Microsture and Properties of a Cu-Cr-Zr-Fe-Ti Alloy

2015 ◽  
Vol 723 ◽  
pp. 556-560
Author(s):  
Fu Xiang Huang
Keyword(s):  
Electron Microscopy ◽  
Electrical Conductivity ◽  
Transmission Electron Microscopy ◽  
Age Hardening ◽  
Peak Hardness ◽  
Ti Alloy ◽  
Hardening Behavior ◽  
Transmission Electron ◽  
Zn Alloys ◽  
Scanning Electron

The effect of 0.45 wt. % Fe and 0.2 wt. % Ti additions on the age hardening behavior of Cu-Cr-Zr-Zn alloys has been investigated with respect to hardness, electrical conductivity and microstructure. It was showed that the addition of Fe /Ti to Cu-Cr-Zr-Zn alloys enhance strength and hardness, but decrease the electrical conductivity, and increase the aging temperature and time for attaining peak hardness. The scanning electron microscope (SEM) and transmission electron microscopy (TEM) results showed that there are four types of phases in the alloy, Cu-matrix, Cr-rich, (Cu,Zr)-rich and (Fe,Ti)-rich phases.

scholarly journals Physical Properties and Precipitate Microstructures of Cu-Hf Alloys at Different Processing Stages

Scanning ◽  
2018 ◽  
Vol 2018 ◽  
pp. 1-10
Author(s):  
Mingmao Li ◽  
Leqing Zhang ◽  
Mingbiao Zhu ◽  
Hang Wang ◽  
Haigen Wei
Keyword(s):  
Electron Microscopy ◽  
Electrical Conductivity ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Physical Properties ◽  
Slow Rate ◽  
Softening Temperature ◽  
Transmission Electron ◽  
20 Nm ◽  
Scanning Electron

The microstructural evolution and hardness and physical properties of a Cu-Hf alloy at the different processing stages were investigated using hardness, conductivity and tensile measurements, metallographic microscopy, scanning electron microscopy, and transmission electron microscopy. The results reveal that the electrical conductivity of these alloys was above 80% IACS after aging at 450°C, and the hardness and conductivity of the Cu-0.9Hf alloy were 180 HV0.5 and 80% IACS, respectively. The softening temperature of the Cu-0.15Hf alloy is 525°C, and the softening temperature of Cu-0.4Hf and Cu-0.9Hf alloys is 550°C. The precipitated Hf-containing phase exhibited a short rod-like structure, the size of which increased with aging time at a slow rate and resulted in the size of ~20 nm after aging at 450°C for 300 min.

Two- or three-way observations of the identical cell elements within the same sections by LM, TEM and/or SEM

1978 ◽  
Vol 36 (2) ◽  
pp. 82-83 ◽  
Author(s):  
Nakazo Watari ◽  
Yasuaki Hotta ◽  
Yoshio Mabuchi
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Fine Structure ◽  
Light Microscopy ◽  
Thin Sections ◽  
Transmission Electron ◽  
Identical Cell ◽  
Electron Microscopes ◽  
Scanning Electron

It is very useful if we can observe the identical cell elements within the same sections by light microscopy (LM), transmission electron microscopy (TEM) and/or scanning electron microscopy (SEM) sequentially, because, the cell fine structure can not be indicated by LM, while the color is; on the other hand, the cell fine structure can be very easily observed by EM, although its color properties may not. However, there is one problem in that LM requires thick sections of over 1 μm, while EM needs very thin sections of under 100 nm. Recently, we have developed a new method to observe the same cell elements within the same plastic sections using both light and transmission (conventional or high-voltage) electron microscopes.In this paper, we have developed two new observation methods for the identical cell elements within the same sections, both plastic-embedded and paraffin-embedded, using light microscopy, transmission electron microscopy and/or scanning electron microscopy (Fig. 1).

