scholarly journals GREEN TECHNOLOGY THROUGH POROUS CONCRETE

2019 ◽  
Vol 1 (2) ◽  
pp. 189-194
Author(s):  
Acep Hidayat ◽  
Muhammad Isradi ◽  
Joewono Prasetijo
Keyword(s):  
Compressive Strength ◽  
Environmental Pollution ◽  
Experimental Method ◽  
Test Object ◽  
Green Technology ◽  
Fine Aggregate ◽  
Test Results ◽  
Normal Concrete ◽  
Porous Concrete ◽  
Aggregate Content

This research uses stone ash waste from the stone crusher industry to preserve the environment. This material is an ingredient in making normal concrete. The use of stone ash as a substitute for sand is expected to increase the compressive strength in the planned slump and can optimize the use of rock ash waste to reduce environmental pollution that occurs. This study uses an experimental method with a total of 32 pieces of specimens. Each variation consists of 3 samples with a variety of fine aggregate levels of 40%, 44%, and 46%. The test object is a concrete cylinder with a diameter of 15 cm and a height of 30 cm. Test results for compressive strength at seven days for fine aggregate content variations of 40%: 22.25 Mpa; 44%: 24.30 Mpa; 46%: 17.08 MPa. Test results of compressive strength at the age of 14 days for variations in fine aggregate levels of 40%: 26.10 Mpa; 44%: 28.51 Mpa; 46%: 20.04 Mpa. Test results of compressive strength at the age of 21 days for fine aggregate content variations of 40%: 28.18 Mpa; 44%: 30.78 Mpa; 46%: 21.63 MPa. With these results, the Porous concrete produced can be used as preservation and maintain environmental protection. This product very cheap when compared to the original concrete, which calculated 22 U$ per square. The use of porous concrete has an impact on people's behavior that will preserve the environment, especially water content in the soil.

scholarly journals Study on Compressive Strength of Quarry Dust as Fine Aggregate in Concrete

2016 ◽  
Vol 2016 ◽  
pp. 1-5 ◽  
Author(s):  
K. Shyam Prakash ◽  
Ch. Hanumantha Rao
Keyword(s):  
Compressive Strength ◽  
Environmental Pollution ◽  
Low Cost ◽  
Experimental Investigations ◽  
Fine Aggregate ◽  
Normal Concrete ◽  
Natural Sand ◽  
Alternative Material ◽  
Quarry Dust

The concept of replacement of natural fine aggregate by quarry dust which is highlighted in the study could boost the consumption of quarry dust generated from quarries. By replacement of quarry dust, the requirement of land fill area can be reduced and can also solve the problem of natural sand scarcity. The availability of sand at low cost as a fine aggregate in concrete is not suitable and that is the reason to search for an alternative material. Quarry dust satisfies the reason behind the alternative material as a substitute for sand at very low cost. It even causes burden to dump the crusher dust at one place which causes environmental pollution. From the results of experimental investigations conducted, it is concluded that the quarry dust can be used as a replacement for fine aggregate. It is found that 40% replacement of fine aggregate by quarry dust gives maximum result in strength than normal concrete and then decreases from 50%. The compressive strength is quantified for varying percentage and grades of concrete by replacement of sand with quarry dust.

scholarly journals Fly Ash Utilization Analysis as A Substitute of Cement in Cement Treated Base (CTB)

2021 ◽  
Vol 06 (09) ◽  
Author(s):  
Utami Sylvia Lestari ◽  
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Test Object ◽  
Strength Test ◽  
Fine Aggregate ◽  
Test Results ◽  
Surface Layers ◽  
Road Pavement ◽  
Compressive Strength Test ◽  
Fly Ash Utilization

Cement Treated Base (CTB) is a pavement layer located between the sub-base and surface layers. This pavement layer uses fine aggregate (sand) and cement as a binder. Fly ash is coal burning waste that can be used as an added material for road pavement. This study aimed to analyze the use of fly ash in the cement treated base pavement mixture. Fly ash was used as a substitute of cement. The composition used consists of fine aggregate (sand), cement, fly ash and water. The compressive strength test was carried out on variations in the composition of the test object. The requirements for CTB specifications were to have compressive strength test results ranging between 45 kg/cm2 – 55 kg/cm2 at the age of the test object for 7 days. After being tested, it was found that the composition of 70% fine aggregate (sand), 5% Portland cement, and 25% fly ash had an average compressive strength of 49.823 kg/cm2.

