Effect of Annealing Temperature on The Refrective Index and Dielectric Properties of TiO2/MnO2 CORE/SHELL Thin Films

2014 ◽  
Vol 6 (3) ◽  
pp. 1227-1232
Author(s):  
Peter Ekuma Agbo
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Refractive Index ◽  
Dielectric Properties ◽  
Dielectric Property ◽  
Annealing Temperature ◽  
Xrd Analysis ◽  
Core Shell ◽  
Structural Nature ◽  
Deposited Film

Thin film of the form TiO2/MnO2 was deposited using the chemical bath method. The deposited thin films were annealed at temperatures of in order to investigate the effect of annealing temperature on the refractive index and dielectric property. To do this the films were characterized using UV-Spectrophotometer and XRD analysis was also carriedout to study the structural nature of the deposited film. Our results reaveled that annealing has profound effect on theindex of refraction and the dielectric properties.  

Effects of Annealing Temperature on Morphology and Dielectric Property of BiFeO3 Films

2012 ◽  
Vol 512-515 ◽  
pp. 1736-1739
Author(s):  
Li Li Zhang ◽  
Guo Qiang Tan ◽  
Meng Cheng ◽  
Hui Jun Ren ◽  
Ao Xia
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Dielectric Property ◽  
Annealing Temperature ◽  
Raw Materials ◽  
Sol Gel ◽  
Frequency Range ◽  
Annealing Temperatures ◽  
Pure Phase ◽  
Lower Loss

Fe(NO3)3•9H2O and Bi(NO3)3•5H2O were used as raw materials. BiFeO3 thin films were prepared by sol-gel method. The effects of annealing temperatures on the morphology and dielectric property of the thin films were studied. XRD results show that the multi-crystal thin films with pure phase are obtained when annealed at 500°C and 550°C. But annealing at 580°C will lead to the appearance of Bi2.46Fe5O12 phase.AFM images show that as the increase of annealing temperatures the surface toughness of the thin film is decreased, but the surface undulation of the thin films is decreased gradually. Within the frequency range of 1KHz~1MHz, the dielectric constant of BiFeO3 thin films is kept over 125 and it does not change very much from 500°C to 580°C. Annealed at 550°C, the BiFeO3 thin films with the lower loss are obtained. At 1MHz, the dielectric loss is 0.12.

scholarly journals Effect of Annealing Temperature in Improvement the Optical Properties of TiO2 Doped Fe2O3 to Use in Thin Film

2019 ◽  
pp. 1-12
Author(s):  
Abubakr Mahmoud Hamid ◽  
Hassan Wardi Hassan ◽  
Fatima Ahmed Osman
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Refractive Index ◽  
Optical Properties ◽  
Iron Oxide ◽  
Titanium Oxide ◽  
Extinction Coefficient ◽  
Tio2 Thin Film ◽  
Annealing Temperature ◽  
Spray Pyrolysis Deposition

Solar energy is already has being widely successfully used in residential and industrial setting for thermal and electrical application such as space technology, communication, etc. I. Aims: The aim of this study the effect of the annealing temperature in improvement optical properties of titanium oxide nanostructure doped iron oxide for use in thin film. Study Design: The spray pyrolysis deposition method used for preparation the nanostructure material. Place and Duration of Study: This study was conducted in department of physics and department of materials sciences, Al-Neelain University, between January 2016 and January 2019.  Methodology: Thin films of Titanium Oxide (TiO2) doped Iron Oxide (Fe2O3) have been prepared by chemical spray pyrolysis deposition technique. A laboratory designed glass atomizer was used for spraying the aqueous solution. Which has an output nozzle about 1 mm. then film were deposited on preheated cleaned glass substrates at temperature of 400°C. we used different concentration to study optical parameters. A 1.5 g TiO2 powder of anatase structure doped with 1.5 g of Fe2O3 was mixed with 2 ml of ethanol and stirred using a magnetic stirrer for 30 minutes to form TiO2 paste to obtain the starting solution for deposition and spray time was 10 s and spray interval 2 min was kept constant. The carrier gas (filtered compressed air) was maintained at a pressure of 105 Nm-2, and distance between nozzle and substrate was about 30 cm ± 1 cm. Thickness of sample was measured using the weighting method and was found to be around 400nm. Optical transmittance and absorbance were record in wavelength range of (200-1100) nm using UV-Visible spectrophotometer (Shimadzu Company Japan). Results: The results obtained showed that the optical band gap decreased from 5.6eV before annealing to (3.9, 3.26, 3.24 and 3.27 eV) after annealing temperature at(450° – 500°) for TiO2:Fe2O3 thin films, this result refer to the broadening of  secondary levels that product by TiO2: doping to the Fe2O2thin films. Also the results showed the variation of refractive index with wavelength for different concentration after annealing temperature at (450° – 500°) of TiO2: Fe2O3 films from this figure, it is clear that n decrease with low concentration and increase with high concentration after annealing temperature that mean the density is decreased of this films. In addition the extinction coefficient of TiO2:Fe2O3 thin films recorded before annealing and with different concentration (1.1, 1.2, 1,5 and 1,6) and in the range of (300 – 1200) nm and at annealing temperature from (450° – 500°). It observed from that the extinction coefficient, decrease sharply with the increase of wavelength for all prepared films and all the sample after annealing is interference between them accept the sample before annealing is far from the other sample. Conclusion: The TiO2 thin film shows better result after annealing; By exposing temperature during annealing process degree at (450o- 500o) is found to be the best temperature for annealing TiO2 thin film. The study concluded that an annealing temperature Contributes to the improvement of optical properties related to increasing the efficiency of the solar cell, especially the refractive index, energy gap, extinction coefficient.

