scholarly journals Effects of the Interfacial Bonding Behavior on the Mechanical Properties of E-Glass Fiber/Nanographite Reinforced Hybrid Composites

2021 ◽  
Vol 2021 ◽  
pp. 1-9
Author(s):  
N. Saravanan ◽  
V. Yamunadevi ◽  
V. Mohanavel ◽  
V. Kumar Chinnaiyan ◽  
Murugesan Bharani ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
High Resolution ◽  
Hybrid Composites ◽  
Interfacial Bonding ◽  
Tensile Fracture ◽  
Sem Images ◽  
Tensile Fracture Surface ◽  
Epoxy Nanocomposite ◽  
Mechanical Stirring ◽  
The Impact

The nanoparticles are incorporated into the composite to mark their unique properties. This work investigates the hybrid epoxy nanocomposite and the impact of nanographite reinforcement. The composite was prepared by using a mechanical stirring technique. The amount of nanographite was added in different volumes, i.e., 1.0, 1.5, and 2.0 wt.%. Results of mechanical and dynamic loading properties were analyzed in accordance to the quantity of nano-G. The fiber and matrix interfacial bonding enrichments were evident in high-resolution SEM images-tensile fracture surface. Finally, the optimum content of nanoparticle which impacts the sample greatly was found to be 1.5 wt.%.

scholarly journals INFLUENCE OF ALBASIA WOOD ON MECHANICAL PROPERTIES AND MORPHOLOGY OF EPOXY COMPOSITES

2018 ◽  
Vol 10 (2) ◽  
pp. 116
Author(s):  
Henny Pratiwi
Keyword(s):  
Mechanical Properties ◽  
Tensile Properties ◽  
Epoxy Composites ◽  
Tensile Fracture ◽  
Tensile Fracture Surface ◽  
Alternative Reinforcement ◽  
Filler Size ◽  
Pull Out ◽  
The Impact ◽  
Properties Of Composites

This research aims to investigate the effects of albasia wood filler as alternative reinforcement for extravagant and non-renewable filler being used in epoxy composites. The filler size used was 30 mesh and various filler volume fractions were 10, 20, 30 and 40 percent. Composites were manufactured using hand lay-up method. Properties such as tensile strength, elongation, modulus elasticity and strain energy absorption were determined based on ASTM standard. The results show that filler volume content significantly affects the tensile properties and impact strength of albasia wood-epoxy composites. The optimum tensile properties are achieved when 10 percent filler is added into epoxy matrix. The impact test also shows the same results. Further addition of filler decreases the mechanical properties of composites due to the existence of weak interfacial interaction between the albasia wood filler and polymer matrix for higher filler volume concentration beyond 10 vol. %. The scanning electron micrograph reveals that there are voids and pull-out mechanism on tensile fracture surface which are the cause of the composites failure.

scholarly journals Effect of Secondary Carbon Nanofillers on the Electrical, Thermal, and Mechanical Properties of Conductive Hybrid Composites Based on Epoxy Resin and Graphite

Materials ◽  
2021 ◽  
Vol 14 (15) ◽  
pp. 4169
Author(s):  
Marcel Zambrzycki ◽  
Krystian Sokolowski ◽  
Maciej Gubernat ◽  
Aneta Fraczek-Szczypta
Keyword(s):  
Mechanical Properties ◽  
Specific Surface ◽  
Epoxy Resin ◽  
Surface Area ◽  
Specific Surface Area ◽  
Hybrid Composites ◽  
Department Of Energy ◽  
Carbon Nanofillers ◽  
The Impact ◽  
Secondary Carbon

In this work, we present a comparative study of the impact of secondary carbon nanofillers on the electrical and thermal conductivity, thermal stability, and mechanical properties of hybrid conductive polymer composites (CPC) based on high loadings of synthetic graphite and epoxy resin. Two different carbon nanofillers were chosen for the investigation—low-cost multi-layered graphene nanoplatelets (GN) and carbon black (CB), which were aimed at improving the overall performance of composites. The samples were obtained by a simple, inexpensive, and effective compression molding technique, and were investigated by the means of, i.a., scanning electron microscopy, Raman spectroscopy, electrical conductivity measurements, laser flash analysis, and thermogravimetry. The tests performed revealed that, due to the exceptional electronic transport properties of GN, its relatively low specific surface area, good aspect ratio, and nanometric sizes of particles, a notable improvement in the overall characteristics of the composites (best results for 4 wt % of GN; σ = 266.7 S cm−1; λ = 40.6 W mK−1; fl. strength = 40.1 MPa). In turn, the addition of CB resulted in a limited improvement in mechanical properties, and a deterioration in electrical and thermal properties, mainly due to the too high specific surface area of this nanofiller. The results obtained were compared with US Department of Energy recommendations regarding properties of materials for bipolar plates in fuel cells. As shown, the materials developed significantly exceed the recommended values of the majority of the most important parameters, indicating high potential application of the composites obtained.

