Elevated Temperature Mechanical Properties of Al-8.5Fe-1.3V-1.7Si/SiCP Composite Prepared by Multi-Layer Spray Deposition

2011 ◽  
Vol 694 ◽  
pp. 708-712
Author(s):  
Yi Qiang He ◽  
Bin Qiao ◽  
Li Chao Feng
Keyword(s):  
Mechanical Properties ◽  
Elevated Temperature ◽  
Spray Deposition ◽  
Partial Dissolution ◽  
Sic Particles ◽  
The Stability

Al-8.5Fe-1.3V-1.7Si/SiCP composite prepared by multi-layer spray deposition in different states were investigated. Ultimate tensile strengths of the composite sheets as-rolled tested at 315°C and 400°C are up to 300MPa and 186MPa respectively. The fine dispersoids and fine grains, and homogeneous SiC particles contribute to the excellent mechanical properties of the composite at elevated temperature. Specially, partial dissolution of SiC particles contributes to the stability of Al12(Fe,V)3Si phase.

An analysis of the transport properties and mechanical stability of rapidly solidified Al-Sb alloy

2015 ◽  
Vol 10 (2) ◽  
pp. 2663-2681
Author(s):  
Rizk El- Sayed ◽  
Mustafa Kamal ◽  
Abu-Bakr El-Bediwi ◽  
Qutaiba Rasheed Solaiman
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Melt Spinning ◽  
Elastic Moduli ◽  
Mechanical Stability ◽  
Microstructural Analysis ◽  
Alloy System ◽  
Antimony Content ◽  
The Stability ◽  
Rapidly Solidified

The structure of a series of AlSb alloys prepared by melt spinning have been studied in the as melt–spun ribbons  as a function of antimony content .The stability  of these structures has  been  related to that of the transport and mechanical properties of the alloy ribbons. Microstructural analysis was performed and it was found that only Al and AlSb phases formed for different composition.  The electrical, thermal and the stability of the mechanical properties are related indirectly through the influence of the antimony content. The results are interpreted in terms of the phase change occurring to alloy system. Electrical resistivity, thermal conductivity, elastic moduli and the values of microhardness are found to be more sensitive than the internal friction to the phase changes. 

Effect of the surface chemistry on the stability and mechanical properties of the Zirconia-Hydroxyapatite bioceramic

2021 ◽  
Vol 23 ◽  
pp. 100980
Author(s):  
M. Es-saddik ◽  
S. Laasri ◽  
M. Taha ◽  
A. Laghzizil ◽  
A. Guidara ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Chemistry ◽  
The Stability

scholarly journals Studies on the Volumetric Stability and Mechanical Properties of Cement-Fly-Ash-Stabilized Steel Slag

Materials ◽  
2021 ◽  
Vol 14 (3) ◽  
pp. 495
Author(s):  
Mingkai Zhou ◽  
Xu Cheng ◽  
Xiao Chen
Keyword(s):  
Mechanical Properties ◽  
Fly Ash ◽  
Steel Slag ◽  
Critical Issue ◽  
Expansion Behavior ◽  
Strength Tests ◽  
Road Materials ◽  
Base Course ◽  
The Stability ◽  
Aggregate Base

The stability of steel-slag road materials remains a critical issue in their utilization as an aggregate base course. In this pursuit, the present study was envisaged to investigate the effects of fly ash on the mechanical properties and expansion behavior of cement-fly-ash-stabilized steel slag. Strength tests and expansion tests of the cement-fly-ash-stabilized steel slag with varying additions of fly ash were carried out. The results indicate that the cement-fly-ash-stabilized steel slag exhibited good mechanical properties. The expansion rate and the number of bulges of the stabilized material reduced with an increase in the addition. When the addition of fly ash was 30–60%, the stabilized material was not damaged due to expansion. Furthermore, the results of X-CT, XRD and SEM-EDS show that fly ash reacted with the expansive component of the steel slag. In addition, the macro structure of the stabilized material was found to be changed by an increase in the concentration of the fly ash, in order to improve the volumetric stability. Our study shows that the cement-fly-ash-stabilized steel slag exhibits good mechanical properties and volumetric stability with reasonable additions of fly ash.

scholarly journals Effect of Photoinitiator on Precursory Stability and Curing Depth of Thiol-Ene Clickable Gelatin

Polymers ◽  
2021 ◽  
Vol 13 (11) ◽  
pp. 1877
Author(s):  
Kai-Hung Yang ◽  
Gabriella Lindberg ◽  
Bram Soliman ◽  
Khoon Lim ◽  
Tim Woodfield ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Visible Light ◽  
Rheological Properties ◽  
Swelling Ratio ◽  
Sodium Persulfate ◽  
Photo Polymerization ◽  
Gelation Kinetics ◽  
The Stability ◽  
Over Time

