Microstructure, Texture and Property of Interstitial-Free (IF) Steel after Ultra-Fast Annealing

2015 ◽  
Vol 1120-1121 ◽  
pp. 1003-1007 ◽  
Author(s):  
He Long Cai ◽  
Jun Sheng Mou ◽  
Zi Yong Hou

In this paper, common continous annealing (CCA) and ultra-fast annealing (UFA) were carried out on a cold-rolled interstitial-free (IF) steel, respectively. The microstructure of the annealed IF steel was characterized by means of scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). The mechanical property was examined using tensile test. The optimum annealing process parameters were then obtained. The results showed that, the recrystallization occurs at the temperature in the range of 780-830°C. The fraction of equiaxed grain increases with the annealing temperature increasing. The well combination of mechanical properties and formability was obtained when the IF steel annealed at 820°C, which was the result of the fine dispersed second phase particles. {001} texture was absent in the whole thickness of all the annealed IF steels. In addition, the strongest γ texture was found, and this was a potential way to improve the deep drawability of annealed steel sheets.

2009 ◽  
Vol 24 (3) ◽  
pp. 647-651 ◽  
Author(s):  
M. Rester ◽  
C. Motz ◽  
R. Pippan

Electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) analyses of small indentations in copper single crystals exhibit only slight changes of the crystal orientation in the surroundings of the imprints. Far-reaching dislocations might be the reason for these small misorientation changes. Using EBSD and TEM technique, this work makes an attempt to visualize the far-propagating dislocations by introducing a twin boundary in the vicinity of small indentations. Because dislocations piled up at the twin boundary produce a misorientation gradient, the otherwise far-propagating dislocations can be detected.


2021 ◽  
Author(s):  
Olga Ageeva ◽  
Ge Bian ◽  
Gerlinde Habler ◽  
Rainer Abart

<p>Magnetite micro-inclusions in silicate minerals are important carriers of the remanent magnetization of rocks. Their shape orientation relationships (SOR) and crystallographic orientation relationships (COR) to the host crystal are of interest in the context of the bulk magnetic properties of the inclusion-host assemblage. We investigated the SOR and COR of magnetite (MT) micro-inclusions in plagioclase (PL) from oceanic gabbro using correlated optical microscopy, scanning electron microscopy, Electron backscatter diffraction analysis and Transmission electron microscopy.</p><p>In the mm-sized PL crystals of the investigated gabbros MT is present as equant, needle- and lath-shaped (sub)micrometer sized inclusions. More than 95% of the needle-shaped inclusions show SOR and specific COR to the plagioclase host. Most of the needles are elongated perpendicular to one of the MT{111} planes, which is aligned parallel to one of the (112), (1-12), (-312), (-3-12), (150), (1-50) or (100) planes of plagioclase. These inclusions are classified as “plane-normal type”. The needle elongation parallel to MT<111>, which is the easy direction of magnetization, ensures high magnetic susceptibility of these inclusions. The underlying formation mechanism is related to the parallel alignment of oxygen layers with similar lattice spacing across the MT-PL interfaces that are parallel to the elongation direction [1].</p><p>Apart from the SOR and the alignment of a MT{111} with one of the PL low index planes, the MT crystals rotate about the needle elongation direction. The rotation angles are statistically distributed with several maxima representing specific orientation relationships. In some cases one of the MT<001> axes is aligned with PL[14 10 7] or PL[-14 10 -7], which ensures that FeO<sub>6 </sub>octahedra of MT well fit into channels // [001] of PL, which are formed by six membered rings of SiO<sub>4</sub> and AlO<sub>4</sub> tetrahedra [2]. This COR is referred to as the “nucleation orientation” of magnetite with respect to PL. There are several other possibilities to fit FeO<sub>6</sub> octahedra into the [001] channels of PL, but the alignment stated above allows for the additional parallel alignment of one of the MT{111} with one of the above mentioned low index lattice planes of PL. MT crystals with one of these nucleation orientations can undergo directional growth to develop laths and needles. MT crystals with other nucleation orientations that do not allow for the parallel alignment of MT{111} with the above mentioned PL lattice planes, do not significantly grow and form the equant inclusions.</p><p>For some needles one or more of the MT{011} planes that are parallel to the needle elongation direction, are aligned with low-index planes of plagioclase such as PL (112), PL(150), PL(1-50) etc., and form MT facets. This situation corresponds to achievement of the best possible match between the two crystal lattices. This can either be generated during primary growth or during re-equilibration of the micro-inclusions and the plagioclase host.</p><p>Funding by RFBR project 18-55-14003 and Austrian Science fund (FWF): I 3998-N29 is acknowledged.</p><p>Reference</p><p>[1] Ageeva et al (2020) Contrib. Mineral. Petrol. 175(10), 1-16.</p><p>[2] Wenk et al (2011) Am. Min. 96, 1316-1324</p>


Materials ◽  
2020 ◽  
Vol 13 (17) ◽  
pp. 3869
Author(s):  
Mengmeng Wang ◽  
Jiang Ju ◽  
Jingjing Li ◽  
Yang Zhou ◽  
Haiyang Lv ◽  
...  

A periodic-layered structure was observed in solid-(Cr, Fe)2B/liquid-Al diffusion couple at 750 °C. The interface morphology, the reaction products, and the potential formation mechanism of this periodic-layered structure were investigated using an electron probe microanalyzer (EPMA), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM), and energy-dispersive spectroscopy (EDS). The results indicate that the reaction between (Cr, Fe)2B and liquid Al is a diffusion-controlled process. The formation of intermetallics involves both the superficial dissolution of Fe and Cr atoms and the inward diffusion of Al at the interface. The layered structure, as characterized by various experimental techniques, is alternated by a single FeAl3 layer and a (FeAl3 + Cr3AlB4) dual-phase layer. A potential mechanism describing the formation process of this periodic-layered structure was proposed based on the diffusion kinetics based on the experimental results.


