solid Solution ◽  
Wear Resistance ◽  
Sliding Wear ◽  
Room Temperature ◽  
Wear Test ◽  
Melting Process ◽  
Dry Sliding Wear ◽  
Metal Silicide ◽  
X Ray Diffraction ◽  
X Ray

Wear-resistant Cu-based solid-solution-toughened Cr5Si3/CrSi metal silicide alloy with a microstructure consisting of predominantly the dual-phase primary dendrites with a Cr5Si3 core encapsulated by CrSi phase and a small amount of interdendritic Cu-based solid solution (Cuss) was designed and fabricated by the laser melting process using Cr–Si–Cu elemental powder blends as the precursor materials. The microstructure of the Cuss-toughened Cr5Si3/CrSi metal silicide alloy was characterized by optical microscopy, powder x-ray diffraction, and energy dispersive spectroscopy. The Cuss-toughened silicide alloys have excellent wear resistance and low coefficient of friction under room temperature dry sliding wear test conditions with hardened 0.45% C carbon steel as the sliding–mating counterpart.

Tungsten Carbide Dispersed High Cr-Ni Cast Iron Produced by Plasma Spraying

2017 ◽  
Vol 891 ◽  
pp. 565-568
Author(s):  
Yasuhiro Hoshiyama ◽  
Kyouhei Yamaguchi ◽  
Hidekazu Miyake
Keyword(s):  
Wear Resistance ◽  
Cast Iron ◽  
Tungsten Carbide ◽  
Alloy Powder ◽  
Treatment Temperature ◽  
Heat Treated ◽  
Ni Alloy ◽  
Low Pressure Plasma ◽  
Plasma Sprayed ◽  
Carbide Particles

Fe-C-W-Cr-Ni alloy powder in diameter of 32-53 μm made by argon atomization was low-pressure plasma sprayed to produce high Cr-Ni cast iron base deposits with finely dispersed tungsten carbide particles. The as-sprayed deposit produced on a non-cooled substrate was composed of γFe, αFe and carbide. The fine precipitates in the as-sprayed deposit were carbide. With increasing heat treatment temperature up to 1273 K, the carbide particles coarsened. The as-sprayed deposit produced on a non-cooled substrate had higher hardness than the heat-treated deposits. The wear resistance of the as-sprayed deposit produced on a non-cooled substrate was lower than that of heat-treated deposits. The as-sprayed deposit produced on a non-cooled substrate and heat-treated deposits had higher wear resistance than commercial stainless steel.

scholarly journals Differences in Dry Sliding Wear Behavior between Al–12Si–CuNiMg Alloy and Its Composite Reinforced with Al2O3 Fibers

Materials ◽  
2019 ◽  
Vol 12 (11) ◽  
pp. 1749 ◽  
Author(s):  
Qing Zhang ◽  
Jie Gu ◽  
Shuo Wei ◽  
Ming Qi
Keyword(s):  
Sliding Wear ◽  
Volume Fraction ◽  
Wear Behavior ◽  
Testing Machine ◽  
Matrix Alloy ◽  
Wear Testing ◽  
Dry Sliding Wear ◽  
Dry Sliding ◽  
The Matrix ◽  
Pin On Disk

The dry sliding wear behavior of the Al-12Si-CuNiMg matrix alloy and its composite reinforced with Al2O3 fibers was investigated using a pin-on-disk wear-testing machine. The volume fraction of Al2O3 fibers in the composite was 17 vol.%. Wear tests are conducted under normal loads of 2.5, 5.0, and 7.5 N, and sliding velocities of 0.25, 0.50, and 1.0 m/s. Furthermore, the worn surfaces of the matrix alloy and the composite were examined using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results showed that the wear resistance of the composite was inferior to that of the matrix alloy, which could be attributed to the high content of reinforcement and casting porosities in the composite. Worn-surface analysis indicates that the dominant wear mechanisms of both materials were abrasive wear and adhesive wear under the present testing conditions.

scholarly journals Effect of Necklace-Type Distribution of SiC Particles on Dry Sliding Wear Behavior of As-Cast AZ91D/SiCp Composites

Crystals ◽  
2020 ◽  
Vol 10 (4) ◽  
pp. 296 ◽  
Author(s):  
Chao Sun ◽  
Nannan Lu ◽  
Huan Liu ◽  
Xiaojun Wang ◽  
Xiaoshi Hu ◽  
...  
Keyword(s):  
Wear Resistance ◽  
Sliding Wear ◽  
Wear Behavior ◽  
Dry Sliding Wear ◽  
Dry Sliding ◽  
Interface Bonding ◽  
Type Distribution ◽  
Wear Rates ◽  
Sic Particles ◽  
The Matrix

In this study, the dry sliding wear behaviors of SiC particle reinforced AZ91D matrix composites fabricated by stirring casting method were systematically investigated. The SiC particles in as-cast composites exhibited typical necklace-type distribution, which caused the weak interface bonding between SiC particles and matrix in particle-segregated zones. During dry sliding at higher applied loads, SiC particles were easy to debond from the matrix, which accelerated the wear rates of the composites. While at the lower load of 10 N, the presence of SiC particles improved the wear resistance. Moreover, the necklace-type distribution became more evident with the decrease of particle sizes and the increase of SiC volume fractions. Larger particles had better interface bonding with the matrix, which could delay the transition of wear mechanism from oxidation to delamination. Therefore, composites reinforced by larger SiC particles exhibited higher wear resistance. Similarly, owing to more weak interfaces in the composites with high content of SiC particles, more severe delamination occurred and the wear resistance of the composites was impaired.

