LOWER TEMPERATURE FORMATION OF ALUMINA THIN FILMS THROUGH SOL–GEL ROUTE

2008 ◽  
Vol 15 (05) ◽  
pp. 681-688 ◽  
Author(s):  
S. RIAZ ◽  
S. SHAMAILA ◽  
B. KHAN ◽  
S. NASEEM
Keyword(s):  
Thin Films ◽  
Band Gap ◽  
Structural Changes ◽  
Sol Gel ◽  
Stable Form ◽  
X Ray Diffraction ◽  
Glass Substrates ◽  
Lower Temperature ◽  
Xrd Patterns ◽  
Scanning Electron

Bayerite sol is spun onto single crystal Si substrate, after synthesis and optimization, to obtain films of thickness ~ 0.2 μm. The deposited films are room temperature dried and then heated up to a temperature of 350°C in order to obtain Al 2 O 3. Surface and structural changes, during heating, are observed with optical microscopy. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) are used for post-treatment analyses/characterization. The as-deposited and heated samples' surfaces are smooth as seen with optical and scanning electron microscope in case of optimized conditions. XRD patterns show the change from amorphous to crystalline behavior of these films when heated under various conditions. The most stable form of aluminum oxide, i.e. α- Al 2 O 3, is obtained when samples are heated up to a temperature of as low as 350°C. The thin films are also deposited onto sodalime glass substrates in order to confirm Al 2 O 3 formation through band gap probing. Photoconduction is used to find the energy band gap, which comes out to be 4.7 eV; lower value is correlated to the defect induced states in the band gap.

High Transmission and Low Resistivity Cadmium Tin Oxide Thin Films Deposited by Sol-Gel

2014 ◽  
Vol 1675 ◽  
pp. 151-156 ◽  
Author(s):  
Carolina. J. Diliegros Godines ◽  
Rebeca Castanedo Pérez ◽  
Gerardo Torres Delgado ◽  
Orlando Zelaya Ángel
Keyword(s):  
Thin Films ◽  
Tin Oxide ◽  
Sol Gel ◽  
Dip Coating ◽  
X Ray Diffraction ◽  
Glass Substrates ◽  
Corning Glass ◽  
Vacuum Atmosphere ◽  
Xrd Patterns ◽  
Quartz Substrates

ABSTRACTTransparent conducting cadmium tin oxide (CTO) thin films were obtained from a mixture of CdO and SnO2 precursor solutions by the dip-coating sol-gel technique. The thin films studied in this work were made with 7 coats (∼200 nm) on corning glass and quartz substrates. Each coating was deposited at a withdrawal speed of 2 cm/min, dried at 100°C for 1 hour and then sintered at 550°C for 1 hour in air. In order to decrease the resistivity values of the films, these were annealed in a vacuum atmosphere and another set of films were annealed in an Ar/CdS atmosphere. The annealing temperatures (Ta) were 450°C, 500°C and 550°C, as well as 600°C and 650°C, when corning glass and quartz substrates were used, respectively. X-Ray diffraction (XRD) patterns of the films annealed in a vacuum showed that there is only the presence of CTO crystals for 450°C≤ Ta ≤ 600°C and CTO+SnO2 crystals for Ta=650°C. The films annealed in Ar/CdS atmosphere were only constituted of CTO crystals independent of the Ta. The minimum resistivity value obtained was ∼4 x 10-4 Ωcm (Rsheet= 20 Ω/□) for the films deposited on quartz and annealed at Ta=600°C under an Ar/CdS atmosphere. The films deposited on quartz showed the higher optical transmission (∼90%) with respect to the films deposited on corning glass substrates (∼85%) in the Uv-vis region. For their optical and electrical characteristics, these films are good candidates as transparent electrodes in solar cells.

