The Two-Stage Curing Method for Shape-Memory Materials

2012 ◽  
Vol 476-478 ◽  
pp. 2227-2230
Author(s):  
He Sun ◽  
Yu Yan Liu ◽  
Hui Feng Tan ◽  
Chang Guo Wang
Keyword(s):  
Shape Memory ◽  
Memory Performance ◽  
Mechanical Analysis ◽  
Scanning Calorimetry ◽  
Two Stage ◽  
Memory Tests ◽  
Second Stage ◽  
Shape Memory Properties ◽  
Shape Memory Materials ◽  
Curing Method

In this paper, a various shape-memory materials had been prepared by two-stage curing method. The purpose of using this approach was to maintain the excellent shape memory properties and low glass transition temperature (Tg) of shape-memory materials after first stage curing, furthermore, improve the Tg and heat resistence effectively after second stage curing. Differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA) and fold-deploy shape memory tests were used to characterize the feasibility of two-stage curing, thermodynamics properties and shape memory performance of these polymers. DSC results showed that two different curing stages could be achieved successfully, DMA results suggested that heat resistance of materials had been improved after second curing stage, while the fold-deploy shape memory tests proved that the composites possessed excellent shape memory properties, it could be deformed into different shape and recovered its original shape fully within three minutes.

scholarly journals Bio-Based Epoxy Shape-Memory Thermosets from Triglycidyl Phloroglucinol

Polymers ◽  
2020 ◽  
Vol 12 (3) ◽  
pp. 542 ◽  
Author(s):  
David Santiago ◽  
Dailyn Guzmán ◽  
Francesc Ferrando ◽  
Àngels Serra ◽  
Silvia De la Flor
Keyword(s):  
Shape Memory ◽  
Shape Recovery ◽  
Memory Performance ◽  
Crosslinking Agent ◽  
Shape Memory Polymers ◽  
Crosslinking Density ◽  
Mechanical Analysis ◽  
Diglycidyl Ether ◽  
Partial Substitution ◽  
Scanning Calorimetry

A series of bio-based epoxy shape-memory thermosetting polymers were synthesized starting from a triglycidyl phloroglucinol (3EPOPh) and trimethylolpropane triglycidyl ether (TPTE) as epoxy monomers and a polyetheramine (JEF) as crosslinking agent. The evolution of the curing process was studied by differential scanning calorimetry (DSC) and the materials obtained were characterized by means of DSC, thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), stress-strain tests, and microindentation. Shape-memory properties were evaluated under free and totally constrained conditions. All results were compared with an industrial epoxy thermoset prepared from standard diglycidyl ether of Bisphenol A (DGEBA). Results revealed that materials prepared from 3EPOPh were more reactive and showed a tighter network with higher crosslinking density and glass transition temperatures than the prepared from DGEBA. The partial substitution of 3EPOPh by TPTE as epoxy comonomer caused an increase in the molecular mobility of the materials but without worsening the thermal stability. The shape-memory polymers (SMPs) prepared from 3EPOPh showed good mechanical properties as well as an excellent shape-memory performance. They showed almost complete shape-recovery and shape-fixation, fast shape-recovery rates, and recovery stress up to 7 MPa. The results obtained in this study allow us to conclude that the triglycidyl phloroglucinol derivative of eugenol is a safe and environmentally friendly alternative to DGEBA for preparing thermosetting shape-memory polymers.

scholarly journals Mechanical, Thermal, and Shape Memory Properties of Three-Dimensional Printing Biomass Composites

Polymers ◽  
2018 ◽  
Vol 10 (11) ◽  
pp. 1234 ◽  
Author(s):  
Hongjie Bi ◽  
Min Xu ◽  
Gaoyuan Ye ◽  
Rui Guo ◽  
Liping Cai ◽  
...  
Keyword(s):  
Shape Memory ◽  
Wood Flour ◽  
Memory Performance ◽  
Thermoplastic Polyurethane ◽  
Tensile Elongation ◽  
Three Dimensional ◽  
Mechanical Analysis ◽  
Shape Memory Properties ◽  
Shape Memory Composites ◽  
Recovery Angle

In this study, a series of heat-induced shape memory composites was prepared by the hot-melt extrusion and three-dimensional (3D) printing of thermoplastic polyurethane (TPU) using wood flour (WF) with different contents of EPDM-g-MAH. The mechanical properties, microtopography, thermal property analysis, and heat-induced shape memory properties of the composites were examined. The results showed that, when the EPDM-g-MAH content was 4%, the tensile elongation and tensile strength of the composites reached the maximum value. The scanning electron microscopy and dynamic mechanical analysis results revealed a good interface bonding between TPU and WF when the EPDM-g-MAH content was 4%. The thermogravimetric analysis indicated that the thermal stability of TPU/WF composites was enhanced by the addition of 4% EPDM-g-MAH. Heat-induced shape memory test results showed that the shape memory performance of composites with 4% EPDM-g-MAH was better than that of unmodified-composites. The composites’ shape recovery performance at a temperature of 60 °C was higher than that of the composites at ambient temperature. It was also found that, when the filling angle of the specimen was 45°, the recovery angle of the composites was larger.

