scholarly journals A Study of Some Mechanical Properties of Composite Materials with a Dammar-Based Hybrid Matrix and Reinforced by Waste Paper

Polymers ◽  
2020 ◽  
Vol 12 (8) ◽  
pp. 1688
Author(s):  
Marius Marinel Stănescu ◽  
Dumitru Bolcu
Keyword(s):  
Mechanical Properties ◽  
Composite Materials ◽  
Epoxy Resin ◽  
Volume Ratio ◽  
Tensile Tests ◽  
Sem Analysis ◽  
Waste Paper ◽  
Hybrid Resin ◽  
Natural Resin ◽  
Tensile Response

When obtaining environment-friendly hybrid resins made of a blend of Dammar natural resin, in a prevailing volume ratio, with epoxy resin, it is challenging to find alternatives for synthetic resins. Composite materials reinforced with waste paper and matrix made of epoxy resin or hybrid resin with a volume ratio of 60%, 70% and 80% Dammar were studied. All samples obtained have been submitted to tensile tests and Scanning Electron Microscopy (SEM) analysis. The tensile response, tensile strength, modulus of elasticity, elongation at break and the analysis of the fracture surface were determined. The damping properties of vibrations of bars in hybrid resins and in the composite materials under study were also examined. The mechanical properties of the four types of resins and of the composite materials were compared. The chemical composition for a hybrid resin specimen were obtained using the Fourier Transformed Infrared Spectroscopy (FTIR) and Energy, Dispersive X-ray Spectrometry (EDS) analyzes.

scholarly journals A Study of Some Mechanical Properties of a Category of Composites with a Hybrid Matrix and Natural Reinforcements

Polymers ◽  
2019 ◽  
Vol 11 (3) ◽  
pp. 478 ◽  
Author(s):  
Marius Stănescu ◽  
Dumitru Bolcu
Keyword(s):  
Mechanical Properties ◽  
Composite Materials ◽  
Epoxy Resin ◽  
Wheat Straw ◽  
Damping Properties ◽  
Hybrid Resin ◽  
Hybrid Matrix ◽  
Natural Resin

The current composite materials must meet a double challenge, one that involves obtaining mechanical properties suitable to the field of activity in which they are used and another one, equally important, that requires that they be renewable. In this paper, we have obtained a category of composite materials that have natural reinforcements (fabrics of flax, cotton, hemp, cattail leaves, and wheat straw). As a matrix, we have used three types of hybrid resin, in the composition of which we used the natural resin dammar, in different majority volume proportions. The differences, up to 100%, were represented by epoxy resin and its associated reinforcement, to generate a quick process of polymerization. We have measured certain mechanical properties and the damping properties of the three types of hybrid resin and of the composite materials under study. Based on these properties, we point out a few fields of activity where these composite materials can be used.

scholarly journals A Study Regarding the Mechanical Properties of a Hybrid Matrix with Various Volume Proportions of Dammar

2020 ◽  
Vol 57 (1) ◽  
pp. 133-140
Author(s):  
Dumitru Bolcu ◽  
Marius Marinel Stanescu ◽  
Ion Ciuca ◽  
Cosmin Mihai Miritoiu ◽  
Alin Dinita ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Epoxy Resin ◽  
Vibration Mode ◽  
Vibration Damping ◽  
The Other ◽  
Damping Properties ◽  
Elongation At Break ◽  
Hybrid Resin ◽  
Natural Resin ◽  
Volume Proportion

This paper studies the influence of the volume proportion between components on the mechanical behaviour of a hybrid resin obtained by combining the natural resin Dammar and epoxy resin. We analyse three sets of hybrid resin samples, in which we used a Dammar volume proportion of 60%, 70%, and 80% respectively and epoxy resin (employed together with its associated reinforcement in order to generate a quick process of polymerization). Following the tensile test we found the characteristic curves, the tensile strength and the elongation at break for each of the three types of resins. We also looked into the vibration damping properties of bars made of this resin. We experimentally determined the frequency and the damping coefficient of the first particular vibration mode for one bar taken out of each set of resins, with one end fixed and the other free. On the basis of the results, we calculated the loss coefficient for each type of resin.