Preparation and characterization of V2O5 doped SiO2-TiO2 thin films

2012 ◽  
Vol 2 (1) ◽  
Author(s):  
Marek Nocuń ◽  
Sławomir Kwaśny
Keyword(s):  
Thin Films ◽  
Band Gap ◽  
Photoelectron Spectroscopy ◽  
Sol Gel ◽  
Dip Coating ◽  
Band Gap Energy ◽  
Tio2 Thin Films ◽  
Glass Substrates ◽  
Gel Technique

AbstractIn our investigation, V doped SiO2/TiO2 thin films were prepared on glass substrates by dip coating sol-gel technique. Chemical composition of the samples was studied by X-ray photoelectron spectroscopy (XPS). Transmittance of the samples was characterized using UV-VIS spectrophotometry. Subsequently band-gap energy (Eg) was estimated for these films. Powders obtained from sols were characterized by FTIR spectroscopy. It was found that vanadium decreases optical band gap of SSiO2/TiO2 films.

scholarly journals Studies on the Optical Properties and Surface Morphology of Nickel Phthalocyanine Thin Films

2007 ◽  
Vol 4 (2) ◽  
pp. 255-264 ◽  
Author(s):  
Benny Joseph ◽  
C. S. Menon
Keyword(s):  
Thin Films ◽  
Surface Morphology ◽  
Band Gap ◽  
Electron Micrographs ◽  
Optical Band Gap ◽  
Scanning Electron Micrographs ◽  
Nickel Phthalocyanine ◽  
Glass Substrates ◽  
Substrate Temperatures ◽  
Scanning Electron

Thin films of Nickel Phthalocyanine (NiPc) are fabricated at a base pressure of 10-5m.bar using Hind-Hivac thermal evaporation plant. The films are deposited on to glass substrates at various temperatures 318, 363, 408 and 458K. The optical absorption spectra of these thin films are measured. Present studies reveal that the optical band gap energies of NiPc thin films are highly dependent on the substrate temperatures. The structure and surface morphology of the films deposited on glass substrates of temperatures 303, 363 and 458K are studied using X-ray diffractograms and Scanning Electron Micrographs (SEM), show that there is a change in the crystallinity and surface morphology due to change in the substrate temperatures. Full width at half maximum (FWHM) intensity of the diffraction peaks is also found reduced with increasing substrate temperatures. Scanning electron micrographs show that these crystals are fiber like at high substrate temperatures. The optical band gap increases with increase in substrate temperature and is then reduced with fiber-like grains at 408K. The band gap increases again at 458K with full of fiber like grains. Trap energy levels are also observed for these films.

LUMINESCENT PROPERTIES OF SOL-GEL DEPOSITED Eu:TiO2 THIN FILMS

2001 ◽  
Vol 15 (17n19) ◽  
pp. 769-773 ◽  
Author(s):  
M. GARCIA-ROCHA ◽  
A. CONDE-GALLARDO ◽  
I. HERNANDEZ-CALDERON ◽  
R. PALOMINO-MERINO
Keyword(s):  
Thin Films ◽  
Sol Gel ◽  
Luminescent Properties ◽  
X Ray Diffraction ◽  
Si Substrates ◽  
Glass Substrates ◽  
Corning Glass ◽  
Different Temperatures ◽  
Hecd Laser

In this work we show the results on tile growth and optical characterization of TiO 2 thin films doped with Eu atoms. Eu:TiO2 films were grown at room temperature with different Eu concentrations by sol-gel on Si Corning glass substrates. A different crystalline structure is developed for the films deposited on Corning glass than those deposited on Si as observed from x-ray diffraction experiments. Room and low temperature photoluminescence (PL) was measured by using two different lines (325 and 442 nm) of a HeCd laser. A strong PL signal associated to the 5 D 0→7 F 2 transition from Eu +3 was observed. A better emission was obtained from those films deposited on Si substrates, Finally, the evolution of the PL signal is studied when the samples are annealed at different temperatures in O 2 atmosphere.