scholarly journals Reprogrammable Permanent Shape Memory Materials Based on Reversibly Crosslinked Epoxy/PCL Blends

Molecules ◽  
2020 ◽  
Vol 25 (7) ◽  
pp. 1568
Author(s):  
Iker Razquin ◽  
Alvaro Iregui ◽  
Lidia Orduna ◽  
Loli Martin ◽  
Alba González ◽  
...  
Keyword(s):  
Differential Scanning Calorimetry ◽  
Glass Transition ◽  
Shape Memory ◽  
Curing Process ◽  
Scanning Calorimetry ◽  
Disulfide Exchange ◽  
Shape Memory Properties ◽  
Permanent Shape ◽  
Shape Memory Materials ◽  
Very High

Epoxy/Polycaprolactone (PCL) blends cured with a conventional diamine (4,4′-diaminodiphenylmethane, DDM) and with different amounts of a disulfide containing diamine (4, 4´-dithioaniline, DSS) were prepared through melting. The curing process was studied by FTIR and differential scanning calorimetry (DSC) and the mechanical behavior of the networks was studied by DMA. The shape memory properties and the recyclability of the materials were also analyzed. All blends showed a very high curing degree and temperature activated shape memory effect, related to the glass transition of the epoxy resin. The PCL plasticized the mixture, allowing tailoring of the epoxy glass transition. In addition, in the blends cured with DSS, as a consequence of the disulfide exchange reaction, the permanent shape could be erased and a new shape could be reprogrammed. Using this strategy, reprogrammable permanent shape memory materials were obtained.

A strengthening approach for damping property and shape memory property of acrylic rubber/polylactide blends

2018 ◽  
Vol 51 (7-8) ◽  
pp. 626-643
Author(s):  
Chengliang Li ◽  
Xingxing Ji ◽  
Yang Lyu ◽  
Xinyan Shi
Keyword(s):  
Shape Memory ◽  
Loss Factor ◽  
Phenol Formaldehyde ◽  
Mechanical Analysis ◽  
Damping Properties ◽  
Shape Memory Property ◽  
Memory Property ◽  
Damping Material ◽  
Shape Memory Properties ◽  
Shape Memory Effects

In this work, a damping material was successfully prepared by blending acrylic rubber (ACM) and polylactide (PLA) with sulfur and soap salt as the curing agents. A phenol-formaldehyde (PF) resin was used as a modifier. The effects of PF on the mechanical properties, damping properties, compatibility and shape memory properties of the blends were studied. The compatibility and damping properties were characterized by dynamic mechanical analysis, Fourier transform infrared spectroscope and microstructure analysis. The shape memory properties were examined by thermal mechanical analyser. The results revealed that the tensile strength of the blends was decreased and the toughness was increased with the increase of PF loadings. The introduction of PF improved the compatibility between PLA and ACM, which was deduced from the fact that the glass transition temperature of ACM was increased and the two loss factor peaks became closer. It was also found that the loss factor peak became higher and the effective damping temperature range became wider due to the formation of hydrogen bonding, implying that the damping properties of ACM/PLA blends were significantly improved. The ACM/PLA blends exhibited good dual-shape memory effect and its shape recovery ratio was increased by introduction of PF and raising the trigger temperature. The blends also exhibited good triple-shape memory property, which was dramatically improved by the introduction of PF. The mechanisms for the enhanced shape memory effects were then analysed.

scholarly journals The Effect of POSS Type on the Shape Memory Properties of Epoxy-Based Nanocomposites

Molecules ◽  
2020 ◽  
Vol 25 (18) ◽  
pp. 4203
Author(s):  
Avraham I. Bram ◽  
Irina Gouzman ◽  
Asaf Bolker ◽  
Noam Eliaz ◽  
Ronen Verker
Keyword(s):  
Transition Temperature ◽  
Shape Memory ◽  
Crosslinking Density ◽  
Mechanical Analysis ◽  
Thermomechanical Properties ◽  
Space Environment ◽  
Scanning Calorimetry ◽  
Space Applications ◽  
Curing Conditions ◽  
Oligomeric Silsesquioxane