COMPUTATIONAL MODELING OF EPOXY-BASED HYBRID COMPOSITES REINFORCED WITH CARBON FIBERS AND FUNCTIONALIZED GRAPHENE NANOPLATELETS

2021 ◽  
Author(s):  
HASHIM AL MAHMUD ◽  
, MATTHEW RADUE ◽  
WILLIAM PISANI ◽  
GREGORY ODEGARD
Keyword(s):  
Mechanical Properties ◽  
Graphene Oxide ◽  
Hybrid Composites ◽  
Graphene Nanoplatelets ◽  
Pristine Graphene ◽  
Functionalized Graphene ◽  
Functionalized Graphene Oxide ◽  
Aspect Ratios ◽  
The Impact ◽  
Nanoscale Level

The impact on the mechanical properties of unidirectional carbon fiber (CF)/epoxy composites reinforced with pristine graphene nanoplatelets (GNP), highly concentrated graphene oxide (GO), and Functionalized Graphene Oxide (FGO) are investigated in this study. The localized reinforcing effect of each of the graphene nanoplatelet types on the epoxy matrix is predicted at the nanoscale-level by molecular dynamics. The bulk-level mechanical properties of unidirectional CF/epoxy hybrid composites are predicted using micromechanics techniques considering the reinforcing function, content, and aspect ratios for each of the graphene nanoplatelets. In addition, the effect of nanoplatelets dispersion level is also investigated for the pristine graphene nanoplatelets considering a lower dispersion level with four layers of graphene nanoplatelets (4GNP). The results indicate that the shear and transverse properties are significantly affected by the nanoplatelet type, loading and aspect ratio. The results of this study can be used in the design of hybrid composites to tailor specific laminate properties by adjusting nanoplatelet parameters.

Effect of graphite and silicon carbide fillers on mechanical properties of PA6 polymer composites

2017 ◽  
Vol 37 (6) ◽  
pp. 547-557 ◽  
Author(s):  
Sekaran Sathees Kumar ◽  
Ganesan Kanagaraj
Keyword(s):  
Mechanical Properties ◽  
Silicon Carbide ◽  
Polymer Composites ◽  
Interfacial Adhesion ◽  
Hybrid Composites ◽  
Fracture Morphology ◽  
Tensile Fracture ◽  
Injection Molded ◽  
The Individual

Abstract In this paper, the combined effect of different weight percentages of silicon carbide (SiC) and graphite (Gr) reinforcement on the mechanical properties of polyamide (PA6) composite is studied. Test specimens of pure PA6, 85 wt% PA6+10 wt% SiC+5 wt% Gr and 85 wt% PA6+5 wt% SiC+10 wt% Gr are prepared using an injection molding machine. The tensile, impact, hardness, morphology and thermal properties of the injection molded composites were investigated. The obtained results showed that mechanical properties, such as tensile and impact strength and modulus of the PA6 composites, were significantly higher than the pure PA6, and hybridization with silicon carbide and graphite further enhanced the performance properties, as well as the thermal resistance of the composites. The tensile fracture morphology and the characterization of PA6 polymer composites were observed by scanning electron microscope (SEM) and Fourier transform infrared spectroscopic methods. SEM observation of the fracture surfaces showed the fine dispersion of SiC and Gr for strong interfacial adhesion between fibers and matrix. The individual and combined reinforcing effects of silicon carbide and graphite on the mechanical properties of PA6 hybrid composites were compared and interpreted in this study. Improved mechanical properties were observed by the addition of small amount of SiC and Gr concurrently reinforced with the pure PA6. Finally, thermogravimetric analysis showed that the heat resistance of the composites tended to increase with increasing silicon carbide and graphite content simultaneously.

scholarly journals Thermal, mechanical and morphological properties of polyurethane–zirconia loading

2020 ◽  
Author(s):  
Ali J Salman ◽  
Ali Assim Al-Obaidi ◽  
Dalya H Al-Mamoori ◽  
Lina M Shaker ◽  
Ahmed A Al-Amiery
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Thermal Properties ◽  
Material Science ◽  
Morphological Properties ◽  
Flexural Stress ◽  
Renewable Materials ◽  
Sem Images ◽  
The Impact ◽  
Scanning Electron

