Preparation and Characterization of Mesoporous Activated Carbon from Alligator Weed with H3PO4

2014 ◽  
Vol 936 ◽  
pp. 868-874
Author(s):  
Hui Min Xu ◽  
Guo Fu He ◽  
Min Tao Shi ◽  
Jun Tu ◽  
Wei Liu ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Low Cost ◽  
Average Pore Size ◽  
Chemical Activation ◽  
Total Pore Volume ◽  
Alligator Weed ◽  
Average Pore ◽  
Orthogonal Experiments ◽  
Renewable Material ◽  
Impregnation Time

Alligator weed, containing ash of 8.56 wt.% (dry basis), is a low-cost and renewable material for preparing activated carbon (AC) by chemical activation. Yield and iodine number results of orthogonal experiments showed H3PO4 was the optimal activator comparing with NaOH and (NH4)2HPO4. And optimal condition was at impregnation ratio of 4 to 1 with the impregnation time of 6h, carbonization temperature of 873K and carbonization time of 1h. According to calculation of Brunauer-Emmett-Teller (BET), the surface area of P1 (AC prepared by H3PO4 under optimum condition) attained the value of 1100.720 m2/g. Calculated by Barrett-Joyner-Halenda (BJH), the total pore volume and average pore size of P1 were 0.610 cm3/g and 2.216nm. The rate of mesoporous range, as high as 72.00%, revealed P1 was mesoporous AC. FT-IR spectrum suggested P1 contained carboxyl, phenol, ether and other functional groups. XRD showed a graphitization degree of 65.12% indicating its high stability in application.

scholarly journals Preparation of High-Performance Activated Carbon from Coffee Grounds after Extraction of Bio-Oil

Molecules ◽  
2021 ◽  
Vol 26 (2) ◽  
pp. 257
Author(s):  
Jie Ren ◽  
Nanwei Chen ◽  
Li Wan ◽  
Guojian Li ◽  
Tao Chen ◽  
...  
Keyword(s):  
Activated Carbon ◽  
High Performance ◽  
Average Pore Size ◽  
Total Pore Volume ◽  
Micropore Volume ◽  
Bet Surface Area ◽  
Average Pore ◽  
Activation Temperature ◽  
Coffee Grounds ◽  
Bio Oil

In this study, a new method for economical utilization of coffee grounds was developed and tested. The resulting materials were characterized by proximate and elemental analyses, thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and N2 adsorption–desorption at 77 K. The experimental data show bio-oil yields reaching 42.3%. The optimal activated carbon was obtained under vacuum pyrolysis self-activation at an operating temperature of 450 °C, an activation temperature of 600 °C, an activation time of 30 min, and an impregnation ratio with phosphoric acid of 150 wt.%. Under these conditions, the yield of activated carbon reached 27.4% with a BET surface area of 1420 m2·g−1, an average pore size of 2.1 nm, a total pore volume of 0.747 cm3·g−1, and a t-Plot micropore volume of 0.428 cm3·g−1. In addition, the surface of activated carbon looked relatively rough, containing mesopores and micropores with large amounts of corrosion pits.

scholarly journals The Production and Characterization of Activated Carbon Electrodes from Pineapple Leaf Fibers for Supercapacitor Application

2020 ◽  
Vol 9 (1) ◽  
pp. 1-8
Author(s):  
Agustino Agustino ◽  
Rakhmawati Farma ◽  
Erman Taer
Keyword(s):  
Activated Carbon ◽  
Chemical Activation ◽  
Total Pore Volume ◽  
Amorphous Structure ◽  
Physical Activation ◽  
Carbon Electrode ◽  
Average Pore ◽  
Average Pore Radius ◽  
Supercapacitor Application

