scholarly journals Analysis Of The Mechanical Properties Of Brick With The Addition Of Cotton

2021 ◽  
Vol 4 (2) ◽  
pp. 36
Author(s):  
Ety Jumiati ◽  
Nita Zahara Nasution ◽  
Abdul Halim Daulay
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fracture Strength ◽  
C 30

<p align="center"><strong><em>Abstract</em></strong></p><p>It has been done making bricks with the addition of cotton.Variations in the mixture of cement, sand and cotton are sample A (30%:70% :0%), sample B (30%:69,5%:0,5%), sample C (30%:69%:1%), sample D (30%:68,5%:1,5%), Water Cement Factor of 0,5 and dry time one day. Characteristic of the tests carried out include: compressive strength and fracture strength.Analysis of the mechanical properties of the bricks produced in sample A with a compressive strength value = 28.81 kg/cm<sup>2</sup> and fracture strength value = 23.11kg/cm<sup>2</sup>, sample B with acompressive strength value = 26.85 kg/cm<sup>2</sup> and fracture strength value = 22.32 kg/cm<sup>2</sup>, sample C with a compressive strength value = 25.10 kg/cm<sup>2</sup> and fracture strength value = 15.09 kg/cm<sup>2</sup>, sample D with a compressive strength of 17.14 kg/ cm<sup>2</sup> and a fracture strength value 15.51kg/cm<sup>2</sup>. The bricks produced namely in sample B.</p><pre><strong><em>Keywords :</em></strong>Bricks, Cotton, and Cement</pre>

scholarly journals Effect of Deformation Conditions on Mechanical Properties of Zr-based Metallic Glasses

2020 ◽  
Vol 2 (2) ◽  
Author(s):  
Zhenxiang ZHAO ◽  
Chunyan LI ◽  
Fuping ZHU ◽  
Xinling LI ◽  
Shengzhong KOU
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Aspect Ratio ◽  
Plastic Strain ◽  
Strain Rate ◽  
Fracture Strength ◽  
Metallic Glasses ◽  
Room Temperature

In this paper, the effects of different strain rate(1×10-5 s-1, 5×10-5 s-1, 1×10-4 s-1, 5×10-4 s-1, 1×10-3 s-1) and aspect ratio(1:1, 1.5:1, 2:1, 2.5:1, 3:1) on mechanical properties of Zr-based metallic glasses at room temperature were investigated. The results indicate that as the strain rate increases, the plastic strain and compressive strength of the specimens gradually decrease. The specimen with the strain rate of 1×10-5 s-1 exhibits the higher plastic strain of 10.25 %, compressive strength of 2002 MPa and fracture strength of 1999 MPa. In addition, accompanied with the increase in aspect ratio, the plastic strain of the specimens declines from 25.42 % to 1.97 %, meanwhile, the compressive strength and fracture strength of the specimens also present declining trend.

Effect of combined drink cans and steel fibers on the impact resistance and mechanical properties of concrete

2020 ◽  
Vol 14 (2) ◽  
pp. 6734-6742
Author(s):  
A. Syamsir ◽  
S. M. Mubin ◽  
N. M. Nor ◽  
V. Anggraini ◽  
S. Nagappan ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Reinforced Concrete ◽  
Impact Resistance ◽  
Fiber Reinforced Concrete ◽  
Steel Fibers ◽  
Fiber Reinforced ◽  
Indirect Tensile ◽  
The Impact

This study investigated the combine effect of 0.2 % drink cans and steel fibers with volume fractions of 0%, 0.5%, 1%, 1.5%, 2%, 2.5% and 3% to the mechanical properties and impact resistance of concrete. Hooked-end steel fiber with 30 mm and 0.75 mm length and diameter, respectively was selected for this study.  The drinks cans fiber were twisted manually in order to increase friction between fiber and concrete. The results of the experiment showed that the combination of steel fibers and drink cans fibers improved the strength performance of concrete, especially the compressive strength, flexural strength and indirect tensile strength. The results of the experiment showed that the combination of steel fibers and drink cans fibers improved the compressive strength, flexural strength and indirect tensile strength by 2.3, 7, and 2 times as compare to batch 1, respectively. Moreover, the impact resistance of fiber reinforced concrete has increase by 7 times as compared to non-fiber concretes. Moreover, the impact resistance of fiber reinforced concrete consistently gave better results as compared to non-fiber concretes. The fiber reinforced concrete turned more ductile as the dosage of fibers was increased and ductility started to decrease slightly after optimum fiber dosage was reached. It was found that concrete with combination of 2% steel and 0.2% drink cans fibers showed the highest compressive, split tensile, flexural as well as impact strength.    

