Kenaf Nanofiber/Polylactic Acid (PLA) Nanocomposite

2011 ◽  
Vol 471-472 ◽  
pp. 1095-1100 ◽  
Author(s):  
Agnes Surai Lasat ◽  
Abdan Khalina ◽  
Nor Azowa Ibrahim
Keyword(s):  
Electron Microscopy ◽  
Lignin Content ◽  
Tensile Modulus ◽  
Kenaf Fiber ◽  
Transmission Electron ◽  
Acetyl Group ◽  
Treated Fiber ◽  
High Pressure Homogenizer ◽  
Internal Mixer ◽  
Scanning Electron

Kenaf fiber was treated with alkaline to reduce lignin content and tested under Fourier transform infrared spectroscopy (FTIR). FTIR result showed that peak at 1146 cm-1 which is acetyl group of lignin was reduced in treated fiber while disappearing of carbonyl group in treated kenaf fiber at 1750cm-1 was significantly shown compared to untreated kenaf fiber. Treated fiber undergoes mechanical size decrement process by high pressure homogenizer with 500bar pressure and 60 passes. Transmission Electron microscopy (TEM) was used to determine size and distribution of fiber. Moreover, morphology of nanofiber was observed under scanning electron microscope (SEM). Nanofiber (3%, 5%, 8% and 10%) was mixed with PLA using internal mixer and then compressed with hot pressed to produce specimen for tensile test. Tensile strength and tensile modulus of nanocomposite with 10% of nanofiber increased by 30% and 85% respectively compared to pure PLA.

Ultrastructural Analysis of the Salivary Glands of Gromphadorhina Portentosa (Schaum)

1977 ◽  
Vol 35 ◽  
pp. 638-639
Author(s):  
P.J. Dailey
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Salivary Glands ◽  
Secretory Vesicles ◽  
The Past ◽  
Transmission Electron ◽  
Means Of Transmission ◽  
Gromphadorhina Portentosa ◽  
Scanning Electron ◽  
Topographical Relief

The structure of insect salivary glands has been extensively investigated during the past decade; however, none have attempted scanning electron microscopy (SEM) in ultrastructural examinations of these secretory organs. This study correlates fine structure by means of SEM cryofractography with that of thin-sectioned epoxy embedded material observed by means of transmission electron microscopy (TEM).Salivary glands of Gromphadorhina portentosa were excised and immediately submerged in cold (4°C) paraformaldehyde-glutaraldehyde fixative1 for 2 hr, washed and post-fixed in 1 per cent 0s04 in phosphosphate buffer (4°C for 2 hr). After ethanolic dehydration half of the samples were embedded in Epon 812 for TEM and half cryofractured and subsequently critical point dried for SEM. Dried specimens were mounted on aluminum stubs and coated with approximately 150 Å of gold in a cold sputtering apparatus.Figure 1 shows a cryofractured plane through a salivary acinus revealing topographical relief of secretory vesicles.

Two- or three-way observations of the identical cell elements within the same sections by LM, TEM and/or SEM

1978 ◽  
Vol 36 (2) ◽  
pp. 82-83 ◽  
Author(s):  
Nakazo Watari ◽  
Yasuaki Hotta ◽  
Yoshio Mabuchi
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Fine Structure ◽  
Light Microscopy ◽  
Thin Sections ◽  
Transmission Electron ◽  
Identical Cell ◽  
Electron Microscopes ◽  
Scanning Electron

It is very useful if we can observe the identical cell elements within the same sections by light microscopy (LM), transmission electron microscopy (TEM) and/or scanning electron microscopy (SEM) sequentially, because, the cell fine structure can not be indicated by LM, while the color is; on the other hand, the cell fine structure can be very easily observed by EM, although its color properties may not. However, there is one problem in that LM requires thick sections of over 1 μm, while EM needs very thin sections of under 100 nm. Recently, we have developed a new method to observe the same cell elements within the same plastic sections using both light and transmission (conventional or high-voltage) electron microscopes.In this paper, we have developed two new observation methods for the identical cell elements within the same sections, both plastic-embedded and paraffin-embedded, using light microscopy, transmission electron microscopy and/or scanning electron microscopy (Fig. 1).