SiO2ZrO2 Thin Films as Low Temperature NO2 and O3 Sensors

2015 ◽  
Vol 1088 ◽  
pp. 81-85 ◽  
Author(s):  
T.N. Myasoedova ◽  
Victor V. Petrov ◽  
Nina K. Plugotarenko ◽  
Dmitriy V. Sergeenko ◽  
Galina Yalovega ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Thin Films ◽  
Scanning Electron Microscopy ◽  
Low Temperature ◽  
Annealing Temperature ◽  
Sol Gel ◽  
X Ray Diffraction ◽  
X Ray ◽  
Operating Temperatures ◽  
Scanning Electron

Thin SiO2ZrO2films were prepared, up to 0.2 μm thick, by means of the sol–gel technology and characterized by a Scanning electron microscopy and X-ray diffraction. It is shown the presence of monoclinic, cubic and tetragonal phases of ZrO2in the SiO2matrix. The crystallites sizes depend on the annealing temperature of the film and amount to 35 and 56 nm for the films annealed at 773 and 973 K, respectively. The films resistance is rather sensitive to the presence of NO2and O3impurity in air at lower operating temperatures in the range of 30-60°C.

Influence of Copper Concentration on the Structural and Optical Properties of Chemically Deposited CuSbS2 Thin Films

2016 ◽  
Vol 19 (1) ◽  
pp. 015-019 ◽  
Author(s):  
Jebadurai Joy Jeba Vijila ◽  
Kannusamy Mohanraj ◽  
Sethuramachandran Thanikaikarasan ◽  
Ganesan Sivakumar ◽  
Thaiyan Mahalingam ◽  
...  
Keyword(s):  
Thin Films ◽  
Field Emission ◽  
Secondary Phase ◽  
Diffraction Field ◽  
Spectroscopic Techniques ◽  
X Ray Diffraction ◽  
X Ray ◽  
Glass Substrates ◽  
Simple Chemical ◽  
Scanning Electron

Thin films of CuSbS2 have been deposited on ultrasonically cleaned glass substrates using a simple chemical bath deposition technique. Prepared films have been characterized using X-ray diffraction, Field Emission Scanning Electron Microscopy and UV-Vis-NIR spectroscopic techniques, respectively. X-ray diffraction analysis revealed that the prepared films possess polycrystalline in nature with orthorhombic CuSbS2 in addition to secondary phase of monoclinic Cu3SbS3 and cubic Cu12Sb4S13 for different copper concentrations. Field Emission Scanning Electron Spectroscopic analysis showed that the prepared films possess spherical shaped grains with irregular shaped clusters. Optical absorption analysis showed that the prepared films possess band gap value in the range between 1.7 and 2.4 eV.

Properties of CdS Thin Films Grown by Chemical Bath Deposition as a Function of Bath Temperature

2009 ◽  
Vol 609 ◽  
pp. 243-247 ◽  
Author(s):  
H. Moualkia ◽  
S. Hariech ◽  
M.S. Aida
Keyword(s):  
Thin Films ◽  
Optical Properties ◽  
Band Gap ◽  
Chemical Bath Deposition ◽  
Bath Temperature ◽  
Band Gap Energy ◽  
X Ray Diffraction ◽  
Glass Substrates ◽  
Cds Thin Films ◽  
Direct Band

The present work deals with the preparation and characterization of cadmium sulfur (CdS) thin films. These films are prepared by chemical bath deposition on the well cleaned glass substrates. The thickness of the samples was measured by using profilometer DEKTAK, structural and optical properties were studied by X-ray diffraction analysis, and UV-visible spectrophotometry. The optical properties of the films have been investigated as a function of temperature. The band gap energy and Urbach energy were also investigated as a function of temperature. From the transmittance data analysis the direct band gap ranges from 2.21 eV to 2.34 eV. A dependence of band gap on temperature has been observed and the possible raisons are discussed. Transmission spectra indicates a high transmission coefficient (75 %). Structural analysis revealed that the films showed cubic structure, and the crystallite size decreased at a higher deposition temperature.

scholarly journals Characteristics and optical properties of Fe3+ doped SiO2/TiO2 thin films prepared by the sol-gel dip-coating method