PEMANFAATAN KAYU AKASIA MANGIUM (Acacia mangium Willd) UNTUK MEBEL

2012 ◽  
Vol 4 (1) ◽  
pp. 1
Author(s):  
Djoko Purwanto
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Physical Properties ◽  
Treatment Process ◽  
Acacia Mangium ◽  
Physical And Mechanical Properties ◽  
Wood Fibers ◽  
Test Parameters ◽  
Mechanical And Physical Properties ◽  
Scale Scores

Timber Acacia mangium (Acacia mangium, Willd) for Furniture. The study aims to determine the mechanical and physical properties and the decorative value (color and fiber) wood of acacia mangium with using finishing materials. This type of finishing material used is ultran lasur natural dof ,ultran lasur classic teak, aqua politur clear dof, aqua politur akasia dan aqua politur cherry. After finishing the wood is stored for 3 months. Test parameters were observed, namely, physical and mechanical properties of wood, adhesion of finishing materials, color and appearance of the fiber, and timber dimensions expansion. The results showed that the mechanical physical properties of acacia wood qualified SNI. 01-0608-89 about the physical and mechanical properties of wood for furniture, air dry the moisture content from 13.78 to 14.89%, flexural strength from 509.25 to 680.50 kg/cm2, and compressive strength parallel to fiber 342.1 - 412.9 kg/cm2. Finishing the treatment process using five types of finishing materials can increase the decorative value (color and fiber) wood. Before finishing the process of acacia mangium wood has the appearance of colors and fibers and less attractive (scale scores 2-3), after finishing acacia wood fibers have the appearance of colors and interesting and very interesting (scale 4-5).Keywords: mangium wood, mechanical properties, decorative value, finishing, furniture.

Incorporation of Iraqi Rocks in the Production of Eco-Friendly Cement Mortar

2020 ◽  
Vol 38 (10A) ◽  
pp. 1522-1530
Author(s):  
Rawnaq S. Mahdi ◽  
Aseel B. AL-Zubidi ◽  
Hassan N. Hashim
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Compressive Strength ◽  
Water Absorption ◽  
Structural Properties ◽  
Mechanical Milling ◽  
Cement Mortar ◽  
Cement Mortars

This work reports on the incorporation of Flint and Kaolin rocks powders in the cement mortar in an attempt to improve its mechanical properties and produce an eco-friendly mortar. Flint and Kaolin powders are prepared by dry mechanical milling. The two powders are added separately to the mortars substituting cement partially. The two powders are found to improve the mechanical properties of the mortars. Hardness and compressive strength are found to increase with the increase of powders constituents in the cement mortars. In addition, the two powders affect water absorption and thermal conductivity of the mortar specimens which are desirable for construction applications. Kaolin is found to have a greater effect on the mechanical properties, water absorption, and thermal conductivity of the mortars than Flint. This behavior is discussed and analyzed based on the compositional and structural properties of the rocks powders.

scholarly journals Mechanical Behavior of Brick Masonry in an Acidic Atmospheric Environment

Materials ◽  
2019 ◽  
Vol 12 (17) ◽  
pp. 2694 ◽  
Author(s):  
Shansuo Zheng ◽  
Lihua Niu ◽  
Pei Pei ◽  
Jinqi Dong
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Acid Rain ◽  
Cement Mortar ◽  
Brick Masonry ◽  
Atmospheric Environment ◽  
Peak Strain ◽  
Lime Mortar ◽  
Attenuation Model

In order to evaluate the deterioration regularity for the mechanical properties of brick masonry due to acid rain corrosion, a series of mechanical property tests for mortars, bricks, shear prisms, and compressive prisms after acid rain corrosion were conducted. The apparent morphology and the compressive strength of the masonry materials (cement mortar, cement-lime mortar, cement-fly ash mortar, and brick), the shear behavior of the masonry, and the compression behavior of the masonry were analyzed. The resistance of acid rain corrosion for the cement-lime mortar prisms was the worst, and the incorporation of fly ash into the cement mortar did not improve the acid rain corrosion resistance. The effect of the acid rain corrosion damage on the mechanical properties for the brick was significant. With an increasing number of acid rain corrosion cycles, the compressive strength of the mortar prisms, and the shear and compressive strengths of the brick masonry first increased and then decreased. The peak stress first increased and then decreased whereas the peak strain gradually increased. The slope of the stress-strain curve for the compression prisms gradually decreased. Furthermore, a mathematical degradation model for the compressive strength of the masonry material (cement mortar, cement-lime mortar, cement-fly ash mortar, and brick), as well as the shear strength attenuation model and the compressive strength attenuation model of brick masonry after acid rain corrosion were proposed.