Recent advances highlight the potential of photopolymerizable allylated gelatin (GelAGE) as a versatile hydrogel with highly tailorable properties. It is, however, unknown how different photoinitiating system affects the stability, gelation kinetics and curing depth of GelAGE. In this study, sol fraction, mass swelling ratio, mechanical properties, rheological properties, and curing depth were evaluated as a function of time with three photo-initiating systems: Irgacure 2959 (Ig2959; 320–500 nm), lithium phenyl-2,4,6-trimethylbenzoylphosphinate (LAP; 320–500 nm), and ruthenium/sodium persulfate (Ru/SPS; 400–500 nm). Results demonstrated that GelAGE precursory solutions mixed with either Ig2959 or LAP remained stable over time while the Ru/SPS system enabled the onset of controllable redox polymerization without irradiation during pre-incubation. Photo-polymerization using the Ru/SPS system was significantly faster (<5 s) compared to both Ig2959 (70 s) and LAP (50 s). Plus, The Ru/SPS system was capable of polymerizing a thick construct (8.88 ± 0.94 mm), while Ig2959 (1.62 ± 0.49 mm) initiated hydrogels displayed poor penetration depth with LAP (7.38 ± 2.13 mm) in between. These results thus support the use of the visible light based Ru/SPS photo-initiator for constructs requiring rapid gelation and a good curing depth while Ig2959 or LAP can be applied for photo-polymerization of GelAGE materials requiring long-term incubation prior to application if UV is not a concern.

scholarly journals Effect of Elevated Temperature on Mechanical Properties of High-Volume Fly Ash-Based Geopolymer Concrete, Mortar and Paste Cured at Room Temperature

Polymers ◽  
2021 ◽  
Vol 13 (9) ◽  
pp. 1473
Author(s):  
Jun Zhao ◽  
Kang Wang ◽  
Shuaibin Wang ◽  
Zike Wang ◽  
Zhaohui Yang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Elevated Temperature ◽  
Fly Ash ◽  
Residual Strength ◽  
Elevated Temperatures ◽  
High Volume ◽  
Sem Analysis ◽  
Geopolymer Concrete ◽  
Ordinary Concrete ◽  
Exposure Temperature

This paper presents results from experimental work on mechanical properties of geopolymer concrete, mortar and paste prepared using fly ash and blended slag. Compressive strength, splitting tensile strength and flexural strength tests were conducted on large sets of geopolymer and ordinary concrete, mortar and paste after exposure to elevated temperatures. From Thermogravimetric analyzer (TGA), X-ray diffraction (XRD), Scanning electron microscope (SEM) test results, the geopolymer exhibits excellent resistance to elevated temperature. Compressive strengths of C30, C40 and C50 geopolymer concrete, mortar and paste show incremental improvement then followed by a gradual reduction, and finally reach a relatively consistent value with an increase in exposure temperature. The higher slag content in the geopolymer reduces residual strength and the lower exposure temperature corresponding to peak residual strength. Resistance to elevated temperature of C40 geopolymer concrete, mortar and paste is better than that of ordinary concrete, mortar and paste at the same grade. XRD, TGA and SEM analysis suggests that the heat resistance of C–S–H produced using slag is lower than that of sulphoaluminate gel (quartz and mullite, etc.) produced using fly ash. This facilitates degradation of C30, C40 and C50 geopolymer after exposure to elevated temperatures.

scholarly journals The Effect of Long-Term Impact of Elevated Temperature on Changes in Microstructure and Mechanical Properties of HR3C Steel

2016 ◽  
Vol 61 (2) ◽  
pp. 761-766 ◽  
Author(s):  
A. Zieliński ◽  
M. Sroka ◽  
A. Hernas ◽  
M. Kremzer
Keyword(s):  
Mechanical Properties ◽  
Elevated Temperature ◽  
X Ray ◽  
Qualitative And Quantitative ◽  
Microstructure And Mechanical Properties ◽  
Transmission Electron ◽  
Quantitative Identification ◽  
Working Parameters ◽  
Long Term Impact

Abstract The HR3C is a new steel for pressure components used in the construction of boilers with supercritical working parameters. In the HR3C steel, due to adding Nb and N, the compounds such as MX, CrNbN and M23C6 precipitate during service at elevated temperature, resulting in changes in mechanical properties. This paper presents the results of microstructure investigations after ageing at 650, 700 and 750 °C for 5,000 h. The microstructure investigations were carried out using scanning and transmission electron microscopy. The qualitative and quantitative identification of the existing precipitates was carried out using X-ray analysis of phase composition. The effect elevated temperature on microstructure and mechanical properties of the examined steel was described.

Sign in / Sign up

Export Citation Format

Share Document