scholarly journals Strain-controlled bulge test

2008 ◽  
Vol 23 (12) ◽  
pp. 3295-3302 ◽  
Author(s):  
B. Erdem Alaca ◽  
K. Bugra Toga ◽  
Orhan Akar ◽  
Tayfun Akin
Keyword(s):  
Strain Rate ◽  
Rate Control ◽  
Closed Loop ◽  
Temporal Evolution ◽  
Constant Strain Rate ◽  
Rate Sensitivity ◽  
Bulge Test ◽  
Strain Rates ◽  
Strain Formulation ◽  
Control Criterion

A closed-loop approach is adopted to implement strain rate control during the bulge test. Due to the difficulty of measuring strains directly, the technique is based on the conversion of displacement measurements to the corresponding strains using the plane-strain formulation. The necessary temporal evolution of the midpoint displacement of a rectangular diaphragm is derived under the condition of constant strain rate and is imposed as a control criterion. The technique is demonstrated on 500-nm-thick Au diaphragms by applying strain rates ranging from 2 × 10−6 to 2 × 10−4 s–1. By measuring the corresponding yield strength values, a strain rate sensitivity of 0.11 is obtained, which is close to what was previously reported on similar specimens using the microbending test.

The Effect of Strain Rate and Temperature on Yielding in Steels

1972 ◽  
Vol 94 (1) ◽  
pp. 207-212 ◽  
Author(s):  
D. P. Kendall
Keyword(s):  
Yield Strength ◽  
Mild Steel ◽  
Strain Rate ◽  
Maraging Steel ◽  
Elastic Strain ◽  
Constant Strain Rate ◽  
Rate Sensitivity ◽  
Strain Rates ◽  
Aging Effects ◽  
Increasing Temperature

The effect of elastic strain rates ranging from 10−14 to 10 sec−1 and temperatures ranging from 200 K (−100 F) to 590 K (600 F) on the yield strength of several steels is reported. The steels utilized are a 1018 mild steel, 4340 steel, H-11 tool steel, and 300 grade maraging steel. The results are interpreted in terms of the Cottrell-Bilby yielding model based on release of dislocations from locking carbon atmospheres. The results for all of the materials except the maraging steel are consistent with this model if it is modified to account for relocking of dislocations by migration of carbon atoms. The maraging steel shows a constant strain rate sensitivity at a constant temperature, over the range of strain rates investigated. This rate sensitivity decreases with increasing temperature and at 590 K (600 F) a decreasing strength with increasing strain rate is found. This is attributed to stress aging effects.

Enhanced Plasticity of WE54/SiC Composite Prepared by Powder Metallurgy

2011 ◽  
Vol 465 ◽  
pp. 419-422 ◽  
Author(s):  
Zoltán Száraz ◽  
Zuzanka Trojanová
Keyword(s):  
Powder Metallurgy ◽  
Strain Rate ◽  
Elevated Temperatures ◽  
High Strain ◽  
Constant Strain Rate ◽  
Rate Sensitivity ◽  
Tensile Tests ◽  
Strain Rates ◽  
Deformation Characteristics ◽  
Powder Metallurgy Technique

The deformation characteristics of the WE54 magnesium alloy reinforced by 13% of SiC particles have been investigated in tension at elevated temperatures. Composite material was prepared by powder metallurgy technique. The strain rate sensitivity parameter m has been estimated by the abrupt strain rate changes (SRC) method. SRC tests and tensile tests with constant strain rate ( ) were performed at temperatures from 350 to 500 °C. Increased ductility has been found at high strain rates. The corresponding m value was 0.3. The activation energy Q has been estimated. Microstructure evolution has been observed by the light microscope and scanning electron microscope.

scholarly journals Effects of Cu Addition on Mechanical Behaviour, Microstructural Evolution and Anti-Corrosion Performance of TiAl-Based Intermetallic Alloy under Different Strain Rates

