Electrodeposition of Sn-Ni Alloy Coatings and their Characterization

2015 ◽  
Vol 830-831 ◽  
pp. 655-658 ◽  
Author(s):  
Sandhya Shetty ◽  
Ampar Chitharanjan Hegde
Keyword(s):  
Sem Analysis ◽  
Nacl Solution ◽  
X Ray Diffraction ◽  
Corrosion Resistant ◽  
X Ray ◽  
Ni Alloy ◽  
Corrosion Behaviors ◽  
Current Densities ◽  
Alkaline Bath ◽  
Scanning Electron

A new alkaline bath has been proposed for deposition of bright Sn-Ni alloy coatings on mild steel (MS). Depositions were carried out at different current densities (c.d.) and their corrosion behaviors were studied in 5 % NaCl solution by electrochemical AC and DC methods. Sn-Ni coating, deposited at low c.d. i.e. at 1.0 A/dm2 was found to be the most corrosion resistant compared to those at other higher c.d., even up to 4.0 A/dm2. This least corrosion rate (CR) is attributed to high wt. % Sn in the deposit. Increase of CR at high c.d. range is due to decrease of wt. % Sn, explained by the observed anomalous type of codeposition, followed by the bath. Regardless of the deposition c.d., the bath developed bright coatings, inherent of Sn-Ni alloy. Experimental results are discussed taking in account of the phase structure, composition and surface morphology of the coatings, evidenced by X-ray diffraction (XRD), Energy Dispersive X-ray (EDX) and Scanning Electron Microscopy (SEM) analysis.

scholarly journals Corrosion and Tensile Behaviors of Ti-4Al-2V-1Mo-1Fe and Ti-6Al-4V Titanium Alloys

Metals ◽  
2019 ◽  
Vol 9 (11) ◽  
pp. 1213 ◽  
Author(s):  
Yanxin Qiao ◽  
Daokui Xu ◽  
Shuo Wang ◽  
Yingjie Ma ◽  
Jian Chen ◽  
...  
Keyword(s):  
Corrosion Resistance ◽  
Low Cost ◽  
Tensile Tests ◽  
Nacl Solution ◽  
X Ray Diffraction ◽  
X Ray ◽  
Β Phase ◽  
Mass Losses ◽  
Corrosion Behaviors ◽  
Scanning Electron

X-ray diffraction (XRD), scanning electron microscope (SEM), immersion, electrochemical, and tensile tests were employed to analyze the phase constitution, microstructure, corrosion behaviors, and tensile properties of a Ti-6Al-4V alloy and a newly-developed low cost titanium alloy Ti-4Al-2V-1Mo-1Fe. The results showed that both the Ti-6Al-4V and Ti-4Al-2V-1Mo-1Fe alloys were composed of α and β phases. The volume fractions of β phase for these two alloys were 7.4% and 47.3%, respectively. The mass losses after 180-day immersion tests in 3.5 wt.% NaCl solution of these alloys were negligible. The corrosion resistance of the Ti-4Al-2V-1Mo-1Fe alloy was higher than that of the Ti-6Al-4V alloy. The tensile tests showed that the Ti-4Al-2V-1Mo-1Fe alloy presented a slightly higher strength but a lower ductility compared to the Ti-6Al-4V alloy.

Wear Behavior of TiB2/GNPs and B4C/GNPs Reinforced AA6061 Matrix Composites

2021 ◽  
Vol 143 (11) ◽  
Author(s):  
Safa Polat ◽  
Yavuz Sun ◽  
Engin C¸evik
Keyword(s):  
Wear Behavior ◽  
Sem Analysis ◽  
Matrix Composites ◽  
X Ray Diffraction ◽  
Pressure Infiltration ◽  
X Ray ◽  
Wear Rates ◽  
Graphene Nanoparticles ◽  
Infiltration Method ◽  
Scanning Electron

Abstract In this study, it was aimed to investigate the effects of reinforcements used for improving the thermal properties of AA6061 alloy on wear resistance. For this purpose, AA6061 matrix composites were produced by pressure infiltration method using ceramic microparticles (TiB2 and B4C) and graphene nanoparticles (GNPs). The produced composites were first characterized by porosity measurement, X-ray diffraction (XRD), and scanning electron microscopy (SEM) analysis. Then, the wear behavior was examined under three different loads (20–40–60 N) with the reciprocating ball on the flat method in a dry environment. Specific wear-rates were calculated according to the Archard principle by measuring the depth and width of the traces after tests with a profilometer. Wearing mechanisms were determined with the help of optical and microstructure images. According to the obtained results, it was found that B4C + GNPs reinforced samples were more resistant to abrasion at low loads, but TiB2 + GNPs reinforced samples were higher at higher loads.

