The adhesion of thermoplastic fibre composites

1992 ◽  
Vol 338 (1649) ◽  
pp. 83-112 ◽  
Keyword(s):  
Photoelectron Spectroscopy ◽  
Fibre Composite ◽  
Critical Value ◽  
Surface Polarity ◽  
Engineering Structures ◽  
Angle Measurements ◽  
Fibre Composites ◽  
Before And After ◽  
Polar Force ◽  
Composite Substrates

Fibre composites based upon thermoplastic polymeric matrices containing continuous fibres of carbon or ‘ Kevlar' are being increasingly used in engineering structures. Engineering applications frequently require that they be joined to components fabricated from similar fibre composites, or to other types of materials, and the use of structural adhesives, typically based upon epoxy resins, offers many advantages compared with other methods of joining. The present paper describes in detail the mechanics and mechanisms of the adhesion of thermoplastic fibre composites. The surface topography and chemistry of the composites have been characterized using contact angle measurements and X-ray photoelectron spectroscopy, both before and after using various surface treatments. Joints have then been prepared using epoxy adhesives and the adhesive fracture energies, Gc, of the joints have been measured. Two major aspects of the observed results, with wide applicability to many adhesion problems, have been analysed in detail. First, the need to apply a critical intensity of surface treatment to the thermoplastic fibre composite to prevent interfacial failure, and hence give relatively high values of G has been interpreted by relating the chemical composition of the surface of the composite to the corresponding value of the polar force component of the surface free energy. It is thereby shown that the fundamental requirement is that a critical value of the surface polarity has to be attained. Secondly, after this critical value is reached, it is shown that the locus of joint failure may then be accurately predicted from a knowledge of the stress field in the joint and the experimentally measured interlaminar fracture stress of the fibre composite substrates.

scholarly journals Effect of sizing agent on interfacial properties of carbon fiber-reinforced PMMA composite

2021 ◽  
Vol 30 ◽  
pp. 2633366X2097865
Author(s):  
Li Jian
Keyword(s):  
Shear Strength ◽  
Surface Treatment ◽  
Photoelectron Spectroscopy ◽  
Resin Composite ◽  
Contact Angles ◽  
Static Contact ◽  
Before And After ◽  
C Value ◽  
Interlayer Shear Strength ◽  
Pmma Resin

The surface treatment of carbon fibers (CFs) was carried out using a self-synthesized sizing agent. The effects of sizing agent on the surface of CFs and the interface properties of CF/polymethyl methacrylate (PMMA) composites were mainly studied. Scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and static contact angle were used to compare and study the CFs before and after the surface treatment, including surface morphology, surface chemical element composition, and wettability of the surface. The influence of sizing agent on the mechanical properties of CF/PMMA resin composite interface was investigated. The results show that after sizing treatment, the CF surface O/C value increased by 35.1% and the contact angles of CF and resin decreased by 16.2%. The interfacial shear strength and interlayer shear strength increased by 12.6%.

scholarly journals Synthesis of Novel Arginine-Based Flame Retardant and Its Application in Lyocell Fabric

Molecules ◽  
2021 ◽  
Vol 26 (12) ◽  
pp. 3588
Author(s):  
Jiayi Chen ◽  
Yansong Liu ◽  
Jiayue Zhang ◽  
Yuanlin Ren ◽  
Xiaohui Liu
Keyword(s):  
Fourier Transform ◽  
Heat Release ◽  
Flame Retardant ◽  
Photoelectron Spectroscopy ◽  
Fourier Transform Infrared ◽  
Ftir Analysis ◽  
Excellent Thermal Stability ◽  
X Ray ◽  
Cone Calorimeter Test ◽  
Before And After

Lyocell fabrics are widely applied in textiles, however, its high flammability increases the risk of fire. Therefore, to resolve the issue, a novel biomass-based flame retardant with phosphorus and nitrogen elements was designed and synthesized by the reaction of arginine with phosphoric acid and urea. It was then grafted onto the lyocell fabric by a dip-dry-cure technique to prepare durable flame-retardant lyocell fabric (FR-lyocell). X-ray photoelectron spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FTIR) analysis demonstrated that the flame retardant was successfully introduced into the lyocell sample. Thermogravimetric (TG) and Raman analyses confirmed that the modified lyocell fabric featured excellent thermal stability and significantly increased char residue. Vertical combustion results indicated that FR-lyocell before and after washing formed a complete and dense char layer. Thermogravimetric Fourier-transform infrared (TG-FTIR) analysis suggested that incombustible substances (such as H2O and CO2) were produced and played a significant fire retarding role in the gas phase. The cone calorimeter test corroborated that the peak of heat release rate (PHRR) and total heat release (THR) declined by 89.4% and 56.4%, respectively. These results indicated that the flame retardancy of the lyocell fabric was observably ameliorated.