2013 ◽  
Vol 16 (1) ◽  
pp. 92-100
Author(s):  
Chien Mau Dang ◽  
Dam Duy Le ◽  
Tam Thi Thanh Nguyen ◽  
Dung Thi My Dang
Keyword(s):  
Thin Films ◽  
Optical Properties ◽  
Sol Gel ◽  
Dip Coating ◽  
X Ray Diffraction ◽  
Tio2 Thin Films ◽  
Water Contact ◽  
Glass Substrates ◽  
Coating Method ◽  
Dip Coating Method

In this study, we have successfully synthesized Fe3+ doped SiO2/TiO2 thin films on glass substrates using the sol-gel dip-coating method. After synthesizing, the samples were annealed at 5000C in the air for 1 hour. The characteristics and optical properties of Fe3+ doped SiO2/TiO2 films were then investigated by X-ray diffraction (XRD), ultraviolet-visible spectroscopy (UV-vis) and Fourier transform infrared spectroscopy (FT-IR). An antifogging ability of the glass substrates coated with the fabricated film is investigated and explained by a water contact angle under visible-light. The analyzed results also show that the crystalline phase of TiO2 thin films comprised only the anatase TiO2, but the crystalline size decreased from 8.8 to 5.9 nm. We also observed that the absorption edge of Fe3+- doped SiO2/TiO2 thin films shifted towards longer wavelengths (i.e. red shifted) from 371.7nm to 409.2 nm when the Fe3+-doped concentration increased from 0 to 1 % mol.

Characterization of MnS Thin Films Deposited by Chemical Bath Deposition

2019 ◽  
Vol 969 ◽  
pp. 433-438 ◽  
Author(s):  
Dattatraya K. Sonavane ◽  
S.K. Jare ◽  
M.A. Shaikh ◽  
R.V. Kathare ◽  
R.N. Bulakhe
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Band Gap ◽  
Chemical Bath Deposition ◽  
Band Gap Energy ◽  
Sulfur Source ◽  
X Ray Diffraction ◽  
Glass Substrates ◽  
Double Beam

Glass substrates are used to deposit thin films utilizing basic and value effective chemical bath deposition (CBD) technique. The films were prepared from the mixture as solutions of manganous acetate tetrahydrate [C4H6MnO44H2O] as a manganese source, thiourea [(H2 N) 2 CS] as a sulfur source and triethanolamine (TEA) [(HOC2H4)3N] as a complexing agent.In the present paper the deposition was successfully done at 60 °C temperature. The absorption properties and band gap energy were determined employing double beam spectrophotometer. The optical band gap value calculated from absorption spectra of MnS thin film is found to be about 3.1eV.The MnS thin film was structurally characterized by X-ray Diffraction (XRD). The MnS thin film was morphologically characterized by Scanning Electron Microscopy (SEM) and elemental analysis was performed using EDS to confirm the formation of MnS.

Growth of the Sol-Gel Based ZnO:Al Thin Films with High Doping Concentration

2012 ◽  
Vol 485 ◽  
pp. 144-148
Author(s):  
Jian Lin Chen ◽  
Yan Jie Ren ◽  
Jian Chen ◽  
Jian Jun He ◽  
Ding Chen
Keyword(s):  
Thin Films ◽  
Doping Concentration ◽  
Sol Gel ◽  
Zno Thin Films ◽  
X Ray Diffraction ◽  
X Ray ◽  
Glass Substrates ◽  
High Doping Concentration ◽  
Doped Zno ◽  
Surface Morphologies

Preferentially oriented Al-doped ZnO thin films with doping concentration of 1, 2, 3, 5 and 10 mol% respectively were prepared on glass substrates via sol-gel route. The crystallinity of films was characterized by X-ray diffraction and the surface morphologies were observed by scanning electron microscopy. The results show that ZnO:Al films at low doping concentration (1, 2 mol%) grow into dense homogenous microstructure. However, as for high doping concentration (3, 5, 10 mol%), Al3+ precipitate in the form of amorphous Al2O3 and ZnO:Al films exhibit heterogeneous nucleation and exceptional growth of the big plate-like crystals at the interface of the amorphous Al2O3 and ZnO:Al matrix.