Thermally activated shape memory polymers (SMPs) can memorize a temporary shape at low temperature and return to their permanent shape at higher temperature. These materials can be used for light and compact space deployment mechanisms. The control of transition temperature and thermomechanical properties of epoxy-based SMPs can be done using functionalized polyhedral oligomeric silsesquioxane (POSS) additives, which are also known to improve the durability to atomic oxygen in the space environment. In this study, the influence of varying amounts of two types of POSS added to epoxy-based SMPs on the shape memory effect (SME) were studied. The first type contained amine groups, whereas the second type contained epoxide groups. The curing conditions were defined using differential scanning calorimetry and glass transition temperature (Tg) measurements. Thermomechanical and SME properties were characterized using dynamic mechanical analysis. It was found that SMPs containing amine-based POSS show higher Tg, better shape fixity and faster recovery speed, while SMPs containing epoxide-based POSS have higher crosslinking density and show superior thermomechanical properties above Tg. This work demonstrates how the Tg and SME of SMPs can be controlled by the type and amount of POSS in an epoxy-based SMP nanocomposite for future space applications.

Novel shape-memory polyurethane fibers for textile applications

2018 ◽  
Vol 89 (6) ◽  
pp. 1027-1037 ◽  
Author(s):  
Míriam Sáenz-Pérez ◽  
Tariq Bashir ◽  
José Manuel Laza ◽  
Jorge García-Barrasa ◽  
José Luis Vilas ◽  
...  
Keyword(s):  
Differential Scanning Calorimetry ◽  
Shape Memory ◽  
Tensile Testing ◽  
Melt Spinning ◽  
Mechanical Analysis ◽  
Knitted Fabric ◽  
Scanning Calorimetry ◽  
Moisture Management ◽  
Potential Applications ◽  
Shape Memory Polyurethane

In this work, thermoresponsive shape-memory polyurethane (SMPU) fibers were produced by melt spinning from different SMPU pellets. Afterwards, the knitted fabric samples were prepared by the obtained fibers. Some of the SMPUs used were synthesized previously in our laboratory whereas a commercial one, named DIAPLEX MM4520, was also evaluated in order to carry out comparative studies. All the SMPUs were characterized by different techniques, such as thermogravimetric analysis, differential scanning calorimetry, dynamic mechanical analysis and tensile testing. Moreover, the shape-memory capabilities of the fabrics were measured by thermo-mechanical analysis. The obtained results show that the synthesized SMPUs could be attractive candidates for potential applications such as breathable fabrics or moisture-management textiles.

Shape-Memory Properties of Radiopaque Micro-Composites from Amorphous Polyether Urethanes Designed for Medical Application

2009 ◽  
Vol 1190 ◽  
Author(s):  
Jing Cui ◽  
Karl Kratz ◽  
Andreas Lendlein
Keyword(s):  
Shape Memory ◽  
Polymer Composites ◽  
Medical Application ◽  
Tensile Tests ◽  
Barium Sulphate ◽  
Mechanical Analysis ◽  
Gravimetric Analysis ◽  
Micro Particles ◽  
Shape Memory Properties

AbstractBiocompatible shape-memory polymers are of high significance for application in medical devices or instruments for minimally invasive surgery. To follow the medical device placement or changes in shape of the device in vivo by imaging methods like X-ray techniques, radiopacity of the polymer is required. In this work, we explored the shape-memory properties of radiopaque polymer composites prepared by incorporation of barium sulphate micro-particles in a biomedical grade polyether urethane (PEU) by co-extrusion technique. The filler content was varied from 5 wt% to 40 wt%, which was confirmed by thermal gravimetric analysis (TGA) measurements, while the particle distribution was visualized by scanning electron microscopy (SEM). The thermal and mechanical properties of the composites were investigated by means of dynamic mechanical analysis at varied temperature (DMTA) and tensile tests. The shape-memory properties of PEU composites were quantified in cyclic, thermomechanical experiments. A significant increase in Young’s modulus and a decrease in elongation at break were observed for PEU composites with increasing content of BaSO4, while the DMTA results were not affected by incorporation of the fillers. All samples exhibited excellent shape-memory properties with shape fixity rates (Rf) above 98% and values for shape recovery rate (Rr) in the range of 81% to 93%. The maximum stress (σmax) obtained under constant strain recovery conditions increased from 0.6 MPa to 1.4 MPa with raising amount of BaSO4, while the corresponding temperature (Tσ,max) as well as the switching temperature (Tsw) determined under stress-free conditions remained constant for all polymer composites.

