Mechanical Properties and Fracture Toughness of Alkali Treated Oil Palm Fruit Bunch (OPFB) Fibre/Epoxy Composites

2013 ◽  
Vol 390 ◽  
pp. 521-525
Author(s):  
Anizah Kalam ◽  
Aidah Jumahat ◽  
Z. Salleh ◽  
Koay Mei Hyie
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Tensile Strength ◽  
Flexural Strength ◽  
Oil Palm ◽  
Alkali Treatment ◽  
Epoxy Composites ◽  
Palm Fruit ◽  
Fibre Composites ◽  
Fracture Tests

Mechanical properties of oil palm fruit bunch (OPFB) fibre composites have been quite extensively research by many researchers. However fracture toughness of this composite is still not fully understood. Hence this research used Sodium hydroxide (NaOH) at three different concentrations (1%, 3% and 5%) to treat the Oil palm fruit bunch (OPFB) fibre to investigate the effects of alkali treatment on the mechanical properties and facture toughness of OPFB fibre/epoxy composites. Tensile and fracture tests results indicate that the 3% NaOH concentration gave the best mechanical properties. An increase of 12% and 18% were observed for tensile and flexural moduli, meanwhile the increament of 9% was observed for tensile strength. However no increase on flexural strength was observed due to the OPFB treatment. Suggestion has been made to further study on the NaOH concentration in the range of 2% - 4%.

Degradation Behaviour of Nanosilica Enhanced Oil Palm Empty Fruit Bunch Fiber Epoxy Composites

2020 ◽  
Vol 305 ◽  
pp. 28-35
Author(s):  
Anslem Wong Tsu An ◽  
Sujan Debnath ◽  
Vincent Lee Chieng Chen ◽  
Moola Mohan Reddy ◽  
Alokesh Pramanik
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Oil Palm ◽  
Environmental Conditions ◽  
Natural Fiber ◽  
Fiber Composites ◽  
Epoxy Composites ◽  
Empty Fruit Bunch ◽  
Degradation Behaviour ◽  
Brine Solution

In recent years, studies regarding natural fiber reinforced composites have been increased as they are biodegradable with good mechanical performance therefore can help to overcome the environmental issue. As the natural fibers are easy to obtain, many industries have started to make use of natural fiber composites which are light in weight and possess good mechanical properties. However, the natural fiber composites also possess certain limitations most importantly their high moisture absorption ability which makes them incompatible at degradable environment. The fiber constituents of natural fiber composite may have different type of interactions at different environmental conditions. In addition, the involvement of nanoparticles in the composite may be the solution to overcome the deficiencies. In this research, the degradation behaviour of Oil palm empty fruit bunch (OPEFB) fibers reinforced epoxy composites upon exposure to degradable environmental conditions and the effect of adding nanoparticles have been studied. The tensile tests were conducted before and after the exposure to different environmental conditions including plain water, moist soil, brine solution, and cooking oil. Results shows that the addition of 10wt% of OPEFB fiber to the epoxy composites had improved the mechanical tensile strength up to 15.97% and composites exposed to brine solution have the most prominent sign of degradation in mechanical properties in both composites with and without nanosilica. Nevertheless, the composites with nanosilica have shown up to 24.28% improvement in tensile strength after exposure to different environmental conditions. The improvement were attributed due to filling the voids of the composites with nanosilica and good interfacial adhesion between the nanofiller, fiber, and matrix.

Effect of Preheating and Fatiguing on Mechanical Properties of Bulk-fill and Conventional Composite Resin

2019 ◽  
Vol 45 (4) ◽  
pp. 387-395
Author(s):  
AA Abdulmajeed ◽  
TE Donovan ◽  
R Cook ◽  
TA Sulaiman
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Tensile Strength ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Composite Resin ◽  
Statistical Significance ◽  
Composite Resins ◽  
Significant Difference ◽  
Diametral Tensile Strength