scholarly journals Experimental Analysis of the Mechanical Properties and Resistivity of Tectonic Coal Samples with Different Particle Sizes

Energies ◽  
2021 ◽  
Vol 14 (8) ◽  
pp. 2303
Author(s):  
Congyu Zhong ◽  
Liwen Cao ◽  
Jishi Geng ◽  
Zhihao Jiang ◽  
Shuai Zhang
Keyword(s):  
Mechanical Properties ◽  
Particle Size ◽  
Compressive Strength ◽  
Elastic Modulus ◽  
Uniaxial Compressive Strength ◽  
Coalbed Methane ◽  
Coal Sample ◽  
Fine Particles ◽  
Particle Sizes ◽  
Tectonic Coal

Because of its weak cementation and abundant pores and cracks, it is difficult to obtain suitable samples of tectonic coal to test its mechanical properties. Therefore, the research and development of coalbed methane drilling and mining technology are restricted. In this study, tectonic coal samples are remodeled with different particle sizes to test the mechanical parameters and loading resistivity. The research results show that the particle size and gradation of tectonic coal significantly impact its uniaxial compressive strength and elastic modulus and affect changes in resistivity. As the converted particle size increases, the uniaxial compressive strength and elastic modulus decrease first and then tend to remain unchanged. The strength of the single-particle gradation coal sample decreases from 0.867 to 0.433 MPa and the elastic modulus decreases from 59.28 to 41.63 MPa with increasing particle size. The change in resistivity of the coal sample increases with increasing particle size, and the degree of resistivity variation decreases during the coal sample failure stage. In composite-particle gradation, the proportion of fine particles in the tectonic coal sample increases from 33% to 80%. Its strength and elastic modulus increase from 0.996 to 1.31 MPa and 83.96 to 125.4 MPa, respectively, and the resistivity change degree decreases. The proportion of medium particles or coarse particles increases, and the sample strength, elastic modulus, and resistivity changes all decrease.

scholarly journals Preparation of Electric- and Magnetic-Activated Water and Its Influence on the Workability and Mechanical Properties of Cement Mortar

2021 ◽  
Vol 13 (8) ◽  
pp. 4546
Author(s):  
Kaiyue Zhao ◽  
Peng Zhang ◽  
Bing Wang ◽  
Yupeng Tian ◽  
Shanbin Xue ◽  
...  
Keyword(s):  
Magnetic Field ◽  
Mechanical Properties ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Cement Paste ◽  
Cement Mortar ◽  
Environmental Issues ◽  
Chemical Admixtures ◽  
Untreated Water ◽  
Alternating Voltage

Cement-based materials prepared with activated water induced by a magnetic field or electric field represent a possible solution to environmental issues caused by the worldwide utilization of chemical admixtures. In this contribution, electric- and magnetic-activated water have been produced. The workability and mechanical properties of cement mortar prepared with this activated water have been investigated. The results indicate that the pH and absorbance (Abs) values of the water varied as the electric and magnetic field changed, and their values increased significantly, exhibiting improved activity compared with that of the untreated water. In addition, activated water still retains activity within 30 min of the resting time. The fluidity of the cement paste prepared with electric-activated water was significantly larger than that of the untreated paste. However, the level of improvement differed with the worst performance resulting from cement paste prepared with alternating voltage activated water. In terms of mechanical properties, both compressive strength and flexural strength obtained its maximum values at 280 mT with two processing cycles. The compressive strength increased 26% as the curing time increased from 7 days to 28 days and flexural strength increased by 31%. In addition, through the introduction of magnetic-activated water into cement mortar, the mechanical strength can be maintained without losing its workability when the amount of cement is reduced.

scholarly journals The Effect of Different Types of Internal Curing Liquid on the Properties of Alkali-Activated Slag (AAS) Mortar

2021 ◽  
Vol 13 (4) ◽  
pp. 2407
Author(s):  
Guang-Zhu Zhang ◽  
Xiao-Yong Wang ◽  
Tae-Wan Kim ◽  
Jong-Yeon Lim ◽  
Yi Han
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Deionized Water ◽  
Internal Curing ◽  
Control Group ◽  
Alkali Activated Slag ◽  
Different Types ◽  
Naoh Solution ◽  
Activated Slag ◽  
Alkali Activated

