scholarly journals Evaluation of Energy Absorption Capabilities of Polyethylene Foam under Impact Deformation

Materials ◽  
2021 ◽  
Vol 14 (13) ◽  
pp. 3613
Author(s):  
Baohui Yang ◽  
Yangjie Zuo ◽  
Zhengping Chang
Keyword(s):  
Energy Absorption ◽  
Failure Modes ◽  
High Strain ◽  
Early Stage ◽  
High Energy ◽  
Test Method ◽  
Test Theory ◽  
Strain Rates ◽  
Impact Properties ◽  
The Impact

Foams are widely used in protective applications requiring high energy absorption under impact, and evaluating impact properties of foams is vital. Therefore, a novel test method based on a shock tube was developed to investigate the impact properties of closed-cell polyethylene (PE) foams at strain rates over 6000 s−1, and the test theory is presented. Based on the test method, the failure progress and final failure modes of PE foams are discussed. Moreover, energy absorption capabilities of PE foams were assessed under both quasi-static and high strain rate loading conditions. The results showed that the foam exhibited a nonuniform deformation along the specimen length under high strain rates. The energy absorption rate of PE foam increased with the increasing of strain rates. The specimen energy absorption varied linearly in the early stage and then increased rapidly, corresponding to a uniform compression process. However, in the shock wave deformation process, the energy absorption capacity of the foam maintained a good stability and exhibited the best energy absorption state when the speed was higher than 26 m/s. This stable energy absorption state disappeared until the speed was lower than 1.3 m/s. The loading speed exhibited an obvious influence on energy density.

scholarly journals Impact Tensile Behaviors of PVDF Building Coated Fabrics

2020 ◽  
Vol 2020 ◽  
pp. 1-10
Author(s):  
Lianqiong Zheng ◽  
Yilong Ye ◽  
Jinping zhuang ◽  
Yongqian Zheng
Keyword(s):  
Energy Absorption ◽  
High Strain ◽  
Absorption Capacity ◽  
Strain Rates ◽  
Membrane Structures ◽  
High Strain Rates ◽  
Stress Strain ◽  
Strain Relationship ◽  
Coated Fabrics ◽  
The Impact

The paper presents the impact tensile behaviors of two common building membranes (Ferrari 1002T2 membrane and XYD 300N membrane) in PVDF-coated-fabric membrane structures. The tests are conducted using the split Hopkinson bar test device. Typical forms of stress and strain are applied for comparing the stress-strain relationship between quasi-static and high strain rates. Besides, the failure mechanism and energy absorption at high strain rates are discussed. The results show that with the increase of strain rates, the growth rate of the stress of PVDF membrane decreases gradually, which is different from the stress-strain relationship in low strain rates. At high strain rates, the ultimate tensile strength increases linearly with the increase of strain rates. In addition, the energy absorption capacity of the material increases with the increase of strain rates. The results can provide an important basis for the design and analysis of membrane structures under the impact loads.

Effect of long-term moisture exposure on impact response of glass-reinforced vinylester

2021 ◽  
pp. 147509022199616
Author(s):  
Fatemeh Alizadeh ◽  
Navid Kharghani ◽  
Carlos Guedes Soares
Keyword(s):  
Water Uptake ◽  
Failure Modes ◽  
Sea Water ◽  
Composite Plates ◽  
Impact Response ◽  
Low Velocity Impact ◽  
Water Type ◽  
Interfacial Damage ◽  
Impact Properties ◽  
The Impact

Glass/Vinylester composite laminates are comprehensively characterised to assess its impact response behaviour under moisture exposure in marine structures. An instrumented drop weight impact machine is utilised to determine the impact responses of dry and immersed specimens in normal, salted and sea water. The specimens, which had three different thicknesses, were subjected to water exposure for a very long period of over 20 months before tested in a low-velocity impact experiment. Water uptake was measured primarily to study the degradation profiles of GRP laminates after being permeated by water. Matrix dissolution and interfacial damage observed on the laminates after prolonged moisture exposure while the absorption behaviour was found typically non-Fickian. The weight of the composite plates firstly increased because of water diffusion up to month 15 and then decreased due to matrix degradation. The specimens with 3, 6 and 9 mm thickness exhibited maximum water absorption corresponding to 2.6%, 0.7% and 0.5% weight gain, respectively. In general, the results indicated that water uptake and impact properties were affected by thickness and less by water type. Impact properties of prolonged immersed specimens reduced remarkably, and intense failure modes detected almost in all cases. The least sensitive to impact damage were wet specimens with 9 mm thickness as they indicated similar maximum load and absorbed energy for different impact energies.