scholarly journals Optimizing the Properties of La0.8Sr0.2CrO3 Thin Films through Post-Annealing for High-Temperature Sensing

Nanomaterials ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 1802
Author(s):  
Dan Liu ◽  
Peng Shi ◽  
Yantao Liu ◽  
Yijun Zhang ◽  
Bian Tian ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Annealing Temperature ◽  
Rf Sputtering ◽  
Maximum Size ◽  
Cross Sectional ◽  
Post Annealing ◽  
Maximum Conductivity ◽  
Different Temperatures ◽  
Post Annealing Temperature

La0.8Sr0.2CrO3 (0.2LSCO) thin films were prepared via the RF sputtering method to fabricate thin-film thermocouples (TFTCs), and post-annealing processes were employed to optimize their properties to sense high temperatures. The XRD patterns of the 0.2LSCO thin films showed a pure phase, and their crystallinities increased with the post-annealing temperature from 800 °C to 1000 °C, while some impurity phases of Cr2O3 and SrCr2O7 were observed above 1000 °C. The surface images indicated that the grain size increased first and then decreased, and the maximum size was 0.71 μm at 1100 °C. The cross-sectional images showed that the thickness of the 0.2LSCO thin films decreased significantly above 1000 °C, which was mainly due to the evaporation of Sr2+ and Cr3+. At the same time, the maximum conductivity was achieved for the film annealed at 1000 °C, which was 6.25 × 10−2 S/cm. When the thin films post-annealed at different temperatures were coupled with Pt reference electrodes to form TFTCs, the trend of output voltage to first increase and then decrease was observed, and the maximum average Seebeck coefficient of 167.8 µV/°C was obtained for the 0.2LSCO thin film post-annealed at 1100 °C. Through post-annealing optimization, the best post-annealing temperature was 1000 °C, which made the 0.2LSCO thin film more stable to monitor the temperatures of turbine engines for a long period of time.

scholarly journals Synthesis, Crystallography, Microstructure, Crystal Defects, Optical and Optoelectronic Properties of ZnO:CeO2 Mixed Oxide Thin Films

Photonics ◽  
2020 ◽  
Vol 7 (4) ◽  
pp. 112
Author(s):  
Qais M. Al-Bataineh ◽  
Mahmoud Telfah ◽  
Ahmad A. Ahmad ◽  
Ahmad M. Alsaad ◽  
Issam A. Qattan ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Refractive Index ◽  
Mixed Oxide ◽  
Visible Region ◽  
Functional Materials ◽  
Crystal Defects ◽  
Optoelectronic Properties ◽  
Oxide Thin Films ◽  
Pure Ceo2

