Characterization of Fluorinated Hβ Zeolite with NH4F

2010 ◽  
Vol 160-162 ◽  
pp. 524-528
Author(s):  
Zhen Tian ◽  
Nai Ci Bing
Keyword(s):  
Aqueous Solution ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Acid Sites ◽  
Total Acid ◽  
Hβ Zeolite ◽  
Surface Performance

Fluorination of the zeolite has been known as a useful method to modify its acidity and surface performance. In this paper, a set of zeolite Hβ were impregnated with aqueous solution of NH4F. The effects of NH4F impregnation on the structure and acidity of Hβ was investigated by XRD, BET measurements, NH3-TPD, and Py-IR. The change of specific surface area and pore volume of the fluorinated samples with NH4F can be attributed the reaction of NH4F with non-framework and framework aluminum. The fluorination increases the strength and changes the distribution of the acid sites; the fluorination also leads to the decrease of the total acid sites and the Brönsted acid sites due to the dealuminization of the samples and the substitution of the OH- by fluorine atoms.

The Preparation and Characterization of the Mesoporous Poly(bisphenol-A carbonate) – Silica Nanocomposites

2014 ◽  
Vol 513-517 ◽  
pp. 82-85
Author(s):  
Rui Rui Li ◽  
Yue Shi ◽  
Lei Zu ◽  
Hui Qin Lian ◽  
Yang Liu ◽  
...  
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Pore Diameter ◽  
Ph Value ◽  
Sol Gel ◽  
Synthesis System ◽  
Silica Nanocomposites

The mesoporous polycarbonate-silica nanocomposite materials were synthesized through the modified sol-gel approach under acidic condition. The specific surface area, pore diameter and pore volume of polycarbonate-silica could be controlled by changing the acidity of the synthesis system. The polycarbonate-silica possess an irregular block morphology according to the scanning electron microscopy observations. With decreasing the pH value of the synthesis system, the specific surface area and pore diameter of polycarbonate-silica were raised but the pore volume was reduced. The maximum specific surface area of polycarbonate-silica was 701.71m2/g which presented by the results of Nitrogen adsorptiondesorption isotherms.

Preparation and Characterization of TiO2 Nanoparticles / CNTs Composite Particles

2012 ◽  
Vol 268-270 ◽  
pp. 172-175
Author(s):  
Ming Qiu Wang ◽  
Jun Yan ◽  
Shi Guo Du ◽  
Bin Wang ◽  
Hao Qin
Keyword(s):  
Aqueous Solution ◽  
Surface Roughness ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Tetrabutyl Titanate ◽  
Composite Particles ◽  
Absorption Intensity ◽  
Main Material

By using tetrabutyl titanate as the main material, TiO2 nanoparticles / CNTs composite particles have been prepared in acidic abundant aqueous solution at low temperature without calcination. The microstructure of the composite particles, including surface morphology, phase composition and specific surface area was characterized by SEM, TEM, Raman, XPS and BET. The results reveal that TiO2 nanoparticles coated uniformly on CNTs surfaces were mainly anatase type. The surface roughness of CNTs was remarkably increased after coating. However, the specific surface area of composite particles decreased by 23.4 m2•g-1 than that of CNTs with uncoated TiO2. Photocatalytic activity of TiO2 nanoparticles / CNTs composite particles shows a significant increase of absorption intensity both in ultraviolet band and visible light band according to UV-vis spectra.

Fuels Desulphurisation by Adsorbtion on Fe / Bentonite

2017 ◽  
Vol 68 (3) ◽  
pp. 483-486
Author(s):  
Constantin Sorin Ion ◽  
Mihaela Bombos ◽  
Gabriel Vasilievici ◽  
Dorin Bombos
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Pore Diameter ◽  
Adsorption Process ◽  
Continuous System ◽  
Gas Oil ◽  
Average Pore ◽  
Atmospheric Distillation

Desulfurisation of atmospheric distillation gasoline and gas oil was performed by adsorption process on Fe/ bentonite. The adsorbent was characterized by determining the adsorption isotherms, specific surface area, pore volume and average pore diameter. Adsorption experiments of atmospheric distillation gasoline and gas oil were performed in continuous system at 280�320oC, 5 atm and volume hourly space velocities of 1�2 h-1. The efficiency of adsorption on Fe / bentonite was better at desulphurisation of gasoline versus gas oil.

scholarly journals Nanometer Pore Structure Characterization of Taiyuan Formation Shale in the Lin-Xing Area Based on Nitrogen Adsorption Experiments