Effect of SiO2 Nanoparticles on the Mechanical and Low Velocity Impact Properties of Epoxy/Glass Composites

2016 ◽  
Vol 838 ◽  
pp. 29-35
Author(s):  
Michał Landowski ◽  
Krystyna Imielińska
Keyword(s):  
Flexural Strength ◽  
Energy Absorption ◽  
Impact Energy ◽  
Epoxy Matrix ◽  
Low Velocity Impact ◽  
Low Velocity ◽  
Nanoparticle Suspension ◽  
Impact Properties ◽  
Velocity Impact ◽  
The Impact

Flexural strength and low velocity impact properties were investigated in terms of possibile improvements due to epoxy matrix modification by SiO2 nanoparticles (1%, 2%, 3%, 5%, 7%wt.) in glass/epoxy laminates formed using hand lay-up method. The matrix resin was Hexion L285 (DGEBA) with Nanopox A410 - SiO2 (20 nm) nanoparticle suspension in the base epoxy resin (DGEBA) supplied by Evonic. Modification of epoxy matrix by variable concentrations of nanoSiO2 does not offer significant improvements in the flexural strength σg, Young’s modulus E and interlaminar shear strength for 1% 3% and 5% nanoSiO2 and for 7% a slight drop (up to ca. 15-20%) was found. Low energy (1J) impact resistance of nanocomposites represented by peak load in dynamic impact characteristics was not changed for nanocompoosites compared to the unmodified material. However at higher impact energy (3J) nanoparticles appear to slightly improve the impact energy absorption for 3% and 5%. The absence or minor improvements in the mechanical behaviour of nanocomposites is due to the failure mechanisms associated with hand layup fabrication technique: (i.e. rapid crack propagation across the extensive resin pockets and numerous pores and voids) which dominate the nanoparticle-dependent crack energy absorption mechanisms (microvoids formation and deformation).

Equipment to Measure the Energy Absorption of Films at High Strain Rates

1957 ◽  
Vol 28 (3) ◽  
pp. 329-333
Author(s):  
R. D. Spangler ◽  
E. B. Cooper
Keyword(s):  
Energy Absorption ◽  
High Strain ◽  
Strain Rates ◽  
High Strain Rates

Experimental assessment of adding carbon nanotubes on the impact properties of Kevlar-ultrahigh molecular weight polyethylene fibers hybrid composites

2020 ◽  
pp. 152808372092148 ◽  
Author(s):  
Mansour B Bigdilou ◽  
Reza Eslami-Farsani ◽  
Hossein Ebrahimnezhad-Khaljiri ◽  
Mohammad A Mohammadi
Keyword(s):  
Carbon Nanotubes ◽  
Molecular Weight ◽  
Energy Absorption ◽  
Hybrid Composites ◽  
Ultrahigh Molecular Weight Polyethylene ◽  
Absorbed Energy ◽  
Impact Properties ◽  
Damage Area ◽  
Ultrahigh Molecular Weight ◽  
The Impact

In the present study, the effect of adding various percentage (0.1, 0.3, 0.5, and 0.9 wt.%) of carbon nanotubes on the impact properties of hybrid composites reinforced with the different stacking sequence of Kevlar fibers and ultrahigh molecular weight polyethylene was investigated. The obtained results showed that the composite with the configuration of sandwiched ultrahigh molecular weight polyethylene layers by Kevlar layers had the higher impact properties as compared with other hybrid configurations. Adding 0.1 wt.% carbon nanotubes in this configuration was caused to increase the normalized absorbed energy more than 6.5 times. The fracture surface of this configuration showed that the branching and expanding the damage area were the dominant mechanisms for the energy absorption of impactor. Also, the field emission scanning electron microscope illustrated that the carbon nanotubes by bridging, pulling out, and fracturing mechanisms increased the capability of energy absorption in the hybrid composites.

