scholarly journals Development of Heavyweight Self-Compacting Concrete and Ambient-Cured Heavyweight Geopolymer Concrete Using Magnetite Aggregates

Materials ◽  
2019 ◽  
Vol 12 (7) ◽  
pp. 1035 ◽  
Author(s):  
Afsaneh Valizadeh ◽  
Farhad Aslani ◽  
Zohaib Asif ◽  
Matt Roso
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Tensile Tests ◽  
Offshore Structures ◽  
Experimental Program ◽  
Geopolymer Concrete ◽  
Self Compacting Concrete ◽  
Coarse Aggregates ◽  
Maximum Compressive Strength ◽  
Heavyweight Concrete

Heavyweight self-compacting concrete (HWSCC) and heavyweight geopolymer concrete (HWGC) are new types of concrete that integrate the advantages of heavyweight concrete (HWC) with self-compacting concrete (SCC) and geopolymer concrete (GC), respectively. The replacement of natural coarse aggregates with magnetite aggregates in control SCC and control GC at volume ratios of 50%, 75%, and 100% was considered in this study to obtain heavyweight concrete classifications, according to British standards, which provide proper protection from sources that emit harmful radiations in medical and nuclear industries and may also be used in many offshore structures. The main aim of this study is to examine the fresh and mechanical properties of both types of mixes. The experimental program investigates the fresh properties of HWSCC and HWGC through the slump flow test. However, J-ring tests were only conducted for HWSCC mixes to ensure the flow requirements in order to achieve self-compacting properties. Moreover, the mechanical properties of both type of mixes were investigated after 7 and 28 days curing at an ambient temperature. The standard 100 × 200 mm cylinders were subjected to compressive and tensile tests. Furthermore, the flexural strength were examined by testing 450 × 100 × 100 mm prisms under four-point loading. The flexural load-displacement relationship for all mixes were also investigated. The results indicated that the maximum compressive strength of 53.54 MPa was achieved by using the control SCC mix after 28 days. However, in HWGC mixes, the maximum compressive strength of 31.31 MPa was achieved by 25% magnetite replacement samples. The overall result shows the strength of HWSCC decreases by increasing magnetite aggregate proportions, while, in HWGC mixes, the compressive strength increased with 50% magnetite replacement followed by a decrease in strength by 75% and 100% magnetite replacements. The maximum densities of 2901 and 2896 kg/m3 were obtained by 100% magnetite replacements in HWSCC and HWGC, respectively.

scholarly journals Properties of Ambient-Cured Normal and Heavyweight Geopolymer Concrete Exposed to High Temperatures

Materials ◽  
2019 ◽  
Vol 12 (5) ◽  
pp. 740 ◽  
Author(s):  
Farhad Aslani ◽  
Zohaib Asif
Keyword(s):  
Mass Loss ◽  
High Temperatures ◽  
Offshore Structures ◽  
Normal Weight ◽  
Geopolymer Concrete ◽  
Coarse Aggregates ◽  
Residual Properties ◽  
New Type ◽  
Heavyweight Concrete ◽  
Underwater Structures

Ambient-cured heavyweight geopolymer concrete (HWGC) is a new type of concrete that combines the benefits of both heavyweight concrete (HWC) and geopolymer concrete (GC). HWGC provides proper protection from the sources that emit harmful radiations in medical and nuclear industries. Furthermore, HWGC may also be used in offshore structures for pipeline ballasting and similar underwater structures. In this study, heavyweight aggregates (magnetite) have been used and replaced by normal-weight coarse aggregates in GC at volume ratios of 50, 75, and 100% to attain heavyweight classification according to British standards. This study investigates the impacts of high temperatures on standard ambient-cured geopolymer concrete and ambient-cured HWGC through its residual properties regarding compressive and tensile strengths, mass loss, spalling intensity, and flexural strength. The residual properties were examined by heating 100 × 200 mm cylinder specimens to 100, 300, 600, and 900 °C. The results indicated that the maximum compressive strengths of 40.1 and 39.0 MPa were achieved by HWGC at 300 and 100 °C, respectively. The overall result shows that the strength of HWGC increases by increasing magnetite aggregate proportion, while the mass loss, intensity of spalling, and loss of strengths is proportional to temperature after a certain point. Minor spalling with holes and cracking was observed only at 900 °C in HWGC.

scholarly journals The Mechanics Properties of Self-Compacting Concrete Using Red-Tile Waste as Substitution of Fine Aggregates

