Influence of AlN etching process on MISFET structures

Purpose The purpose of this paper is to present the influence of gate dielectric etching on obtained MISFET (metal insulator semiconductor field effect transistor) structures. Because of its properties, aluminum nitride (AlN) layers can be successfully used in a large area of applications. In addition, AIN has a wide bandgap (6.2eV) and high thermal conductivity (3.2 W/cm * K). Its melting temperature is greater than 2,000°C. The relative permittivity is about 9. All these features (especially high power, high temperature and high-frequency) make AlN a useful material in the fields of electronic, optical and acoustic applications. Design/methodology/approach To fabricate n-channel transistors, silicon technology was used. The 50-nm thick AlN films were deposited using the magnetron sputtering. After preparation of SiO2/AlN stack as the gate dielectric, the optimization processes of dry etching in plasma environment by Taguchi method were realized. In the next step, three methods of AlN etching were selected and used to MISFET device fabrication. Atomic force microscopy and scanning electron microscopy allowed to surfacing of the state observation after etching process. The current–voltage (I–V) output and transfer characteristics of structures with modified etch technology were measured. Keithley SMU 236/237/238 measurement set was used. Findings In this research work, a method of AlN etching in a field effect transistor technology was developed and improved. Current−voltage characteristics of obtained MISFET structures were measured and compared. Influence of etching procedure on transistors properties was examined. Originality/value The obtained results allow improving the MISFET technology based on AlN film as a gate dielectric. The complete research work will allow using the developed technologies to implement in highly sensitive ion-sensitive field effect transistor (ISFET) structures in the future. The improvement of the etching element in the technology strongly influences the detection capabilities and operating range of the transistor.

Download Full-text

Field effect transistor with thin AlOxNy film as gate dielectric

Microelectronics International ◽

10.1108/mi-11-2019-0074 ◽

2020 ◽

Vol 37 (2) ◽

pp. 103-107

Author(s):

Piotr Firek ◽

Jakub Szarafiński ◽

Grzegorz Głuszko ◽

Jan Szmidt

Keyword(s):

Magnetron Sputtering ◽

Field Effect ◽

Field Effect Transistor ◽

Gate Dielectric ◽

Gate Dielectrics ◽

Field Effect Transistors ◽

Etching Process ◽

Content Type ◽

Wide Range ◽

Effect Transistor

Purpose The purpose of this study is to directly measure and determine the Si/SiO2/AlOxNy interface state density on metal insulator semiconductor field effect transistor (MISFET) structures. The primary advantage of using aluminum oxynitride (AlOxNy) is the perfectly controlled variability of the properties of these layers depending on their stoichiometry, which can be easily controlled by the parameters of the magnetron sputtering process. Therefore, a continuous spectrum of properties can be achieved from the specific values for oxide to the specific ones for nitride, thus opening a wide range of applications in high power, high temperature and high frequency electronics, optics and sensors and even acoustic devices. Design/methodology/approach The basic subject of this study is n-channel transistors manufactured using silicon with 50-nm-thick AlOxNy films deposited on a silicon dioxide buffer layer via magnetron sputtering in which the gate dielectric was etched with wet solutions and/or dry plasma mixtures. Furthermore, the output, transfer and charge pumping (CP) characteristics were measured and compared for all modifications of the etching process. Findings An electrical measurement of MISFETs with AlOxNy gate dielectrics was conducted to plot the current-voltage and CP characteristics and examine the influence of the etching method on MISFET parameters. Originality/value In this report, a flat band and threshold voltage and the density of interface traps were determined to evaluate and improve an AlOxNy-based MISFET performance toward highly sensitive field effect transistors for hydrogen detection by applying a Pd-based nanocrystalline layer. The sensitivity of the detectors was highly correlated with the quality of the etching process of the gate dielectrics.

Download Full-text