scholarly journals Change in Interface Characteristics of ITO Modified with n-decyltrimethoxysilane

Crystals ◽  
2020 ◽  
Vol 10 (8) ◽  
pp. 645
Author(s):  
Myung-Gyun Baek ◽  
Johng-Eon Shin ◽  
Dong-Hyun Hwang ◽  
Sung-Hoon Kim ◽  
Hong-Gyu Park ◽  
...  
Keyword(s):  
Contact Angle ◽  
Work Function ◽  
Indium Tin Oxide ◽  
Photoelectron Spectroscopy ◽  
Deposition Time ◽  
Interfacial Properties ◽  
Average Roughness ◽  
Light Emitting ◽  
Force Microscopy ◽  
Angle Measurements

Herein, we examined changes in the interfacial properties of organic light-emitting diodes when n-decyltrimethoxysilane (CH3SAM) was deposited on the surface of an indium tin oxide (ITO) electrode for various deposition times. It was revealed that the interfacial properties varied with deposition time. As the latter increased, so did the measured value of the contact angle, and ITO substrate exhibited a lower wettability. The contact angle measurements for bare ITO at 1, 10, 30, and 90 min were 57.41°, 63.43°, 73.76°, 81.47°, respectively, and the highest value obtained was 93.34°. In addition, the average roughness and work function of the ITO were measured using atomic force microscopy and X-ray photoelectron spectroscopy. As the deposition time of CH3SAM on the ITO substrates increased, it was evident that the former was well aligned with the latter, improving surface modification. The work function of CH3SAM, modified on the ITO substrates, improved by approximately 0.11 eV from 5.05–5.16 eV. The introduction of CH3SAM to the ITO revealed the ease of adjustment of the characteristics of ITO substrates.

Hybrid silica micro and PDDA/nanoparticles-reinforced carbon fibre composites

2016 ◽  
Vol 51 (6) ◽  
pp. 783-795 ◽  
Author(s):  
Júlio C Santos ◽  
Luciano MG Vieira ◽  
Túlio H Panzera ◽  
André L Christoforo ◽  
Marco A Schiavon ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Carbon Fibre ◽  
Silica Nanoparticles ◽  
Fibre Composite ◽  
Flexural Modulus ◽  
Specific Chemical ◽  
Diallyldimethylammonium Chloride ◽  
Fibre Composites ◽  
Carbon Fibre Composites ◽  
Hybrid Carbon

The work describes the manufacturing and testing of novel hybrid epoxy/carbon fibre composites with silica micro and poly-diallyldimethylammonium chloride-functionalised nanoparticles. A specific chemical dispersion procedure was applied using the poly-diallyldimethylammonium chloride to avoid clustering of the silica nanoparticles. The influence of the various manufacturing parameters, particles loading, and mechanical properties of the different phases has been investigated with a rigorous Design of Experiment technique based on a full factorial design (2131). Poly-diallyldimethylammonium chloride-functionalised silica nanoparticles were able to provide a homogenous dispersion, with a decrease of the apparent density and enhancement of the mechanical properties in the hybrid carbon fibre composites. Compared to undispersed carbon fibre composite laminates, the use of 2 wt% functionalised nanoparticles permitted to increase the flexural modulus by 47% and the flexural strength by 15%. The hybrid carbon fibre composites showed also an increase of the tensile modulus (9%) and tensile strength (5.6%).

Oxidation of Alloy-X in Subcritical, Transition, and Supercritical Water

CORROSION ◽  
10.5006/3881 ◽  
2021 ◽  
Author(s):  
Zachary Karmiol ◽  
Dev Chidambaram
Keyword(s):  
Supercritical Water ◽  
Photoelectron Spectroscopy ◽  
Focused Ion Beam ◽  
Elevated Temperatures ◽  
Subcritical Water ◽  
Ion Beam ◽  
X Ray Diffraction ◽  
X Ray ◽  
Nickel Based Superalloy ◽  
Before And After

This work investigates the oxidation of a nickel based superalloy, namely Alloy X, in water at elevated temperatures: subcritical water at 261°C and 27 MPa, the transition between subcritical and supercritical water at 374°C and 27 MPa, and supercritical water at 380°C and 27 MPa for 100 hours. The morphology of the sample surfaces were studied using scanning electron microscopy coupled with focused ion beam milling, and the surface chemistry was investigated using X-ray diffraction, Raman spectroscopy, energy dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy before and after exposure studies. Surfaces of all samples were identified to comprise of a ferrite spinel containing aluminum.