2017 ◽  
Vol 23 (2) ◽  
pp. 149
Author(s):  
Crezensia Alfiora Deadema Dias Octobenita ◽  
Ade Lisantono
Keyword(s):  
Compressive Strength ◽  
Modulus Of Elasticity ◽  
Maximum Modulus ◽  
Modulus Of Rupture ◽  
Experimental Program ◽  
Self Compacting Concrete ◽  
Fine Aggregates ◽  
Maximum Compressive Strength

This paper presents the experimental program about the mechanics properties of Self-Compacting Concrete (SCC) using red-tile waste as substitution of fine aggregates. The proportion of red-tile waste substitution was 10 %; 20 %; 30; 40 %; and 50 % of fine aggregates by weight. Viscocrete-10 was used to maintain the workability and flowability of SCC. 72 cylinder specimens with the size of (150×300) mm and 18 beam specimens with the size of (100×100×500) mm were cast and tested in this study. The mechanics properties of SCC that were studied in this research were compressive strength, modulus of elasticity, and modulus of rupture. The compressive strength of SCC was tested at age 7; 14; and 28 days. While the modulus of elasticity and modulus of rupture of SCC were tested only at age 28 days. The result shows that the maximum compressive strength of SCC was obtained using red-tile waste with the proportion of 50 % as substitution of fine aggregates. The compressive strength of SCC using red-tile with the proportion of 50 % at age 7; 14; and 28 days were 64.746 MPa;, 65.564 MPa; and 71.940 MPa, respectively. While the maximum modulus of elasticity and modulus of rupture of SCC were obtained using red-tile with the proportion 50 % at age 28 days, and the modulus elasticity and modulus of rupture were 25863.192 MPa and 7.076 MPa, respectively.

scholarly journals Assessment of the Rheological and Mechanical Properties of Geopolymer Concrete Comprising Fly Ash and Fluid Catalytic Cracking Residue as Aluminosilicate Precursor

2021 ◽  
Vol 11 (7) ◽  
pp. 3032
Author(s):  
Tuan Anh Le ◽  
Sinh Hoang Le ◽  
Thuy Ninh Nguyen ◽  
Khoa Tan Nguyen
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Elastic Modulus ◽  
Fly Ash ◽  
Flexural Strength ◽  
Catalytic Cracking ◽  
Fluid Catalytic Cracking ◽  
High Alumina ◽  
Geopolymer Concrete ◽  
Sem Images

The use of fluid catalytic cracking (FCC) by-products as aluminosilicate precursors in geopolymer binders has attracted significant interest from researchers in recent years owing to their high alumina and silica contents. Introduced in this study is the use of geopolymer concrete comprising FCC residue combined with fly ash as the requisite source of aluminosilicate. Fly ash was replaced with various FCC residue contents ranging from 0–100% by mass of binder. Results from standard testing methods showed that geopolymer concrete rheological properties such as yield stress and plastic viscosity as well as mechanical properties including compressive strength, flexural strength, and elastic modulus were affected significantly by the FCC residue content. With alkali liquid to geopolymer solid ratios (AL:GS) of 0.4 and 0.5, a reduction in compressive and flexural strength was observed in the case of geopolymer concrete with increasing FCC residue content. On the contrary, geopolymer concrete with increasing FCC residue content exhibited improved strength with an AL:GS ratio of 0.65. Relationships enabling estimation of geopolymer elastic modulus based on compressive strength were investigated. Scanning electron microscope (SEM) images and X-ray diffraction (XRD) patterns revealed that the final product from the geopolymerization process consisting of FCC residue was similar to fly ash-based geopolymer concrete. These observations highlight the potential of FCC residue as an aluminosilicate source for geopolymer products.

scholarly journals Evaluation of Self-Compacting Concrete Strength with Non-Destructive Tests for Concrete Structures

2019 ◽  
Vol 9 (23) ◽  
pp. 5109 ◽  
Author(s):  
Miguel C. S. Nepomuceno ◽  
Luís F. A. Bernardo
Keyword(s):  
Compressive Strength ◽  
Concrete Strength ◽  
Surface Hardness ◽  
Pulse Velocity ◽  
Concrete Compressive Strength ◽  
Self Compacting Concrete ◽  
Coarse Aggregates ◽  
Pull Out ◽  
Concrete Maturity ◽  
Non Destructive