Variasi Penambahan Sika Cim Dan Fiber Kawat Pada Beton Mutu Fc’ 30 Mpa

2018 ◽  
Vol 9 (2) ◽  
pp. 67-73
Author(s):  
M Zainul Arifin
Keyword(s):  
Tensile Strength ◽  
Compressive Strength ◽  
Curing Temperature ◽  
Test Results ◽  
Concrete Compressive Strength ◽  
Normal Concrete ◽  
Astm Method ◽  
Additive Type ◽  
Composition Variation ◽  
Compressive Strength Of Concrete

This research was conducted to determine the value of the highest compressive strength from the ratio of normal concrete to normal concrete plus additive types of Sika Cim with a composition variation of 0.25%, 0.50%, 0.75%, 1.00%, 1.25%, 1 , 50% and 1.75% of the weight of cement besides that in this study also aims to find the highest tensile strength from the ratio of normal concrete to normal concrete in the mixture of sika cim composition at the highest compressive strength above and after that added fiber wire with a size diameter of 1 mm in length 100 mm with a ratio of 1% of material weight. The concrete mix plan was calculated using the ASTM method, the matrial composition of the normal concrete mixture as follows, 314 kg / m3 cement, 789 kg / m3 sand, 1125 kg / m3 gravel and 189 liters / m3 of water at 10 cm slump, then normal concrete added variations of the composition of sika cim 0.25%, 0.50%, 0.75%, 1.00%, 1.25%, 1.5%, 1.75% by weight of cement and fiber, the tests carried out were compressive strength of concrete and tensile strength of concrete, normal maintenance is soaked in fresh water for 28 days at 30oC. From the test results it was found that the normal concrete compressive strength at the age of 28 days was fc1 30 Mpa, the variation in the addition of the sika cim additive type mineral was achieved in composition 0.75% of the cement weight of fc1 40.2 Mpa 30C. Besides that the tensile strength test results were 28 days old with the addition of 1% fiber wire mineral to the weight of the material at a curing temperature of 30oC of 7.5%.

Experimental Study on Sand and Cement Replacement by Termite Mound Soil

2019 ◽  
pp. 279-287
Author(s):  
Harish R ◽  
Ramesh S ◽  
Tharani A ◽  
Mageshkumar P
Keyword(s):  
Experimental Study ◽  
Experimental Investigation ◽  
Compressive Strength ◽  
Natural Environment ◽  
Fine Aggregate ◽  
Test Results ◽  
Termite Mound ◽  
Cement Concrete ◽  
Cement Ratio ◽  
Compressive Strength Of Concrete

This paper presents the results of an experimental investigation of the compressive strength of concrete cubes containing termite mound soil. The specimens were cast using M20 grade of concrete. Two mix ratios for replacement of sand and cement are of 1:1.7:2.7 and 1:1.5:2.5 (cement: sand: aggregate) with water- cement ratio of 0.45 and varying combination of termite mound soil in equal amount ranging from 30% and 40% replacing fine aggregate (sand) and cement from 10%,15%,20% were used. A total of 27 cubes, 18 cylinders and 6 beams were cast by replacing fine aggregate, specimens were cured in water for 7,14 and 28 days. The test results showed that the compressive strength of the concrete cubes increases with age and decreases with increasing percentage replacement of cement and increases with increasing the replacement of sand with termite mound soil cured in water. The study concluded that termite mound cement concrete is adequate to use for construction purposes in natural environment.