Clinical Relevance Bulk-fill composite resins may have comparable mechanical properties to conventional composite resin. Preheating does not reduce the mechanical properties of composite resins. SUMMARY Statement of Problem: Bulk-fill composite resins are increasingly used for direct restorations. Preheating high-viscosity versions of these composites has been advocated to increase flowability and adaptability. It is not known what changes preheating may cause on the mechanical properties of these composite resins. Moreover, the mechanical properties of these composites after mastication simulation is lacking. Purpose: The purpose of this study was to evaluate the effect of fatiguing and preheating on the mechanical properties of bulk-fill composite resin in comparison to its conventional counterpart. Methods and Materials: One hundred eighty specimens of Filtek One Bulk Fill Restorative (FOBR; Bulk-Fill, 3M ESPE) and Filtek Supreme Ultra (FSU; Conventional, 3M ESPE) were prepared for each of the following tests: fracture toughness (International Organization for Standardization, ISO 6872), diametral tensile strength (No. 27 of ANSI/ADA), flexural strength, and elastic modulus (ISO Standard 4049). Specimens in the preheated group were heated to 68°C for 10 minutes and in the fatiguing group were cyclically loaded and thermocycled for 600,000 cycles and then tested. Two-/one-way analysis of variance followed by Tukey Honest Significant Difference (HSD) post hoc test was used to analyze data for statistical significance (α=0.05). Results: Preheating and fatiguing had a significant effect on the properties of both FSU and FOBR. Fracture toughness increased for FOBR specimens when preheated and decreased when fatigued (p=0.016). FOBR had higher fracture toughness value than FSU. Diametral tensile strength decreased significantly after fatiguing for FSU (p=0.0001). FOBR had a lower diametral tensile strength baseline value compared with FSU (p=0.004). Fatiguing significantly reduced the flexural strength of both FSU and FOBR (p=0.011). Preheating had no effect on the flexural strength of either FSU or FOBR. Preheating and fatiguing significantly decreased the elastic modulus of both composite resins equally (p>0.05). Conclusions: Preheating and fatiguing influenced the mechanical properties of composite resins. Both composites displayed similar mechanical properties. Preheating did not yield a major negative effect on their mechanical properties; the clinical implications are yet to be determined.

Effect of Reprocessing Palm Fiber Composite on the Mechanical Properties

2014 ◽  
Vol 699 ◽  
pp. 146-150 ◽  
Author(s):  
Sivakumar Dhar Malingam ◽  
Muhammad Hilmi Ruzaini bin Hashim ◽  
Md Radzai bin Said ◽  
Ahmad Rivai ◽  
Mohd Ahadlin bin Daud ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Flexural Strength ◽  
Waste Disposal ◽  
Oil Palm ◽  
Fiber Composite ◽  
Young Modulus ◽  
Palm Fiber ◽  
Polypropylene Composites ◽  
Useful Life

Concern for the environment, both in terms of limiting the use of finite resources and the need to manage waste disposal, has led to increasing pressure to recycle materials at the end of their useful life. This work describes the effects of reprocessing on the mechanical properties of oil palm fiber reinforced polypropylene composites (PFC). Composites, containing 30wt% fiber with 3wt% Maleate Polypropylene as a coupling agent, were reprocessed up to six times. For this composite, tensile strength (TS) and Young modulus (YM) were found to decrease by 9.6% and 4.7% after being reprocessed for six times. Flexural strength was found to decrease by 23.8% with increased number of reprocessing. The hardness numbers of the composite were found to increase by 7.43% from 72.10 to 77.89 after the sixth reprocessing. In general the degradation on the mechanical properties is considered to be small and PFC has potential to be reprocessed.

scholarly journals Halloysite reinforced epoxy composites with improved mechanical properties

2016 ◽  
Vol 18 (1) ◽  
pp. 133-135 ◽  
Author(s):  
Muhammad Jawwad Saif ◽  
Muhammad Asif ◽  
Muhammad Naveed ◽  
Khalid Mahmood Zia ◽  
Waheed -uz- Zaman ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Flexural Strength ◽  
Flexural Modulus ◽  
Halloysite Nanotubes ◽  
Epoxy Composites ◽  
Gravimetric Analysis ◽  
Thermal Gravimetric ◽  
Interfacial Coupling ◽  
Uniform Dispersion

Abstract Halloysite nanotubes (HNTs) reinforced epoxy composites with improved mechanical properties were prepared. The prepared HNTs reinforced epoxy composites demonstrated improved mechanical properties especially the fracture toughness and flexural strength. The flexural modulus of nanocomposite with 6% mHNTs loading was 11.8% higher than that of neat epoxy resin. In addition, the nanocomposites showed improved dimensional stability. The prepared halloysite reinforced epoxy composites were characterized by thermal gravimetric analysis (TGA). The improved properties are attributed to the unique characteristics of HNTs, uniform dispersion of reinforcement and interfacial coupling.