Experimental Study for the Choice of a Matrix Epoxy Resin for the Elaboration of Laminates

2013 ◽  
Vol 550 ◽  
pp. 17-23 ◽  
Author(s):  
C. Aribi ◽  
B. Bezzazi ◽  
A. Mir
Keyword(s):  
Mechanical Properties ◽  
Experimental Study ◽  
Composite Materials ◽  
Comparative Study ◽  
Epoxy Resin ◽  
Tensile Tests ◽  
Dynamic Tests ◽  
Epoxy Network ◽  
The Matrix ◽  
Static And Dynamic Tests

The performances of composite materials are influenced by the properties of the matrix used. The latter ensures the desired form and the protection of the reinforcements against the external attacks. This work comprises a comparative study between laminates developed with different matrices in epoxy resin. Their characterization has to choose the best matrix able to give best results in static and dynamic tests. The resins used are provided by Granitex Algéria and which are primary Médapoxy STR resins, Médapoxy inject 812 and Médapoxy Al resin. Hence, the results of tensile tests prove a fragility of the AL resin which influences the maximal constraint of traction compared to the STR primary resin. Furthermore, Inject 812 resin shows very limited mechanical properties due to the changes of the epoxy network with the addition of diluents which has significantly decreased its viscosity.

scholarly journals Experimental Research into the Mechanical Behaviour of Dammar and Sandarac - Based Bio Resins

2019 ◽  
Vol 56 (1) ◽  
pp. 1-5
Author(s):  
Dumitru Bolcu ◽  
Marius Marinel Stanescu ◽  
Ion Ciuca ◽  
Alin Dinita ◽  
Adrian Rosca ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Roughness ◽  
Epoxy Resin ◽  
Mechanical Behaviour ◽  
Tensile Testing ◽  
Sem Analysis ◽  
Polymerization Process ◽  
Natural Resin ◽  
Volume Proportion ◽  
Reinforcing Material

In this paper, we examine two types of Dammar-based bio resins. In the first type, Dammar alone is used as natural resin, while in the second type a mixture of 70% Dammar and 30% Sandarac is used. Three sample sets were made of each of these resins with a bio resin volume proportion of 55, 65 and 75% respectively, the rest being epoxy resin (used, together with the associated reinforcing material, to generate a quick polymerization process). A SEM analysis is carried out and the surface roughness of each of the studied materials. A series of mechanical properties, determined by tensile testing, are presented. We have determined the characteristic curves, tensile strength and modulus of elasticity and the influence of the epoxy resin volume proportion on the mechanical behaviour of bio resins.

The Mechanical Properties of Organic Modified Epoxy Resin

2020 ◽  
Vol 43 (3) ◽  
pp. 10-14
Author(s):  
Georgel MIHU ◽  
Claudia Veronica UNGUREANU ◽  
Vasile BRIA ◽  
Marina BUNEA ◽  
Rodica CHIHAI PEȚU ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Composite Materials ◽  
Epoxy Resin ◽  
Epoxy Matrix ◽  
Epoxy Resins ◽  
Mechanical Tests ◽  
Organic Modification ◽  
Three Point Bending ◽  
Modified Epoxy

Epoxy resins have been presenting a lot of scientific and technical interests and organic modified epoxy resins have recently receiving a great deal of attention. For obtaining the composite materials with good mechanical proprieties, a large variety of organic modification agents were used. For this study gluten and gelatin had been used as modifying agents thinking that their dispersion inside the polymer could increase the polymer biocompatibility. Equal amounts of the proteins were milled together and the obtained compound was used to form 1 to 5% weight ratios organic agents modified epoxy materials. To highlight the effect of these proteins in epoxy matrix mechanical tests as three-point bending and compression were performed.

scholarly journals Influence of Alkali Treatment on the Microstructure and Mechanical Properties of Coir and Abaca Fibers

