Effect of water immersion at different times (from 1/2h to 24 h) on raw and expanded vermiculite from Uganda was investigated. The expansion was carried out by electrical heating at different temperatures and by irradiation with microwaves. After, the expansibility (k) and the water absorption content (WA) were obtained and the samples were characterized. The elemental and mineral composition was determined by X-ray fluorescence and X-ray diffraction, respectively; the thermal behavior by thermal gravimetric analyses; and the textural parameters by BET. The expansibility of Ugandan vermiculite is relatively lower than the other commercial vermiculites due basically to its lower K2O content (0.36%) and higher water content (about 20%). The water absorption capacity of samples significantly increased with the increase in heating temperature. The maximum WA content, about 130 mg/g, was obtained at 900 °C for 24 h. The loss of water during the expansion process in the Ugandan vermiculite caused loss of structural order and crystallinity. Moreover, in the samples expanded and subsequently immersed in water, the structural order and crystallinity increased with increasing WA values. Specific surface area and porosity hardly vary with temperature and are practically independent of vermiculite purity. Expanded commercial vermiculites could be a suitable hygroscopic material, given its efficient water absorption. Microwave expanded commercial vermiculites, in this case, would not be recommended

scholarly journals Mineralogical and Geochemiccal Assessment of Edda Clays for Possible Use in the Ceramics Industry,Afikpo Sub-Basin,Nigeria

2021 ◽  
Vol 3 (2) ◽  
Author(s):  
J. C. Ike ◽  
H. N. Ezeh ◽  
M. O. Eyankware ◽  
A. I. Haruna
Keyword(s):  
Water Absorption ◽  
Bulk Density ◽  
Clay Mineral ◽  
Silica Content ◽  
Absorption Capacity ◽  
Oxide Content ◽  
Water Absorption Capacity ◽  
Loss On Ignition ◽  
X Ray Diffraction ◽  
X Ray

 Clay samples from selected part of Edda were analyzed to identify the clay mineral types present, their chemical and physical properties with a view to appraising their industrial suitability as ceramic materials. The mineralogical and geochemical analyses were done using the principles of X-Ray diffraction and X-ray fluorescence respectively. A total of seven clay samples were used for the study, other tests such as plasticity, bulk density, shrinkage, loss on ignition (LOI) and water absorption capacity was carried out to determine the amount of water absorbed under specified conditions. The basic industrial properties assessment showed that more than 70% of the clays are fine-grained. The clays exhibited low to moderate plasticity, moderate shrinkage and bulk density, low to moderate values of both loss on ignition and water absorption capacity. The clays are buff to yellowish in colour. The results of x-ray fluorescence revealed that the mean concentration of major oxide in the clays is shown as follows: SiO2 (62.78%), Al2O3 (20.25%), total Fe (6.09%), CaO (0.56%), MgO (3.21%), Na2O (0.47%), K2O, (1.44%) and TiO2 (0.52%). The samples have high silica content, low alumina and low oxide content. The results of x-ray diffraction revealed that kaolinite is the dominant clay mineral with illite and montmorillonite occurring in subordinate amounts, while quartz and feldspar are the non-clay components present. The characteristics of the clays for each parameter were compared with industrial standards. These properties are appropriate for the Afikpo clays to be useful in the manufacturing of ceramics. However, since the silica content of the clays is high further beneficiation is recommended.

scholarly journals A Superhydrophobic, Antibacterial, and Durable Surface of Poplar Wood

Nanomaterials ◽  
2021 ◽  
Vol 11 (8) ◽  
pp. 1885
Author(s):  
Xinyu Wu ◽  
Feng Yang ◽  
Jian Gan ◽  
Zhangqian Kong ◽  
Yan Wu
Keyword(s):  
Stearic Acid ◽  
Antibacterial Properties ◽  
Alkali Resistance ◽  
Poplar Wood ◽  
X Ray Diffraction ◽  
X Ray ◽  
Different Temperatures ◽  
Acid And Alkali Resistance ◽  
The Stability