The Effect of Alkali Treatment Mechanical Properties of Kenaf Fiber Epoxy Composite

2011 ◽  
Vol 471-472 ◽  
pp. 191-196 ◽  
Author(s):  
Saad A. Mutasher ◽  
Adrian Poh ◽  
Aaron Mark Than ◽  
Justin Law
Keyword(s):  
Tensile Strength ◽  
Impact Strength ◽  
Flexural Strength ◽  
Alkali Treatment ◽  
Curing Temperature ◽  
Sustainable Construction ◽  
Kenaf Fiber ◽  
Kenaf Fibre ◽  
Fibre Composites ◽  
The Impact

Increasing worldwide environmental awareness is an encouraging scientific research into the development of cheaper, more environmentally friendly and sustainable construction and packaging materials. Kenaf fibre is a natural fibre which is growing in popularity due environmental issues and its properties as filler. Epoxy is a versatile thermosetting polymer which has a low curing temperature and used in making carbon fibre and glass composites. In this paper the properties of kenaf bast fibre epoxy reinforced composite have been investigated. The effects of alkali surface treatment of the fiber on the composite properties are also investigated. A hand layup method was use to fabricate the test specimens. Generally, all the treated fibre composites performed better than the untreated fibre with an improvement approximately 5% to 10%. Epoxy has the highest tensile strength and flexural strength among all specimens. The 24wt% treated kenaf fibre composites has the highest tensile strength, 27.72MPa and flexural strength, 56.91MPa. The kenaf fiber weight fraction of 40% gave the highest impact strength. The impact strength of the 40wt% kenaf fiber increased 14.3% after alkali treatment.

scholarly journals Effect of Technological Factors on some Properties of Composite tube with Epoxy Resin K-153 Matrix

2019 ◽  
Vol 35 (3) ◽  
Author(s):  
Nguyen Trung Thanh
Keyword(s):  
Mechanical Properties ◽  
Experimental Study ◽  
Tensile Strength ◽  
Flexural Strength ◽  
Glass Fiber ◽  
Epoxy Resin ◽  
Polymer Composite ◽  
Epoxy Composites ◽  
Glass Fiber Reinforced ◽  
Pressure Resistance

The tube is made of polymer composite material based on K-153 epoxy resin (K-153 epoxy resin is made from ED-20 epoxy resin modified by thiokol and oligomer acrylate), T-13 glassfiber, hardener polyethylenepolyaminemade by wrapping on machine. The effect of drying temperature on mechanical properties (tensile strength, flexural strength) of polymercomposite materialwas studied. The paper also mentions to select suitable hardener to beused for polymercomposite tube wrapping. The results show that the strength at break, flexural strength of polymercomposite material are changedmuch when changing wrapping angle. The drying temperature increases, the curing time of polymercomposite material is much reduced. The time to stabilize after drying also greatly affects the pressure resistance of polymer composite tubes. Keywords Polymercomposite, K-153, tensile strength, flexural strength, pressure resistance. References [1] M. J. Mochane, T. C. Mokhena, T. H. Mokhothu, Recent progress on natural fiber hybrid composites foradvanced applications: A review, eXPRESS Polymer Letters 13 (2) (2019) 159-198.[2] J. Kim, H. J. Yoon, K. Shin, A study on crushing behaviors of composite circular tubes with different reinforcing fibers, International Journal of Impact Engineering 38(4) (2014) 198-207.[3] T. D. Jagannatha1, G. Harish, Mechanical Properties of carbon/ glass fiber reinforced epoxy hybrid polymer composites, Journal of Reinforced Plastics and Composites 4 (2) (2015) 131–137.[4] Vitalii Bezgin, Agata Dudek, Composites based on high-molecular weigh epoxy resin modified with polysulfide rubber, Composite Theory and practice 17(2) (2017) 79-83. [5] Abdouss, Majid, Farajpour, Tohid, Derakhshani, Morteza, The Effect of Epoxy-Polysulfide Copolymer Curing Methods on Mechanical-Dynamical and Morphological Properties, Iran. J. Chem. Chem. Eng. 30(4) (2011) 37-44.[6] G. Devendhar Rao, K. Srinivasa Reddy, P. Raghavendra Rao, Mechanical properties of E-glass fiber reinforced epoxy composites with SnO2 and PTFE, International Journal of Emerging Research in Management and Technology 6 (7) (2017) 208-214.[7] Hu Dayong, Jialiang Yang, Experimental study on crushing characteristics of brittle fibre/epoxy hybrid composite tubes, International Journal of Crashworthiness 15(4) (2010) 401-412 .[8] G.U. Raju, S. Kumarappa, Experimental Study on Mechanicaland Thermal Properties of Epoxy Composites Filled with Agricultural Residue, Polymers from Renewable Resources 3 (3) (2012) 118–138.          

scholarly journals Improvement in Mechanical Properties of Cantala Fiber and Short Cantala/Recycled High-Density Polyethylene Composite through Chemical Treatment

2017 ◽  
Author(s):  
Wijang Wisnu Raharjo ◽  
Rudy Soenoko ◽  
Yudy Surya Irawan ◽  
Agus Suprapto
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Flexural Strength ◽  
Alkali Treatment ◽  
Amorphous Material ◽  
Tensile Modulus ◽  
Fiber Surface ◽  
Degree Of Crystallinity ◽  
Polyethylene Composite ◽  
Treated Fiber

