scholarly journals Effect of Aggregate Size on Strength Characteristics of High Strength Lightweight Concrete

Materials ◽  
2020 ◽  
Vol 13 (6) ◽  
pp. 1314
Author(s):  
Hui Wei ◽  
Yang Liu ◽  
Tao Wu ◽  
Xi Liu
Keyword(s):  
Compressive Strength ◽  
Lightweight Concrete ◽  
Aggregate Size ◽  
Lightweight Aggregate ◽  
High Strength ◽  
Medium Size ◽  
Test Results ◽  
Estimation Model ◽  
Strength Tests ◽  
Single Size

Effects of aggregate size on the mechanical properties of lightweight concrete (LC) were investigated. Four gradings of lightweight aggregate (LWA) were designed and used to prepare the specimens for compressive strength, splitting tensile strength, and flexural strength tests. An estimating method for compressive strength of LC was then established. The compressive strength of tested LC was up to 95 MPa at 90-day curing time. The test results suggested that the absence of medium-size particles decreased the compaction of LC, therefore the density and compressive strength were negatively affected. Specimens having single size of aggregate showed lower splitting tensile and flexural strengths than that having three sizes of LWA. The parameters of the estimating model were determined according to the test results, and the compressive strength predictions of estimation model were compared with the results from other literature.

Effect of confinement on the behaviour of high-strength lightweight concrete columns

1986 ◽  
Vol 13 (6) ◽  
pp. 741-751 ◽  
Author(s):  
R. Basset ◽  
S. M. Uzumeri
Keyword(s):  
Experimental Investigation ◽  
Lightweight Concrete ◽  
Concrete Strength ◽  
Lightweight Aggregate ◽  
High Strength ◽  
Concrete Columns ◽  
Lightweight Aggregate Concrete ◽  
Test Results ◽  
Aggregate Concrete ◽  
Concrete Confinement

This paper summarizes an experimental investigation into the behaviour of high strength sand – lightweight concrete columns confined with rectangular ties. Fifteen reinforced and three unreinforced specimens were tested under monotonically increasing axial compression. Variables considered in this study were the longitudinal steel distribution and tie configuration, the tie steel spacing, the amount of tie steel, and the amount of longitudinal steel.The results indicated that unconfined high-strength lightweight aggregate concrete is a brittle material. The addition of lateral confining steel significantly improved the behaviour of this material, with a large amount of lateral steel resulting in very ductile behaviour. The tie configuration and resulting distribution of longitudinal steel contributed significantly to the confinement of concrete, with well-distributed steel resulting in improved behaviour. The ratio of specimen to cylinder concrete strength was observed to be 0.98, which is much higher than the commonly assumed value of 0.85.The test results were compared with results from selected theoretical confinement models. Based on the results of this investigation, existing models for concrete confinement give unconservative results for high-strength lightweight aggregate concrete and overestimate the ductility that can be achieved with this material. Key words: columns, confinement, ductility, high-strength concretes, lightweight aggregate concretes, reinforcement, stress–strain relationships, tests, ties, toughness.

scholarly journals Properties and Internal Curing of Concrete Containing Recycled Autoclaved Aerated Lightweight Concrete as Aggregate

2017 ◽  
Vol 2017 ◽  
pp. 1-11 ◽  
Author(s):  
Teewara Suwan ◽  
Pitiwat Wattanachai
Keyword(s):  
Compressive Strength ◽  
Lightweight Concrete ◽  
Value Added ◽  
Aggregate Size ◽  
Lightweight Aggregate ◽  
Normal Weight ◽  
Green Technology ◽  
Internal Curing ◽  
Low Carbon ◽  
Mix Proportion

Global warming is a vital issue addressed to every sector worldwide, including the construction industry. To achieve the concept of green technology, many attempts have been carried out to develop low-carbon footprint products. In the construction sector, Autoclaved Aerated Concrete (AAC) has become more popular and been manufactured to meet the construction demand. However, errors from manufacturing process accounted for approximately 3 to 5% of the AAC production. The development of AAC waste as lightweight aggregate in concrete is one of the potential approaches which was extendedly studied in this paper. The results showed that the compressive strength of AAC-LWA concrete was decreased with an increase in volume and coarse size. The optimum mix proportion was the AAC aggregate size of 1/2′′ to 3/8′′ with 20 to 40% replacement to normal weight aggregate. Internal curing by AAC-LWA was also observed and found to provide sufficient water inside the specimens, leading to an achievement in higher compressive strength. The main goal of this study is not only utilising unwanted wastes from industry (recycling of waste materials) but also building up a new knowledge of using AAC-LWA as an internal curing agent as well as the production of value-added lightweight concrete products.