Materials ◽  
2021 ◽  
Vol 14 (17) ◽  
pp. 5056
Author(s):  
Cheng-Hsien Kuo ◽  
Tao-Hsing Chen ◽  
Ting-Yang Zeng
Keyword(s):  
Flow Stress ◽  
Strain Rate ◽  
Fracture Strain ◽  
Split Hopkinson Pressure Bar ◽  
Constant Strain Rate ◽  
Rate Sensitivity ◽  
Strain Rates ◽  
Phase Content ◽  
Corrosion Performance ◽  
Hopkinson Pressure Bar

TiAl-based intermetallic alloys are prepared with Cu concentrations of 3–5 at.% (atomic ratio). The mechanical properties and microstructural characteristics of the alloys are investigated under static and dynamic loading conditions using a material testing system (MTS) and split-Hopkinson Pressure Bar (SHPB), respectively. The electrochemical properties of the various alloys are then tested in Ringer’s solution. It is shown that the level of Cu addition significantly affects both the flow stress and the ductility of the samples. For Cu contents of 3 and 4 at.%, respectively, the flow stress and strain rate sensitivity increase at higher strain rates. Furthermore, for a constant strain rate, a Cu content of 4 at.% leads to an increased fracture strain. However, for the sample with the highest Cu addition of 5 at.%, the flow stress and fracture strain both decrease. The X-ray diffraction (XRD) patterns and optical microscopy (OM) images reveal that the lower ductility is due to the formation of a greater quantity of γ phase in the binary TiAl alloy system. Among all the specimens, that with a Cu addition of 4 at.% has the best anti-corrosion performance. Overall, the results indicate that the favourable properties of the TiAlCu4 sample stem mainly from the low γ phase content of the microstructure and the high α2 phase content.

The effects of strain and strain rate on residual microstructures in copper

1986 ◽  
Vol 44 ◽  
pp. 420-421
Author(s):  
M. F. Stevens ◽  
P. S. Follansbee
Keyword(s):  
Strain Rate ◽  
Applied Stress ◽  
Threshold Stress ◽  
Rate Sensitivity ◽  
Viscous Drag ◽  
Strain Rates ◽  
Strain And Strain Rate ◽  
Threshold Strength ◽  
Mechanism Transition ◽  
Intrinsic Strength

The strain rate sensitivity of a variety of materials is known to increase rapidly at strain rates exceeding ∼103 sec-1. This transition has most often in the past been attributed to a transition from thermally activated guide to viscous drag control. An important condition for imposition of dislocation drag effects is that the applied stress, σ, must be on the order of or greater than the threshold stress, which is the flow stress at OK. From Fig. 1, it can be seen for OFE Cu that the ratio of the applied stress to threshold stress remains constant even at strain rates as high as 104 sec-1 suggesting that there is not a mechanism transition but that the intrinsic strength is increasing, since the threshold strength is a mechanical measure of intrinsic strength. These measurements were made at constant strain levels of 0.2, wnich is not a guarantee of constant microstructure. The increase in threshold stress at higher strain rates is a strong indication that the microstructural evolution is a function of strain rate and that the dependence becomes stronger at high strain rates.

Local Investigations of the Mechanical Properties of Ultrafine Grained Metals by Nanoindentations

2006 ◽  
Vol 503-504 ◽  
pp. 31-36 ◽  
Author(s):  
Johannes Mueller ◽  
Karsten Durst ◽  
Dorothea Amberger ◽  
Matthias Göken
Keyword(s):  
Mechanical Properties ◽  
Strain Rate ◽  
Strain Rate Sensitivity ◽  
Room Temperature ◽  
Rate Sensitivity ◽  
Strain Rates ◽  
Fcc Metals ◽  
Angular Pressing ◽  
Ultrafine Grained ◽  
Indentation Strain