Tensile behaviors of co-woven-knitted fabric reinforced composites under various strain rates

2011 ◽  
Vol 45 (24) ◽  
pp. 2495-2506 ◽  
Author(s):  
Pibo Ma ◽  
Hong Hu ◽  
Lvtao Zhu ◽  
Baozhong Sun ◽  
Bohong Gu
Keyword(s):  
Strain Rate ◽  
Failure Modes ◽  
Shear Failure ◽  
High Strain ◽  
Tensile Failure ◽  
Knitted Fabric ◽  
Strain Rates ◽  
High Strain Rates ◽  
Textile Composite ◽  
Interface Failure

This article reports the tensile behaviors of a novel kind of 3D textile composite, named as co-woven-knitted fabric (CWKF) reinforced composite, under quasi-static and high strain rates. The tensile tests were conducted along the warp direction (0°), bias direction (45°), and weft direction (90°) at quasi-static strain rate of 0.001/s and high strain rates ranging from 1589/s to 2586/s. The results indicate that the tensile strength, failure strain, tensile stiffness, energy absorption, and resilient energy are strain rate sensitive along all the three directions. The relationships between the mechanical parameters and the strain rate were also analyzed. The fractograph of the CWKF composite demonstrate that the tensile failure modes are matrix shear failure and fibers breakage under the quasi-static testing condition while interface failure and fibers pullout are at high strain rates.

Hybrid composite laminates reinforced with flax-basalt-glass woven fabrics for lightweight load bearing structures

2020 ◽  
pp. 152808372096074
Author(s):  
Mohamed A Attia ◽  
Marwa A Abd El-baky ◽  
Mostafa M Abdelhaleem ◽  
Mohamed A Hassan
Keyword(s):  
Mechanical Properties ◽  
Composite Laminates ◽  
Failure Modes ◽  
Woven Fabrics ◽  
Plane Shear ◽  
Load Bearing ◽  
Impact Properties ◽  
Basalt Glass ◽  
Interlaminar Shear ◽  
The Impact

An experimental investigation on the mechanical performance of interlayer hybrid flax-basalt-glass woven fabrics reinforced epoxy composite laminates has been performed. The tensile, flexural, in-plane shear, interlaminar shear, bearing, and impact properties of the fabricated laminates were investigated. Test specimens were fabricated using vacuum bagging process. Failure modes of all specimens were recorded and discussed. Results proved that the mechanical properties of flax-basalt-glass hybrid laminates are highly dominated by the reinforcement combinations and plies stacking sequence. Hybridizing flax fiber reinforced composite with basalt and/or glass fabrics provides an effective method for enhancing its tensile, flexural, in-plane shear, interlaminar shear, and bearing properties as well as controls the impact strength of the composite. The fabricated hybrids are found to have good specific mechanical properties benefits. Amongst the studied flax/basalt/glass hybrids, FBGs has the highest tensile properties, GBFs has the highest flexural and impact properties, and GFBs has the best shear and bearing properties. Flax-basalt-glass hybrid composites with different layering sequence seem to be an appropriate choice for lightweight load bearing structures.

Low-velocity impact response of wood-strand sandwich panels and their components

Holzforschung ◽  
2018 ◽  
Vol 72 (8) ◽  
pp. 681-689 ◽  
Author(s):  
Mostafa Mohammadabadi ◽  
Vikram Yadama ◽  
LiHong Yao ◽  
Debes Bhattacharyya
Keyword(s):  
Energy Absorption ◽  
Impact Energy ◽  
Failure Modes ◽  
Sandwich Panels ◽  
Low Velocity Impact ◽  
Insulation Material ◽  
Low Velocity ◽  
Velocity Impact ◽  
Section Modulus ◽  
The Impact