Scanning and Transmission Electron Microscopy of Human Red Blood Cells

1969 ◽  
Vol 27 ◽  
pp. 44-45
Author(s):  
A.J. Tousimis ◽  
T.R. Padden
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Blood Cells ◽  
Room Temperature ◽  
Type Specimen ◽  
New Combination ◽  
Human Red Blood Cells ◽  
Transmission Electron ◽  
Microscope Slides ◽  
Scanning Electron

The size, shape and surface morphology of human erythrocytes (RBC) were examined by scanning electron microscopy (SEM), of the fixed material directly and by transmission electron microscopy (TEM) of surface replicas to compare the relative merits of these two observational procedures for this type specimen.A sample of human blood was fixed in glutaraldehyde and washed in distilled water by centrifugation. The washed RBC's were spread on freshly cleaved mica and on aluminum coated microscope slides and then air dried at room temperature. The SEM specimens were rotary coated with 150Å of 60:40- gold:palladium alloy in a vacuum evaporator using a new combination spinning and tilting device. The TEM specimens were preshadowed with platinum and then rotary coated with carbon in the same device. After stripping the RBC-Pt-C composite film, the RBC's were dissolved in 2.5N HNO3 followed by 0.2N NaOH leaving the preshadowed surface replicas showing positive topography.

Precipitation in Al-Li-Cu Alloys

1981 ◽  
Vol 39 ◽  
pp. 44-45
Author(s):  
J. E. O'Neal ◽  
K. K. Sankaran
Keyword(s):  
Electron Microscopy ◽  
Age Hardening ◽  
Precipitation Behavior ◽  
Zone Formation ◽  
Specific Strength ◽  
Hardening Behavior ◽  
Cu Alloys ◽  
High Specific Strength ◽  
Transmission Electron ◽  
Structural Applications

Al-Li-Cu alloys combine high specific strength and high specific modulus and are potential candidates for aircraft structural applications. As part of an effort to optimize Al-Li-Cu alloys for specific applications, precipitation in these alloys was studied for a range of compositions, and the mechanical behavior was correlated with the microstructures.Alloys with nominal compositions of Al-4Cu-2Li-0.2Zr, Al-2.5Cu-2.5Li-0.2Zr, and Al-l.5Cu-2.5Li-0.5Mn were argon-atomized into powder at solidification rates ≈ 103°C/s. Powders were consolidated into bar stock by vacuum pressing and extruding at 400°C. Alloy specimens were solution annealed at 530°C and aged at temperatures up to 250°C, and the resultant precipitation was studied by transmission electron microscopy (TEM).The low-temperature (≲100°C) precipitation behavior of the Al-4Cu-2Li-0.2Zr alloy is a combination of the separate precipitation behaviors of Al-Cu and Al-Li alloys. The age-hardening behavior at these temperatures is characteristic of Guinier-Preston (GP) zone formation, with additional strengthening resulting from the coherent precipitation of δ’ (Al3Li, Ll2 structure), the presence of which is revealed by the selected-area diffraction pattern (SADP) shown in Figure la.

Comparative Study of the Fine Morphology of Sensory Receptors in Aspidogaster conchicola and Cotylaspis insignis

1972 ◽  
Vol 30 ◽  
pp. 150-151
Author(s):  
Venita F. Allison ◽  
J. E. Ubelaker ◽  
J. H. Martin
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Nervous System ◽  
Osmic Acid ◽  
Sensory Receptors ◽  
Transmission Electron ◽  
Sensory Structures ◽  
Fine Morphology ◽  
Scanning Electron

It has been suggested that parasitism results in a reduction of sensory structures which concomitantly reflects a reduction in the complexity of the nervous system. The present study tests this hypothesis by examining the fine morphology and the distribution of sensory receptors for two species of aspidogastrid trematodes by transmission and scanning electron microscopy. The species chosen are an ectoparasite, Cotylaspis insignis and an endoparasite, Aspidogaster conchicola.Aspidogaster conchicola and Cotylaspis insignis were obtained from natural infections of clams, Anodonta corpulenta and Proptera purpurata. The specimens were fixed for transmission electron microscopy in phosphate buffered paraformaldehyde followed by osmic acid in the same buffer, dehydrated in an ascending series of ethanol solutions and embedded in Epon 812.