scholarly journals Development of High Performance Aerogel Concrete (HPAC) and statistical evaluation of compressive strength for practical use in construction

2021 ◽  
Vol 2069 (1) ◽  
pp. 012196
Author(s):  
S Fickler ◽  
T Welsch ◽  
M Schnellenbach-Held
Keyword(s):  
Compressive Strength ◽  
High Performance ◽  
Lightweight Concrete ◽  
High Strength ◽  
Cement Matrix ◽  
Strength Tests ◽  
Materials Research ◽  
Anderson Darling ◽  
German Aerospace ◽  
The University

Abstract The Institute for Structural Concrete (ISC) at the University of Duisburg-Essen and the Institute of Materials Research of the German Aerospace Center (DLR) developed a new lightweight concrete, called “High Performance Aerogel Concrete” (HPAC). HPAC is made by embedding of silica aerogel granules in a high strength cement matrix. It exhibits a remarkable relation between compressive strength and thermal conductivity. HPAC for the load bearing layer of double-leaf external walls contains approx. 50 vol% aerogel and has a compressive strength in the range of normal concrete (20 MPa – 30 MPa). Up to now, the compressive strength of each mixture was determined on three to six cubes or cylinders. The scattering of the results has not been investigated yet. For this reason, 30 test specimens of a 50 vol%-mixture have been produced in two batches. The results of the compressive strength tests were then statistically evaluated. The underlying statistical distribution was determined by the Anderson-Darling-Test. Subsequently the 5 % fractile values of the mixtures, which represent the characteristic concrete compressive strength, were determined.

scholarly journals Effects of carbon nanotubes on expanded glass and silica aerogel based lightweight concrete

2021 ◽  
Vol 11 (1) ◽  
Author(s):  
Suman Kumar Adhikary ◽  
Žymantas Rudžionis ◽  
Simona Tučkutė ◽  
Deepankar Kumar Ashish
Keyword(s):  
Carbon Nanotubes ◽  
Compressive Strength ◽  
Silica Aerogel ◽  
Lightweight Concrete ◽  
Lightweight Aggregate ◽  
Cementitious Materials ◽  
Lightweight Aggregate Concrete ◽  
Multi Wall Carbon Nanotubes ◽  
Sem Image ◽  
Study Results

AbstractThis study is aimed to investigate the effect of carbon nanotubes on the properties of lightweight aggregate concrete containing expanded glass and silica aerogel. Combinations of expanded glass (55%) and hydrophobic silica aerogel particles (45%) were used as lightweight aggregates. Carbon nanotubes were sonicated in the water with polycarboxylate superplasticizer by ultrasonication energy for 3 min. Study results show that incorporating multi-wall carbon nanotubes significantly influences the compressive strength and microstructural performance of aerogel based lightweight concrete. The addition of carbon nanotubes gained almost 41% improvement in compressive strength. SEM image of lightweight concrete shows a homogeneous dispersal of carbon nanotubes within the concrete structure. SEM image of the composite shows presence of C–S–H gel surrounding the carbon nanotubes, which confirms the cites of nanotubes for the higher growth of C–S–H gel. Besides, agglomeration of carbon nanotubes and the presence of ettringites was observed in the transition zone between the silica aerogel and cementitious materials. Additionally, flowability, water absorption, microscopy, X-ray powder diffraction, and semi-adiabatic calorimetry results were analyzed in this study.