We report the synthesis and characterization of pure ZnO, pure CeO2, and ZnO:CeO2 mixed oxide thin films dip-coated on glass substrates using a sol-gel technique. The structural properties of as-prepared thin film are investigated using the XRD technique. In particular, pure ZnO thin film is found to exhibit a hexagonal structure, while pure CeO2 thin film is found to exhibit a fluorite cubic structure. The diffraction patterns also show the formation of mixed oxide materials containing well-dispersed phases of semi-crystalline nature from both constituent oxides. Furthermore, optical properties of thin films are investigated by performing UV–Vis spectrophotometer measurements. In the visible region, transmittance of all investigated thin films attains values as high as 85%. Moreover, refractive index of pure ZnO film was found to exhibit values ranging between 1.57 and 1.85 while for CeO2 thin film, it exhibits values ranging between 1.73 and 2.25 as the wavelength of incident light decreases from 700 nm to 400 nm. Remarkably, refractive index of ZnO:CeO2 mixed oxide-thin films are tuned by controlling the concentration of CeO2 properly. Mixed oxide-thin films of controllable refractive indices constitute an important class of smart functional materials. We have also investigated the optoelectronic and dispersion properties of ZnO:CeO2 mixed oxide-thin films by employing well-established classical models. The melodramatic boost of optical and optoelectronic properties of ZnO:CeO2 mixed oxide thin films establish a strong ground to modify these properties in a skillful manner enabling their use as key potential candidates for the fabrication of scaled optoelectronic devices and thin film transistors.

PREPARATION AND FERROELECTRIC PROPERTY OF (100)-ORIENTED Ca0.4Sr0.6Bi4Ti4O15 THIN FILM ON Pt/Ti/SiO2/Si SUBSTRATE

2010 ◽  
Vol 17 (05n06) ◽  
pp. 445-449 ◽  
Author(s):  
SUHUA FAN ◽  
QUANDE CHE ◽  
FENGQING ZHANG
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Ferroelectric Property ◽  
Remanent Polarization ◽  
Sol Gel ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
Si Substrate ◽  
Degree Of Orientation ◽  
Equiaxed Grains

The (100)-oriented Ca0.4Sr0.6Bi4Ti4O15(C0.4S0.6BTi ) thin film was successfully prepared by a sol-gel method on Pt/Ti/SiO2/Si substrate. The orientation and formation of thin films under different annealing schedules were studied using XRD and SEM. XRD analysis indicated that (100)-oriented C0.4S0.6BTi thin film with degree of orientation of I(200)/I(119) = 1.60 was prepared by preannealing the film at 400°C for 3 min followed by rapid thermal annealing at 800°C for 5 min. SEM analysis further indicated that the (100)-oriented C0.4S0.6BTi thin film with a thickness of about 800 nm was mainly composed of equiaxed grains. The remanent polarization and coercive field of the film were 16.1 μC/cm2 and 85 kV/cm, respectively.

The Dielectric Properties of Pb0.65Ba0.35ZrO3 Thin Films

2006 ◽  
Vol 306-308 ◽  
pp. 1313-1318
Author(s):  
J.S. Kim ◽  
B.H. Park ◽  
T.J. Choi ◽  
Se Hyun Shin ◽  
Jae Chul Lee ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Dielectric Properties ◽  
Dielectric Loss ◽  
Deposition Temperature ◽  
Pulsed Laser ◽  
Laser Deposition ◽  
Axis Orientation ◽  
Capacitance Voltage ◽  
Bst Thin Film

Pb0.65Ba0.35ZrO3 (PBZ) thin films have been grown on MgO (001) substrates by pulsed-laser deposition (PLD). We have compared the structural and dielectric properties of PBZ films grown at various temperatures. A highly c-axis orientation has appeared at PBZ film grown at the deposition temperature of 550oC. The c-axis oriented PBZ film has also shown the largest tunability among all the PBZ films in capacitance-voltage measurements. The tunability and dielectric loss of the PBZ film was 20% and 0.00959, respectively. In addition, we have compared the temperature coefficient of capacitance (TCC) of a PBZ film with that of a Ba0.5Sr0.5TiO3 (BST) film which is a well-known material applicable to tunable microwave devices. We have confirmed that TCC value of a PBZ thin film was three-times smaller than that of a BST thin film.

scholarly journals Annealing Effect on Some Optical Properties of Cr2O3 Thin Films Prepared by Spray Pyrolysis Technique

2011 ◽  
Vol 8 (2) ◽  
pp. 561-565
Author(s):  
Baghdad Science Journal
Keyword(s):  
Thin Films ◽  
Dielectric Constant ◽  
Refractive Index ◽  
Optical Properties ◽  
Absorption Coefficient ◽  
Spray Pyrolysis ◽  
Annealing Temperature ◽  
Spray Pyrolysis Technique ◽  
Annealing Effect ◽  
Before And After

Cr2O3 thin films have been prepared by spray pyrolysis on a glass substrate. Absorbance and transmittance spectra were recorded in the wavelength range (300-900) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of dielectric constant and optical conductivity were expected. It was found that all these parameters increase as the annealing temperature increased to 550°C.

