scholarly journals Effect of Disinfectants on Mechanical Properties of Orthodontic Acrylics

2019 ◽  
Vol 2019 ◽  
pp. 1-10 ◽  
Author(s):  
Tobias Bensel ◽  
Jens J. Bock ◽  
Anne Kebernik ◽  
Christin Arnold ◽  
Sonia Mansour ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Flexural Strength ◽  
Significant Influence ◽  
Colour Change ◽  
Water Disinfection ◽  
Distilled Water ◽  
Micro Hardness ◽  
Average Roughness ◽  
The Impact

Objective. Infection control protocols in dentistry dictate that orthodontic acrylics have to be disinfected. No specific products for orthodontic acrylics are available. The objective of this study was to investigate the influence of chemical disinfectants on mechanical properties of orthodontic acrylics.Materials and Methods. 260 test specimens of two cold-curing orthodontic acrylics were manufactured. Three chemical disinfecting agents were tested: Impresept, D050 Instru-Gen, and Stammopur DR. Test specimens were stored in distilled water and divided into test groups. E-Modulus, flexural strength, macro hardness, micro hardness, average roughness, and colour change were measured.Results. Disinfection agents showed no significant influence on E-modulus. Values ranged from 1783.80 ± 163.80 MPa (Forestacryl colourless) to 2474.00 ± 135.00 MPa (Orthocryl green) after storage in distilled water. Disinfection agents performed no significant influence on flexural strength. Values ranged from 18.64±1.59 N/mm2(Forestacryl colourless) to 25.64 ± 1.43 N/mm2(Orthocryl green) after storage in distilled water. Orthocryl colourless showed a reduction of the macro hardness after disinfection (Stammopur DR (p≤0.001), D050 Instru-Gen (p≤0.037)). Disinfection of Orthocryl green with D050 Instru-Gen (p<0.001) and Forestacryl colourless with Impresept (p≤0.001) led to a reduction of macro hardness. Micro hardness of Orthocryl colourless altered significantly after disinfection with D050 Instru-Gen (p≤0.001). Micro hardness of Forestacryl colourless increased (Impresept (p≤0.039)) and decreased (Stammopur DR (p≤0.006) Instru-Gen (p≤0.001)) after disinfection. Average roughness did not change significantly (Orthocryl colourless). Forestacryl colourless performed a significant change after disinfection with Stammopur DR (p≤0.05). This is also true for the disinfection of Orthocryl green and Forestacryl pink with Instru-Gen (p≤0.05). Disinfection performed no significant influence on colour change. ΔE-values were in a range of 1 to 2.Conclusions. Some orthodontic acrylics disinfection caused significant changes of determined parameters. Changes were specific for the applied disinfectant and tested orthodontic acrylic. Further studies should verify the impact of long-term disinfection intervals. Thus, from manufacturers of orthodontic acrylics recommendations for appropriate disinfectants would be desirable.

scholarly journals Mechanical Properties of Cement-Treated Soil Mixed with Cellulose Nanofibre

2021 ◽  
Vol 11 (14) ◽  
pp. 6425
Author(s):  
Hidenori Takahashi ◽  
Shinya Omori ◽  
Hideyuki Asada ◽  
Hirofumi Fukawa ◽  
Yusuke Gotoh ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Flexural Strength ◽  
Geotechnical Engineering ◽  
Strength Development ◽  
Soft Ground ◽  
Wood Cellulose ◽  
Treated Soil ◽  
Made In ◽  
Cement Treatment

Cellulose nanofibre (CNF), a material composed of ultrafine fibres of wood cellulose fibrillated to nano-order level, is expected to be widely used because of its excellent properties. However, in the field of geotechnical engineering, almost no progress has been made in the development of techniques for using CNFs. The authors have focused on the use of CNF as an additive in cement treatment for soft ground, where cement is added to solidify the ground, because CNF can reduce the problems associated with cement-treated soil. This paper presents the results of a study on the method of mixing CNF, the strength and its variation obtained by adding CNF, and the change in permeability. CNF had the effect of mixing the cement evenly and reducing the variation in the strength of the treated soil. The CNF mixture increased the strength at the initial age but reduced the strength development in the long term. The addition of CNF also increased the flexural strength, although it hardly changed the permeability.