Effects of Nano-CaCO3 on the Compressive Strength and Microstructure of High Strength Concrete in Different Curing Temperature

2011 ◽  
Vol 121-126 ◽  
pp. 126-131 ◽  
Author(s):  
Qing Lei Xu ◽  
Tao Meng ◽  
Miao Zhou Huang
Keyword(s):  
Compressive Strength ◽  
Low Temperature ◽  
High Strength Concrete ◽  
High Strength ◽  
Curing Temperature ◽  
Test Results ◽  
Strength Concrete ◽  
Calcium Nitrite ◽  
Orientation Index ◽  
Early Strength

In this paper, effects of nano-CaCO3 on compressive strength and Microstructure of high strength concrete in standard curing temperature(21±1°C) and low curing temperature(6.5±1°C) was studied. In order to improve the early strength of the concrete in low temperature, the early strength agent calcium nitrite was added into. Test results indicated that 0.5% dosage of nano-CaCO3 could inhibit the effect of calcium nitrite as early strength agent, but 1% and 2% dosage of nano-CaCO3 could improve the strength of the concrete by 13% and 18% in standard curing temperature and by 17% and 14% in low curing temperature at the age of 3days. According to the XRD spectrum, with the dosage up to 1% to 2%, nano-CaCO3 can change the orientation index significantly, leading to the improvement of strength of concrete both in standard curing temperature and low curing temperature.

scholarly journals Properties of High-Strength Flowable Mortar Reinforced with Palm Fibers

2012 ◽  
Vol 2012 ◽  
pp. 1-5 ◽  
Author(s):  
Eethar Thanon Dawood ◽  
Mahyuddin Ramli
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Physical And Mechanical Properties ◽  
High Strength ◽  
Test Results ◽  
Palm Fiber ◽  
Toughness Index ◽  
Strength And Toughness

This study was conducted to determine some physical and mechanical properties of high-strength flowable mortar reinforced with different percentages of palm fiber (0, 0.2, 0.4, 0.6, 0.8, 1.0, 1.2, 1.4, and 1.6% as volumetric fractions). The density, compressive strength, flexural strength, and toughness index were tested to determine the mechanical properties of this mortar. Test results illustrate that the inclusion of this fiber reduces the density of mortar. The use of 0.6% of palm fiber increases the compressive strength and flexural strength by about 15.1%, and 16%, respectively; besides, the toughness index (I5) of the high-strength flowable mortar has been significantly enhanced by the use of 1% and more of palm fiber.

Effect of Chopped Basalt Fiber on the Fresh and Hardened Properties of Fly Ash High Strength Concrete

2014 ◽  
Vol 567 ◽  
pp. 381-386 ◽  
Author(s):  
Nasir Shafiq ◽  
Muhd Fadhil Nuruddin ◽  
Ali Elheber Ahmed Elshekh ◽  
Ahmed Fathi Mohamed Salih
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
High Strength Concrete ◽  
Basalt Fiber ◽  
High Strength ◽  
Progressive Increase ◽  
Test Results ◽  
Strength Concrete ◽  
Hardened Properties ◽  
Chopped Basalt Fiber

In order to improve the mechanical properties of high strength concrete, HSC, several studies have been conducted using fly ash, FA. Researchers have made it possible to achieve 100-150MPa high strength concrete. Despite the popularity of this FAHSC, there is a major shortcoming in that it becomes more brittle, resulting in less than 0.1% tensile strain. The main objective of this work was to evaluate the fresh and hardened properties of FAHSC utilizing chopped basalt fiber stands, CBFS, as an internal strengthening addition material. This was achieved through a series of experimental works using a 20% replacement of cement by FA together with various contents of CBFS. Test results of concrete mixes in the fresh state showed no segregation, homogeneousness during the mixing period and workability ranging from 60 to 110 mm. Early and long terms of compressive strength did not show any improvement by using CBFS; in fact, it decreased. This was partially substituted by the effect of FA. Whereas, the split and flexural strengths of FASHC were significantly improved with increasing the content of CBFS as well as the percentage of the split and flexural tensile strength to the compressive strength. Also, test results showed a progressive increase in the areas under the stress-strain curves of the FAHSC strains after the CBFS addition. Therefore, the brittleness and toughness of the FAHSC were enhanced and the pattern of failure moved from brittle failure to ductile collapse using CBFS. It can be considered that the CBFS is a suitable strengthening material to produce ductile FAHSC.