Study of a Cu-Al-Mn Shape Memory Alloy Produced by Plasma Melting Followed by Injection Molding

2014 ◽  
Vol 1611 ◽  
pp. 25-30
Author(s):  
Francisco Fernando Roberto Pereira ◽  
Maria Goretti Ferreira Coutinho ◽  
Bruno Moura Miranda ◽  
Carlos José de Araújo
Keyword(s):  
Injection Molding ◽  
Shape Memory ◽  
Shape Recovery ◽  
Permanent Deformation ◽  
Melting Process ◽  
Mechanical Analysis ◽  
Scanning Calorimetry ◽  
Dynamical Mechanical Analysis ◽  
Plasma Melting ◽  
New Applications

ABSTRACTShape Memory Alloys (SMA) are characterized by the capacity to recover a permanent deformation after being heated above a critical temperature called Final Austenite Temperature (Af). The Ni-Ti SMA are the most commercially used, however recent studies showed that the Cu-Al-Mn SMA present significant shape recovery and mechanical properties, showing a strong potential for developing new applications. In this context, the main goal of this work is to manufacture a Cu-Al-Mn SMA through a plasma melting process followed by injection molding of liquid metal and then characterize the samples, using the following techniques: Optical Microscopy (OM), Differential Scanning Calorimetry (DSC), Electrical Resistance as a function of Temperature (ERT) tests, Dynamical Mechanical Analysis (DMA) and Microhardness (MH).

scholarly journals Block Copolymers of Poly(ω-Pentadecalactone) in Segmented Polyurethanes: Novel Biodegradable Shape Memory Polyurethanes

Polymers ◽  
2020 ◽  
Vol 12 (9) ◽  
pp. 1928
Author(s):  
Katalin Czifrák ◽  
Csilla Lakatos ◽  
Marcell Árpád Kordován ◽  
Lajos Nagy ◽  
Lajos Daróczi ◽  
...  
Keyword(s):  
Shape Memory ◽  
Shape Recovery ◽  
Mechanical Analysis ◽  
Attenuated Total Reflectance ◽  
Dibutyltin Dilaurate ◽  
Scanning Calorimetry ◽  
Dynamical Mechanical Analysis ◽  
Good Shape ◽  
Segmented Polyurethanes ◽  
Shape Fixity

In this report, the synthesis of poly(ω-pentadecalactone) (PPDL) (co)polymers and their incorporation into polyurethanes (PUs) are reported. Optimal conditions for the ring-opening polymerization (ROP) of ω-pentadecalactone (PDL) using dibutyltin dilaurate catalyst were established. For the synthesis of linear and crosslinked PUs, 50 kDa poly(ε-caprolactone) (PCL) and 1,6-hexamethylenediisocyanate (HDI) were used. The obtained polyurethanes were characterized by Attenuated Total Reflectance Fourier-Transform Infrared spectroscopy (AT-FTIR), differential scanning calorimetry (DSC), and dynamical mechanical analysis (DMA). The DMA of the selected sample showed a rubbery plateau on the storage modulus versus temperature curve predicting shape memory behavior. Indeed, good shape memory performances were obtained with shape fixity (Rf) and shape recovery (Rr) ratios.

scholarly journals Shape Memory Epoxy Polymer (SMEP) Composite Mechanical Properties Enhanced by Introducing Graphene Oxide (GO) into the Matrix

Materials ◽  
2019 ◽  
Vol 12 (7) ◽  
pp. 1107 ◽  
Author(s):  
Zhengwei Yu ◽  
Zhenqing Wang ◽  
Hao Li ◽  
Jianxin Teng ◽  
Lidan Xu
Keyword(s):  
Graphene Oxide ◽  
Shape Memory ◽  
Polymer Composites ◽  
Epoxy Polymer ◽  
Mechanical Performance ◽  
Memory Performance ◽  
Mechanical Analysis ◽  
Tensile Fracture ◽  
Good Shape ◽  
The Matrix

Shape memory epoxy polymer (SMEP) composite specimens with different graphene oxide (GO) contents were manufactured to study the effects of GO mass fractions on epoxy polymer composites. While ensuring the shape memory effect of SMEP, the addition of GO also remarkably strengthened the mechanical performance of the polymers. Analyses of the epoxy polymer composites’ thermal, mechanical, and shape memory performance were conducted through carrying out dynamic mechanical analysis (DMA), thermogravimetric analysis (TGA), and static tensile, three-point bending, impact, and shape memory tests. Moreover, the tensile fracture, bending fracture, and impact fracture interfaces of epoxy resin composites were examined with scanning electron microscopy. The final test results indicated that when the GO content was 0.8 wt %, SMEP composites had good shape memory performance and optimum thermal and mechanical performance.

Sign in / Sign up

Export Citation Format

Share Document