Characterization of X-ray irradiated graphene oxide coatings using X-ray diffraction, X-ray photoelectron spectroscopy, and atomic force microscopy

2013 ◽  
Vol 28 (2) ◽  
pp. 68-71 ◽  
Author(s):  
Thomas N. Blanton ◽  
Debasis Majumdar
Keyword(s):  
Atomic Force Microscopy ◽  
Graphene Oxide ◽  
Photoelectron Spectroscopy ◽  
High Energy ◽  
X Ray Diffraction ◽  
Carbon Phase ◽  
X Ray ◽  
Force Microscopy ◽  
Atomic Force ◽  
Before And After

In an effort to study an alternative approach to make graphene from graphene oxide (GO), exposure of GO to high-energy X-ray radiation has been performed. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM) have been used to characterize GO before and after irradiation. Results indicate that GO exposed to high-energy radiation is converted to an amorphous carbon phase that is conductive.

scholarly journals Enhanced removal of hexavalent chromium by different acid-modified biochar derived from corn straw: behavior and mechanism

2020 ◽  
Vol 81 (10) ◽  
pp. 2270-2280
Author(s):  
Yonggang Xu ◽  
Tianxia Bai ◽  
Yubo Yan ◽  
Yunfeng Zhao ◽  
Ling Yuan ◽  
...  
Keyword(s):  
Photoelectron Spectroscopy ◽  
Hydrogen Ion ◽  
Corn Straw ◽  
Order Model ◽  
Freundlich Model ◽  
X Ray ◽  
Modified Biochar ◽  
Before And After ◽  
Pseudo Second Order ◽  
Kinetics Of

Abstract It is of great significance to remove Cr(VI) from water as a result of its high toxicity. Biochar from corn straw was modified by different acids (HNO3, H2SO4 and H3PO4) to remove Cr(VI) from aqueous solution. To estimate the removal mechanisms of Cr(VI) by the acid-modified biochars, batch experiments were performed in the light of contact time, Cr(VI) concentration, and pH, and the characteristics of acid-modified biochars before and after Cr(VI) adsorption were investigated by Fourier transform infrared spectra (FTIR) and X-ray photoelectron spectroscopy (XPS). The adsorption kinetics of Cr(VI) by acid-modified biochars were consistent with the pseudo-second-order model, and the adsorption isotherm obeyed the Freundlich model. Furthermore, the acid- modified biochars could supply more oxygen-containing functional groups (-COOH and -OH) as electron donor (e−) and hydrogen ion (H+) to enhance the reduction of Cr(VI) to Cr(III), resulting in enhanced removal of Cr(VI). HNO3-modified biochar exhibited the highest removal efficiency of Cr(VI). In general, the acid modifition of biochar was an effective method to increase the removal of Cr(VI).

scholarly journals Synthesis of Nanoscale Zerovalent Iron (nZVI) Supported on Biochar for Chromium Remediation from Aqueous Solution and Soil

2019 ◽  
Vol 16 (22) ◽  
pp. 4430 ◽  
Author(s):  
Haixia Wang ◽  
Mingliang Zhang ◽  
Hongyi Li
Keyword(s):  
Aqueous Solution ◽  
Photoelectron Spectroscopy ◽  
Zero Valent Iron ◽  
Zerovalent Iron ◽  
X Ray ◽  
Nanoscale Zerovalent Iron ◽  
Before And After ◽  
Pseudo Second Order ◽  
Xrd Patterns ◽  
Co Precipitation

Maize straw biochar-supported nanoscale zero-valent iron composite (MSB-nZVI) was prepared for efficient chromium (Cr) removal through alleviating the aggregation of zero-valent iron particles. The removal mechanism of MSB-nZVI was investigated by scanning electron microscopy with energy dispersive X-ray (SEM-EDX), X-ray diffractometry (XRD), and X-ray photoelectron spectroscopy (XPS). Cr(VI) removal from aqueous solution by MSB-nZVI was greatly affected by pH and initial concentration. The removal efficiency of Cr(VI) decreased with increasing pH, and the removal kinetics followed the pseudo-second-order model. XRD patterns of MSB-nZVI before and after reaction showed that reduction and precipitation/co-precipitation (FeCr2O4, Fe3O4, Fe2O3) occurred with the conversion of Cr(VI) to Cr(III) and Fe(0) to Fe(II)/Fe(III). The produced precipitation/co-precipitation could be deposited on the MSB surface rather than being only coated on the surface of nZVI particles, which can alleviate passivation of nZVI. For remediation of Cr(VI)-contaminated saline–alkali soil (pH 8.6–9.0, Cr 341 mg/kg), the released amount of Cr(VI) was 70.7 mg/kg, while it sharply decreased to 0.6–1.7 mg/kg at pH 4.0–8.0, indicating that the saline–alkali environment inhibited the remediation efficiency. These results show that MSB-nZVI can be used as an effective material for Cr(VI) removal from aqueous solution and contaminated soil.