A novel recycled polyethylene terephthalate/polyamide 11 (rPET/PA11) thermoplastic blend

2021 ◽  
pp. 147776062110010
Author(s):  
Zahid Iqbal Khan ◽  
Zurina Binti Mohamad ◽  
Abdul Razak Bin Rahmat ◽  
Unsia Habib ◽  
Nur Amira Sahirah Binti Abdullah
Keyword(s):  
Mechanical Properties ◽  
Impact Strength ◽  
Flexural Strength ◽  
Polyethylene Terephthalate ◽  
Practical Implication ◽  
Polyamide 11 ◽  
Recycled Polyethylene ◽  
Twin Screw ◽  
Electron Microscopy Analysis ◽  
The Impact

This work explores a novel blend of recycled polyethylene terephthalate/polyamide 11 (rPET/PA11). The blend of rPET/PA11 was introduced to enhance the mechanical properties of rPET at various ratios. The work’s main advantage was to utilize rPET in thermoplastic form for various applications. Three different ratios, i.e. 10, 20 and 30 wt.% of PA11 blend samples, were prepared using a twin-screw extruder and injection moulding machine. The mechanical properties were examined in terms of tensile, flexural and impact strength. The tensile strength of rPET was improved more than 50%, while the increase in tensile strain was observed 42.5% with the addition of 20 wt.% of PA11. The improved properties of the blend were also confirmed by the flexural strength of the blends. The flexural strength was increased from 27.9 MPa to 48 MPa with the addition of 30 wt.% PA11. The flexural strain of rPET was found to be 1.1%. However, with the addition of 10, 20 and 30 wt.% of PA11, the flexural strain was noticed as 1.7, 2.1, and 3.9% respectively. The impact strength of rPET/PA11 at 20 wt.% PA11 was upsurged from 110.53 to 147.12 J/m. Scanning electron microscopy analysis revealed a dispersed PA11 domain in a continuous rPET matrix morphology of the blends. This work practical implication would lead to utilization of rPET in automobile, packaging, and various industries.

scholarly journals Influence of Different Concentration and Ratio of a Photoinitiator System on the Properties of Experimental Resin Composites

2017 ◽  
Vol 28 (6) ◽  
pp. 726-730 ◽  
Author(s):  
Caio Vinícius Signorelli Grohmann ◽  
Eveline Freitas Soares ◽  
Eduardo José Carvalho Souza-Junior ◽  
William Cunha Brandt ◽  
Regina Maria Puppin-Rontani ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Tertiary Amine ◽  
Water Sorption ◽  
Water Solubility ◽  
Distilled Water ◽  
Resin Composites ◽  
Amine Concentration ◽  
One Way Anova

Abstract The aim in this study was to evaluate the influence of different ratio of camphorquinone/tertiary amine concentration on the flexural strength (FS), elastic modulus (EM), degree of conversion (DC), yellowing (YL), water sorption (WS) and water solubility (WSL) of experimental composites. Thus, acrylate blends were prepared with different camphorquinone (CQ) and amine (DABE) concentrations and ratios by weight: (CQ/DABE%): 0.4/0.4% (C1), 0.4/0.8% (C2), 0.6/0.6% (C3), 0.6/1.2% (C4), 0.8/0.8% (C5), 0.8/1.6% (C6), 1.0/1.0% (C7), 1.0/2.0% (C8), 1.5/1.5% (C9), 1.5/3.0% (C10). For the FS and EM, rectangular specimens (7x2x1 mm, n=10) were photo-activated by single-peak LED for 20 s and tested at Instron (0.5 mm/min). Then, the same specimens were evaluated by FTIR for DC measurement. For YL, disks (5x2 mm, n=10) were prepared, light-cured for 20 s and evaluated in spectrophotometer using the b aspect of the CIEL*a*b* system. For WS and WSL, the volume of the samples was calculated (mm³). For WS and WSL, composites disks (5x0.5 mm, n=5) were prepared. After desiccation, the specimens were stored in distilled water for 7 days and again desiccated, in order to measure the WS and WSL. Data were submitted to one-way ANOVA and Tukey’s test (5%). The groups C8, C9 and C10 showed higher DC, EM and YL means, compared to other composites. Therefore, the FS and WS values were similar among all groups. Also, C1, C2 and C3 presented higher WSL in 7 days, compared to other composites. In general, higher concentrations of camphorquinone promoted higher physical-mechanical properties; however, inducing higher yellowing effect for the experimental composites