Deterioration of Mechanical Properties of High-Strength Pumpcrete after Exposure to High Temperatures

2010 ◽  
Vol 168-170 ◽  
pp. 564-569
Author(s):  
Guang Lin Yuan ◽  
Jing Wei Zhang ◽  
Jian Wen Chen ◽  
Dan Yu Zhu
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Heating Rate ◽  
High Strength Concrete ◽  
Heating Temperature ◽  
High Strength ◽  
Air Cooling ◽  
Test Results ◽  
Strength Deterioration ◽  
Residual Compressive Strength

This paper makes an experimental study of mechanical properties of high-strength pumpcrete under fire, and the effects of heating rate, heating temperature and cooling mode on the residual compressive strength(RCS) of high-strength pumpcrete are investigated. The results show that under air cooling, the strength deterioration speed of high-strength concrete after high temperature increases with the increase of concrete strength grade. Also, the higher heating temperature is, the lower residual compressive strength value is. At the same heating rate (10°C/min), the residual compressive strength of C45 concrete after water cooling is a little higher than that after air cooling; but the test results are just the opposite for C55 and C65 concrete. The strength deterioration speed of high-strength concrete after high temperature increases with the increase of heating rate, but not in proportion. And when the heating temperature rises up between 200°C and 500°C, heating rate has the most remarkable effect on the residual compressive strength of concrete. These test results provide scientific proofs for further evaluation and analysis of mechanical properties of reinforced-concrete after exposure to high temperatures.

scholarly journals Efficiency factor and modulus of elasticity of lightweight concrete with expanded clay aggregate

2010 ◽  
Vol 3 (2) ◽  
pp. 195-204 ◽  
Author(s):  
W.G Moravia ◽  
A. G. Gumieri ◽  
W. L. Vasconcelos
Keyword(s):  
Compressive Strength ◽  
Modulus Of Elasticity ◽  
Large Scale ◽  
Lightweight Concrete ◽  
Weight Ratio ◽  
Lightweight Aggregate ◽  
Normal Weight ◽  
Lightweight Aggregate Concrete ◽  
Empirical Methods ◽  
Normal Weight Concrete

Nowadays lightweight concrete is used on a large scale for structural purposes and to reduce the self-weight of structures. Specific grav- ity, compressive strength, strength/weight ratio and modulus of elasticity are important factors in the mechanical behavior of structures. This work studies these properties in lightweight aggregate concrete (LWAC) and normal-weight concrete (NWC), comparing them. Spe- cific gravity was evaluated in the fresh and hardened states. Four mixture proportions were adopted to evaluate compressive strength. For each proposed mixture proportion of the two concretes, cylindrical specimens were molded and tested at ages of 3, 7 and 28 days. The modulus of elasticity of the NWC and LWAC was analyzed by static, dynamic and empirical methods. The results show a larger strength/ weight ratio for LWAC, although this concrete presented lower compressive strength.

scholarly journals Size Effect in Compressive Strength Tests of Cored Specimens of Lightweight Aggregate Concrete

Materials ◽  
2020 ◽  
Vol 13 (5) ◽  
pp. 1187 ◽  
Author(s):  
Lucyna Domagała
Keyword(s):  
Compressive Strength ◽  
Scale Effect ◽  
Lightweight Aggregate ◽  
Normal Weight ◽  
Cement Matrix ◽  
Lightweight Aggregate Concrete ◽  
Core Diameter ◽  
Aggregate Concrete ◽  
Normal Weight Concrete ◽  
Strength Tests

The aim of this paper is to discuss the unrecognized problem of the scale effect in compressive strength tests determined for cored specimens of lightweight aggregate concrete (LWAC) against the background of available data on the effect for normal-weight concrete (NWAC). The scale effect was analyzed taking into consideration the influence of slenderness (λ = 1.0, 1.5, 2.0) and diameter (d = 80, 100, 125, and 150 mm) of cored specimens, as well as the type of lightweight aggregate (expanded clay and sintered fly ash) and the type of cement matrix (w/c = 0.55 and 0.37). The analysis of the results for four lightweight aggregate concretes revealed no scale effect in compressive strength tests determined on cored specimens. Neither the slenderness, nor the core diameter seemed to affect the strength results. This fact should be explained by the considerably better structural homogeneity of the tested lightweight concretes in comparison to normal-weight ones. Nevertheless, there were clear differences between the results obtained on molded and cored specimens of the same shape and size.

Sign in / Sign up

Export Citation Format

Share Document