The silver particles were grown in situ on the surface of wood by the silver mirror method and modified with stearic acid to acquire a surface with superhydrophobic and antibacterial properties. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and X-ray energy spectroscopy (XPS) were used to analyze the reaction mechanism of the modification process. Scanning electron microscopy (SEM) and contact angle tests were used to characterize the wettability and surface morphology. A coating with a micro rough structure was successfully constructed by the modification of stearic acid, which imparted superhydrophobicity and antibacterial activity to poplar wood. The stability tests were performed to discuss the stability of its hydrophobic performance. The results showed that it has good mechanical properties, acid and alkali resistance, and UV stability. The durability tests demonstrated that the coating has the function of water resistance and fouling resistance and can maintain the stability of its hydrophobic properties under different temperatures of heat treatment.

scholarly journals Effect of Water Ingress on the Mechanical and Chemical Properties of Polybutylene Terephthalate Reinforced with Glass Fibers

Materials ◽  
2021 ◽  
Vol 14 (5) ◽  
pp. 1261
Author(s):  
Catarina S. P. Borges ◽  
Alireza Akhavan-Safar ◽  
Eduardo A. S. Marques ◽  
Ricardo J. C. Carbas ◽  
Christoph Ueffing ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Water Absorption ◽  
Water Uptake ◽  
Significant Influence ◽  
Water Immersion ◽  
Water Diffusion ◽  
Polybutylene Terephthalate ◽  
Chemical Changes ◽  
Water Ingress ◽  
Effect Of Water

Short fiber reinforced polymers are widely used in the construction of electronic housings, where they are often exposed to harsh environmental conditions. The main purpose of this work is the in-depth study and characterization of the water uptake behavior of PBT-GF30 (polybutylene terephthalate with 30% of short glass fiber)as well as its consequent effect on the mechanical properties of the material. Further analysis was conducted to determine at which temperature range PBT-GF30 starts experiencing chemical changes. The influence of testing procedures and conditions on the evaluation of these effects was analyzed, also drawing comparisons with previous studies. The water absorption behavior was studied through gravimetric tests at 35, 70, and 130 °C. Fiber-free PBT was also studied at 35 °C for comparison purposes. The effect of water and temperature on the mechanical properties was analyzed through bulk tensile tests. The material was tested for the three temperatures in the as-supplied state (without drying or aging). Afterwards, PBT-GF30 was tested at room temperature following water immersion at the three temperatures. Chemical changes in the material were also analyzed through Fourier-transform infrared spectroscopy (FTIR). It was concluded that the water diffusion behavior is Fickian and that PBT absorbs more water than PBT-GF30 but at a slightly higher rate. However, temperature was found to have a more significant influence on the rate of water diffusion of PBT-GF30 than fiber content did. Temperature has a significant influence on the mechanical properties of the material. Humidity contributes to a slight drop in stiffness and strength, not showing a clear dependence on water uptake. This decrease in mechanical properties occurs due to the relaxation of the polymeric chain promoted by water ingress. Between 80 and 85 °C, after water immersion, the FTIR profile of the material changes, which suggests chemical changes in the PBT. The water absorption was simulated through heat transfer analogy with good results. From the developed numerical simulation, the minimum plate size to maintain the water ingress unidirectional was 30 mm, which was validated experimentally.

scholarly journals Hydrothermal Ageing and Its Effect on Fracture Load of Zirconia Dental Implants

Materials ◽  
2021 ◽  
Vol 14 (11) ◽  
pp. 3103
Author(s):  
Laurent Gremillard ◽  
Agnès Mattlet ◽  
Alexandre Mathevon ◽  
Damien Fabrègue ◽  
Bruno Zberg ◽  
...  
Keyword(s):  
Dental Implants ◽  
Fracture Load ◽  
Accelerated Ageing ◽  
Dental Ceramics ◽  
X Ray Diffraction ◽  
X Ray ◽  
Dental Restorations ◽  
Different Temperatures ◽  
Mechanical Performances ◽  
Kinetics Of

Due to growing demand for metal-free dental restorations, dental ceramics, especially dental zirconia, represent an increasing share of the dental implants market. They may offer mechanical performances of the same range as titanium ones. However, their use is still restricted by a lack of confidence in their durability and, in particular, in their ability to resist hydrothermal ageing. In the present study, the ageing kinetics of commercial zirconia dental implants are characterized by X-ray diffraction after accelerated ageing in an autoclave at different temperatures, enabling their extrapolation to body temperature. Measurements of the fracture loads show no effect of hydrothermal ageing even after ageing treatments simulated a 90-year implantation.