This study shows the effect of different types of internal curing liquid on the properties of alkali-activated slag (AAS) mortar. NaOH solution and deionized water were used as the liquid internal curing agents and zeolite sand was the internal curing agent that replaced the standard sand at 15% and 30%, respectively. Experiments on the mechanical properties, hydration kinetics, autogenous shrinkage (AS), internal temperature, internal relative humidity, surface electrical resistivity, ultrasonic pulse velocity (UPV), and setting time were performed. The conclusions are as follows: (1) the setting times of AAS mortars with internal curing by water were longer than those of internal curing by NaOH solution. (2) NaOH solution more effectively reduces the AS of AAS mortars than water when used as an internal curing liquid. (3) The cumulative heat of the AAS mortar when using water for internal curing is substantially reduced compared to the control group. (4) For the AAS mortars with NaOH solution as an internal curing liquid, compared with the control specimen, the compressive strength results are increased. However, a decrease in compressive strength values occurs when water is used as an internal curing liquid in the AAS mortar. (5) The UPV decreases as the content of zeolite sand that replaces the standard sand increases. (6) When internal curing is carried out with water as the internal curing liquid, the surface resistivity values of the AAS mortar are higher than when the alkali solution is used as the internal curing liquid. To sum up, both NaOH and deionized water are effective as internal curing liquids, but the NaOH solution shows a better performance in terms of reducing shrinkage and improving mechanical properties than deionized water.

scholarly journals Undergraduate Research Program to Recycle Composite Waste

2021 ◽  
Vol 11 (7) ◽  
pp. 354
Author(s):  
Waleed Ahmed ◽  
Essam Zaneldin ◽  
Amged Al Hassan
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Carbon Fiber ◽  
Undergraduate Students ◽  
Research Program ◽  
Modulus Of Elasticity ◽  
Undergraduate Research ◽  
Undergraduate Research Program ◽  
Structural Applications ◽  
Cfrp Composite

With the rapid growth in the manufacturing industry and increased urbanization, higher amounts of composite material waste are being produced, causing severe threats to the environment. These environmental concerns, coupled with the fact that undergraduate students typically have minimal experience in research, have initiated the need at the UAE University to promote research among undergraduate students, leading to the development of a summer undergraduate research program. In this study, a recycling methodology is presented to test lab-fabricated Carbon-Fiber-Reinforced Polymer (CFRP) for potential applications in industrial composite waste. The work was conducted by two groups of undergraduate students at the UAE University. The methodology involved the chemical dissolution of the composite waste, followed by compression molding and adequate heat treatment for rapid curing of CFRP. Subsequently, the CFRP samples were divided into three groups based on their geometrical distinctions. The mechanical properties (i.e., modulus of elasticity and compressive strength) were determined through material testing, and the results were then compared with steel for prompt reference. The results revealed that the values of mechanical properties range from 2 to 4.3 GPa for the modulus of elasticity and from 203.7 to 301.5 MPa for the compressive strength. These values are considered competitive and optimal, and as such, carbon fiber waste can be used as an alternate material for various structural applications. The inconsistencies in the values are due to discrepancies in the procedure as a result of the lack of specialized equipment for handling CFRP waste material. The study concluded that the properties of CFRP composite prepreg scrap tend to be reusable instead of disposable. Despite the meager experimental discrepancies, test values and mechanical properties indicate that CFRP composite can be successfully used as a material for nonstructural applications.

scholarly journals A new expansion material used for roof-contacted filling based on smelting slag

2021 ◽  
Vol 11 (1) ◽  
Author(s):  
Hua Na ◽  
Guocheng Lv ◽  
Lijuan Wang ◽  
Libing Liao ◽  
Dan Zhang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Hydrogen Peroxide ◽  
Compressive Strength ◽  
Sodium Silicate ◽  
Utilization Rate ◽  
Ammonium Bromide ◽  
Foaming Agent ◽  
Copper Nickel ◽  
Smelting Slag ◽  
Nickel Smelting

AbstractThe improper handling of smelting slag will seriously pollute the environment, and the unfilled roof of the goaf of the mine will threaten the safety of the mine. Expansion materials have attracted more and more attention because of their excellent properties. In this paper, copper-nickel smelting slag that has some active ingredients of gelling is used instead of traditional aggregate and some part of cement in order to reduce its pollution to the environment and its costs. For safety reasons, hydrogen peroxide was chosen as the foaming agent. Sodium silicate and hexadecyl trimethyl ammonium bromide (CTAB) are used as additives. Our results showed that after 28 days of curing, the material has better mechanical properties and the early compressive strength of the material was enhanced by sodium silicate. The efficiency of foaming was improved by CTAB. It also proves that copper–nickel smelting slag can be used in expansion material. At the same time, the utilization rate of the copper–nickel smelting slag of this formula can reach 70%, reduce its pollution to the environment.

Sign in / Sign up

Export Citation Format

Share Document