Utilization of Cockle Shell (Anadara Granosa) as Partial Replacement of Fine Aggregates in Concrete

2021 ◽  
Vol 6 (2) ◽  
pp. 96-103
Author(s):  
Ranno Marlany Rachman ◽  
Try Sugiyarto Soeparyanto ◽  
Edward Ngii
Keyword(s):  
Compressive Strength ◽  
National Standard ◽  
Partial Replacement ◽  
Fine Aggregate ◽  
Concrete Compressive Strength ◽  
Concrete Technology ◽  
Normal Concrete ◽  
Fine Aggregates ◽  
Blood Clam ◽  
Anadara Granosa

This research aimed to utilize Anadara Granosa (Blood clam shell) clamshell waste as a new innovation in concrete technology and to investigate the effect of Anadara Granosa clamshell powder utilization as an aggregate substitution on the concrete compressive strength. The sample size was made of cylinders with a size of 10 cm x 20 cm with variations of clamshell powder 10%, 20% and 30% from the fine aggregate volume then soaked for 28 days as per the method of the Indonesian National Standard. The evaluation results exhibited that the slump value exceeded the slump value of normal concrete with a slump value of 0% = 160 mm, 10% = 165 mm, 20% = 180 mm and 30% = 180 mm. Additionally, it was found that the concrete compressive strength obtained post 28 days were 20.78 Mpa, 21.95 Mpa, 21.17 Mpa and 24.28 Mpa for normal concrete (0%), substitution concrete (10%), substitution concrete (20%) and substitution concrete (30%), respectively. Leading on from these results, it was concluded that the increment of Anadara Granosa clamshell powder substitution led to the increase of concrete compressive strength test.

scholarly journals PENGARUH PENGGUNAAN TANAH MEDITERAN SEBAGAI BAHAN SUBSTITUSI SEMEN TERHADAP KUAT TEKAN DAN TARIK BETON

2020 ◽  
Vol 5 (2) ◽  
pp. 59-71
Author(s):  
Sri Devi Nilawardani
Keyword(s):  
Tensile Strength ◽  
Compressive Strength ◽  
Coarse Aggregate ◽  
Comparative Method ◽  
Fine Aggregate ◽  
Main Ingredient ◽  
Normal Concrete ◽  
Long Run ◽  
Cement Manufacture ◽  
Initial Idea

Title: The Effect of Using Mediteran Soil as Cement Substitution Materials in Compressive Strength and Tensile Strength of Concrete Concrete is a composite material (mixture) of cement, fine aggregate, coarse aggregate, and water. The potential of limestone in Indonesia is very large, reaching 28.678 billion tons which is the main ingredient in the cement manufacture. In the long run it will be depleted because it is a non-renewable natural resources. So to reduce the use of limestone the utilization of Mediteran soil as a substitution for some cement in the manufacture of concrete is required. The initial idea is based on the chemical composition contained in the Mediteran soil almost identical to the cement, which is carbonate (CaO) and silica (SiO2). The purpose of this research is to reveal the influence of substitution of Mediteran soil by 20% and 40% in the compressive strength and tensile of the concrete at age 3, 7, 14, and 28 days with the number of test specimen each 3 pieces on each variation in 10cm x20cm cylinder with planning of concrete mixture refers to SK SNI method T-15-1900-03. The type of research used is quantitative with the experimental method of laboratory test and data analysis of comparative method and regression. The results show that compressive strength and tensile strength of concrete using Mediteran soil substitution comparable to  the strength of normal concrete with dry treatment. In the composition of 20% Mediteran soils decreased by 51.35% or 7.9 MPa (compressive strength) and 30.60% or 0.93 MPa (tensile strength). While the composition of 40% Mediteran soil decreased by 43.78% or 9.13 MPa (compressive strength) and 2.24% or 1.31 MPa (tensile strength).  

scholarly journals Pengaruh Pemanfaatan Abu Tumbuhan Perumpung Terhadap Peningkatan Kuat Tekan Beton K300

Jurnal Tekno ◽  
2021 ◽  
Vol 18 (2) ◽  
pp. 11-20
Author(s):  
Ahmad Junaidi ◽  
R Dewo Hiraliyamaesa Hariyanto
Keyword(s):  
Compressive Strength ◽  
Test Object ◽  
Concrete Mixture ◽  
Wild Plant ◽  
Concrete Compressive Strength ◽  
Normal Concrete ◽  
Compressive Strength Of Concrete ◽  
Test Objects