The improvement of mechanical properties of cantala fiber and its composites. Treatments including alkali, silane, and the combination of both were carried out to modify the fiber surface. The influence of chemical treatments on fiber properties such as the degree of crystallinity and tensile strength was investigated. A variety of short cantala fiber reinforced rHDPE composites were produced by hot press, and the effect of fiber treatment on the flexural strength of composites was observed. SEM observations also carried out to highlight these changes. The result shows that alkali treatment improves tensile strength and tensile modulus of alkali treated fiber (NF12) which was predicted as a result of the enhancement of the cellulose crystallinity. In contrast, the tensile strength and tensile modulus of silane (SF05) and alkali-silane treated fiber (NSF05) decreased compared to untreated fiber (UF) which is caused by the addition of amorphous material. The tensile strength of alkali-silane treated fiber (NSF05) was lower than alkali treated fiber (NF12), but the composites prepared with NSF05 showed the highest increment of flexural strength of 25.9%. This may be due the combination of alkali and silane treatment helped in the better formation of fiber-matrix interface adhesion.

scholarly journals Effect of Clay Addition on Mechanical Properties of Unsaturated Polyester/Glass Fiber Composites

2013 ◽  
Vol 2013 ◽  
pp. 1-7 ◽  
Author(s):  
Kusmono ◽  
Zainal Arifin Mohd Ishak
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Tensile Strength ◽  
Flexural Strength ◽  
Glass Fiber ◽  
Unsaturated Polyester ◽  
Flexural Modulus ◽  
Charpy Impact ◽  
Fiber Composites ◽  
Glass Fiber Composites

Unsaturated polyester (UP)/glass fiber/clay composites were prepared by hand layup method. The effect of clay loading on the morphological and mechanical properties of UP/glass fiber composites was investigated in this study. X-ray diffraction (XRD) was used to characterize the structure of the composites. The mechanical properties of the composites were determined by tensile, flexural, unnotched Charpy impact and fracture toughness tests. XRD results indicated that the exfoliated structure was found in the composite containing 2 wt% of clay while the intercalated structure was obtained in the composite with 6 wt% of clay. The tensile strength, flexural strength, and flexural modulus of the composites were increased in the presence of clay. The optimum loading of clay in the UP/glass fiber composites was attained at 2 wt%, where the improvement in in tensile strength, flexural strength, and flexural modulus was approximately 13, 21, and 11%, respectively. On the other hand, the highest values in impact toughness and fracture toughness were observed in the composites with 4 wt% of clay.

KAISER ALUMINUM ALLOY 7050

Alloy Digest ◽  
2000 ◽  
Vol 49 (1) ◽  
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Tensile Strength ◽  
Aluminum Alloy ◽  
Heat Treating ◽  
High Fracture Toughness ◽  
High Fracture ◽  
Kaiser Aluminum ◽  
Structural Parts ◽  
Very High

Abstract Kaiser Aluminum Alloy 7050 has very high mechanical properties including tensile strength, high fracture toughness, and a high resistance to exfoliation and stress-corrosion cracking. The alloy is typically used in aircraft structural parts. This datasheet provides information on composition, physical properties, hardness, tensile properties, and shear strength as well as fracture toughness and fatigue. It also includes information on forming, heat treating, machining, and joining. Filing Code: AL-366. Producer or source: Tennalum, A Division of Kaiser Aluminum.

Mechanical Property Improvement of Poly(Butylene Succinate) by Reinforcing with Modified Fumed Silica

2014 ◽  
Vol 1025-1026 ◽  
pp. 215-220 ◽  
Author(s):  
Sasirada Weerasunthorn ◽  
Pranut Potiyaraj
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Impact Strength ◽  
Flexural Strength ◽  
Fumed Silica ◽  
Tensile Modulus ◽  
Silica Particles ◽  
Melt Mixing ◽  
Butylene Succinate ◽  
Ir Spectrophotometry

Fumed silica particles (SiO2) were directly added into poly (butylene succinate) (PBS) by melt mixing process. The effects of amount of fumed silica particles on mechanical properties of PBS/fumed silica composites, those are tensile strength, tensile modulus, impact strength as well as flexural strength, were investigated. It was found that the mechanical properties decreased with increasing fumed silica loading (0-3 wt%). In order to increase polymer-filler interaction, fumed silica was treated with 3-glycidyloxypropyl trimethoxysilane (GPMS), and its structure was analyzed by FT-IR spectrophotometry. The PBS/modified was found to possess better tensile strength, tensile modulus, impact strength and flexural strength that those of PBS/fumed silica composites.