Incremental Damage Development in a 3D Woven Carbon Fibre Composite

2007 ◽  
Vol 15 (7) ◽  
pp. 521-533
Author(s):  
S. King ◽  
G. Stewart ◽  
A.T. McIlhagger ◽  
J.P. Quinn
Keyword(s):  
Carbon Fibre ◽  
Fibre Composite ◽  
Weight Ratio ◽  
Matrix Cracking ◽  
Limiting Factors ◽  
Damage Development ◽  
Carbon Fibre Composite ◽  
Damage Initiation ◽  
Fibre Composites ◽  
Carbon Fibre Composites

Interest in 3D woven carbon fibre composites has increased within industries such as aerospace, automotive and marine, due to their high strength to weight ratio, their increased tailorability and their capacity to be manufactured into near net shape preforms, thereby reducing parts count, assembly time, labour intensity and costs. It is vital that critical areas of concern such as damage (and in particular damage initiation and development) are studied and understood, thereby reducing the limiting factors to their acceptance. The damage initiation and subsequent intervals of development for ILSS (Interlaminar Shear Strength) were determined experimentally. Particular focus is paid to the significance of binder edge and binder middle testing and the influence of through-the-thickness (T-T-T) reinforcement in relation to damage types and development. Control samples for binder edge and binder middle loading locations were tested to failure as a means of determining an average point of failure, allowing the generation of testing intervals. The performance and architecture of samples from each incremental interval were characterised using a combination of graphical analysis and optical microscopy with the aid of dye-penetrant to highlight fibre damage and matrix cracking. Samples displayed specific damage initiation points, thus allowing the generation of a damage guide relating to applied force. In addition, the results imply that a relationship exists between the location of applied load and subsequent damage, thus showing the significant influence played by the T-T-T binder loading location on damage development within 3D woven carbon fibre composites. Some of the preliminary data shown in this paper was presented at IMC23 at the University of Ulster, UK in August 2006 and at Texcomp 8 in Nottingham, UK October 2006.

scholarly journals Adsorption of Lead (II) from Aqueous Solution with High Efficiency by Hydrothermal Biochar Derived from Honey

2020 ◽  
Vol 17 (10) ◽  
pp. 3441 ◽  
Author(s):  
Bo Wang ◽  
Jie Yu ◽  
Hui Liao ◽  
Wenkun Zhu ◽  
Pingping Ding ◽  
...  
Keyword(s):  
Aqueous Solution ◽  
Photoelectron Spectroscopy ◽  
High Efficiency ◽  
Raw Material ◽  
Before And After ◽  
Initial Ph ◽  
Carboxylic Groups ◽  
Langmuir Isotherm Model ◽  
Pseudo Second Order ◽  
Natural Honey

A novel natural honey hydrothermal biochar (HHTB) was prepared using natural honey as raw material. The as-prepared adsorbent was applied to adsorb Pb2+ from aqueous solution and characterized by scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy to investigate the structure and morphology change of the adsorbent before and after Pb2+ adsorption. The influence of the pH, initial Pb2+ concentration, temperature, and contact time on the adsorption of Pb2+ was systematically investigated. The results revealed that the adsorption capacity for Pb2+ is up to 133.2 mg·g−1 at initial pH of 5.0 and adsorption temperature of 298 K. Meanwhile, the adsorption of Pb2+ on HHTB can be well fitted by the pseudo-second-order model and Langmuir isotherm model. The adsorbent had great selectivity for Pb2+ from the aqueous solution containing coexisting ions including Cd2+, Co2+, Cr3+, Cu2+, Ni2+ and Zn2+. Furthermore, the adsorption of Pb2+ on HHTB was attributed to complexation coordination, where it involved hydroxyl and carboxylic groups on HHTB in the process of adsorption of Pb2+.

Sign in / Sign up

Export Citation Format

Share Document