Research on the Dyeing Property of Natural Food Pigments on Cotton Fabric

2012 ◽  
Vol 441 ◽  
pp. 57-60
Author(s):  
Xia Zhu ◽  
Qing Tao Meng
Keyword(s):  
Cotton Fabric ◽  
Cotton Fabrics ◽  
Natural Food ◽  
Dyeing Property ◽  
Washing Fastness ◽  
Pre Treatment ◽  
Mordant Dyeing ◽  
Color Depth

t is pre-mordant dyeing. Dyeing property of Carmine, gardenia yellow and sodium copper chlorophyll on cotton fabrics which were pre-treated by metal mordant (FeSO4AlCl3 and ZnCl2 ) was studied. The reasonable pre-treatment was determined by comparing the color depth (K/S value) of dyed samples. And then, the dyed samples were treated with no-iron finishing resin 931-33 to fix the color. The result shows that the color depth of cotton fabric is greatly improved after determined pre-treatment, and the washing fastness is improved after color fixing.

Green natural dye from Buddleja officinalis and its ultrasonic dyeing on cotton fabric

2021 ◽  
Vol ahead-of-print (ahead-of-print) ◽  
Author(s):  
Guizhen Ke ◽  
Ziying Zhao ◽  
Chen Shuhui ◽  
Jianqiang Li
Keyword(s):  
Cotton Fabric ◽  
Ph Value ◽  
Cotton Fabrics ◽  
Natural Dye ◽  
Color Strength ◽  
Content Type ◽  
Washing Fastness ◽  
Uv Transmittance ◽  
Protection Capability ◽  
Ultrasonic Conditions

Purpose The purpose of this paper is to explore a new eco-friendly green textile dyeing. Natural plant Buddleja officinalis is traditionally used as yellow pigment addition in rice. It is worth developing its application and dyeing performance in cotton fabric. Design/methodology/approach Buddleja officinalis dried flower was extracted with ethanol aqueous. The extraction conditions including ethanol concentration, material to liquor ratio, extract time and temperature were optimized. Then cotton fabrics were dyed with Buddleja officinalis extraction under conventional and ultrasonic conditions. The effects of dyeing time, bath ratio, pH value of dyeing bath, dyeing temperature and mordants on K/S values were studied and the resulting color strength obtained by conventional and ultrasonic dyeing were compared. The ultraviolet (UV) transmittance of Buddleja officinalis dyed cotton fabric was also evaluated. Findings The color strength of the fabric dyed with Buddleja officinalis under ultrasonic conditions was higher than that under conventional conditions. Alum, Fe and Cu as simultaneous mordants improved the K/S value of the dyed cotton fabrics. Both washing fastness and rubbing fastness were fairly good in all Buddleja officinalis dyed cotton fabrics, washing fastness = 3–4 and rubbing fastness = 4. What’s more, the dyed cotton fabrics showed lower transmittance values as compared to undyed cotton fabrics and indicated potential UV protection capability. Practical implications Buddleja officinalis can be a new natural dye source for the ultrasonic dyeing of cotton fabric. Originality/value It is for the first time that Buddleja officinalis is used as a natural dye in cotton fabric dyeing with less water and the dyeing using ultrasound has been found to have an obvious improvement in the color strength and color-fastness.

Finishing Process of Modified Nano TiO2 Photocatalyst on Cotton

2012 ◽  
Vol 441 ◽  
pp. 320-325
Author(s):  
Li Ming Wang ◽  
Ying Ding ◽  
Yong Shen ◽  
Zai Sheng Cai
Keyword(s):  
Cotton Fabric ◽  
Breaking Strength ◽  
Crosslinking Agent ◽  
Cotton Fabrics ◽  
Polymerization Degree ◽  
Cure Process ◽  
Curing Conditions ◽  
Washing Fastness ◽  
Finishing Process ◽  
Tearing Strength

A series of modified nanoTiO2 photocatalysts, nanoPC, was applied to cotton fabrics through a pad-dry-cure process. The effect of nanoPC dosage, the ratio of nanoPC to crosslinking agent, and curing conditions on the degradation of formaldehyde were discussed. The optimal finishing process of cotton fabric with nanoPC was determined as follows: 1%~1.5% photocatalyst, curing at 130°C for 5 minutes. Cotton fabric treated with the above process demonstrated over 90% degradation of formaldehyde, good washing fastness and soft handle, as well as little loss in breaking strength, tearing strength and polymerization degree.

scholarly journals Colour Strength and Washing Fastness Properties of Cotton Fabric Dyed with Kasunda Flower Extract