Materials ◽  
2021 ◽  
Vol 14 (10) ◽  
pp. 2636
Author(s):  
Petr Valášek ◽  
Miroslav Müller ◽  
Vladimír Šleger ◽  
Viktor Kolář ◽  
Monika Hromasová ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Composite Materials ◽  
Alkali Treatment ◽  
Fiber Surface ◽  
Cellulose Fibers ◽  
Sem Analysis ◽  
Experimental Program ◽  
Time Interval ◽  
The European Union ◽  
Vegetable Fibers

Composite materials with natural fillers have been increasingly used as an alternative to synthetically produced materials. This trend is visible from a representation of polymeric composites with natural cellulose fibers in the automotive industry of the European Union. This trend is entirely logical, owing to a preference for renewable resources. The experimental program itself follows pronounced hypotheses and focuses on a description of the mechanical properties of untreated and alkali-treated natural vegetable fibers, coconut and abaca fibers. These fibers have great potential for use in composite materials. The results and discussion sections contribute to an introduction of an individual methodology for mechanical property assessment of cellulose fibers, and allows for a clear definition of an optimal process of alkalization dependent on the content of hemicellulose and lignin in vegetable fibers. The aim of this research was to investigate the influence of alkali treatment on the surface microstructure and tensile properties of coir and abaca fibers. These fibers were immersed into a 5% solution of NaOH at laboratory temperature for a time interval of 30 min, 1 h, 2 h, 3 h, 6 h, 12 h, 24 h, and 48 h, rinsed and dried. The fiber surface microstructures before and after the alkali treatment were evaluated by SEM (scanning electron microscopy). SEM analysis showed that the alkali treatment in the NaOH solution led to a gradual connective material removal from the fiber surface. The effect of the alkali is evident from the visible changes on the surface of the fibers.

Development of green nanocomposites reinforced by cellulose nanofibers extracted from paper sludge

2015 ◽  
Vol 29 (06n07) ◽  
pp. 1540025 ◽  
Author(s):  
Hitoshi Takagi ◽  
Antonio N. Nakagaito ◽  
Kazuya Kusaka ◽  
Yuya Muneta
Keyword(s):  
Mechanical Properties ◽  
Composite Materials ◽  
Mechanical Treatment ◽  
Raw Materials ◽  
Cellulose Nanofibers ◽  
Tensile Tests ◽  
Cellulose Nanofiber ◽  
Paper Sludge ◽  
Reinforcing Effect ◽  
Mechanical And Physical Properties

Cellulose nanofibers have been showing much greater potential to enhance the mechanical and physical properties of polymer-based composite materials. The purpose of this study is to extract the cellulose nanofibers from waste bio-resources; such as waste newspaper and paper sludge. The cellulosic raw materials were treated chemically and physically in order to extract individualized cellulose nanofiber. The combination of acid hydrolysis and following mechanical treatment resulted in the extraction of cellulose nanofibers having diameter of about 40 nm. In order to examine the reinforcing effect of the extracted cellulose nanofibers, fully biodegradable green nanocomposites were fabricated by composing polyvinyl alcohol (PVA) resin with the extracted cellulose nanofibers, and then the tensile tests were conducted. The results showed that the enhancement in mechanical properties was successfully obtained in the cellulose nanofiber/PVA green nanocomposites.

scholarly journals THE EFFECT OF COCONUT COIR FIBER POWDER CONTENT AND HARDENER WEIGHT FRACTIONS ON MECHANICAL PROPERTIES OF AN EPR-174 EPOXY RESIN COMPOSITE

SINERGI ◽  
2021 ◽  
Vol 25 (3) ◽  
pp. 361
Author(s):  
Muhamad Fitri ◽  
Shahruddin Mahzan ◽  
Imam Hidayat ◽  
Nurato Nurato
Keyword(s):  
Mechanical Properties ◽  
Shear Strength ◽  
Composite Materials ◽  
Impact Strength ◽  
Epoxy Resin ◽  
Resin Composite ◽  
Weight Fraction ◽  
Resin Matrix ◽  
Powder Content ◽  
Made In