Minerals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 298
Author(s):  
Chenlong Ding ◽  
Jinxian He ◽  
Hongchen Wu ◽  
Xiaoli Zhang
Keyword(s):  
Specific Surface ◽  
Pore Structure ◽  
Surface Area ◽  
Specific Surface Area ◽  
Shale Gas ◽  
Pore Volume ◽  
Ordos Basin ◽  
Total Pore Volume ◽  
Nitrogen Adsorption ◽  
Taiyuan Formation

Ordos Basin is an important continental shale gas exploration site in China. The micropore structure of the shale reservoir is of great importance for shale gas evaluation. The Taiyuan Formation of the lower Permian is the main exploration interval for this area. To examine the nanometer pore structures in the Taiyuan Formation shale reservoirs in the Lin-Xing area, Northern Shaanxi, the microscopic pore structure characteristics were analyzed via nitrogen adsorption experiments. The pore structure parameters, such as specific surface area, pore volume, and aperture distribution, of shale were calculated; the significance of the pore structure for shale gas storage was analyzed; and the main controlling factors of pore development were assessed. The results indicated the surface area and hole volume of the shale sample to be 0.141–2.188 m2/g and 0.001398–0.008718 cm3/g, respectively. According to the IUPAC (International Union of Pure and Applied Chemistry) classification, mesopores and macropores were dominant in the pore structure, with the presence of a certain number of micropores. The adsorption curves were similar to the standard IV (a)-type isotherm line, and the hysteresis loop type was mainly similar to H3 and H4 types, indicating that most pores are dominated by open type pores, such as parallel plate-shaped pores and wedge-shaped slit pores. The micropores and mesopores provide the vast majority of the specific surface area, functioning as the main area for the adsorption of gas in the shale. The mesopores and macropores provide the vast majority of the pore volume, functioning as the main storage areas for the gas in the shale. Total organic carbon had no notable linear correlation with the total pore volume and the specific surface area. Vitrinite reflectance (Ro) had no notable correlation with the specific surface area, but did have a low “U” curve correlation with the total pore volume. There was no relationship between the quartz content and specific surface area and total pore volume. In addition, there was no notable correlation between the clay mineral content and total specific surface area and total pore volume.

The relationship between geotechnical index properties and the pore-size distribution of compacted clayey silts

2015 ◽  
Vol 22 (6) ◽  
Author(s):  
Nazile Ural
Keyword(s):  
Specific Surface ◽  
Pore Size Distribution ◽  
Pore Size ◽  
Size Distribution ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Correlation Coefficients ◽  
Liquid Limit ◽  
Index Properties

AbstractIn this study, the relationships between geotechnical index properties and the pore-size distribution of compacted natural silt and artificial soil mixtures, namely, silt with two different clays and three different clay percentages (10%, 20%, and 40%), were examined and compared. Atterberg’s limit tests, standard compaction tests, mercury intrusion porosimetry, X-ray diffraction, scanning electron microscopy (SEM) analysis, and Brunauer-Emmett-Teller specific surface analysis were conducted. The results show that the liquid limit, the cumulative pore volume, and specific surface area of artificially mixed soils increase with an increase in the percentage of clay. The cumulative pore volume and specific surface area with geotechnical index properties were compared. High correlation coefficients were observed between the specific areas and both the liquid limit and the plasticity index, as well as between the cumulative pore volume and both the clay percentage and the

Study of the Porous Structure and High Adsorption Capacity of Biomass-Based Activated Carbon Prepared from Aspen Wood by Ferric Nitrate III Activation

2021 ◽  
Vol 15 (2) ◽  
pp. 131-144
Author(s):  
Chunjiang Jin ◽  
Huimin Chen ◽  
Luyuan Wang ◽  
Xingxing Cheng ◽  
Donghai An ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Adsorption Capacity ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Mass Ratio ◽  
Aspen Wood ◽  
Surface Functional Groups ◽  
Wood Sawdust