scholarly journals Modeling of magneto-conductivity of bismuth selenide: a topological insulator

2021 ◽  
Vol 3 (4) ◽  
Author(s):  
Yogesh Kumar ◽  
Rabia Sultana ◽  
Prince Sharma ◽  
V. P. S. Awana
Keyword(s):  
Magnetic Field ◽  
Magnetic Fields ◽  
Single Crystal ◽  
Single Crystals ◽  
X Ray Diffraction ◽  
Field Range ◽  
X Ray ◽  
Bulk Carriers ◽  
Different Temperatures

AbstractWe report the magneto-conductivity analysis of Bi2Se3 single crystal at different temperatures in a magnetic field range of ± 14 T. The single crystals are grown by the self-flux method and characterized through X-ray diffraction, Scanning Electron Microscopy, and Raman Spectroscopy. The single crystals show magnetoresistance (MR%) of around 380% at a magnetic field of 14 T and a temperature of 5 K. The Hikami–Larkin–Nagaoka (HLN) equation has been used to fit the magneto-conductivity (MC) data. However, the HLN fitted curve deviates at higher magnetic fields above 1 T, suggesting that the role of surface-driven conductivity suppresses with an increasing magnetic field. This article proposes a speculative model comprising of surface-driven HLN and added quantum diffusive and bulk carriers-driven classical terms. The model successfully explains the MC of the Bi2Se3 single crystal at various temperatures (5–200 K) and applied magnetic fields (up to 14 T).

In situ X-ray diffraction of Fischer-Tropsch catalysts—Effect of water on the reduction of cobalt oxides

2017 ◽  
Vol 546 ◽  
pp. 103-110 ◽  
Author(s):  
James Paterson ◽  
Mark Peacock ◽  
Ewen Ferguson ◽  
Manuel Ojeda ◽  
Jay Clarkson
Keyword(s):  
Cobalt Oxides ◽  
X Ray Diffraction ◽  
Fischer Tropsch ◽  
X Ray ◽  
Effect Of Water

Preparation of Ultra–Fine La3NbO7 Powder by Solid State Reaction

2012 ◽  
Vol 512-515 ◽  
pp. 158-161 ◽  
Author(s):  
Ling Dai ◽  
Qiang Xu ◽  
Shi Zhen Zhu ◽  
Ling Liu
Keyword(s):  
Solid State ◽  
Solid State Reaction ◽  
Single Phase ◽  
Thermal Barrier ◽  
X Ray Diffraction ◽  
X Ray ◽  
Granular Particle ◽  
Fine Particle Size ◽  
Ultra Fine Particle ◽  
Different Temperatures

As a new candidate material for the ceramic layer in thermal barrier coatings (TBCs) system, La3NbO7 was synthesized with La2O3 powder and Nb2O5 powder by solid state reaction. The stating powders with a mole ratio of La to Nb of 3:1 were mixed and then the mixture was calcined under the different temperatures(800°C, 1000°C, 1200°C) and dwell times(2h, 6h, 10h). The phase structure of the powder was observed by X–ray diffraction(XRD), and the microstructure of the sample was observed by scanning electron microscope(SEM). The effect of calcination temperature and dwell Time on the phase formation were examined. The results indicate that the La3NbO7 powder with single phase can be synthesized successfully at 1200°C for 10h in air, and the La3NbOsub>7 powders synthesized have an ultra-fine particle size of 0.5˜1µm with a granular particle shape. With the temperature increasing, LaNbO4/sub> was synthesized firstly and then La3NbO7 was synthesized with a mole ratio of La2O3 to LaNbO4 of 1:1.

scholarly journals Study on High Energy Propellant Waste in the Processing of Fired Clay Bricks

2020 ◽  
Vol 70 (6) ◽  
pp. 596-602
Author(s):  
P.K. Mehta ◽  
A. Kumaraswamy ◽  
V. K. Saraswat ◽  
Praveen Kumar B.
Keyword(s):  
Compressive Strength ◽  
Water Absorption ◽  
Pore Formation ◽  
High Energy ◽  
X Ray Diffraction ◽  
X Ray ◽  
Clay Bricks ◽  
Baking Process ◽  
Fired Bricks ◽  
Xrd Studies