2020 ◽  
Vol 8 (5) ◽  
pp. 2019-2022
Keyword(s):  
Cotton Fabric ◽  
Cotton Fabrics ◽  
Natural Dyes ◽  
Chemical Processing ◽  
Fastness Properties ◽  
Washing Fastness ◽  
Textile Materials ◽  
Flower Extract ◽  
Colour Strength ◽  
The One

Colouration of textile materials is most important step in whole chemical processing of textiles department. There are various sources of obtain colours/dyes for the application. Natural dyes are the one of the emerging area in the field of dyeing of textile materials due to their eco-friendly in nature. In the present study the kasunda flower powder is used as a dye along with the mordants, which improves the dye up take and colour strength. The kasunda flower powder and natural mordants were applied in different concentrations to cotton fabrics and measured the colour strength in terms of K/S and washing fastness properties.

scholarly journals Established an eco-friendly cotton fabric treating process with enhancing anti-wrinkle performance

2021 ◽  
Vol 16 ◽  
pp. 155892502110034
Author(s):  
Xiongfang Luo ◽  
Pei Cheng ◽  
Wencong Wang ◽  
Jiajia Fu ◽  
Weidong Gao
Keyword(s):  
Tensile Strength ◽  
Citric Acid ◽  
Cotton Fabric ◽  
Crosslinking Agent ◽  
Cost Effective ◽  
Waterborne Polyurethane ◽  
Cotton Fabrics ◽  
Wrinkle Resistance ◽  
Before And After ◽  
Strength Retention

This study establishes an eco-friendly anti-wrinkle treating process for cotton fabric. Sodium hydroxide-liquid ammonia pretreatment followed by 6% (w/w) PU100 adding citric acid pad-cure-dry finishing. In this process, citric acid (CA) was used as the fundamental crosslinking agent during finishing because it is a non-formaldehyde based, cost-effective and well wrinkle resistance agent. Environmental-friendly waterborne polyurethane (WPU) was used as an additive to add to the CA finishing solution. Six commercial WPUs were systematically investigated. Fabric properties like wrinkle resistance, tensile strength retention, whiteness, durable press, softness, and wettability were well investigated. Fourier transform infrared spectra and X-ray diffraction spectra were also measured and discussed before and after adding waterborne polyurethane. Tentative mechanism of the interaction among the WPU, CA, and modified cotton fabrics is provided. The effect of cotton fabric pretreatment on fabric performance was also investigated. After the eco-process’s treatment, the fabric wrinkle resistant angle was upgraded to 271 ± 7°, tensile strength retention was maintained at 66.77% ± 3.50% and CIE whiteness was elevated to 52.13 ± 3.21, which are much better than the traditional CA anti-wrinkle finishing based on mercerized cotton fabrics. This study provides useful information for textile researchers and engineers.

Durable Antibacterial Finish on Cotton Fabrics with PAMAM/Ag+

2011 ◽  
Vol 332-334 ◽  
pp. 77-80 ◽  
Author(s):  
Chuan Jie Zhang ◽  
Hong Yang ◽  
Yun Liu ◽  
Ping Zhu
Keyword(s):  
Cotton Fabric ◽  
Antibacterial Agent ◽  
Antibacterial Property ◽  
Breaking Strength ◽  
Antibacterial Properties ◽  
Pamam Dendrimers ◽  
Cotton Fabrics ◽  
E Coli ◽  
Strength Retention ◽  
Better Than

Cotton fabric with excellent antibacterial properties was obtained by treated with polyamide-amine (PAMAM) dendrimers as a carrier and silver nitrate as an antibacterial agent. The antibacterial cotton fabrics were prepared by the methods of one-bath process and two-bath process. Antibacterial activity of cotton fabrics treated by two different methods was good, but the antibacterial durability of cotton fabric treated with two-bath process was better than that treated with one-bath process. After 50 washing cycles, cotton fabric treated with two-bath process still had good antibacterial property and its inhibitory rate to Gram-positive S. aureus and Gram-negative E. coli was over 99 %. It was found that the breaking strength retention of finished cotton fabrics was 85.83 % and the decrease of cotton fabrics’ whiteness index was about 15 %.