Self-compacting concrete (SCC) shows to have some specificities when compared to normal vibrated concrete (NVC), namely higher cement paste dosage and smaller volume of coarse aggregates. In addition, the maximum size of coarse aggregates is also reduced in SCC to prevent blocking effect. Such specificities are likely to affect the results of non-destructive tests when compared to those obtained in NVC with similar compressive strength and materials. This study evaluates the applicability of some non-destructive tests to estimate the compressive strength of SCC. Selected tests included the ultrasonic pulse velocity test (PUNDIT), the surface hardness test (Schmidt rebound hammer type N), the pull-out test (Lok-test), and the concrete maturity test (COMA-meter). Seven sets of SCC specimens were produced in the laboratory from a single mixture and subjected to standard curing. The tests were applied at different ages, namely: 1, 2, 3, 7, 14, 28, and 94 days. The concrete compressive strength ranged from 45 MPa (at 24 h) to 97 MPa (at 94 days). Correlations were established between the non-destructive test results and the concrete compressive strength. A test variability analysis was performed and the 95% confidence limits for the obtained correlations were computed. The obtained results for SCC showed good correlations between the concrete compressive strength and the non-destructive tests results, although some differences exist when compared to the correlations obtained for NVC.

Microstructure and Mechanical Properties of Ambiently-Cured Blended Coal Ash-Based Geopolymer Concrete

2016 ◽  
Vol 857 ◽  
pp. 400-404
Author(s):  
Tian Yu Xie ◽  
Togay Ozbakkaloglu
Keyword(s):  
Mechanical Properties ◽  
Experimental Study ◽  
Compressive Strength ◽  
Fly Ash ◽  
Bottom Ash ◽  
Coal Ash ◽  
Geopolymer Concrete ◽  
Mass Ratio ◽  
Blended Coal ◽  
Microstructure And Mechanical Properties

This paper presents the results of an experimental study on the behavior of fly ash-, bottom ash-, and blended fly and bottom ash-based geopolymer concrete (GPC) cured at ambient temperature. Four bathes of GPC were manufactured to investigate the influence of the fly ash-to-bottom ash mass ratio on the microstructure, compressive strength and elastic modulus of GPC. All the results indicate that the mass ratio of fly ash-to-bottom ash significantly affects the microstructure and mechanical properties of GPCs

scholarly journals Influence of Glass Fibers on Mechanical Properties of Concrete with Recycled Coarse Aggregates

2019 ◽  
Vol 5 (5) ◽  
pp. 1007-1019 ◽  
Author(s):  
Babar Ali ◽  
Liaqat Ali Qureshi ◽  
Ali Raza ◽  
Muhammad Asad Nawaz ◽  
Safi Ur Rehman ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Mechanical Performance ◽  
Volume Fraction ◽  
Glass Fibers ◽  
Construction Material ◽  
Concrete Compressive Strength ◽  
Coarse Aggregates ◽  
Highly Sensitive

Despite plain cement concrete presenting inferior performance in tension and adverse environmental impacts, it is the most widely used construction material in the world. Consumption of fibers and recycled coarse aggregates (RCA) can add ductility and sustainability to concrete. In this research, two mix series (100%NCA, and 100%RCA) were prepared using four different dosages of GF (0%GF, 0.25%GF, 0.5%GF, and 0.75%GF by volume fraction).  Mechanical properties namely compressive strength, splitting tensile strength, and flexural strength of each concrete mixture was evaluated at the age of 28 days. The results of testing indicated that the addition of GF was very useful in enhancing the split tensile and flexural strength of both RCA and NCA concrete. Compressive strength was not highly sensitive to the addition of GF. The loss in strength that occurred due to the incorporation of RCA was reduced to a large extent upon the inclusion of GF. GF caused significant improvements in the split tensile and flexural strength of RCA concrete. Optimum dosage of GF was determined to be 0.25% for NCA, and 0.5% for RCA concrete respectively, based on the results of combined mechanical performance (MP).

Investigation of the mechanical properties of concrete containing recycled aggregate and scrap crumb rubber and polypropylene fibers

2020 ◽  
pp. 147776062097750
Author(s):  
Moein Khoshroo ◽  
Ali Akbar Shirzadi Javid ◽  
Nima Rajabi Bakhshandeh ◽  
Mohamad Shalchiyan
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Polypropylene Fiber ◽  
Crumb Rubber ◽  
Recycled Aggregate ◽  
Recycled Aggregates ◽  
Fine Aggregate ◽  
Mixture Ratio ◽  
Coarse Aggregates

In this study, the effect of using crumb rubber and recycled aggregates on the mechanical properties of concrete has been evaluated as areplacement of fine and coarse aggregates In order to add the admixtures and evaluate their combined effect, 20 different types of concrete mixture ratio were prepared. The results indicated that in those samples containing crumb rubber and recycled aggregates the compressive strength is reduced and adding fiber up to 0.1%. to these concrete samples can improve the compressive strength Also, the tensile strength of the samples mixed with crumb rubber and recycled aggregates were decreased, and with the addition of propylene fiber up to 0.4%. the tensile strength slightly increased Moreover by adding the crumb rubber to the samples the elasticity modulus was reduced but by adding fiber to samples about 0.1% and 0.2.% the modulus of elasticity of concrete in all samples were increased. According to the results, it can be said that using the combination of 5% of crumb rubber as a replacement of fine aggregate, and the combination of 35% of recycled aggregates as a replacement of coarse aggregate, and also by adding 0.1% polypropylene fiber in volumetric percentage of concrete along with adding 7% of micro silica as a replacement of cement led to the best effect on the mechanical properties of concrete.