Scanning and Transmission Microscopy of Nematocyst Batteries in Epitheliomuscular Cells of Hydra

1971 ◽  
Vol 29 ◽  
pp. 410-411 ◽  
Author(s):  
Jane A. Westfall ◽  
S. Yamataka ◽  
Paul D. Enos
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Osmium Tetroxide ◽  
External Surface ◽  
Three Dimensional ◽  
Surface Structures ◽  
Transmission Microscopy ◽  
Transmission Electron ◽  
Freeze Dried ◽  
Scanning Electron

Scanning electron microscopy (SEM) provides three dimensional details of external surface structures and supplements ultrastructural information provided by transmission electron microscopy (TEM). Animals composed of watery jellylike tissues such as hydras and other coelenterates have not been considered suitable for SEM studies because of the difficulty in preserving such organisms in a normal state. This study demonstrates 1) the successful use of SEM on such tissue, and 2) the unique arrangement of batteries of nematocysts within large epitheliomuscular cells on tentacles of Hydra littoralis.Whole specimens of Hydra were prepared for SEM (Figs. 1 and 2) by the fix, freeze-dry, coat technique of Small and Màrszalek. The specimens were fixed in osmium tetroxide and mercuric chloride, freeze-dried in vacuo on a prechilled 1 Kg brass block, and coated with gold-palladium. Tissues for TEM (Figs. 3 and 4) were fixed in glutaraldehyde followed by osmium tetroxide. Scanning micrographs were taken on a Cambridge Stereoscan Mark II A microscope at 10 KV and transmission micrographs were taken on an RCA EMU 3G microscope (Fig. 3) or on a Hitachi HU 11B microscope (Fig. 4).

Application of Scanning Electron Microscopy to Medical Research

1969 ◽  
Vol 27 ◽  
pp. 12-13
Author(s):  
J. D. Hutchison
Keyword(s):  
Electron Microscopy ◽  
Electron Microscope ◽  
Medical Research ◽  
Prosthetic Heart Valve ◽  
School Of Medicine ◽  
Transmission Electron ◽  
Definition Of ◽  
Mechanism Of Failure ◽  
The Brain ◽  
Scanning Electron

When the transmission electron microscope was commercially introduced a few years ago, it was heralded as one of the most significant aids to medical research of the century. It continues to occupy that niche; however, the scanning electron microscope is gaining rapidly in relative importance as it fills the gap between conventional optical microscopy and transmission electron microscopy.IBM Boulder is conducting three major programs in cooperation with the Colorado School of Medicine. These are the study of the mechanism of failure of the prosthetic heart valve, the study of the ultrastructure of lung tissue, and the definition of the function of the cilia of the ventricular ependyma of the brain.

A Comparative Study of Fractographic Replicas

1974 ◽  
Vol 32 ◽  
pp. 566-567
Author(s):  
Loren Anderson ◽  
Pat Pizzo ◽  
Glen Haydon
Keyword(s):  
Electron Microscopy ◽  
Electron Microscopic Examination ◽  
Direct Examination ◽  
Electron Microscopic ◽  
Reliable Technique ◽  
Service Failures ◽  
Transmission Electron ◽  
Mode Of Failure ◽  
Scanning Electron Microscopic ◽  
Scanning Electron

Transmission electron microscopy of replicas has long been used to study the fracture surfaces of components which fail in service. Recently, the scanning electron microscope (SEM) has gained popularity because it allows direct examination of the fracture surface. However, the somewhat lower resolution of the SEM coupled with a restriction on the sample size has served to limit the use of this instrument in investigating in-service failures. It is the intent of this paper to show that scanning electron microscopic examination of conventional negative replicas can be a convenient and reliable technique for determining mode of failure.

Scanning and Transmission Electron Microscopy of Human Red Blood Cells

1969 ◽  
Vol 27 ◽  
pp. 44-45
Author(s):  
A.J. Tousimis ◽  
T.R. Padden
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Blood Cells ◽  
Room Temperature ◽  
Type Specimen ◽  
New Combination ◽  
Human Red Blood Cells ◽  
Transmission Electron ◽  
Microscope Slides ◽  
Scanning Electron

The size, shape and surface morphology of human erythrocytes (RBC) were examined by scanning electron microscopy (SEM), of the fixed material directly and by transmission electron microscopy (TEM) of surface replicas to compare the relative merits of these two observational procedures for this type specimen.A sample of human blood was fixed in glutaraldehyde and washed in distilled water by centrifugation. The washed RBC's were spread on freshly cleaved mica and on aluminum coated microscope slides and then air dried at room temperature. The SEM specimens were rotary coated with 150Å of 60:40- gold:palladium alloy in a vacuum evaporator using a new combination spinning and tilting device. The TEM specimens were preshadowed with platinum and then rotary coated with carbon in the same device. After stripping the RBC-Pt-C composite film, the RBC's were dissolved in 2.5N HNO3 followed by 0.2N NaOH leaving the preshadowed surface replicas showing positive topography.