Study on the Enzyme Desizing Process for Cotton Fabric Using Ultrasonication

2011 ◽  
Vol 331 ◽  
pp. 261-264 ◽  
Author(s):  
Qi Ming Zhao ◽  
Shan Yan Zhang
Keyword(s):  
Cotton Fabric ◽  
Ph Value ◽  
Orthogonal Experiment ◽  
Research Result ◽  
Strength Loss ◽  
Cotton Fabrics ◽  
Optimum Process ◽  
Process Conditions ◽  
Fabric Strength ◽  
Enzyme Dosage

The auxiliary devices of ultrasonic treatment was designed and manufactured. The cotton fabric was desized using 2000L desizing enzyme with the conventional enzyme desizing process and ultrasonic enzyme desizing process respectively. Through the orthogonal experiment, the optimum process conditions of conventional enzyme desizing process and ultrasonic enzyme desizing process were determined. For the conventional enzyme desizing process, the optimized desizing conditions of cotton fabrics were: desizing enzyme dosage was 1.5g/l, temperature was 80°C, PH value was 6, and time was 60mins. The optimum process conditions of ultrasonic enzyme desizing process were: desizing enzyme dosage was 1.5g/l, temperature was 50°C, PH value was 6 and time was 45minutes. The research result indicates that, under the same desizing condition, ultrasonication can improve the desizing percentage and whiteness of cotton fabric, but the fabric strength loss increases slightly. And for the same required desizing percentage, the ultrasonic enzyme desizing process saved time and reduced the temperature of experiments compared with traditional enzyme desizing process

Smart control of cotton fabric comfort by cross-linking thermo-responsive poly(2-(2-methoxyethoxy) ethoxyethyl methacrylate-co-ethylene glycol methacrylate)

2016 ◽  
Vol 87 (13) ◽  
pp. 1620-1630 ◽  
Author(s):  
Yangyi Chen ◽  
Jie An ◽  
Qi Zhong ◽  
Peter Müller-Buschbaum ◽  
Jiping Wang
Keyword(s):  
Ethylene Glycol ◽  
Cotton Fabric ◽  
Random Copolymer ◽  
Cotton Fabrics ◽  
Molar Ratio ◽  
Cross Linking ◽  
Glycol Methacrylate ◽  
Moisture Permeability ◽  
Smart Control ◽  
Fabric Comfort

The smart control of cotton fabric comfort by cross-linking thermo-responsive random copolymer is investigated. The monomers 2-(2-methoxyethoxy) ethoxyethyl methacrylate (MEO2MA) and ethylene glycol methacrylate (EGMA) with a molar ratio of 17:3 are selected to synthesize the thermo-responsive random copolymer poly(2-(2-methoxyethoxy) ethoxyethyl methacrylate- co-ethylene glycol methacrylate), abbreviated as P(MEO2MA- co-EGMA). By using citric acid as a cross-linking agent, the obtained P(MEO2MA- co-EGMA) is successfully immobilized onto cotton fabrics. Smart control is achieved from the thermo-responsive behavior of the copolymer. Cross-linked P(MEO2MA- co-EGMA) will collapse when the ambient temperature exceeds its transition temperature. Therefore, the formerly compact P(MEO2MA- co-EGMA) layer will switch to a porous structure, and the air/moisture permeability of the textiles is enhanced. As the comfort of the textiles is closely related to the air/moisture permeability, a smart control of the cotton fabric comfort can be realized. In addition, the softness of cotton fabrics with and without thermo-responsive polymers does not show a prominent change, even when the applied solution concentration is as high as 16% (wt%). On the contrary, the stiffness of the cotton fabric coated with poly( N-isopropylacrylamide) (PNIPAM) is significantly higher than the original cotton fabric, indicating that homo PNIPAM is less suitable for textiles used in daily lives. Moreover, the whiteness and mechanical properties are studied and stay unchanged after cross-linking. As a consequence, the introduction of P(MEO2MA- co-EGMA) into textiles can provide textiles with smart control of cotton comfort, and it will not influence the wearabilities of the textiles.

Alkali Pre-Treatment Dyeing Technology for Hemp/Cotton/Polyester Knitted Fabric

2014 ◽  
Vol 915-916 ◽  
pp. 871-874 ◽  
Author(s):  
Xian Ping Zeng ◽  
Jin Fa Liu
Keyword(s):  
Cotton Fabric ◽  
Alkali Treatment ◽  
Orthogonal Experiment ◽  
Optimum Process ◽  
Knitted Fabric ◽  
Polyester Mesh ◽  
Liquor Ratio ◽  
Pre Treatment ◽  
C 50

In this paper, the hemp / cotton / polyester mesh knitted fabric (Han / C / T) is treated by alkali treatment, conventional dyeing and alkali pre-treatment dyeing. We have obtained the conclusion that alkali treatment improves the dyeing effect. Alkali pre-treatment dyeing was done after alkali treatment. The fabric dyeing effect is improved obviously. The optimum process come from orthogonal experiment (dyes 2.5% owf, Na2SO4 :30g/L, Na2CO3:10g/L, liquor ratio (1:50) and 90°C×50 min). Through this optimum process, dyeing effect for hemp / cotton / polyester mesh knitted fabric is close to the pure cotton fabric dyeing effect.