Experimental Research on Compressive Strength of Self-Compacting Concrete with Recycled Coarse Aggregates

2011 ◽  
Vol 306-307 ◽  
pp. 1084-1087 ◽  
Author(s):  
Jing Li ◽  
Xian Feng Qu ◽  
Lin Fu Wang ◽  
Chong Qing Zhu ◽  
Juan Li
Keyword(s):  
Compressive Strength ◽  
Design Method ◽  
Self Compacting Concrete ◽  
Longitudinal Splitting ◽  
Coarse Aggregates ◽  
Hydraulic Concrete ◽  
Mix Proportion ◽  
Splitting Failure ◽  
Concrete Blocks ◽  
Waste Solid

In order to study cubic compressive strength of recycled coarse aggregates-filled concrete systematically, recycled coarse aggregates with the particle size from 50 to150mm are made from waste solid contents, which are artificially broken from abandoned rubble and concrete blocks. Based on the mix proportion design method of ordinary concrete and test code for hydraulic concrete, 3 groups of recycled coarse aggregates-filled concrete cubic specimens were prepared and the compressive strength of the specimens were tested. The results showed that basic failure pattern of recycled coarse aggregates-filled concrete are longitudinal splitting failure, and that cubic compressive strength is higher than that of self-compacting concrete.

The Effect of Polypropylene Fiber on the Mechanical Properties of Self-Compacting Concrete

2010 ◽  
Vol 168-170 ◽  
pp. 1325-1329
Author(s):  
Ye Ran Zhu ◽  
Jun Cai ◽  
Dong Wang ◽  
Guo Hong Huang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Polypropylene Fiber ◽  
Flexural Properties ◽  
Test Results ◽  
Self Compacting Concrete ◽  
Bending Tests ◽  
Flexural Toughness ◽  
Four Point Bending

This paper investigates the mechanical properties (compressive strength, splitting tensile strength and flexural toughness) of polypropylene fiber reinforced self-compacting concrete (PFRSCC). The effect of the incorporation of polypropylene fiber on the mechanical properties of PFRSCC is determined. Four point bending tests on beam specimens were performed to evaluate the flexural properties of PFRSCC. Test results indicate that flexural toughness and ductility are remarkably improved by the addition of polypropylene fiber.

scholarly journals Prediction Models for the Mechanical Properties of Self-Compacting Concrete with Recycled Rubber and Silica Fume

Materials ◽  
2020 ◽  
Vol 13 (8) ◽  
pp. 1821 ◽  
Author(s):  
Robert Bušić ◽  
Mirta Benšić ◽  
Ivana Miličević ◽  
Kristina Strukar
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Silica Fume ◽  
Prediction Models ◽  
Crumb Rubber ◽  
Fine Aggregate ◽  
Rubberized Concrete ◽  
Self Compacting Concrete ◽  
Recycled Rubber ◽  
European Standards

The paper aims to investigate the influence of waste tire rubber and silica fume on the fresh and hardened properties of self-compacting concrete (SCC) and to design multivariate regression models for the prediction of the mechanical properties of self-compacting rubberized concrete (SCRC). For this purpose, 21 concrete mixtures were designed. Crumb rubber derived from end-of-life tires (grain size 0.5–3.5 mm) was replaced fine aggregate by 0%, 5%, 10%, 15%, 20%, 25%, and 30% of total aggregate volume. Silica fume was replaced cement by 0%, 5%, and 10% of the total cement mass. The optimal replacement level of both materials was investigated in relation to the values of the fresh properties and mechanical properties of self-compacting concrete. Tests on fresh and hardened self-compacting concrete were performed according to the relevant European standards. Furthermore, models for predicting the values of the compressive strength, modulus of elasticity, and flexural strength of SCRC were designed and verified with the experimental results of 12 other studies. According to the obtained results, mixtures with up to 15% of recycled rubber and 5% of silica fume, with 28 days compressive strength above 30 MPa, were found to be optimal mixtures for the potential future investigation of reinforced self-compacting rubberized concrete structural elements.

Sign in / Sign up

Export Citation Format

Share Document