Abstract The polyurethane (PU) has been showing a dramatic increase in applications related to material science and technology. However, the mechanical, physical and thermal properties could be further improved by loading PU with zirconia (Zr) to create renewable materials known as polyurethane–zirconia (PUZ) composites. In this study, PU matrix was treated with wt.% Zr at 0.5, 1.0, 1.5 and 2.0. In this study, the thermo-mechanical properties and the morphology were investigated of PU and PUZ nano-samples. The images of the scanning electron microscope (SEM) were the prime tool in investigating PU and PUZ surfaces and fractured surfaces showing vanishing the cracks and formation of agglomeration on the sample PUZ-1.5%. In addition, the tensile strength, Young’s modulus and maximum loading were improved by 36.7, 31.8 and 39.1%, respectively, at Zr loading of 1.5 wt.%. The flexural stress and the load were improved by 94.3% and 93.6%, respectively, when Zr loading was 1.5 wt.%. The impact without and with a notch was improved by 110.7% and 62.6%, respectively, at Zr loading of 1.5 wt.%. The the morphologies of the PU surface and Zr surface supported by SEM images. Regarding the storage modulus ability of PU and PUZ composites, Zr loading has negatively influenced E. The E functioning temperature was observed to move from 142 to 183°C. Another effect was determined by adding a small amount of Zr. This small amount was enough to shift the crystallization temperature (${T}_c$) and the melting temperature (${T}_m$) of PU from 125 to 129°C and from 150 to 144°C, respectively.

Evaluation of Mechanical Properties and Microstructures of Casing-Drilling Steels

2010 ◽  
Vol 146-147 ◽  
pp. 674-677
Author(s):  
Tian Han Xu ◽  
Yao Rong Feng ◽  
Sheng Yin Song ◽  
Zhi Hao Jin
Keyword(s):  
Mechanical Properties ◽  
Fracture Surface ◽  
Impact Energy ◽  
Cleavage Fracture ◽  
Fracture Mechanism ◽  
Tensile Fracture ◽  
Tensile Fracture Surface ◽  
Dimple Fracture ◽  
Drilling Technology ◽  
Casing Drilling

An investigation into the mechanical properties of K55，N80 and P110 steels was carried out for casing-drilling technology. The obvious presence of bright facets on broken K55 Charpy V-Notch (CVN) sample surfaces was indicative of the effect of microstructure on the cleavage fracture. The appearing of bright facet surfaces of K55 was attributed to the microstructure of ferrite and pearlite. The fracture surfaces of N80 and P110 CVN samples included quasi-cleavage fracture mechanism and dimple fracture mechanism, respectively. The tensile fracture surface of all three types of casing-drilling steels included dimple fracture mechanism, both the N80 and P110 specimen show higher UTS and impact energy values compared to the K55 specimen.

Properties Evaluation of Micro-Crystalline Cellulose and Starch as Bio-Filler in Rubber Compounding

2016 ◽  
Vol 1133 ◽  
pp. 593-597 ◽  
Author(s):  
Mohd Khairulniza Mansor ◽  
Ruslimie Che Ali
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Filler Loading ◽  
Tensile Fracture ◽  
Crystalline Cellulose ◽  
Tensile Fracture Surface ◽  
Homogenous Distribution ◽  
Cure Time ◽  
Internal Mixer ◽  
Scanning Electron

Effects of filler loading on the mechanical properties of Epoxidised natural rubber (ENR) filled with bio-fillers were studied. The compounds with different filler loadings (0, 30, 50, 70 phr) were prepared in a Haake internal mixer. Result showed that the viscosity of the compounds increased with filler loading and exhibited longer cure time with higher loading of the bio-filler. The mechanical properties of starch-filled vulcanisates present better tensile strength at 50 phr when compared to micro-crystalline cellulose (MCC) filled vulcanisates at similar filler loadings. The scanning electron microscopy (SEM) of tensile fracture surface of 50 phr starch-filled vulcanisates illustrated a homogenous distribution in comparison with MCC-filled compounds.

scholarly journals The Influence of MMA Esterification on Interfacial Adhesion and Mechanical Properties of Hybrid Kenaf Bast/Glass Fiber Reinforced Unsaturated Polyester Composites

Materials ◽  
2021 ◽  
Vol 14 (9) ◽  
pp. 2276
Author(s):  
Rozyanty Rahman ◽  
Syed Zhafer Firdaus Syed Putra ◽  
Shayfull Zamree Abd Rahim ◽  
Irwana Nainggolan ◽  
Bartłomiej Jeż ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Glass Fiber ◽  
Interfacial Adhesion ◽  
Natural Fiber ◽  
Hybrid Composites ◽  
Unsaturated Polyester ◽  
Research Work ◽  
Tensile Fracture ◽  
Kenaf Bast

