Corrosion behavior of steel bar embedded in high-ductility cementitious composites under the coupled action of dry–wet cycles and chloride attack

2021 ◽  
Vol ahead-of-print (ahead-of-print) ◽  
Author(s):  
Li-Ping Guo ◽  
Li-Juan Chai ◽  
Yan-Hui Xu ◽  
Cong Ding ◽  
Yuan-Zhang Cao
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Steel Corrosion ◽  
High Ductility ◽  
Chloride Permeability ◽  
Content Type ◽  
Steel Bar ◽  
Chloride Attack ◽  
Structure Engineering

Purpose High-ductility cementitious composites (HDCC) have an excellent crack controlled capacity and corrosion resistance capacity, which has a promising application in structure engineering under harsh environment. The purpose of this study is to explore the corrosion mechanism of steel bar in HDCC. Design/methodology/approach Intact and the pre-cracked HDCC specimens under the coupled action of different dry–wet cycles and chloride attack were designed, and intact normal concrete (NC) was also considered for comparison. Corrosion behavior of a steel bar embedded in HDCC was analyzed by an electrochemical method, a chloride permeability test and X-ray computed tomography. Findings Steel corrosion probability is related to the chloride permeability of the HDCC cover, and the chloride permeability resistance of HDCC is better than that of NC. Besides, crack is the key factor affecting the corrosion of steel bars, and the HDCC with narrower cracks have a lower corrosion rate. Slight pitting occurs at the crack tips. In addition, the self-healing products and corrosion products fill up the cracks in HDCC, preventing the external aggressive ions from entering and thereby decreasing the steel corrosion rate. Originality/value HDCC has a superior corrosion resistance than that of NC, effects of variable crack width on corrosion behavior of steel bar in HDCC under the coupled actions of different dry–wet cycles and chloride attack are investigated, which can provide the guide for the design application of HDCC material in structure engineering exposed to marine environment.

Evaluation of the corrosion behavior of AZ31 magnesium alloy with different protein concentrations

2021 ◽  
Vol ahead-of-print (ahead-of-print) ◽  
Author(s):  
Yucong Ma ◽  
Mohd Talha ◽  
Qi Wang ◽  
Zhonghui Li ◽  
Yuanhua Lin
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Behavior ◽  
Electrochemical Impedance ◽  
Surface Film ◽  
Energy Dispersive Spectrometer ◽  
Inhibitory Effect ◽  
Corrosion Process ◽  
High Concentration ◽  
Content Type ◽  
Atomic Force

Purpose The purpose of this paper is to study systematically the corrosion behavior of AZ31 magnesium (Mg) alloy with different concentrations of bovine serum albumin (BSA) (0, 0.5, 1.0, 1.5, 2.0 and 5.0 g/L). Design/methodology/approach Electrochemical impedance spectroscopy and potential dynamic polarization tests were performed to obtain corrosion parameters. Scanning electrochemical microscopy (SECM) was used to analyze the local electrochemical activity of the surface film. Atomic force microscope (AFM), Scanning electron microscope-Energy dispersive spectrometer and Fourier transform infrared spectroscopy were used to determine the surface morphology and chemical composition of the surface film. Findings Experimental results showed the presence of BSA in a certain concentration range (0 to 2.0 g/L) has a greater inhibitory effect on the corrosion of AZ31, however, the presence of high-concentration BSA (5.0 g/L) would sharply reduce the corrosion resistance. Originality/value When the concentration of BSA is less than 2.0 g/L, the corrosion resistance of AZ31 enhances with the concentration. The adsorption BSA layer will come into being a physical barrier to inhibit the corrosion process. However, high-concentration BSA (5.0 g/L) will chelate with dissolved metal ions (such as Mg and Ni) to form soluble complexes, which increases the roughness of the surface and accelerates the corrosion process.