Effect of vacuum annealing on the properties of one step thermally evaporated Sb2S3 thin films for photovoltaic applications

2021 ◽  
Author(s):  
Emna Gnenna ◽  
Naoufel Khemiri ◽  
Minghua Kong ◽  
Maria Isabel Alonso ◽  
Mounir Kanzari
Keyword(s):  
Thin Films ◽  
Annealing Temperature ◽  
Vacuum Annealing ◽  
Xrd Analysis ◽  
Band Gap Energy ◽  
Chemical Compositions ◽  
Optical Parameters ◽  
X Ray ◽  
Vis Spectroscopy ◽  
One Step

Sb2S3 powder was successfully synthesized by solid state reaction technique using high-purity elemental antimony and sulfur. Sb2S3 thin films were deposited on unheated glass substrates by one step thermal evaporation and annealed under vacuum atmosphere for 2 hours at different temperatures 150, 200 and 250 °C. Different characterization techniques were used to better understand the behavior of the Sb2S3 material. X-ray diffraction (XRD) and Raman spectroscopy confirmed the formation of pure Sb2S3 powder with lattice parameters a = 11.07 Å, b = 11.08 Å and c = 3.81 Å. The effect of vacuum annealing temperature on the properties of the films was studied. XRD analysis revealed that as-deposited and annealed films at 150ºC were amorphous in nature whereas those annealed at T ≥ 200°C were polycrystalline with a preferred orientation along (201) plane. The crystallite size of the polycrystalline films showed a decrease from 75.8 to 62.9 nm with the increase of the annealing temperature from 200 to 250 °C. The Raman analysis showed several peaks corresponding to the stibnite Sb2S3 phase. The surface morphology of the films was examined by atomic force microscopy (AFM). The surface roughness decreases slightly as the transformation from the amorphous to the crystalline phase occurs. The chemical compositions of Sb2S3 films were analyzed by energy dispersive X-ray spectroscopy (EDS), revealing that all films were Sb-rich. The optical parameters were estimated from the transmittance and reflectance spectra recorded by UV-Vis spectroscopy. A reduction in the direct band gap energy from 2.12 to 1.70 eV with the increase of annealing temperature was also found.

Electrical Properties of Multilayer Synthesized CuInSi Thin Film

2011 ◽  
Vol 383-390 ◽  
pp. 822-825
Author(s):  
Ping Luan ◽  
Jian Sheng Xie ◽  
Jin Hua Li
Keyword(s):  
Thin Film ◽  
Crystal Structure ◽  
Thin Films ◽  
Electrical Properties ◽  
Annealing Temperature ◽  
Time Effect ◽  
X Ray Diffraction ◽  
Testing Instrument ◽  
X Ray ◽  
Conductivity Type

Using magnetron sputtering technology, the CuInSi thin films were prepared by multilayer synthesized method. The structure of CuInSi films were detected by X-ray diffraction(XRD), the main crystal phase peak is at 2θ=42.458°; The resistivity of films were measured by SDY-4 four-probe meter; The conductive type of the films were tested by DLY-2 conductivity type testing instrument. The results show that the annealing temperature and time effect on the crystal resistivity and crystal structure greatly.

Characterization of Dielectric Properties of Alkoxy-Derived (Y,Yb)MnO3 Ferroelectrics/Insulator Stacking Layers

2006 ◽  
Vol 301 ◽  
pp. 65-70 ◽  
Author(s):  
Kazuyuki Suzuki ◽  
Kiyotaka Tanaka ◽  
Tatsuo Kimura ◽  
Kaori Nishizawa ◽  
Takeshi Miki ◽  
...  
Keyword(s):  
Thin Films ◽  
Dielectric Properties ◽  
Dielectric Property ◽  
Surface Morphology ◽  
Insulator Layer ◽  
Surface Smoothness ◽  
Y2o3 Layer ◽  
Mno3 Film ◽  
Mfis Structure

The (Y,Yb)MnO3 films were crystallized on Y2O3 layers using alkoxy-derived precursor solutions. As a result of investigation of the effect of the Y2O3 layer on the dielectric properties of the (Y,Yb)MnO3/Y2O3/Si, the crystallographic properties such as the orientation and surface morphology of the (Y,Yb)MnO3 thin films depended on the crystallographic appearance of the insulator layer. Following that, the dielectric properties of the MFIS structures varied. For the construction of excellent MFIS structure, the improvement of the orientation, crystallinity, and surface smoothness of the (Y,Yb)MnO3 film by the optimization of the microstructure and dielectric property of the insulator is necessary.

Sign in / Sign up

Export Citation Format

Share Document