Utilisation of propellant waste in fabrication of bricks is not only used as efficient waste disposal method but also to get better functional properties. In the present study, high energy propellant (HEP) waste additive mixed with soil and fly ash in different proportions during manufacturing of bricks has been investigated experimentally. X-ray diffraction (XRD) studies were carried out to confirm the brick formation and the effect of HEP waste. Ceramic bricks were fabricated with HEP waste additive in proper proportions i.e. 0.5 wt %, 1.0 wt %, 1.5 wt %, 2.0 wt %, 2.5 wt %, 3 wt %, 3.5 wt %, and 4 wt % and then evaluated for water absorption capability and compressive strength. Compressive strength of 6.7 N/mm2, and Water absorption of 22 % have been observed from modified fired bricks impregnated with HEM waste additive. Scanning electron microscopy (SEM) studies were carried out to analyze the effect of HEP waste additive on pore formation and distribution in the bricks. Further, the heat resulting from decomposition of propellants can cause a decrease in the energy required of baking process. The process of manufacturing of bricks with HEP waste additive is first of its kind till date.

Microstructure and Properties of Nanosemicrystalline Si3N4 Ceramics with Doped Sintering Additives: Part II. Phase Transformation and Microstructural Control

1998 ◽  
Vol 13 (9) ◽  
pp. 2588-2596 ◽  
Author(s):  
K. H. Ryu ◽  
J-M. Yang
Keyword(s):  
Electron Microscopy ◽  
Pressureless Sintering ◽  
Particle Sizes ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sintering Additives ◽  
Different Temperatures ◽  
Si3n4 Ceramics ◽  
Scanning Electron ◽  
Microstructural Control

The low temperature pressureless sintering of a nanosized Si3N4 powder with doped sintering additives was investigated. The microstructural evolution during sintering at different temperatures was analyzed using x-ray diffraction and scanning electron microscopy. The effect of using nanosized Si3N4 powder as a catalyst to accelerate the α→β–Si3N4 transformation of a commercial Si3N4 powder with larger particle sizes was also investigated. Finally, two stage sintering was used to study the feasibility of controlling the microstructure and the mechanical properties of the nanosized silicon nitride.

scholarly journals Photocatalytic Activity and Optical Properties of Blue Persistent Phosphors under UV and Solar Irradiation

2016 ◽  
Vol 2016 ◽  
pp. 1-8 ◽  
Author(s):  
C. R. García ◽  
L. A. Diaz-Torres ◽  
J. Oliva ◽  
M. T. Romero ◽  
P. Salas
Keyword(s):  
Photocatalytic Activity ◽  
Annealing Temperature ◽  
Uv Light ◽  
Solar Irradiation ◽  
Photoluminescence Spectra ◽  
X Ray Diffraction ◽  
X Ray ◽  
Water Cleaning ◽  
Different Temperatures ◽  
The Eu

Blue phosphorescent strontium aluminosilicate powders were prepared by combustion synthesis route and a postannealing treatments at different temperatures. X-ray diffraction analysis showed that phosphors are composed of two main hexagonal phases: SrAl2O4and Sr3Al32O51. The morphology of the phosphors changed from micrograins (1000°C) to a mixture of bars and hexagons (1200°C) and finally to only hexagons (1300°C) as the annealing temperature is increased. Photoluminescence spectra showed a strong blue-green phosphorescent emission centered atλem=455 nm, which is associated with4f65d1→4f6  (8S7/2)transition of the Eu2+. The sample annealed at 1200°C presents the highest luminance value (40 Cd/m2) with CIE coordinates (0.1589, 0.1972). Also, the photocatalytic degradation of methylene blue (MB) under UV light (at 365 nm) was monitored. Samples annealed at 1000°C and 1300°C presented the highest percentage of degradation (32% and 38.5%, resp.) after 360 min. In the case of photocatalytic activity under solar irradiation, the samples annealed at 1000°C, 1150°C, and 1200°C produced total degradation of MB after only 300 min. Hence, the results obtained with solar photocatalysis suggest that our powders could be useful for water cleaning in water treatment plants.

Sign in / Sign up

Export Citation Format

Share Document