scholarly journals A microstructural and corrosion resistance study of (Zr, Si, Ti)N-Ni coatings produced through co-sputtering

DYNA ◽  
2018 ◽  
Vol 85 (207) ◽  
pp. 192-197 ◽  
Author(s):  
Estrella Natali Borja-Goyeneche ◽  
Jhon Jairo Olaya-Florez
Keyword(s):  
Corrosion Resistance ◽  
Nickel Content ◽  
Corrosion Current ◽  
Nacl Solution ◽  
X Ray Diffraction ◽  
X Ray ◽  
X Ray Scattering ◽  
Current Densities ◽  
Fcc Phase

This work researches the influence of the nickel content on the structural and anticorrosive properties of ZrSiTiN films deposited by means of reactive co-sputtering on alloys of Ti6Al4V. The morphology and structure were analyzed by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the chemical composition was identified via X-ray scattering spectroscopy (EDS). The corrosion resistance was studied using potentiodynamic polarization (PP) tests employing a 3.5% by weight NaCl solution. In the films, an increase of Ni up to 6.97 at% was observed, while in XRD the FCC phase of (Zr, Ti) N was identified, with a mixed orientation in planes (111) and (200), which tended to diminish with the increase of Ni. Finally, with the addition of Ni, the corrosion current densities were reduced from 5.56 𝑥 10−8 to 2.64 𝑥 10−9 𝐴/𝑐m2. The improvement in the corrosion resistance is due to the effect of the Ni on the microstructure of the system (Zr, Ti) N, which can improve the quality of the passive film and prevent crystalline defects and corrosion zones.

Microstructural and Corrosion Studies by Immersion in 3.5% NaCl Solution on Aged Mg-9Al-1Zn-XCa Alloy

2019 ◽  
Vol 969 ◽  
pp. 93-97
Author(s):  
S. Manivannan ◽  
B. Narenthiran ◽  
A. Sivanantham ◽  
S.P. Kumaresh Babu
Keyword(s):  
Corrosion Behaviour ◽  
Nacl Solution ◽  
X Ray Diffraction ◽  
Corrosion Attack ◽  
X Ray ◽  
Α Phase ◽  
Corrosion Studies ◽  
Different Temperatures ◽  
Xrd Techniques ◽  
Scanning Electron

The experimatal alloys were aged at different temperatures of 180°C, 200°C, 220°C, and 240º C with calcium addition levels of (X=0.5, 1, 1.5, 2%) on Mg-6Al-1Zn-XCa alloy were investigated in 3.5% NaCl solution. All the experimatal alloys were immersed in 3.5% NaCl solutions and the resulted surface were analyzed to study the corrosion behaviour and its surface topography by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersed spectroscopy (EDS) and X-ray diffraction (XRD) techniques. The result shows that corrosion attack occurred predominantly on ß phase and α phase exhibit relatively minor corrosion. In addition to that the increased aging temperature coarsens the intermetallic as well as α- Mg grains, which shows adverse effect to corrosion resistances and the best result were obtained at composition of 0.5wt.% Ca aged at 200°C.

Synthesis, Structural Analysis of Cadmium Sulphide Nanocrystallites

2019 ◽  
Vol 969 ◽  
pp. 169-174
Author(s):  
R. Sivanand ◽  
S. Chellammal ◽  
S. Manivannan
Keyword(s):  
Size Variation ◽  
Cadmium Sulphide ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
Precipitation Method ◽  
Capping Agent ◽  
Energy Dispersive Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

In this paper, the effect of size variation of cadmium sulphide nanocrystallites which have been prepared by precipitation method is analyzed. These prepared samples were studied using X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Energy dispersive analysis of spectroscopy (EDAX) techniques. SEM analysis represents the morphological nature of prepared samples and EDAX indicates the confirmation of elements present in the sample. XRD analysis determines the size of the samples and identifies the structure using miller indices (h k l values) of the nanocrystallies matches with JCPDS. From the XRD analysis, the size variation which depends on dopant, capping agent are discussed and corresponding results are reported in this paper.

scholarly journals Preparation of BaZrO3 powders by a spray-drying process

2003 ◽  
Vol 18 (6) ◽  
pp. 1325-1332 ◽  
Author(s):  
B. Robertz ◽  
F. Boschini ◽  
A. Rulmont ◽  
R. Cloots ◽  
I. Vandriessche ◽  
...  
Keyword(s):  
Spray Drying ◽  
Precursor Solution ◽  
Barium Zirconate ◽  
Drying Process ◽  
X Ray Diffraction ◽  
High Quality ◽  
Corrosion Resistant ◽  
X Ray ◽  
Potential Use ◽  
Scanning Electron

The potential use of barium zirconate for the manufacture of corrosion-resistant substrates emphasizes the need for a simple, inexpensive, and easily scalable process to produce high-quality powders with well-controlled composition and properties. However, the classical solid-state preparation of barium zirconate leads to an inhomogeneous powder unsuitable for applications in highly corrosive environment. For this paper, the possibility to use the spray-drying technique for the preparation of BaZrO3 powders with a controlled size distribution and morphology was investigated. The influence of the nature and concentration of the precursor solution and the influence of the spray-drying step are discussed on the basis of x-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, and dilatometric measurements.