Elektroda karbon aktif berbasis serat daun nanas (SDN) telah berhasil diproduksi dengan proses tiga langkah berikut ini, yaitu: (i) aktivasi kimia, (ii) karbonisasi, dan (iii) aktivasi fisika. Aktivasi kimia dilakukan dengan menggunakan agen pengaktif KOH dengan konsetrasi 0,3 M. Karbonisasi dilakukan dalam lingkungan gas N2 pada temperatur 600oC dan diikuti oleh aktivasi fisika pada temperatur 850oC menggunakan gas CO2 selama 2,5 jam. Luas permukaan spesifik elektroda 512,211 m2×g-1 dengan volume total pori sebesar 0,093 cm3×g–1, dan jari-jari pori rata-rata 1,199 nm. Morfologi permukaan elektroda karbon aktif menunjukkan adanya serat karbon dengan diameter serat dalam kisaran 101 - 185 nm dan memliki kandungan karbon dengan massa atomik sebesar 84,33%. Elektroda karbon aktif memiliki struktur amorf, yang ditunjukkan oleh dua puncak difraksi yang lebar pada sudut hamburan 24,64 dan 43,77o yang bersesuaian dengan bidang (002) dan (100). Kapasitansi spesifik, energi spesifik dan daya spesifik sel superkapasitor yang dihasilkan masing-masing sebesar 110 F×g-1, 15,28 Wh×kg-1 dan 36,69 W×kg-1. Pineapple leaf fiber (PALF) based activated carbon electrode has been successfully produced using three-step process, i.e. (i) chemical activation, (ii) carbonization, and (iii) physical activation. The chemical activation was carried out using KOH activating agent with a concentration of 0.3 M. The carbonization process is conducted out in N2 gas environment at 600oC and followed by physical activation at a temperature of 850oC by using CO2 gas for 2.5 h. The specific surface area of the electrode is 512.211 m2×g-1 with a total pore volume of 0.093 cm3×g-1, and average pore radius of 1.199 nm. The surface morphology of the electrode shown the carbon fibers with diameter in the range of 101 - 185 nm and carbon content with 84.33% of atomic mass. The activated carbon electrode has an amorphous structure, which is shown by two wide diffraction peaks at scattering angles of 24.64 and 43.77o which correspond to the plane (002) and (100), respectively. The specific capacitance, energy and power of the electrode are 110 F×g-1, 15.28 Wh×kg-1 and 36.69 W×kg-1, respectively.Keywords: Serat daun nanas, Kalium hidroksida, Elektroda karbon aktif, Kapasitansi spesifik, Superkapasitor 

Preparation of Activated Carbon from Blue Coke Powder and its Adsorption Properties of Cr(VI)

2010 ◽  
Vol 156-157 ◽  
pp. 1347-1351 ◽  
Author(s):  
Yu Hong Tian ◽  
Xin Zhe Lan ◽  
Lin Bo Li ◽  
Xiang Yang Chen ◽  
Tang Hua Hu
Keyword(s):  
Activated Carbon ◽  
Average Pore Size ◽  
Total Pore Volume ◽  
Adsorption Properties ◽  
Physical Activation ◽  
Order Kinetic ◽  
Average Pore ◽  
Endothermic Process ◽  
Powder Activated Carbon ◽  
Coke Powder

Activated carbon was prepared from blue coke powder by physical activation. The results show that the specific surface area (BET) is 697.05m2/g, the total pore volume is 0.4569cm3/g and the average pore size is 2.6221nm. The adsorption properties of Cr( ) onto blue coke powder activated carbon are discussed from the kinetics and thermodynamics viewpoints. The pseudo-second-order kinetic model shows the best correlation with experimental data. Langmuir and Freundlich models are used to fit the equilibrium, and it is indicated that Freundlich best fits these data. The adsorption of Cr( ) onto blue coke powder activated carbon is found to be an endothermic process in nature.

scholarly journals Meso- and microporous carbon electrode and its effect on the capacitive, energy and power properties of supercapacitor