Effect of electrolysis parameters on corrosion resistance of extra-low carbon high silicon iron-based alloy

2021 ◽  
Vol ahead-of-print (ahead-of-print) ◽  
Author(s):  
Yue Zhang ◽  
Jun Xiao ◽  
Shaoguang Yang ◽  
Aimin Zhao
Keyword(s):  
Corrosion Resistance ◽  
Correlation Analysis ◽  
Corrosion Rate ◽  
Low Carbon ◽  
Silicon Iron ◽  
Content Type ◽  
Grey Correlation ◽  
Grey Correlation Analysis ◽  
Iron Based ◽  
High Silicon

Purpose High silicon iron-based alloys possess excellent corrosion resistance in certain specific media, but the effects of electrolysis parameters on corrosion resistance remain unknown. This study aims to guide the development and application of an extra-low carbon high silicon iron-based alloy (ECHSIA) in electrode plates. Design/methodology/approach The corrosion resistance of ECHSIA and a conventional high-silicon cast iron (CHSCI) was analyzed through experimental characterizations. The morphology was observed by scanning electron microscopy. The influence of electrolysis parameters on the corrosion resistance of ECHSIA was investigated through corrosion experiments. The relationship between the electrolysis parameters and the corrosion resistance of ECHSIA was statistically investigated using the grey correlation analysis method. Findings The corrosion resistance of the ECHSIA is better than that of the CHSCI. The corrosion rate showed an increasing tendency with the increase in the nitric acid concentration (CHNO3), electrolyte temperature and current density. The grey correlation analysis results showed that the CHNO3 was the main factor affecting the corrosion rate of the ECHSIA. Originality/value An ECHSIA with a single ferrite microstructure was prepared. This study provides a guideline for the future development and application of ECHSIAs as electrode plates.

Investigation of mechanical and corrosion behavior of laser hybrid weld joint of 2205 duplex stainless steel

2021 ◽  
Vol ahead-of-print (ahead-of-print) ◽  
Author(s):  
Chuanbo Zheng ◽  
Cheng Zhang ◽  
Xiao Yong Wang ◽  
Jie Gu
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
Duplex Stainless Steel ◽  
Base Metal ◽  
Corrosion Behavior ◽  
Welded Joints ◽  
Two Phase ◽  
Content Type ◽  
2205 Duplex Stainless Steel ◽  
Laser Hybrid

Purpose Duplex stainless steel is composed of equal amounts of austenite and ferrite, which has excellent corrosion resistance and strength. However, after the metal was welded, the ratio of austenite and ferrite in the joint is unbalanced, and secondary phase precipitates are produced, which is also an important cause of pitting corrosion in the joint. Design/methodology/approach This paper aims to study the mechanical and corrosion behavior of welded joints, by adjusting the welding parameters of laser hybrid welding, dual heat sources are used to weld 2205 duplex stainless steel. The two-phase content of different parts of the welded joint is measured to study the influence of the ratio of the two-phase on the mechanical and corrosion properties of the joint. Findings The ratio of austenite and ferrite in different welded joints has an obvious difference, and from top to bottom, the austenite content decreased gradually, and the ferrite content increased gradually. The harmful phases are precipitated in the middle and lower part of the joint. The strength of welded joints is slightly lower than that of base metal. At the same time, the fracture analysis shows that some ferrite phases are affected by the precipitate in the grain and produce quasi-cleavage fracture. The corrosion results show that the corrosion resistance of the welded joints is lower than that of the base metal, and the concentration of chloride ions affects the corrosion resistance. Originality/value In this paper, the authors use the influence of different welding processes on the two-phase ratio of the joint to further study the influence of the microstructure on the corrosion resistance and mechanical properties of the weld.

scholarly journals The Corrosion Behavior of Sputter-Deposited Nanocrystalline W-Cr Alloys in Nacl and NaohaSolutions

1970 ◽  
Vol 25 ◽  
pp. 53-61
Author(s):  
Minu Basnet ◽  
Jagadeesh Bhattarai
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Chromium Content ◽  
Open Circuit ◽  
Nacl Solution ◽  
Corrosion Rates ◽  
Naoh Solution ◽  
Order Of Magnitude ◽  
Sputter Deposited