The demand for natural fiber hybrid composites for various applications has increased, which is leading to more research being conducted on natural fiber hybrid composites due to their promising mechanical properties. However, the incompatibility of natural fiber with polymer matrix limits the performance of the natural fiber hybrid composite. In this research work, the mechanical properties and fiber-to-matrix interfacial adhesion were investigated. The efficiency of methyl methacrylate (MMA)-esterification treatments on composites’ final product performance was determined. The composite was prepared using the hand lay-up method with varying kenaf bast fiber (KBF) contents of 10, 15, 20, 25, 30, 35 (weight%) and hybridized with glass fiber (GF) at 5 and 10 (weight%). Unsaturated polyester (UPE) resin and methyl ethyl ketone peroxide (MEKP) were used as binders and catalysts, respectively. Scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FTIR) were used to examine the effects of MMA-esterification treatment on tensile strength and morphology (tensile fracture and characterization of MMA-esterification treatment) of the composite fabricated. The tensile strength of MMA-treated reinforced UPE and hybrid composites are higher than that of untreated composites. As for MMA treatment, 90 min of treatment showed the highest weight percent gain (WPG) and tensile strength of KBF-reinforced UPE composites. It can be concluded that the esterification of MMA on the KBF can lead to better mechanical properties and adhesion between the KFB and the UPE matrix. This research provides a clear reference for developing hybrid natural fibers, thus contributing to the current field of knowledge related to GF composites, specifically in transportation diligences due to their properties of being lightweight, superior, and involving low production cost.

Impacted of Vacuum Bag Woven Kenaf/Fiberglass Hybrid Composite

2014 ◽  
Vol 660 ◽  
pp. 572-577
Author(s):  
Syarifah Yunus ◽  
Z. Salleh ◽  
M.A. Aznan ◽  
M.N. Berhan ◽  
A. Kalam ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Impact Energy ◽  
Hybrid Composite ◽  
Hybrid Composites ◽  
Advanced Technology ◽  
Damage Area ◽  
Bending Stresses ◽  
Post Impact ◽  
The Impact ◽  
Woven Kenaf

This paper discusses the mechanical properties of woven kenaf/fiberglass hybrid composites which has been fabricating using vacuum bag technique. Kenaf fiber had chosen among others natural fibres due to its excellent mechanical properties and potential natural raw fiber to replace plastic or tobacco in manufacturing a multitude of products for the construction, automotive, textile and advanced technology sectors. This study investigates post impact tensile of kenaf hybrid composites and its surface fractured. The impact energy used consists of 4J, 6J, 8J, 12J and 16J. The specimens were clamped between two plate rings with an internal hole diameter of 18mm and impacted with hemispherical nose impactor shape with diameter size of 12.7mm. The results revealed that this kenaf hybrid composite showed significant decreasing of strength and modulus as increasing the impact energy. The damage area affected with fiber fracture occurred much later in fracture process due to high bending stresses.

scholarly journals The Degradation of Mechanical Properties in Halloysite Nanoclay-Polyester Nanocomposites Exposed in Seawater Environment

2016 ◽  
Vol 2016 ◽  
pp. 1-12 ◽  
Author(s):  
Mohd Shahneel Saharudin ◽  
Jiacheng Wei ◽  
Islam Shyha ◽  
Fawad Inam
Keyword(s):  
Mechanical Properties ◽  
Impact Toughness ◽  
Flexural Modulus ◽  
Resin Matrix ◽  
Matrix Interface ◽  
Sem Images ◽  
Plasticization Effect ◽  
Polyester Matrix ◽  
Seawater Environment ◽  
The Impact

Polyester based polymers are extensively used in aggressive marine environments; however, inadequate data is available on the effects of the seawater on the polyester based nanocomposites mechanical properties. This paper reports the effect of seawater absorption on the mechanical properties degradation of halloysite nanoclay-polyester nanocomposites. Results confirmed that the addition of halloysite nanoclay into polyester matrix was found to increase seawater uptake and reduce mechanical properties compared to monolithic polyester. The maximum decreases in microhardness, tensile and flexural properties, and impact toughness were observed in case of 1 wt% nanoclay. The microhardness decreased from 107 HV to 41.7 HV (61% decrease). Young’s modulus decreased from 0.6 GPa to 0.4 GPa (33% decrease). The flexural modulus decreased from 0.6 GPa to 0.34 GPa (43% decrease). The impact toughness dropped from 0.71 kJ/m2to 0.48 kJ/m2(32% decrease). Interestingly, the fracture toughnessKICincreased with the addition of halloysite nanoclay due to the plasticization effect of the resin matrix. SEM images revealed the significant reduction in mechanical properties in case of 1 wt% reinforcement which is attributed to the degradation of the nanoclay-matrix interface influenced by seawater absorption and agglomeration of halloysite nanoclay.