Development of thermally stable and hygienic colored cotton fabric made by treatment with natural coconut shell extract

2017 ◽  
Vol 48 (1) ◽  
pp. 87-118 ◽  
Author(s):  
MD Teli ◽  
Pintu Pandit
Keyword(s):  
Fourier Transform ◽  
Flame Retardant ◽  
Cotton Fabric ◽  
Oxygen Index ◽  
Fourier Transform Infrared ◽  
Cotton Fabrics ◽  
Energy Dispersive ◽  
Coconut Shell ◽  
Flame Resistance ◽  
Limiting Oxygen Index

As far as the value addition of textile is concerned, flame retardancy of textile materials is considered to be one of the most important properties in textile finishing by both industries as well as academic researchers. Flame-retardant property with thermal stability was imparted to cotton by using green coconut ( Cocos nucifera Linn) shell extract, a natural waste source of coconut. Coconut shell extract was analyzed by high-performance liquid chromatography, Fourier transform infrared spectroscopy, energy-dispersive spectrometry and its phytochemical analysis was also carried out. The coconut shell extract (acidic after extraction) was applied in three different pH (acidic, neutral, and alkaline) conditions to the cotton fabric. Flame-retardant properties of the untreated and the treated cotton fabrics were analyzed by limiting oxygen index and vertical flammability. The study showed that all the treated fabrics had good flame resistance property compared to that of the untreated fabric. The limiting oxygen index value was found to increase by 72.2% after application of the coconut shell extract from alkaline pH. Pyrolysis and char formation behavior of the concerned fabrics were studied using thermogravimetric analysis and differential scanning calorimetric analysis in a nitrogen atmosphere. The physicochemical composition of the untreated and coconut shell extract treated cotton fabrics were analyzed by attenuated total reflection–Fourier transform infrared, scanning electron microscope, and energy-dispersive X-ray spectroscopy. Also, treated cotton fabric showed natural brown color and antibacterial property against both Gram-positive and Gram-negative bacteria. The durability of the flame-retardant functionality to washing with soap solution has also been studied and reported in this paper.

scholarly journals Preparation and Characterization of Some Nanometal Oxides Using Microwave Technique and Their Application to Cotton Fabrics

2015 ◽  
Vol 2015 ◽  
pp. 1-9 ◽  
Author(s):  
M. Gouda ◽  
A. Aljaafari ◽  
Y. Al-Fayz ◽  
W. E. Boraie
Keyword(s):  
Electron Microscopy ◽  
Particle Size ◽  
Cotton Fabric ◽  
Metal Salt ◽  
Metal Oxide Nanoparticles ◽  
High Energy ◽  
Cotton Fabrics ◽  
Oxide Nanoparticles ◽  
Limiting Oxygen Index ◽  
Cobalt Oxide Nanoparticles

The objective of this paper is the synthesis of some nanometal oxides via microwave irradiation technique and their application to augment multifunctional properties of cotton fabric. Cotton fabrics containing nanometal oxides were prepared via a thiol-modification of cotton fabric samples and then dipped into the metal salt solutions precursors and transferred to the microwave oven. The surface morphology and quantitative analysis of the obtained modified cotton fabrics containing nanometal oxides were studied by scanning electron microscopy coupled with high energy dispersive X-ray (SEM-EDX). The shape and distribution of nanometal oxide inside the fabric samples were analyzed by transmission electron microscopy of cross-section fabric samples. The iron oxide nanoparticles had a nanosphere with particle size diameter 15–20 nm, copper oxide nanoparticles had a nanosphere with particle size diameter 25–30 nm, and cobalt oxide nanoparticles had a nanotube-like shape with a length of 100–150 nanometer and a diameter of ~58 nanometer, whereas the manganese oxide nanoparticles had a linear structure forming nanorods with a diameter of 50–55 nanometer and a length of 70–80 nanometers. Antibacterial activity was evaluated quantitatively against gram-positive bacteria such asStaphylococcus aureusand gram-negative bacteria such asEscherichia coli, UV-protection activity was analyzed using UV-DRS spectroscopy, and flame retardation of prepared fabric samples was evaluated according to the limiting oxygen index (LOI). Results revealed that the prepared fabric sample containing nanometal oxide possesses improved antibacterial, LOI, and UV-absorbing efficiency. Moreover, the metal oxide nanoparticles did not leach out the fabrics by washing even after 30 laundering washing cycles.

Sign in / Sign up

Export Citation Format

Share Document