Study of Fluxing Process for Hot Dipping Galfan Alloy on Steel Wire

2011 ◽  
Vol 383-390 ◽  
pp. 1901-1904
Author(s):  
An Du ◽  
Yan Huo ◽  
Jie Hu
Keyword(s):  
Orthogonal Experiment ◽  
Steel Wire ◽  
Optimal Parameters ◽  
X Ray Diffraction ◽  
Experiment Research ◽  
Corrosion Resistant ◽  
X Ray ◽  
Corrosion Resistant Coatings ◽  
Fluxing Agent ◽  
Scanning Electron

Through the orthogonal experiment, research on the process parameters of the qualiity coating with the new auxiliary ,such as different pickled time, parched time, hot-dip time , and analyzed by scanning electron microscopy, X-ray diffraction. The results show that BiOCl is a new fluxing agent and the optimal parameters for pickled time, the parch time , hot-dip time, respectively,10s,120s,9s,through this we can get bright, smooth, corrosion resistant coatings.

The Effect of CaCO3 Addition on Physical Properties of ZnO-Based Crystal Glaze

2012 ◽  
Vol 620 ◽  
pp. 12-16 ◽  
Author(s):  
Abdul Rashid Jamaludin ◽  
Shah Rizal Kasim ◽  
Zainal Arifin Ahmad
Keyword(s):  
Electron Microscope ◽  
Calcium Carbonate ◽  
Scanning Electron Microscope ◽  
Physical Properties ◽  
Crystallization Temperature ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

The effects of calcium carbonate (CaCO3) addition on the physical properties of ZnO-based crystal glaze batches were investigated. Samples were fired at different gloss firing temperatures ranging from 1180-1220°C with 3 hours soaking at 1060°C crystallization temperature. X-ray diffraction (XRD) analysis identifiedthe crystal phase occurred as willemite (Zn2SiO4) and the scanning electron microscope (SEM) analysis indicated that willemite crystals are in the acicular needle like shape that formed spherulite. The intensities of willemite peaks decreased with CaCO3 addition and completely vanished at 5.0 wt% CaCO3. Varied formation of spherulites developed of the surface of crystal glaze as the flows of the glaze stretched further as the amount of CaCO3 increased.

scholarly journals Corrosion Behaviour of Zn-10Al-1.5Cu Alloy

2011 ◽  
Vol 2011 ◽  
pp. 1-6
Author(s):  
C. N. Panagopoulos ◽  
A. G. Tsopani
Keyword(s):  
Electron Microscopy ◽  
Corrosion Resistance ◽  
Corrosion Behaviour ◽  
Solution Concentration ◽  
Solution Temperature ◽  
Nacl Solution ◽  
X Ray Diffraction ◽  
X Ray ◽  
Nacl Concentration ◽  
Scanning Electron

The corrosion behaviour of Zn-10Al-1.5Cu alloy in NaCl solution was examined. The used NaCl solution concentrations were 1M, 0.3M, and 0.003M for a constant temperature values of 7°C or 25°C or 45°C. The corrosion behaviour of this alloy was investigated under potentiodynamic corrosion conditions. The surface of the corroded alloy specimens was studied with the aid of scanning electron microscopy and X-ray diffraction techniques. It was observed that the increase of NaCl concentration in the corrosion solution for a constant value of temperature led to lower corrosion resistance of the alloy. For a constant value of solution concentration, the increase of solution temperature also led to the decrease of corrosion resistance of the same alloy.

scholarly journals Characterization of Fe Doped AC/TiO2

2019 ◽  
Vol 8 (12S) ◽  
pp. 1146-1147
Keyword(s):  
Activated Carbon ◽  
Electron Microscope ◽  
Scanning Electron Microscope ◽  
Anatase Phase ◽  
Sol Gel ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Scanning Electron

Abstract: The photocatalytic composite Fe doped AC/TiO2 has been prepared by sol-gel method. The prepared Fe doped AC/TiO2 composite were characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD).The SEM analysis showed that Fe and TiO2 were attached to the Activated Carbon surfaces. The X-Ray Diffraction data showed that Fe doped AC/TiO2 composite mostly contained anatase phase.

Sign in / Sign up

Export Citation Format