2018 ◽  
Vol 9 (3) ◽  
pp. 1263
Author(s):  
Erman Taer ◽  
R. Taslim ◽  
Sugianto Sugianto ◽  
M. Paiszal ◽  
Mukhlis Mukhlis ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Pore Diameter ◽  
Average Pore Size ◽  
Chemical Activation ◽  
Raw Material ◽  
Carbon Electrode ◽  
Average Pore ◽  
Activated Carbon Monoliths ◽  
Activating Agent

Activated carbon monoliths (ACMs) with average pore diameters in the meso- and micropore regions were successfully produced from biomass material. ACM synthesis uses chemical activation with KOH and ZnCl<sub>2</sub> activating agents. The carbon and activating agent mass ratios were 1:1, 1:3, 1:5 and 1:7. Both activating materials produced an ACM with an average pore diameter of 3.2 nm. The specific capacitance, specific surface area, energy and power were as high as 63 F/g, 650 m<sup>2</sup>/g, and 0.23 Wh/kg for KOH and 73 F/g, and 522 m<sup>2</sup>/g, and 19 W/kg for ZnCl<sub>2</sub> activating agents, respectively. For comparison, we also studied the physical and electrochemical properties of ACM with an average pore size in the micropore range from the same raw material.

scholarly journals Low cost activated carbon prepared from Dipterocarpus alatus fruit

2020 ◽  
Vol 3 (SI3) ◽  
pp. first
Author(s):  
Yuvarat Ngernyen ◽  
Werawit Phiewruangnont ◽  
Narathorn Mahantadsanapong ◽  
Chantakorn Patawat ◽  
Ketsara Silakate ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Pore Size ◽  
Surface Area ◽  
Activated Carbons ◽  
Low Cost ◽  
Average Pore Size ◽  
Carbon Adsorbents ◽  
Average Pore ◽  
Maximum Surface ◽  
Dipterocarpus Alatus

Dipterocarpus alatus tree grows prolifically throughout Thailand and can be tapped to yield significant quantities of oil to be used as natural diesel. However, such practices lead to waste dried fruit dropping from the tree. At present, there is no utilization of this dropped fruit, therefore costeffective processes need to be applied to obtain higher value products from this waste. A possible to utilization is the conversion to activated carbon for adsorption applications including the removal of heavy metals, dyes, and other contaminants in water purification and other decontamination process. A major challenge of current commercial activated carbon is the high production cost and recently it has been shown that chemical activators comprise a significant proportion of these costs. This feasibility study investigates the use of Dipterocarpus alatus fruit as raw material to produce low cost activated carbon adsorbents. Activated carbon was prepared from Dipterocarpus alatus fruit: endocarp, mesocarp, and wing by chemical activation with ZnCl2, FeCl3, and KOH. Each part of the fruit was impregnated with 30 wt% activating agent at a ratio of 1:2 for 1 h and then carbonized at 500 oC for a further 1 h. The surface area, pore volume, and average pore size of the resulting carbons were characterized by nitrogen gas adsorption. Activation of mesocarp with ZnCl2, KOH, and FeCl3 gave activated carbons with the surface area of 447, 256, and 199 m2/g, respectively. In the same way, ZnCl2 activation gave a maximum surface area of 312 and 278 m2/g for wing and endocarp, respectively. All of the aforementioned samples have an average pore size of around 2 nm. In contrast, KOH and FeCl3 activation of wing and endocarp produced activated carbon with very low surface area (below 25 m2/g), but with an average pore size of 5- 14 nm. The maximum surface area of activated carbon prepared from Dipterocarpus alatus fruit was higher than some literature examples for activated carbon from other biomass. Consequently, Dipterocarpus alatus fruit demonstrated significant potential as a feedstock for the preparation of low cost activated carbons.