The mechanical properties of ultrafine-grained metals processed by equal channel angular pressing is investigated by nanoindentations in comparison with measurements on nanocrystalline nickel with a grain size between 20 and 400 nm produced by pulsed electrodeposition. Besides hardness and Young’s modulus measurements, the nanoindentation method allows also controlled experiments on the strain rate sensitivity, which are discussed in detail in this paper. Nanoindentation measurements can be performed at indentation strain rates between 10-3 s-1 and 0.1 s-1. Nanocrystalline and ultrafine-grained fcc metals as Al and Ni show a significant strain rate sensitivity at room temperature in comparison with conventional grain sized materials. In ultrafine-grained bcc Fe the strain rate sensitivity does not change significantly after severe plastic deformation. Inelastic effects are found during repeated unloading-loading experiments in nanoindentations.

The Effects of Physical Ageing and of Prior Immersion on the Esc Behaviour of Polycarbonate in Ethanol

1993 ◽  
Vol 305 ◽  
Author(s):  
J. C. Arnold ◽  
A. R. Eccott
Keyword(s):  
Strain Rate ◽  
Immersion Time ◽  
Constant Strain Rate ◽  
Tensile Tests ◽  
Strain Rates ◽  
Physical Ageing ◽  
Diffusion Effects ◽  
Craze Initiation ◽  
Comparison Of Tests

AbstractThe effects of physical ageing and prior immersion time on the ESC behaviour of polycarbonate in ethanol were studied. Constant strain rate tensile tests were performed at a range of strain rates for samples with ageing times varying from 100 hours to 3000 hours and for prior immersion times of between 1 hour and 500 hours. Comparison of tests performed in ethanol and in air gave a good indication of the point of craze initiation. The results showed that there was a reduction in strain to crazing as the strain rate decreased, apart from with the lowest strain rate used. A longer prior immersion time also promoted craze formation. Both of these results are attributable to diffusion effects. Physical ageing had little effect on the ESC behaviour, due to the large amounts of deformation encountered in this system.

Strain-Rate Effect on the Tensile Behaviour of High Strength Alloys

2011 ◽  
Vol 82 ◽  
pp. 124-129 ◽  
Author(s):  
Ezio Cadoni ◽  
Matteo Dotta ◽  
Daniele Forni ◽  
Stefano Bianchi
Keyword(s):  
Strain Rate ◽  
Rate Sensitivity ◽  
High Strength ◽  
Constitutive Law ◽  
Tensile Behaviour ◽  
Strain Rates ◽  
Cross Sectional ◽  
Split Hopkinson Tensile Bar ◽  
Wide Range ◽  
First Results

In this paper the first results of the mechanical characterization in tension of two high strength alloys in a wide range of strain rates are presented. Different experimental techniques were used for different strain rates: a universal machine, a Hydro-Pneumatic Machine and a JRC-Split Hopkinson Tensile Bar. The experimental research was developed in the DynaMat laboratory of the University of Applied Sciences of Southern Switzerland. An increase of the stress at a given strain increasing the strain-rate from 10-3 to 103 s-1, a moderate strain-rate sensitivity of the uniform and fracture strain, a poor reduction of the cross-sectional area at fracture with increasing the strain-rate were shown. Based on these experimental results the parameters required by the Johnson-Cook constitutive law were determined.

scholarly journals Study on the dynamic properties of AM-SLM AlSi10Mg alloy using the Split Hopkinson Pressure Bar (SHPB) technique

2018 ◽  
Vol 183 ◽  
pp. 04005 ◽  
Author(s):  
Bar Nurel ◽  
Moshe Nahmany ◽  
Adin Stern ◽  
Nahum Frage ◽  
Oren Sadot
Keyword(s):  
Strain Rate ◽  
Split Hopkinson Pressure Bar ◽  
Dynamic Properties ◽  
Rate Sensitivity ◽  
Strain Rate Range ◽  
Strain Rates ◽  
Hopkinson Pressure Bar ◽  
Static Mechanical ◽  
Split Hopkinson ◽  
Pressure Bar