Copper Localization in Cirrhotic Rat Liver by Scanning Electron Microscopy

1969 ◽  
Vol 27 ◽  
pp. 38-39 ◽  
Author(s):  
J. C. Russ ◽  
E. McNatt
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Endoplasmic Reticulum ◽  
Electron Microscope ◽  
Copper Acetate ◽  
Lead Citrate ◽  
Dense Bodies ◽  
Transmission Electron ◽  
Electron Mode ◽  
Scanning Electron

In order to study the retention of copper in cirrhotic liver, rats were made cirrhotic by carbon tetrachloride inhalation twice weekly for three months and fed 0.2% copper acetate ad libidum in drinking water for one month. The liver tissue was fixed in osmium, sectioned approximately 2000 Å thick, and stained with lead citrate. The section was examined in a scanning electron microscope (JEOLCO JSM-2) in the transmission electron mode.Figure 1 shows a typical area that includes a red blood cell in a sinusoid, a disse, and a portion of the cytoplasm of a hepatocyte which contains several mitochondria, peribiliary dense bodies, glycogen granules, and endoplasmic reticulum.

Identification of calcium oxalate crystals in dried or fixed tobacco leaf

1984 ◽  
Vol 42 ◽  
pp. 288-289
Author(s):  
Vicki L. Baliga ◽  
Mary Ellen Counts
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Calcium Oxalate ◽  
Growth And Development ◽  
Polarized Light ◽  
Calcium Oxalate Crystals ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

Calcium is an important element in the growth and development of plants and one form of calcium is calcium oxalate. Calcium oxalate has been found in leaf seed, stem material plant tissue culture, fungi and lichen using one or more of the following methods—polarized light microscopy (PLM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and x-ray diffraction.Two methods are presented here for qualitatively estimating calcium oxalate in dried or fixed tobacco (Nicotiana) leaf from different stalk positions using PLM. SEM, coupled with energy dispersive x-ray spectrometry (EDS), and powder x-ray diffraction were used to verify that the crystals observed in the dried leaf with PLM were calcium oxalate.

Use of SEM, X-ray analysis and TEM to localize Fe3+ reduction in roots

1988 ◽  
Vol 46 ◽  
pp. 392-393 ◽  
Author(s):  
William P. Wergin ◽  
P. F. Bell ◽  
Rufus L. Chaney
Keyword(s):  
Electron Microscopy ◽  
Root Hairs ◽  
Rapid Reduction ◽  
X Ray ◽  
Physical Evidence ◽  
Transmission Electron ◽  
Young Root ◽  
Insoluble Precipitate ◽  
Uptake And Transport ◽  
Scanning Electron

In dicotyledons, Fe3+ must be reduced to Fe2+ before uptake and transport of this essential macronutrient can occur. Ambler et al demonstrated that reduction along the root could be observed by the formation of a stain, Prussian blue (PB), Fe4 [Fe(CN)6]3 n H2O (where n = 14-16). This stain, which is an insoluble precipitate, forms at the reduction site when the nutrient solution contains Fe3+ and ferricyanide. In 1972, Chaney et al proposed a model which suggested that the Fe3+ reduction site occurred outside the cell membrane; however, no physical evidence to support the model was presented at that time. A more recent study using the PB stain indicates that rapid reduction of Fe3+ occurs in a region of the root containing young root hairs. Furthermore the most pronounced activity occurs in plants that are deficient in Fe. To more precisely localize the site of Fe3+ reduction, scanning electron microscopy (SEM), x-ray analysis, and transmission electron microscopy (TEM) were utilized to examine the distribution of the PB precipitate that was induced to form in roots.

Comparative Study of the Fine Morphology of Sensory Receptors in Aspidogaster conchicola and Cotylaspis insignis

1972 ◽  
Vol 30 ◽  
pp. 150-151
Author(s):  
Venita F. Allison ◽  
J. E. Ubelaker ◽  
J. H. Martin
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Nervous System ◽  
Osmic Acid ◽  
Sensory Receptors ◽  
Transmission Electron ◽  
Sensory Structures ◽  
Fine Morphology ◽  
Scanning Electron

It has been suggested that parasitism results in a reduction of sensory structures which concomitantly reflects a reduction in the complexity of the nervous system. The present study tests this hypothesis by examining the fine morphology and the distribution of sensory receptors for two species of aspidogastrid trematodes by transmission and scanning electron microscopy. The species chosen are an ectoparasite, Cotylaspis insignis and an endoparasite, Aspidogaster conchicola.Aspidogaster conchicola and Cotylaspis insignis were obtained from natural infections of clams, Anodonta corpulenta and Proptera purpurata. The specimens were fixed for transmission electron microscopy in phosphate buffered paraformaldehyde followed by osmic acid in the same buffer, dehydrated in an ascending series of ethanol solutions and embedded in Epon 812.

Sign in / Sign up

Export Citation Format

Share Document