Preparation and Characterization of Sewage Sludge-Based Activated Carbon

2012 ◽  
Vol 599 ◽  
pp. 614-617 ◽  
Author(s):  
Zi Jun Tang ◽  
Chao Ping Cen ◽  
Ping Fang ◽  
Yang Ming Liang
Keyword(s):  
Activated Carbon ◽  
Sewage Sludge ◽  
Zinc Chloride ◽  
Removal Rate ◽  
Chemical Activation ◽  
Total Pore Volume ◽  
Bet Surface Area ◽  
Average Pore ◽  
Preparation Conditions

In this study, a sewage sludge-base activated carbon (SSAC) was prepared by means of ZnCl2 chemical activation-pyrolysis-carbonization. Different factors such as activated temperature, activators, additives, sludge/activation solution ratio, activated time and other factors which affecting SSAC characteristics were studied to obtain the optimal preparation conditions. The result shows that when using 3mol/L zinc chloride with the ratio of zinc chloride to sulfuric acid as 10:1(v/v), activated at 550°C with the ratio of sludge to activation solution as 1:4(w/v) for 1 hour of pyrolysis and the rate of N2 was set at 0.5L/min, the BET surface area, total pore volume and average pore diameter of the SSAC was 469.80m2/g, 0.16cm3/g and 2.60nm respectively. Using SSAC to treat simulating wastewater containing 100mg(Ni2+)/L, the removal rate of Ni2+ was 20.59% with the adsorption capacity of 10.57mg/g. When the pH>10.5 the removal efficiency approached 100%.

scholarly journals Preparation of Activated Carbon from the Biodegradable film for Co2 Capture Applications

2018 ◽  
Vol 20 (3) ◽  
pp. 75-80
Author(s):  
J. Serafin ◽  
A.K. Antosik ◽  
K. Wilpiszewska ◽  
Z. Czech
Keyword(s):  
Activated Carbon ◽  
Activated Carbons ◽  
Low Cost ◽  
Chemical Activation ◽  
Total Pore Volume ◽  
Nitrogen Adsorption ◽  
Waste Utilization ◽  
Co2 Production ◽  
Biodegradable Film ◽  
Adsorption Desorption

Abstract In this work for the fi rst time, activated carbons were prepared from carboxymethyl fi lm (low-cost carboxymethyl fi lm waste), using chemical activation with potassium hydroxide. The samples were characterized by nitrogen adsorption-desorption at 77 K, XRD, SEM methods. The high values of the specifi c surface area and total pore volume were achieved and were equal to 2064 m2/g and 1.188 cm3/g, respectively. Waste from the fi lm can be immediately utilized without CO2 production. This is the environmentally friendly way of waste utilization. Through this process, we can protect our environment. This study showed that the activated carbon obtained from carboxymethyl fi lm waste can be used as a good adsorbent for CO2 adsorption.

scholarly journals Nanoporous Activated Carbon Derived from Rice Husk for High Performance Supercapacitor

2014 ◽  
Vol 2014 ◽  
pp. 1-7 ◽  
Author(s):  
Huaxing Xu ◽  
Biao Gao ◽  
Hao Cao ◽  
Xueyang Chen ◽  
Ling Yu ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Specific Capacitance ◽  
Current Density ◽  
Average Pore Size ◽  
Nanoporous Carbon ◽  
Cycle Life ◽  
Potential Candidate ◽  
Average Pore ◽  
Nanoporous Activated Carbon

Nanoporous activated carbon material was produced from the waste rice husks (RHs) by precarbonizing RHs and activating with KOH. The morphology, structure, and specific surface area were investigated. The nanoporous carbon has the average pore size of 2.2 nm and high specific area of 2523.4 m2 g−1. The specific capacitance of the nanoporous carbon is calculated to be 250 F g−1at the current density of 1 A g−1and remains 80% for 198 F g−1at the current density of 20 A g−1. The nanoporous carbon electrode exhibits long-term cycle life and could keep stable capacitance till 10,000 cycles. The consistently high specific capacitance, rate capacity, and long-term cycle life ability makes it a potential candidate as electrode material for supercapacitor.

scholarly journals Effect of Structure and Chemical Activation on the Adsorption Properties of Green Clay Minerals for the Removal of Cationic Dye