In this study, aspen wood sawdust was used as the raw material, and Fe(NO3)3 and CO2 were used as activators. Activated carbon powder (ACP) was produced by the one-step physicochemical activation method in an open vacuum tube furnace. The effects of different mass ratios of Fe(NO3)3 and aspen wood sawdust on the pore structure of ACP were examined under single-variable experimental conditions. The mass ratio was 0–0.4. The detailed characteristics of ACP were examined by nitrogen adsorption, scanning electron microscopy, X-ray diffraction, and Fourier transform infrared spectroscopy. The adsorption capacity of ACP was established by simulating volatile organic compounds (VOCs) using ethyl acetate. The results showed that ACP has a good nanostructure with a large pore volume, specific surface area, and surface functional groups. The pore volume and specific surface area of Fe-AC-0.3 were 0.26 cm3/g and 455.36 m2/g, respectively. The activator played an important role in the formation of the pore structure and morphology of ACP. When the mass ratio was 0–0.3, the porosity increased linearly, but when it was higher than 0.3, the porosity decreased. For example, the pore volume and specific surface area of Fe-AC-0.4 reached 0.24 cm3/g and 430.87 m2/g, respectively. ACP presented good VOC adsorption performance. The Fe-AC-0.3 sample, which contained the most micropore structures, presented the best adsorption capacity for ethyl acetate at 712.58 mg/g. Under the action of the specific reaction products nitrogen dioxide (NO2) and oxygen, the surface of modified ACP samples showed different rich C/O/N surface functional groups, including C-H, C=C, C=O, C-O-C, and C-N.

scholarly journals Effects of microwave modification on the desulfurization and denitrification of activated coke

BioResources ◽  
2020 ◽  
Vol 16 (1) ◽  
pp. 729-746
Author(s):  
Junhong Zhang ◽  
Zhi-jun He ◽  
Qing Guo ◽  
De-chao Xiao ◽  
Wen-long Zhan
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Surface Functional Groups ◽  
Characteristic Peak ◽  
Theoretical Support ◽  
O2 Concentration ◽  
Activated Coke ◽  
Oh Content

Microwave modification of activated coke is reported as a green and simple route to improve its synergistic desulfurization and denitrification. The results showed that microwave irradiation improved the specific surface area and pore volume, decreased the pore size, and activated the surface functional groups of the activated coke. Under the conditions of a microwave power of 500 W and a modification time of 30 min, the specific surface area was increased from 185.9 m2/g to 351.7 m2/g, the pore volume increased from 0.042 m3/g to 0.111 m3/g, and the characteristic peak strengths of C=C and -OH drastically increased. When the reaction temperature was 140 °C and the O2 concentration was 10% (by volume), the desulfurization and denitrification efficiency were maintained at levels greater than 90% and 80% for 30 min and 15 min, respectively. The C-O content increased, and the C=C and -OH content decreased after undergoing desulfurization and denitrification. The desulfurization and denitrification products were primarily sulfate and nitrate. This provides theoretical support for the application of microwave modified active coke in low temperature desulfurization and denitrification.

scholarly journals Structural and fractal characterization of adsorption pores of middle–high rank coal reservoirs in western Yunnan and eastern Guizhou: An experimental study of coals from the Panguan syncline and Laochang anticline

2018 ◽  
Vol 37 (1) ◽  
pp. 251-272 ◽  
Author(s):  
Junjian Zhang ◽  
Chongtao Wei ◽  
Gaoyuan Yan ◽  
Guanwen Lu
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Pore Diameter ◽  
Structural Parameters ◽  
Total Pore Volume ◽  
Type A ◽  
Type B ◽  
Type C

To better understand the structural characteristic of adsorption pores (pore diameter < 100 nm) of coal reservoirs around the coalbed methane production areas of western Yunnan and eastern Guizhou, we analyzed the structural and fractal characteristics of pore size range of 0.40–2.0 nm and 2–100 nm in middle–high rank coals ( Ro,max = 0.93–3.20%) by combining low-temperature N2/CO2 adsorption tests and surface/volume fractal theory. The results show that the coal reservoirs can be divided into three categories: type A ( Ro,max < 2.15%), type B (2.15% <  Ro,max <2.50%), and type C ( Ro,max > 2.15%). The structural parameters of pores in the range from 2 to 100 nm are influenced by the degree of coal metamorphism and the compositional parameters (e.g., ash and volatile matter). The dominant diameters of the specific surface areas are 10–50 nm, 2–50 nm, and 2–10 nm, respectively. The pores in the range from <2 nm provide the largest proportion of total specific surface area (97.22%–99.96%) of the coal reservoir, and the CO2-specific surface area and CO2-total pore volume relationships show a positive linear correlation. The metamorphic degree has a much greater control on the pores (pore diameter less than 2 nm) structural parameters than those of the pore diameter ranges from 2 to 100 nm. Dv1 and Dv2 can characterize the structure of 2–100 nm adsorption pores, and Dv1 (volume heterogeneity) has a positive correlation with the pore structural parameters such as N2-specific surface area and N2-total pore volume. This parameter can be used to characterize volume heterogeneity of 2–10 nm pores. Dv2 (surface heterogeneity) showed type A > type B > type C and was mainly affected by the metamorphism degree. Ds2 can be used to characterize the pore surface heterogeneity of micropores in the range of 0.62–1.50 nm. This parameter has a good correlation with the pore parameters (CO2-total pore volume, CO2-specific surface area, and average pore size) and is expressed as type C < type B < type A. In conclusion, the heterogeneity of the micropores is less than that of the meso- and macropores (2–100 nm). Dv1, Dv2, and Ds2 can be used as effective parameters to characterize the pore structure of adsorption pores. This result can provide a theoretical basis for studying the pore structure compatibility of coal reservoirs in the region.