The corrosion behavior of the sputter-deposited nanocrystalline W-Cr alloys wasstudied in 0.5 M NaCl and alkaline 1 M NaOH solutions at 25°C, open to air usingimmersion tests and electrochemical measurements. Chromium metal acts synergisticallywith tungsten in enhancing the corrosion resistance of the sputter-deposited W-Cr alloys soas to show higher corrosion resistance than those of alloy-constituting elements in both 0.5M NaCl and 1 M NaOH solutions. In particular, the nanocrystalline W-Cr alloys containing25-91 at% chromium showed about one order of magnitude lower corrosion rates (that is,about 1-2 × 10-3 mm.y-1) than those of tungsten and chromium metals even for prolongedimmersion in 0.5 M NaCl solution at 25°C. On the other hand, the corrosion rate of thesputter-deposited W-Cr alloys containing 25-75 at % chromium was decreased significantlywith increasing chromium content and showed lowest corrosion rates (that is, 1.5-2.0 × 10-3 mm.y-1) after immersed for prolonged immersion in 1 M NaOH solution. The corrosion ratesof these nanocrystalline W-(25-75)Cr alloys are nearly two orders of magnitude lower thanthat of tungsten and more than one order of magnitude lower corrosion rate than that ofsputter-deposited chromium metal in 1 M NaOH solution. The corrosion-resistant of all theexamined sputter-deposited W-Cr alloys in 0.5 M NaCl solution is higher than in alkaline 1M NaOH solution at 25°C. Open circuit potentials of all the examined W-Cr alloys areshifted to more noble direction with increasing the chromium content in the alloys afterimmersion for 72 h in both 0.5 M NaCl and 1 M NaOH solutions at 25°C, open to air.Keywords: Sputter deposition, nanocrystalline W-Cr alloys, corrosion test, electrochemicalmeasurement, NaCl and NaOH solutions.DOI:  10.3126/jncs.v25i0.3300Journal of Nepal Chemical Society Volume 25, 2010 pp 53-61

The Influence of Sn Addition on the Corrosion Behavior of Mg-5Al-1Zn Alloy

2009 ◽  
Vol 620-622 ◽  
pp. 153-156 ◽  
Author(s):  
Kyung Chul Park ◽  
Byung Ho Kim ◽  
Jong Jin Jeon ◽  
Yong Ho Park ◽  
Ik Min Park
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Volume Fraction ◽  
Secondary Phases ◽  
Nacl Solution ◽  
High Hydrogen ◽  
Hydrogen Overvoltage ◽  
Mg2sn Phase ◽  
Superior Corrosion Resistance

In the present work, the effect of Sn addition on the corrosion behavior of Mg–5Al–1Zn alloys was investigated. Microstructure, potentiodynamic polarization and immersion tests were carried out in 3.5% NaCl solution of pH 7.2 to estimate the corrosion behavior of AZ51 alloys with and without Sn addition. Mg17Al12 and Mg2Sn phases were mainly precipitated in inter-dendrite structures. With increasing the Sn content, the volume fraction of the Mg2Sn phase was increased and coarsening tendency was observed. The corrosion resistance was increased by Sn addition. Especially, the AZ51-5wt.%Sn alloy characterized the superior corrosion resistance among the four alloys. The Sn is known for a high hydrogen overvoltage and the secondary phases effectively formed the network structure, resulting in a drastically decreasing corrosion rate of AZ51 alloy.

Effects of potassium silicate on corrosion behavior of dacromet coating

2019 ◽  
Vol 66 (6) ◽  
pp. 819-826
Author(s):  
Khashayar Tabi ◽  
Mansour Farzam ◽  
Davood Zaarei
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Behavior ◽  
Automobile Industry ◽  
Electrochemical Impedance ◽  
Salt Spray ◽  
Corrosion Current ◽  
Potassium Silicate ◽  
Coated Steel ◽  
Content Type ◽  
New Information