The development of composite materials is increasingly widespread, which require superior mechanical properties. From many studies, it is found that the mechanical properties of composite materials are influenced by various factors, including the reinforcement content, both in the form of fibers and particle powder. However, those studies have not investigated the effect of the hardener weight fraction on the mechanical properties of resin composite materials. Even though its function as a hardener is likely to affect its mechanical properties, it might obtain the optimum composition of the reinforcing content and hardener fraction to get the specific mechanical properties. This study examines the effect of hardener weight fraction combined with fiber powder content on mechanical properties of EPR-174 epoxy resin matrix composite and determines the optimum of Them. The research was conducted by testing a sample of composite matrix resin material reinforced with coconut fiber powder. The Powder content was made in 3 levels, i.e.: 6%, 8%, and 10%. While the hardener fraction of resin was made in 3 levels, i.e.: 0.4, 0.5, and 0.6. The test results showed that pure resin had the lowest impact strength of 1.37 kJ/m2. The specimen with a fiber powder content of 6% has the highest impact strength i.e.: 4.92 kJ/m2. The hardener fraction of 0.5 has the highest impact strength i.e.: 4.55 kJ/m2. The fiber powder content of 8% produced the highest shear strength i.e.: 1.00 MPa. Meanwhile, the hardener fraction of 0.6 has the highest shear strength i.e.: 2.03 MPa.

Investigation of Mechanical Properties of Silk and Epoxy Composite Materials

2021 ◽  
Vol 889 ◽  
pp. 27-31
Author(s):  
Norie A. Akeel ◽  
Vinod Kumar ◽  
Omar S. Zaroog
Keyword(s):  
Mechanical Properties ◽  
Composite Material ◽  
Composite Materials ◽  
Epoxy Composite ◽  
Mechanical Test ◽  
Weight Ratio ◽  
Industrial Applications ◽  
Sem Analysis ◽  
Equivalent Strength ◽  
Test Impact

This research Investigates the new composite materials are fabricated of two or more materials raised. The fibers material from the sources of natural recycled materials provides certain benefits above synthetic strengthening material given that very less cost, equivalent strength, less density, and the slightest discarded difficulties. In the current experiments, silk and fiber-reinforced epoxy composite material is fabricated and the mechanical properties for the composite materials are assessed. New composite materials samples with the dissimilar fiber weight ratio were made utilizing the compression Molding processes with the pressure of 150 pa at a temperature of 80 °C. All samples were exposed to the mechanical test like a tensile test, impact loading, flexural hardness, and microscopy. The performing results are the maximum stress is 33.4MPa, elastic modulus for the new composite material is 1380 MPa, and hardness value is 20.64 Hv for the material resistance to scratch, SEM analysis of the microstructure of new composite materials with different angles of layers that are more strength use in industrial applications.

Experimental Investigation on Mechanical Properties of Hemp-Banana-Glass Fiber Reinforced Composites

2015 ◽  
Vol 766-767 ◽  
pp. 167-172 ◽  
Author(s):  
R. Bhoopathi ◽  
C. Deepa ◽  
G. Sasikala ◽  
M. Ramesh
Keyword(s):  
Mechanical Properties ◽  
Composite Materials ◽  
Hybrid Composites ◽  
Glass Fibers ◽  
Sem Analysis ◽  
Synthetic Fiber ◽  
Fiber Reinforced ◽  
Fiber Failure ◽  
Morphological Studies ◽  
Reinforced Composite

Due to desirable properties and its role of natural and manmade fibers reinforced composite materials are growing in a faster rate in the field of engineering and technology. Now-a-days the treated natural composites are serves better in terms of corrosive resistance, and other desirable properties when compared to the traditional materials. The main aim of this experimental study is to fabricate and investigate the mechanical properties such as tensile strengths, flexural strengths and impact strengths of NaOH treated and hemp-banana-glass fibers reinforced hybrid composites. From the experimental results, it has been noted that the treated hemp-banana-glass fibers reinforced hybrid epoxy composites exhibited superior properties and used as an alternate material for synthetic fiber reinforced composite materials. Morphological studies are carried out to analyze the interfacial characteristics, internal structures, fiber failure mode and fractured surfaces by using scanning electron microscopy (SEM) analysis.

Sign in / Sign up

Export Citation Format

Share Document