Effect of Filler Compositions on the Mechanical Properties of Bamboo Filled Polyester Composite

2014 ◽  
Vol 879 ◽  
pp. 90-95 ◽  
Author(s):  
Abdul Rahman Noor Leha ◽  
Nor Amalina Nordin
Keyword(s):  
Mechanical Properties ◽  
Flexural Strength ◽  
Impact Test ◽  
Compression Molding ◽  
Engineering Applications ◽  
Maximum Value ◽  
Polyester Composite ◽  
Bamboo Powder ◽  
Flexural Tests ◽  
The Impact

Biocomposite from bamboo powder was fabricated by compression molding technique. The objective of this study was to investigate the mechanical properties of bamboo compounded with epoxy with different ratio. Tensile and flexural tests were done to characterize its mechanical properties. It was observed that the strength of bamboo-polyester was increased with increasing amount of bamboo powder. The tensile and flexural strength shows the highest value at 25 wt.% bamboo. However, the impact test shows the maximum value at 20 wt.% bamboo powder. These results exhibit the bamboo-polyester can be a good candidate to be used in many engineering applications

scholarly journals Mechanical Performance of Unstitched and Silk Fiber-Stitched Woven Kenaf Fiber-Reinforced Epoxy Composites

Materials ◽  
2020 ◽  
Vol 13 (21) ◽  
pp. 4801
Author(s):  
Yasir Khaleel Kirmasha ◽  
Mohaiman J. Sharba ◽  
Zulkiflle Leman ◽  
Mohamed Thariq Hameed Sultan
Keyword(s):  
Mechanical Properties ◽  
Flexural Strength ◽  
Mechanical Performance ◽  
Mechanical Test ◽  
Natural Fibers ◽  
Silk Fiber ◽  
Epoxy Composites ◽  
Test Results ◽  
The Impact ◽  
Woven Kenaf

Fiber composites are known to have poor through-thickness mechanical properties due to the absence of a Z-direction binder. This issue is more critical with the use of natural fibers due to their low strength compared to synthetic fibers. Stitching is a through-thickness toughening method that is used to introduce fibers in the Z-direction, which will result in better through-thickness mechanical properties. This research was carried out to determine the mechanical properties of unstitched and silk fiber-stitched woven kenaf-reinforced epoxy composites. The woven kenaf mat was stitched with silk fiber using a commercial sewing machine. The specimens were fabricated using a hand lay-up method. Three specimens were fabricated, one unstitched and two silk-stitched with deferent stitching orientations. The results show that the stitched specimens have comparable in-plane mechanical properties to the unstitched specimens. For the tensile mechanical test, stitched specimens show similar and 17.1% higher tensile strength compared to the unstitched specimens. The flexural mechanical test results show around a 9% decrease in the flexural strength for the stitched specimens. On the other hand, the Izod impact mechanical test results show a significant improvement of 33% for the stitched specimens, which means that stitching has successfully improved the out-of-plane mechanical properties. The outcome of this research indicates that the stitched specimens have better mechanical performance compared to the unstitched specimens and that the decrease in the flexural strength is insignificant in contrast with the remarkable enhancement in the impact strength.