Purpose Potassium silicate sealer was applied on solvent-cleaned, acid-pickled, dacromet-coated steel to improve its corrosion resistance. The purpose of this paper is to study the corrosion behavior of dacromet-coated steel. Design/methodology/approach Potassium silicate sealer was applied on solvent-cleaned, acid-pickled, dacromet-coated steel to improve its corrosion resistance. Electrochemical impedance spectroscopy (EIS), potentiodynamic polarization, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and salt spray were carried out. SEM was used to study the morphological appearance of the surface. Findings The EIS behavior indicated that solvent-cleaned dacromet-coated steel sealed with potassium silicate showed that the corrosion current density was 2.664E − 5 A.cm2 which was reduced to 8.752E − 6 A.cm2 and the corrosion rate, which was 2.264E − 2 mm.year−1, was reduced to 7.438E − 3 mm.year−1 in NaCl 3.5 wt.per cent. EIS was used in NaCl 3.5 wt.%, and the Bode plot characteristics showed that the corrosion protection of solvent-cleaned, dacromet-coated steel was enhanced when sealed with potassium silicate. The EDS results of salt-sprayed, solvent-cleaned samples after 10 days indicated that the main corrosion products are composed of SiO2, ZnO and Al2O3. Research limitations/implications The detection of Li element in EDS was not possible because of the device limitation. Originality/value The current paper provides new information about the sealing properties of potassium silicate and its effects on the corrosion resistance of dacromet coating, which is widely used in many industries such as the automobile industry.

Influences of Zinc Content and Solution Heat Treatment on Microstructure and Corrosion Behavior of Mg-Zn Binary Alloys

CORROSION ◽  
10.5006/3672 ◽  
2020 ◽  
Author(s):  
Dinh Pham ◽  
Sachiko Hiromoto ◽  
Equo Kobayashi
Keyword(s):  
Heat Treatment ◽  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Volume Fraction ◽  
Galvanic Corrosion ◽  
Zinc Content ◽  
Eutectic Cell ◽  
Zn Content ◽  
Cast Alloys

The influences of Zn content and heat treatment on microstructure and corrosion behavior of Mg-xZn (x=1, 3, 5 and 7 wt.%) alloys were studied. (α-Mg + MgZn) eutectic cells and Zn-segregated regions were formed in the as-cast alloys. The Zn-rich phases acted as micro-cathodes in galvanic corrosion. Volume fraction of the Zn-rich phases increased with Zn content of the as-cast alloys, leading to a decrease in corrosion resistance. The corrosion rate of the as-cast alloys increased by 4 times with an increase of the volume fraction of eutectic cell from 0.07 vol.% of Mg-1Zn alloy to 2.18 vol.% of Mg-5Zn alloy. The corrosion rate of Mg-7Zn alloy with 2.87 vol% eutectic cells was 2 times higher than that of Mg-5Zn alloy. The Zn-rich phases dissolved by the T4 treatment and only the T4-treated Mg-7Zn alloy obviously showed eutectic cells of 1.73 vol.%. The polarization resistance (Rp) of the T4-treated Mg-1, 3 and 5Zn alloys was 2-10 times higher than that of the as-cast alloys. The T4-treated Mg-7Zn showed similar Rp to the as-cast Mg-5Zn alloy. Consequently, the volume fraction of Zn-rich phases dominated the corrosion resistance of Mg-xZn alloys.

scholarly journals Effect of Minor Alloying Elements on the Corrosion Behavior of Fe40Al in NaCl-KCl Molten Salts

2012 ◽  
Vol 2012 ◽  
pp. 1-7 ◽  
Author(s):  
G. Salinas ◽  
J. G. Gonzalez-Rodriguez ◽  
J. Porcayo-Calderon ◽  
V. M. Salinas-Bravo ◽  
M. A. Espinoza-Medina
Keyword(s):  
Weight Loss ◽  
Stainless Steel ◽  
Corrosion Resistance ◽  
Corrosion Rate ◽  
Corrosion Behavior ◽  
Molten Salts ◽  
Electrochemical Techniques ◽  
The Other ◽  
Type Stainless Steel ◽  
Waste Gasification

The hot corrosion behavior of Fe40Al intermetallic alloyed with Ag, Cu, Li, and Ni (1–5 at.%) in NaCl-KCl (1 : 1 M) at 670°C, typical of waste gasification environments, has been evaluated by using polarization curves and weight loss techniques and compared with a 304-type stainless steel. Both gravimetric and electrochemical techniques showed that all different Fe40Al-base alloys have a much higher corrosion resistance than that for stainless steel. Among the different Fe40Al-based alloys, the corrosion rate was very similar among each other, but it was evident that the addition of Li decreased their corrosion rate whereas all the other elements increased it. Results have been explained in terms of the formation and stability of an external, protective Al2O3layer.