scholarly journals Acid Modification of the Unsupported NiMo Catalysts by Y-Zeolite Nanoclusters

Crystals ◽  
2019 ◽  
Vol 9 (7) ◽  
pp. 344
Author(s):  
Chengwu Dong ◽  
Changlong Yin ◽  
Tongtong Wu ◽  
Zhuyan Wu ◽  
Dong Liu ◽  
...  
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Average Pore Size ◽  
Y Zeolite ◽  
Active Components ◽  
Acid Modification ◽  
Total Acid ◽  
Average Pore ◽  
Nimo Catalysts

Unsupported NiMo catalyst has high hydrogenation activity due to its high active site distribution. However, low specific surface area and pore distribution greatly limit the efficient utilization of the active components. The Y-zeolite nanoclusters were hydrothermally synthesized and introduced into the unsupported NiMo catalysts from a layered nickel molybdate complex oxide. The XRD, N2 adsorption-desorption, FT-IR, Py-IR, SEM, NH3-TPD, and TEM were used to characterize all catalysts. The dibenzothiophene (DBT) hydrodesulfurization (HDS) reaction was performed in a continuous high pressure microreactor. The results showed that the specific surface area, pore volume, and average pore size of the unsupported NiMo catalysts were greatly increased by the Y-zeolite nanoclusters, and a more dispersed structure was produced. Furthermore, the Lewis acid and total acid content of the unsupported NiMo catalysts were greatly improved by the Y-zeolite nanoclusters. The HDS results showed that the unsupported NiMo catalysts modified by the nanoclusters had the same high desulfurization efficiency as the unmodified catalyst, but had more proportion of direct desulfurization (DDS) products. The results offer an alternative to reducing hydrogen consumption and save cost in the production of ultra clean diesel.

scholarly journals Adsorption of Ammonium Nitrogen from Aqueous Solution on Chemically Activated Biochar Prepared from Sorghum Distillers Grain

2019 ◽  
Vol 9 (23) ◽  
pp. 5249 ◽  
Author(s):  
Derlin Hsu ◽  
Changyi Lu ◽  
Tairan Pang ◽  
Yuanpeng Wang ◽  
Guanhua Wang
Keyword(s):  
Aqueous Solution ◽  
Specific Surface ◽  
Adsorption Capacity ◽  
Surface Area ◽  
Specific Surface Area ◽  
Adsorption Process ◽  
Ammonium Nitrogen ◽  
Activated Biochar ◽  
Distillers Grain ◽  
Kinetics And Isotherms

Chemically activated biochars prepared from sorghum distillers grain using two base activators (NaOH and KOH) were investigated for their adsorption properties with respect to ammonium nitrogen from aqueous solution. Detailed characterizations, including scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetry (TG), and specific surface area analyses, were carried out to offer a broad evaluation of the prepared biochars. The results showed that the NaOH- and KOH-activated biochars exhibited significantly enhanced adsorption capacity, by 2.93 and 4.74 times, respectively, in comparison with the pristine biochar. Although the NaOH-activated biochar possessed larger specific surface area (132.8 and 117.7 m2/g for the NaOH- and KOH-activated biochars, respectively), the KOH-activated biochar had higher adsorption capacity owing to its much higher content of functional groups. The adsorption kinetics and isotherms of the KOH-activated biochar at different temperatures were further studied. The biochar had a maximum adsorption capacity of 14.34 mg/g at 45 °C, which was satisfactory compared with other biochars prepared using different feedstocks. The adsorption process followed pseudo-second-order kinetics, and chemical adsorption was the rate-controlling step. The equilibrium data were consistent with the Freundlich isotherm, and the thermodynamic parameters suggested that the adsorption process was endothermic and spontaneous. Consequently, this work demonstrates that chemically activated biochar from sorghum distillers grain is effective for ammonium nitrogen removal.

Sign in / Sign up

Export Citation Format

Share Document