Effect of layer thickness on irreversible thermal expansion and interlayer strength in fused deposition modeling

2017 ◽  
Vol 23 (5) ◽  
pp. 943-953 ◽  
Author(s):  
Anthony A. D’Amico ◽  
Analise Debaie ◽  
Amy M. Peterson
Keyword(s):  
Mechanical Properties ◽  
Thermal Expansion ◽  
Flexural Strength ◽  
Layer Thickness ◽  
Fused Deposition Modeling ◽  
Thermal Strain ◽  
Content Type ◽  
Fused Deposition ◽  
Deposition Modeling ◽  
The Impact

Purpose The aim of this paper is to examine the impact of layer thickness on irreversible thermal expansion, residual stress and mechanical properties of additively manufactured parts. Design/methodology/approach Samples were printed at several layer thicknesses, and their irreversible thermal expansion, tensile strength and flexural strength were determined. Findings Irreversible thermal strain increases with decreasing layer thickness, up to 22 per cent strain. Tensile and flexural strengths exhibited a peak at a layer thickness of 200 μm although the maximum was not statistically significant at a 95 per cent confidence interval. Tensile strength was 54 to 97 per cent of reported values for injection molded acrylonitrile butadiene styrene (ABS) and 29 to 73 per cent of those reported for bulk ABS. Flexural strength was 18 to 41 per cent of reported flexural strength for bulk ABS. Practical implications The large irreversible thermal strain exhibited that corresponding residual stresses could lead to failure of additively manufactured parts over time. Additionally, the observed irreversible thermal strains could enable thermally responsive shape in additively manufactured parts. Variation in mechanical properties with layer thickness will also affect manufactured parts. Originality/value Tailorable irreversible thermal strain of this magnitude has not been previously reported for additively manufactured parts. This strain occurs in parts made with both high-end and consumer grade fused deposition modeling machines. Additionally, the impact of layer thickness on tensile and flexural properties of additively manufactured parts has received limited attention in the literature.

Preparing of SMC Artificial Marble and its Mechanical Properties

2011 ◽  
Vol 55-57 ◽  
pp. 447-450 ◽  
Author(s):  
Jian Li ◽  
Zheng Qun Huang ◽  
Yan Qin
Keyword(s):  
Mechanical Properties ◽  
Impact Strength ◽  
Flexural Strength ◽  
Fiber Length ◽  
Filler Content ◽  
Fiber Content ◽  
Molding Temperature ◽  
Overall Performance ◽  
The Impact

In this article, a kind of SMC artificial marble was prepared. In order to enhance the mechanical properties and prolong the using life of SMC artificial marble, some effects such as fiber content, filler content and molding temperature etc. on the mechanical properties were carefully studied, too. Results showed that the increase of fiber content could improve the impact strength of SMC artificial marble when the fiber length was 10mm and the increase of filler content would decrease the flexural strength of SMC artificial marble. And the molding temperature at the range of 130°C ~ 160°C had little influence on the mechanical properties of SMC artificial marble. Comparing with natural marble and casting marble, SMC artificial marble owed superior overall performance and it was much more suitable for industry production.

Electrical and Mechanical Properties of Carbon Aerogels / Phenolic Resin for Nanocomposites

2011 ◽  
Vol 236-238 ◽  
pp. 1725-1730 ◽  
Author(s):  
Wei Jen Chen ◽  
Ming Yuan Shen ◽  
Yi Luen Li ◽  
Chin Lung Chiang ◽  
Ming Chuen Yip
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Impact Strength ◽  
Flexural Strength ◽  
Phenolic Resin ◽  
Surface Conductivity ◽  
Carbon Aerogels ◽  
Polymer Resin ◽  
The Impact ◽  
Humidity Environment