Additive manufacturing by Selective Laser Melting of metals is attracting substantial attention, due to its advantages, such as short-time production of customized structures. This technique is useful for building complex components using a metallic pre-alloyed powder. One of the most used materials in AMSLM is AlSi10Mg powder. Additively manufactured AlSi10Mg may be used as a structural material and it static mechanical properties were widely investigated. Properties in the strain rates of 5×102–1.6×103 s-1 and at higher strain rates of 5×103 –105 s-1 have been also reported. The aim of this study is investigation of dynamic properties in the 7×102–8×103 s-1 strain rate range, using the split Hopkinson pressure bar technique. It was found that the dynamic properties at strain-rates of 1×103–3×103 s-1 depend on a build direction and affected by heat treatment. At higher and lower strain-rates the effect of build direction is limited. The anisotropic nature of the material was determined by the ellipticity of samples after the SHPB test. No strain rate sensitivity was observed.

Tensile Stress-Strain Curves Modeling of Four Kinds of Solders with Temperature and Rate Dependence

2005 ◽  
Vol 297-300 ◽  
pp. 905-911 ◽  
Author(s):  
Xu Chen ◽  
Li Zhang ◽  
Masao Sakane ◽  
Haruo Nose
Keyword(s):  
Tensile Stress ◽  
Constitutive Model ◽  
Strain Rate ◽  
Constant Strain Rate ◽  
Tensile Tests ◽  
Strain Rate Range ◽  
Rate Dependence ◽  
Strain Rates ◽  
Stress Strain ◽  
Rate Range

A series of tensile tests at constant strain rate were conducted on tin-lead based solders with different Sn content under wide ranges of temperatures and strain rates. It was shown that the stress-strain relationships had strong temperature- and strain rate- dependence. The parameters of Anand model for four solders were determined. The four solders were 60Sn-40Pb, 40Sn-60Pb, 10Sn-90Pb and 5Sn-95Pb. Anand constitutive model was employed to simulate the stress-strain behaviors of the solders for the temperature range from 313K to 398K and the strain rate range from 0.001%sP -1 P to 2%sP -1 P. The results showed that Anand model can adequately predict the rate- and temperature- related constitutive behaviors at all test temperatures and strain rates.

scholarly journals Strain rate and thermal softening effects in shear testing of AA7075-T6 sheet

2018 ◽  
Vol 183 ◽  
pp. 02037 ◽  
Author(s):  
Taamjeed Rahmaan ◽  
Ping Zhou ◽  
Cliff Butcher ◽  
Michael J. Worswick
Keyword(s):  
Strain Rate ◽  
High Speed ◽  
Rate Sensitivity ◽  
Thermal Conditions ◽  
Shear Loading ◽  
Image Correlation ◽  
High Rate ◽  
Strain Rates ◽  
Shear Testing ◽  
Plane Shear

Shear tests were performed at strain rates ranging from quasi-static (0.01 s-1) to 500 s-1 for AA7075-T6 sheet metal alloy at room temperature. A miniature sized shear specimen was used in this work to perform high strain rate shear testing. Digital image correlation (DIC) techniques were employed to measure the strains in the experiments. At maximum in-plane shear strains greater than 20%, the AA7075-T6 alloy demonstrated a reduced work hardening rate at elevated strain rates. At lower strains, the AA7075-T6 alloy showed mild positive rate sensitivity. The strain to localization (using the Zener-Holloman criterion), measured using the DIC technique, decreased with strain rate in shear loading. The strain at complete failure, however, exhibited an increase at the highest strain rate (500 s-1). The current work also focused on characterization of the thermal conditions occurring during high rate loading in shear with in situ high speed thermal imaging. Experimental results from the highest strain rate (500 s-1) tests showed a notable increase in temperature within the specimen gauge region as a result of the conversion of plastic deformation energy into heat.

Sign in / Sign up

Export Citation Format

Share Document