2005 ◽  
Vol 495-497 ◽  
pp. 423-428 ◽  
Author(s):  
Q.W. Jiang ◽  
E.B. Zhao ◽  
J.G. Zhang ◽  
Y. Chen ◽  
Gang Wang ◽  
...  

The microstructure of Ti+P IF steel were studied after warm rolling, cold rolling and recrystallization using X-Ray, TEM and SEM. The results show that the characteristics of warm rolled sheet are the same as that of the cold rolled, but the texture displays different characteristics in the subsequent cold rolling and recrystallization because of the numerous second-phase particles. In this work, a Ti+P IF steel sheet with high strength and plastic strain ratio was obtained.


1999 ◽  
Vol 14 (7) ◽  
pp. 2959-2965 ◽  
Author(s):  
Naoto Hirosaki ◽  
Tomohiro Saito ◽  
Fumio Munakata ◽  
Yoshio Akimune ◽  
Yuichi Ikuhara

Silicon nitride was fabricated by adding Y2O3 and Nd2O3 as sintering additives, sintering for 8 h at 1900 °C, and heat treating for 4 h at 2200 °C to enhance grain growth. The microstructure was investigated by scanning electron microscopy, high-resolution electron microscopy, energy dispersive x-ray spectroscopy (EDS), and electron microdiffraction. This material had a duplex microstructure composed of many fine grains and a few coarse grains. In β–Si3N4 grains, second-phase particles with the composition of liquid phase, Y–Nd–Si–O or Y–Nd–Si–O–N, in the size of 10–30 nm were observed. EDS spectra and microdiffraction patterns revealed that those were amorphous or crystalline particles of Y–Nd–apatite, (Y,Nd)10Si6O24N2. These particles were presumably formed during cooling by the precipitation of Y–Nd–Si–O–N, which was trapped in the β–Si3N4 grains as solid solution or trapped liquid. The results suggest that attention should be paid to the trace amounts of trapped elements in β–Si3N4 grains in trying to improve the thermal conductivity of sintered silicon nitride.


2012 ◽  
Vol 535-537 ◽  
pp. 593-596
Author(s):  
Zhi Fen Wang ◽  
Rong Dong Han ◽  
Shun Bing Zhou ◽  
Zhong Hai Yao ◽  
Li Xin Wu

Effect of annealing time on the microstructure and texture of IF steel sheets was investigated. Average grain size, grain boundary character and recrystallization texture were measured by X-ray diffraction (XRD) and electron backscatter diffraction (EBSD) in order to clarify the effect of annealing time on microstructure of recrystallization process. The average grain size increased with increasing annealing time. With rising annealing time, the number of low angle boundary (0~15o) decreased due to the mergence of grain with sub-boundary. The //ND (-fiber) pole intensity had a highest value annealed at 60s. The annealing time played an important role in recrystallization process which affected the mechanical properties and microstructure of IF steels.


Minerals ◽  
2021 ◽  
Vol 11 (9) ◽  
pp. 1018
Author(s):  
Sejin Jung ◽  
Takafumi Yamamoto ◽  
Jun-ichi Ando ◽  
Haemyeong Jung

Amphibole peridotite samples from Åheim, Norway, were analyzed to understand the deformation mechanism and microstructural evolution of olivine and amphibole through the Scandian Orogeny and subsequent exhumation process. Three Åheim amphibole peridotite samples were selected for detailed microstructural analysis. The Åheim amphibole peridotites exhibit porphyroclastic texture, abundant subgrain boundaries in olivine, and the evidence of localized shear deformation in the tremolite-rich layer. Two different types of olivine lattice preferred orientations (LPOs) were observed: B- and A-type LPOs. Electron backscatter diffraction (EBSD) mapping and transmission electron microscopy (TEM) observations revealed that most subgrain boundaries in olivine consist of dislocations with a (001)[100] slip system. The subgrain boundaries in olivine may have resulted from the deformation of olivine with moderate water content. In addition, TEM observations using a thickness-fringe method showed that the free dislocations of olivine with the (010)[100] slip system were dominant in the peridotites. Our data suggest that the subgrain boundaries and free dislocations in olivine represent a product of later-stage deformation associated with the exhumation process. EBSD mapping of the tremolite-rich layer revealed intracrystalline plasticity in amphibole, which can be interpreted as the activation of the (100)[001] slip system.


2020 ◽  
Vol 326 ◽  
pp. 01007
Author(s):  
Shravan K. Kairy ◽  
Nick Birbilis

The localised corrosion associated with Mg2Si in the Al-matrix of an Al-Mg-Si alloy was studied in 0.1 M NaCl at pH 6 by quasi in-situ transmission electron microscopy. Herein, physical imaging of corrosion at the atomic to nanometre scale was performed. Phase transformation and subsequent chemical composition variations associated with the localised corrosion of Mg2Si were studied. It was observed that corrosion initiated upon Mg2Si, often preferentially at the interface with the Al-matrix, and propagated until Mg2Si was completely dealloyed by Mg-dissolution, resulting in an amorphous SiO-rich phase remnant. The SiO-rich remnant became electrochemically inert and did not initiate corrosion in the Al-matrix. This study provides a clear understanding on the localised corrosion of Al-alloys associated with Mg2Si. In addition, the methodology followed in this study can also be applied to understand the role of precipitates and second phase particles in the localised corrosion of Al-alloy systems.


Sign in / Sign up

Export Citation Format

Share Document