Perumpung (Eulalia japonica) is a wild plant that usually grows on the banks of river. The locals consider this plant as a waste/pest, but the authors are interested in researching perumpung because they are similar to bamboo, sugarcane and other fibrous plants. In this study, the authors aims to compare the compressive strength of normal concrete with the compressive strength of concrete added with Perumpung ash at 28-days-old K-300. The study used a cube-shaped test object (15 x 15 x 15 cm) with 6 samples for each condition. The total number of test objects is 48, which consists of 8 conditions, namely normal conditions and 5%, 7.5%, 10%, 12.5%, 15%, 17.5% and 20% addition of perumpung ash by cement weight. The results obtained that the compressive strength of 28-days-old concrete under normal conditions was 316,060 kg/cm2 and the addition of 5% ash was 331.583 kg/cm2, 7.5% was 337.181 kg/cm2, 10% was 341.813 kg/cm2, 12 ,5% is 347,045 kg/cm2, 15% is 353,889 kg/cm2, 17.5% is 311,160 kg/cm2 and 20% is 298.44 kg/cm2. From the results above it can be concluded that the addition of 15% Perumpung Ash to the concrete mixture increases the maximum characteristic concrete compressive strength by 353.889 kg/cm2.

scholarly journals Studi Kuat Tekan Beton Speedcrete Dengan Zat Additive Naphthalene Berdasarkan Variasi Umur

2019 ◽  
Vol 14 (2) ◽  
Author(s):  
Syifa Fauziah ◽  
Anisah Anisah ◽  
Sittati Musalamah
Keyword(s):  
Compressive Strength ◽  
Test Object ◽  
Treatment Process ◽  
Concrete Strength ◽  
Test Machine ◽  
Water Age ◽  
Normal Concrete ◽  
Compressive Strength Of Concrete ◽  
Normal Strength ◽  
Additive Materials

This research aims to determine the maximum compressive strength value of concrete speedcrete using naphthalene additive additive at each test age and compare with normal concrete 28 days. This research used cylindrical test object with diameter 15 cm and height 30 cm. Speedcrete concrete does not undergo the treatment process while the normal concrete test object through the treatment process. Testing compressive strength of concrete speedcrete using Crushing Test Machine tool. In this research the compressive strength was produced by using superplasticizer type naphthalene and compared with normal concrete without using additive. The target quality plan is fc '35 MPa with the use of additive dose of 1.7% of the weight of cement. The results of this research showed an increase in the value of compressive strength of concrete speedcrete with aadditive materials added naphthalene increased with increasing age of concrete. The results showed that the compressive strength of concrete speedcrete with naphthalene additive materials of 12 hours, 18 hours, 28 hours and 48 hours was 0.5 MPa, 17,81 MPa, 31,14 MPa and 45,77 MPa. Normal strength concrete strength with the addition of 20% water age 28 days that is equal to 54.76 MPa.

scholarly journals PENGARUH PENAMBAHAN ABU CANGKANG BEKICOT PADA SEMEN RAMAH LINGKUNGAN TERHADAP KUAT TEKAN MORTAR

2018 ◽  
Vol 8 (2) ◽  
pp. 63-69
Author(s):  
Achendri M. Kurniawan ◽  
Devita Sulistiana
Keyword(s):  
Compressive Strength ◽  
Experimental Method ◽  
Rice Straw ◽  
Research Method ◽  
Environmental Damage ◽  
Fine Aggregate ◽  
Compressive Test ◽  
Snail Shell ◽  
Substitute Material ◽  
Straw Ash

Blitar Regency is one of the strange culinary centers, among which are processed various foods from snail base ingredients, ranging from kripik, sate oseng-oseng and so on as well as the existence of Blitar district is one of the rice barns in East Java. With the existence of Blitar district as a snail-based culinary producer and one of the rice barns in East Java, this is not spared from several problems, such as the disposal of snail shells in the river and burning of rice straw in rice fields which both will cause environmental damage. This study aims to examine the use of snail shell ash and rice straw ash as a substitute material for cement in mortar mixtures against mortar compressive strength. The research method used was the experimental method by mixing fine aggregate main ingredients with snail shell ash and rice straw ash then testing the compressive strength. The results of the compressive test with the addition of the percentage of snail shell shell turned out to increase by 54.78%.

Sign in / Sign up

Export Citation Format

Share Document