Effect of high temperature compression deformation strain rate on the microstructure and corrosion behavior of 2205 duplex stainless steel

2015 ◽  
Vol 62 (3) ◽  
pp. 163-171 ◽  
Author(s):  
Yinhui Yang ◽  
Biao Yan
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
High Temperature ◽  
Strain Rate ◽  
Duplex Stainless Steel ◽  
Corrosion Behavior ◽  
Potentiodynamic Polarization ◽  
Phase Interface ◽  
Content Type ◽  
2205 Duplex Stainless Steel

Purpose – The aim of this paper was to investigate the effect of strain rate on microstructure and corrosion behavior of 2205 duplex stainless steel, after high-temperature compression tests. Design/methodology/approach – The specimens were prepared using a Gleeble3800 thermo-simulation machine over a range of temperatures from 850 to 1,250°C and strain rates from 0.005 to 5 s−1, and the corresponding flow curves and deformation microstructure obtained were further analyzed. To evaluate the effect of strain rate on corrosion behavior, potentiodynamic polarization tests and double-loop electrochemical potentiodynamic reactivation (DL-EPR) were used to characterize the electrochemical performance. Findings – Compared with strain rate of 0.5 s−1, the worst corrosion resistance behavior from the potentiodynamic polarization test results after deformation at 0.005 s−1 was attributed to more austenite (γ) and ferrite (δ) grain boundaries or δ/γ phase interface formation due to the better effect of γ dynamic recrystallization (DRX) or δ dynamic recovery (DRV). Increasing strain rate to 5 s−1 lowered the corrosion resistance, due to the increase in dislocation density. At the low strain rate of 0.005 s−1, the susceptibility to intergranular corrosion (IGC) was comparatively high after deformation at 1050 and 1150°C with more γ/γ grains and δ/γ phase boundary formation, which was lowered with the strain rate increase to 0.5 s−1, due to suppressing effect of γ DRX. Originality/value – The paper provides the scientific basis for the practical application of hot working of 2205 duplex stainless steel.

The combined erosion and corrosion resistance of WC-Ni vacuum brazed coating

2017 ◽  
Vol 64 (6) ◽  
pp. 626-633 ◽  
Author(s):  
Hyung Goun Joo ◽  
Kang Yong Lee ◽  
Guo Ming Luo ◽  
Da Quan Zhang
Keyword(s):  
Corrosion Resistance ◽  
Corrosion Behavior ◽  
Coating Layer ◽  
Diffusion Coating ◽  
Test Time ◽  
Content Type ◽  
X Ray ◽  
Combined Test ◽  
Material Erosion ◽  
Corrosion Behaviors

Purpose The purpose of this paper is to investigate the combined erosion and corrosion behavior of WC-Ni vacuum brazed coating. Design/methodology/approach Al2O3 particles and 10 wt% NaCl solution are used to evaluate erosion and corrosion resistance of WC-Ni vacuum brazed coating. Combined test of erosion and corrosion is also conducted. The microstructure of each specimen is characterized by the scanning electron microscopy. The chemical composition was determined by energy-dispersive X-ray spectroscopy. Findings WC-Ni vacuum brazed coating layer is effective protective coating under combined erosion and corrosion environment. The weight loss of coating layer is more reduced as the cumulative test time. Originality/value WC-Ni vacuum brazed coatings are investigated to check characteristic of the combined erosion and corrosion environment. WC-Ni vacuum brazed coatings are kind of diffusion coating that attract attention because of the resistance of superb impact and corrosion in comparison with other coatings. Some previous researches reported the properties of vacuum brazed WC material. Erosion and corrosion behaviors of WC-Ni vacuum brazed coatings were studied in our previous research, respectively. Hence, in this research, the principal objective is to examine the combined erosion and corrosion behavior of WC-Ni vacuum brazed coating.

Sign in / Sign up

Export Citation Format

Share Document