2018 ◽  
Vol 8 (11) ◽  
pp. 2302 ◽  
Author(s):  
Abdelfattah Amari ◽  
Hatem Gannouni ◽  
Mohammad Khan ◽  
Mohammed Almesfer ◽  
Abubakr Elkhaleefa ◽  
...  
Keyword(s):  
Clay Minerals ◽  
Pore Volume ◽  
Acid Treatment ◽  
Structural Changes ◽  
Chemical Activation ◽  
Total Pore Volume ◽  
Batch Adsorption ◽  
Acid Activation ◽  
Cationic Dye ◽  
Average Pore

In this study, natural clay minerals with green appearance were treated with sulfuric acid. Mass percentage of acid (wt%), temperature (T), contact time (t) and liquid-to-solid mass ratio (R) are used as the prevailing factors that determine the extent of acid-activation. The values of these factors range from 15–50%, 60–90 °C, 1.5–6 h and 4–7, respectively. The study has focused on the structural changes as well as textural characteristics of the clay. Three activated clay samples were prepared under different treatment conditions. The samples were characterized using X-ray powder diffraction (XRD), fourier transform infrared (FTIR), scanning electron microscope (SEM), chemical analysis and N2 adsorption techniques. Characterization of the treated clay minerals exhibited significant structural changes to a greater extent of acid-activation, from being partially crystalline to being amorphous silica. The surface area and total pore volume of clay increased proportionally with the level of acid treatment. The average pore diameter behaved differently. During the strong acid treatment, a large increase in pore volume and the enlargement of the pore size distribution were observed. This suggests that considerable structural changes and partial destruction may have occurred in this condition. The removal of methylene blue, used as cationic dye, from aqueous solution by the batch adsorption technique on three prepared acid-activated clay samples was studied. The Langmuir model was found to agree well with the experimental data.

scholarly journals Synthesis and Characterisation of Pyridinium-Based Ionic Liquid as Activating Agent in Rubber Seed Shell Activated Carbon Production for CO2 Capture

2021 ◽  
Vol 82 (1) ◽  
pp. 85-95
Author(s):  
Nawwarah Mokti ◽  
Azry Borhan ◽  
Siti Nur Azella Zaine ◽  
Hayyiratul Fatimah Mohd Zaid
Keyword(s):  
Ionic Liquid ◽  
Activated Carbon ◽  
Adsorption Capacity ◽  
Co2 Capture ◽  
Low Cost ◽  
Chemical Activation ◽  
Green Technology ◽  
Activation Process ◽  
Rubber Seed ◽  
Activating Agent

The use of an activating agent in chemical activation of activated carbon (AC) production is very important as it will help to open the pore structure of AC as adsorbents and could enhance its performance for adsorption capacity. In this study, a pyridinium-based ionic liquid (IL), 1-butylpyridinium bis(trifluoromethylsulfonyl) imide, [C4Py][Tf2N] has been synthesized by using anion exchange reaction and was characterized using few analyses such as 1H-NMR, 13C-NMR and FTIR. Low-cost AC was synthesized by chemical activation process in which rubber seed shell (RSS) and ionic liquid [C4Py][Tf2N] were employed as the precursor and activating agent, respectively. AC has been prepared with different IL concentration (1% and 10%) at 500°C and 800°C for 2 hours. Sample AC2 shows the highest SBET and VT which are 392.8927 m2/g and 0.2059 cm3/g respectively. The surface morphology of synthesized AC can be clearly seen through FESEM analysis. A high concentration of IL in sample AC10 contributed to blockage of pores by the IL. On the other hand, the performance of synthesized AC for CO2 adsorption capacity also studied by using static volumetric technique at 1 bar and 25°C. Sample AC2 contributed the highest CO2 uptakes which is 50.783 cm3/g. This current work shows that the use of low concentration IL as an activating agent has the potential to produce porous AC, which offers low-cost, green technology as well as promising application towards CO2 capture.

Sign in / Sign up

Export Citation Format

Share Document