This study used carbon aerogels (CA) and phenolic resin in fixed proportations to produce nano high polymer resin, and used poly ehtylene oxide (PEO) as the modifying agent for phenolic resin to improve the mechanical properties of phenolic resin and promote the surface conductivity. The prepared nano high polymer resin and carbon cloth were made into nano-prepreg by using ultrasonic impregnation method, and a nano-prepreg composite material was prepared by using hot compacting and cut to test pieces to measure its mechanical properties and surface conductivity as well as the influence of temperature-humidity environment (85°C/168hr and 85°C/85%RH/168hr) on mechanical properties. The result showed that the surface conductivity increased by 64.55%, the tensile strength at room temperature increased by 35.7%, the flexural strength increased by 18.4%, and the impact strength increased by 101%. In hot environment (85°C/168hr), the tensile strength decreased by 23.8%, the flexural strength increased by 3.1%, and the impact strength increased by 84.6%. In high temperature-high humidity environment (85°C/85% RH/168hr), the tensile strength decreased by 29.6%, the flexural strength decreased by 17%, and the impact strength increased by 95.7%.Introduction

A method to improve dimensional accuracy and mechanical properties of injection molded polypropylene parts

2017 ◽  
Vol 37 (4) ◽  
pp. 323-334 ◽  
Author(s):  
Shuai Li ◽  
Guoqun Zhao ◽  
Jiachang Wang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Flexural Strength ◽  
Injection Molding ◽  
Weld Line ◽  
Dimensional Accuracy ◽  
Holding Time ◽  
Dimensional Shrinkage ◽  
Injection Molded ◽  
The Impact

Abstract Gas counter pressure (GCP) technology can impose a reverse pressure to melt and thereby effectively increase the pressure acting on the melt at flow front. Theoretically, it has a potential to solve some defects often occurring in conventional injection molding (CIM) process. This paper designed and manufactured a GCP injection mold. GCP injection molding experiments were conducted. Effects of GCP process on melt flow and density, dimensional accuracy, and mechanical properties of molded samples were investigated. The results showed that GCP process can effectively inhibit the “fountain effect” in melt filling process, decrease the dimensional shrinkage of molded samples, increase dimensional accuracy of samples, and effectively improve impact property of samples. For the samples without weld line, tensile strength and flexural strength of GCP injection molded samples are slightly increased in comparison with those of CIM samples, but for the samples with weld line, GCP process can greatly improve the tensile strength and flexural strength of molded samples. When GCP is 9 MPa and GCP holding time is 10 s, the dimensional accuracy of molded samples without weld line, the tensile strength and flexural strength of the molded samples with weld line all increase up to maximum values. In comparison with CIM samples, the dimensional shrinkage of samples without weld line decreases by 17.2%, the tensile strength and flexural strength of samples with weld line increase by 30.51% and 23.69%, respectively. The impact value of the samples molded by process parameter combination of GCP 9 MPa and GCP holding time 20 s is the highest, and the impact value increases by 18.65%.

The Influence of the Long-Term Storage of Hardwood on the Selected Physical and Mechanical Properties in View of Pulping

2016 ◽  
Vol 688 ◽  
pp. 10-16
Author(s):  
Blažej Seman ◽  
Anton Geffert ◽  
Jarmila Geffertova
Keyword(s):  
Mechanical Properties ◽  
Impact Strength ◽  
Continuous Production ◽  
Beech Wood ◽  
Physical And Mechanical Properties ◽  
Long Term Storage ◽  
The Impact ◽  
Term Storage ◽  
Strength In Bending

Wood is loosely stored to ensure continuous production inside paper mills where it is exposed to the effect of external factors. The impact of storage leads to some changes of mechanical and physical properties of wood, but these changes are not the same in all specimens. In this paper, it has been observed that the long term storage of wood influences the impact strength in bending and the permeability of wood for fluids. During the storage, there was a decrease of impact strength in bending of poplar heartwood by 28.3% and oak by 22.1% and mature beech wood by 37.3%. Also, there was decreased a permeability of wood, poplar sapwood 18.3 % and heartwood of 53.9%; oak sapwood by 20.0% and heartwood by 20.3%; beech sapwood 45.8% and mature wood by 48.2%. By decrease of the observed properties of the stored wood, a deterioration a quality of produced pulp can be expected (a higher Kappa number, amount reject and decrease the mechanical properties of pulp).

Sign in / Sign up

Export Citation Format

Share Document