AbstractProfiled hollow core sandwich panels (SPs) and their components (outer layers and core) were manufactured with ponderosa and lodgepole pine wood strands to determine the effects of low-velocity impact forces and to observe their energy absorption (EA) capacities and failure modes. An instrumented drop weight impact system was applied and the tests were performed by releasing the impact head from 500 mm for all the specimens while the impactors (IMPs) were equipped with hemispherical and flat head cylindrical heads. SPs with cavities filled with a rigid foam insulation material (SPfoam) were also tested to understand the change in EA behavior and failure mode. Failure modes induced by both IMPs to SPs were found to be splitting, perforating, penetrating, core crushing and debonding between the core and the outer layers. SPfoams absorbed 26% more energy than unfilled SPs. SPfoams with urethane foam suffer less severe failure modes than SPs. SPs in a ridge-loading configuration absorbed more impact energy than those in a valley-loading configuration, especially when impacted by a hemispherical IMP. Based on the results, it is evident that sandwich structure is more efficient than a solid panel concerning impact energy absorption, primarily due to a larger elastic section modulus of the core’s corrugated geometry.

scholarly journals An Image-Based Impact Test for the High Strain Rate Tensile Properties of Brittle Materials

2018 ◽  
Vol 183 ◽  
pp. 02042
Author(s):  
Lloyd Fletcher ◽  
Fabrice Pierron
Keyword(s):  
Tensile Strength ◽  
Elastic Modulus ◽  
High Strain Rate ◽  
Strain Rate ◽  
Stress Wave ◽  
High Strain ◽  
Brittle Materials ◽  
Test Method ◽  
Strain Rates ◽  
High Strain Rates

Testing ceramics at high strain rates presents many experimental diffsiculties due to the brittle nature of the material being tested. When using a split Hopkinson pressure bar (SHPB) for high strain rate testing, adequate time is required for stress wave effects to dampen out. For brittle materials, with small strains to failure, it is difficult to satisfy this constraint. Because of this limitation, there are minimal data (if any) available on the stiffness and tensile strength of ceramics at high strain rates. Recently, a new image-based inertial impact (IBII) test method has shown promise for analysing the high strain rate behaviour of brittle materials. This test method uses a reflected compressive stress wave to generate tensile stress and failure in an impacted specimen. Throughout the propagation of the stress wave, full-field displacement measurements are taken, from which strain and acceleration fields are derived. The acceleration fields are then used to reconstruct stress information and identify the material properties. The aim of this study is to apply the IBII test methodology to analyse the stiffness and strength of ceramics at high strain rates. The results show that it is possible to identify the elastic modulus and tensile strength of tungsten carbide at strain rates on the order of 1000 s-1. For a tungsten carbide with 13% cobalt binder the elastic modulus was identified as 516 GPa and the strength was 1400 MPa. Future applications concern boron carbide and sapphire, for which limited data exist in high rate tension.

Numerical Investigation on Impact Energy Absorption of Single-Walled Carbon Nanotube Reinforced Composites

2012 ◽  
Author(s):  
Lingyu Sun ◽  
Jian Zhang ◽  
Dingxin Leng
Keyword(s):  
Numerical Investigation ◽  
Energy Absorption ◽  
Impact Energy ◽  
Metal Matrix ◽  
Failure Modes ◽  
Volume Fraction ◽  
Matrix Material ◽  
Reinforced Composites ◽  
Alloy Matrix ◽  
The Impact

With the exceptional mechanical properties, carbon nanotubes (CNTs) are considered to be attractive candidate reinforcements for composite materials and to have potential applications in improving the energy absorption capability of matrix material. However, it is still difficult to reveal the micro-mechanisms of the impact energy absorption of CNT-reinforced composites by experiments, hence, the numerical investigation is helpful. In this paper, a unit cell of single-walled CNTs (SWCNTs) embedded in metal matrix is modeled by nano-scale finite element method. Under impact loads, the failure modes of a single SWCNT and the SWCNT in matrix are predicted, respectively, and several possible energy absorption mechanisms are explained and compared. The investigation shows that, the metal matrix restraints the radial expansion of the SWCNT and therefore improves its crush buckling resistance, and makes it absorb more energy before collapse. The specific energy absorption of SWCNTs-reinforce composites increases with the increasing volume fraction of SWCNTs in both matrixes, and ascends more quickly in magnesium alloy than in aluminum alloy matrix.

Sign in / Sign up

Export Citation Format

Share Document