Dry Sliding Wear Behavior of the Reinforced by Graphite Particle and Heat Treated of Recycled Aluminum AA6061 Based MMC Fabricated by Powder Metallurgy Method

2017 ◽  
Vol 740 ◽  
pp. 9-16
Author(s):  
Ahmed Sahib Mahdi ◽  
Mohammad Sukri Mustapa ◽  
Mahmod Abd Hakim Mohamad ◽  
Abdul Latif M. Tobi ◽  
Muhammad Irfan Ab Kadir ◽  
...  
Keyword(s):  
Wear Resistance ◽  
Powder Metallurgy ◽  
Compression Strength ◽  
Sliding Wear ◽  
Wear Behavior ◽  
High Wear Resistance ◽  
Dry Sliding Wear ◽  
Powder Metallurgy Method ◽  
Heat Treated ◽  
Improvement Ratio

The micro-hardness and compression of recycling aluminum alloy AA6061 were investigated as a function of the different microstructure and constituent powder metallurgy method. Five specimens were selected to investigate the compression strength and microhardness. The first, as fabricated specimen (as compacted), the second was as heat treated by quenching and aging process. Three specimens were mixed with Graphite particles as a reinforcement material. Compression strength values were tested for the specimens as fabricated and heat treated which were 195 and 300 MPa, respectively. The improvement ratio was 52% for the specimen as heat treated. On the other hand, high wear resistance was given by the specimen as heat treated, whereas, the lower wear strength was at the specimen mixed with 4.5% Graphite. These results were attributed to that the wear resistance related to the microhardness value.

The Effect of Boron on the Sliding Wear Behavior of Iron-Based Hardfacing Alloys for Nuclear Power Plants Valves

2006 ◽  
Vol 510-511 ◽  
pp. 562-565
Author(s):  
Jeng Wan Yoo ◽  
Kwon Yeong Lee ◽  
Ji Hui Kim ◽  
Ki Soo Kim ◽  
Seon Jin Kim
Keyword(s):  
Wear Resistance ◽  
Martensitic Transformation ◽  
Nuclear Power ◽  
Sliding Wear ◽  
Power Plants ◽  
Wear Behavior ◽  
Wear Test ◽  
Wear Loss ◽  
The Matrix ◽  
Iron Based

A new iron-based wear resistance alloy was developed to replace the Co-containing Stellite 6 alloys in nuclear power industry. The effect of B addition on the wear resistance was investigated. Sliding wear tests of Fe-Cr-C-Si-xB (x = 0.0, 0.3, 0.6, 1.0 and 2.0 wt%) alloys were performed in air at the room temperature under a contact stress of 103 MPa. Low-boron alloys containing less than 0.6 wt% boron showed an excellent wear resistance than any other tested alloys. The improvement was associated with the matrix hardening by promotion of the γ→α′straininduced martensitic transformation occurring during the wear test. However, the alloys containing more than 1.0 wt% boron showed slightly increased wear loss compared to the low-boron alloys because of the absence of the strain-induced martensitic transformation and the presence of the brittle FeB particles, aiding crack initiation.

Study on the Wear Resistance of Cast-Oozing Different Content of WC

2011 ◽  
Vol 239-242 ◽  
pp. 990-993
Author(s):  
Ai Qin Wang ◽  
Shu Li Wang ◽  
Jing Pei Xie
Keyword(s):  
Wear Resistance ◽  
Cast Iron ◽  
Iron Layer ◽  
Wear Properties ◽  
Metallurgical Bonding ◽  
The Matrix ◽  
Different Content

In this paper, the WC and high-Cr Cast Iron layer were obtained on the surface of ZG30Cr steel by casting-penetrating process, the organization and wear properties of penetrating layer were studied. The results show that the layer is dense, without pores, slag and other defects, the penetrating layer and substrate are metallurgical bonding. When 20 %WC and 80 % Cr-Fe with are added to permeability agent, the penetrating layer has the best wear resistance, is 11.3 times the matrix materials.

scholarly journals The Effect of Palm Kernel Shell Ash on the Mechanical and Wear Properties of White Cast Iron

2020 ◽  
Vol 45 (2) ◽  
pp. 20-27
Author(s):  
Kayode I. Fesomade ◽  
Damilola D. Alewi ◽  
Saliu O. Seidu ◽  
Sheriff O. Saka ◽  
Bonaventure I. Osuide ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Wear Resistance ◽  
Cast Iron ◽  
Elemental Composition ◽  
White Cast Iron ◽  
Palm Kernel ◽  
Rotary Furnace ◽  
Wear Properties ◽  
Palm Kernel Shell ◽  
The Matrix

This study investigates the influence of palm kernel shell ash (PKSA) on mechanical and wear properties of white cast iron (WCI) particularly its influence on its microstructure, elemental composition, hardness and wear resistance. The PKSA was characterized to determine its elemental composition, and it was found to contain high amount of silicon (Si) and iron (Fe) followed by calcium (Ca) and other trace elements. The cast iron was cast into rods of specific dimension with sand casting method using rotary furnace to re-melt cast iron scrap. The WCI rods were then cut into bits for the various test. Heat treatment operation was carried out to determine its properties. Upon completion of the examinations, it was found that the PKSA increased the cementite phase within the matrix of the cast iron, and reduced the pearlitic phase and graphite formation, which gave it increased hardness, and perfect wear resistance due to the increment in carbon content and reduction in silicon content. Also, upon heat treatment, it was found that the PKSA reduced the pearlitic phase within the matrix of the cast iron, increases the formation of transformed ledeburites, austenitic dendrites and tempered graphite, which lead to increased machinability and ductility as well as to reduced hardness, and wear resistance when compared to non-heat treated samples.

Sign in / Sign up

Export Citation Format

Share Document