Anisotropic Membranes as Substrates for Sem

1976 ◽  
Vol 34 ◽  
pp. 444-445
Author(s):  
Thomas P. Turnbull ◽  
W. F. Bowers
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
High Flow ◽  
Polymer Chemistry ◽  
Surface Porosity ◽  
Transmission Electron ◽  
Pore Texture ◽  
Spongy Layer ◽  
Scanning Electron

Until recently the prime purposes of filters have been to produce clear filtrates or to collect particles from solution and then remove the filter medium and examine the particles by transmission electron microscopy. These filters have not had the best characteristics for scanning electron microscopy due to the size of the pores or the surface topography. Advances in polymer chemistry and membrane technology resulted in membranes whose characteristics make them versatile substrates for many scanning electron microscope applications. These polysulphone type membranes are anisotropic, consisting of a very thin (0.1 to 1.5 μm) dense skin of extremely fine, controlled pore texture upon a much thicker (50 to 250μm), spongy layer of the same polymer. Apparent pore diameters can be controlled in the range of 10 to 40 A. The high flow ultrafilters which we are describing have a surface porosity in the range of 15 to 25 angstrom units (0.0015-0.0025μm).

Digital imaging: When should one take the plunge?

1996 ◽  
Vol 54 ◽  
pp. 602-603
Author(s):  
John F. Mansfield
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Optical Microscopy ◽  
Digital Imaging ◽  
Storage Devices ◽  
Major Benefit ◽  
Transmission Electron ◽  
New Instrument ◽  
Scanning Electron

The current imaging trend in optical microscopy, scanning electron microscopy (SEM) or transmission electron microscopy (TEM) is to record all data digitally. Most manufacturers currently market digital acquisition systems with their microscope packages. The advantages of digital acquisition include: almost instant viewing of the data as a high-quaity positive image (a major benefit when compared to TEM images recorded onto film, where one must wait until after the microscope session to develop the images); the ability to readily quantify features in the images and measure intensities; and extremely compact storage (removable 5.25” storage devices which now can hold up to several gigabytes of data).The problem for many researchers, however, is that they have perfectly serviceable microscopes that they routinely use that have no digital imaging capabilities with little hope of purchasing a new instrument.

scholarly journals The Domain and Microstructure of Resin-Bonded Magnets

Materials ◽  
2021 ◽  
Vol 14 (11) ◽  
pp. 2849
Author(s):  
Marcin Jan Dośpiał
Keyword(s):  
Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Grain Size ◽  
Size Distribution ◽  
Domain Structure ◽  
Grain Size Distribution ◽  
Exchange Interactions ◽  
Force Microscopy ◽  
Transmission Electron ◽  
Scanning Electron

This paper presents domain and structure studies of bonded magnets made from nanocrystalline Nd-(Fe, Co)-B powder. The structure studies were investigated using scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), Mössbauer spectroscopy and X-ray diffractometry. On the basis of performed qualitative and quantitative phase composition studies, it was found that investigated alloy was mainly composed of Nd2(Fe-Co)14B hard magnetic phase (98 vol%) and a small amount of Nd1.1Fe4B4 paramagnetic phase (2 vol%). The best fit of grain size distribution was achieved for the lognormal function. The mean grain size determined from transmission electron microscopy (TEM) images on the basis of grain size distribution and diffraction pattern using the Bragg equation was about ≈130 nm. HRTEM images showed that over-stoichiometric Nd was mainly distributed on the grain boundaries as a thin amorphous border of 2 nm in width. The domain structure was investigated using a scanning electron microscope and metallographic light microscope, respectively, by Bitter and Kerr methods, and by magnetic force microscopy. Domain structure studies revealed that the observed domain structure had a labyrinth shape, which is typically observed in magnets, where strong exchange interactions between grains are present. The analysis of the domain structure in different states of magnetization revealed the dynamics of the reversal magnetization process.

Sign in / Sign up

Export Citation Format

Share Document