Study on Permeability Coefficient of Different Bamboo/Fir Veneer Surface

2011 ◽  
Vol 311-313 ◽  
pp. 1634-1637 ◽  
Author(s):  
Li Hong Yao ◽  
Xi Ming Wang ◽  
Ben Hua Fei
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Permeability Coefficient ◽  
Phenolic Resin ◽  
Chinese Fir ◽  
Raw Material ◽  
Important Indicator ◽  
Veneer Surface ◽  
Surface Permeability ◽  
Analysis Models

Permeability coefficient is an important indicator of surface wettability and permeability, which influenced by the surface roughness. In this paper, bamboo and fir veneer as raw material, the contact angle of phenolic resin adhesives in different surface roughness of outer cuticle of bamboo, inner skin of bamboo, tight side of Chinese fir veneer and loose side of Chinese fir veneer were measured, and then use the software Spass non-linear fitting for permeability coefficient, and analysis of variance of the results by SAS software. The results show that permeability coefficient of four different kinds of surface variance analysis models are significantly, permeability coefficient of fir veneer is larger than bamboo surface; permeability coefficient of tight side of fir veneer is larger than loose side; permeability coefficient of inner skin of bamboo is larger than outer cuticle of bamboo. Permeability coefficients decrease first and then increased when mesh sandpaper increasing.

Effect of Water Temperature, pH Value, and Film Thickness on the Wettability Behaviour of Copper Surfaces Coated with Copper Using EB-PVD Technique

2019 ◽  
Vol 60 ◽  
pp. 124-141 ◽  
Author(s):  
Naser Ali ◽  
Joao Amaral Teixeira ◽  
Abdulmajid Addali
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Film Thickness ◽  
Water Temperature ◽  
Ph Value ◽  
Surface Wettability ◽  
Copper Surfaces ◽  
Force Microscopy ◽  
Atomic Force ◽  
Static Contact

This research investigates the effect of surface roughness, water temperature, and pH value on the wettability behaviour of copper surfaces. An electron beam physical vapour deposition technique was used to fabricate 25, 50, and 75 nm thin films of copper on the surface of copper substrates. Surface topographical analysis, of the uncoated and coated samples, was performed using an atomic force microscopy device to observe the changes in surface microstructure. A goniometer device was then employed to examine the surface wettability of the samples by obtaining the static contact angle between the liquid and the attached surface using the sessile drops technique. Waters of pH 4, 7, and 9 were employed as the contact angle testing fluids at a set of fixed temperatures that ranged from 20°C to 60°C. It was found that increasing the deposited film thickness reduces the surface roughness of the as-prepared copper surfaces and thus causing the surface wettability to diverge from its initial hydrophobic nature towards the hydrophilic behaviour region. A similar divergence behaviour was seen with the rise in temperature of water of pH 4, and 9. In contrast, the water of pH 7, when tested on the uncoated surface, ceased to reach a contact angle below 90o. It is believed that the observed changes in surface wettability behaviour is directly linked to the liquid temperature, pH value, surface roughness, along with the Hofmeister effect between the water and the surface in contact.

The Modification of Carbon Included Polyethylene Surface by Plasma Treatment for Metallizing Using a Low Pressure RF Discharge Plasma

2005 ◽  
Vol 8 (1) ◽  
Author(s):  
Jeou-Long Lee ◽  
Chung-Ming Liu ◽  
Kuen Ting ◽  
Wei-Kung Cheng ◽  
Takayoshi Tsuchida ◽  
...  
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Surface Layer ◽  
Discharge Plasma ◽  
Treatment Time ◽  
Low Pressure ◽  
Rf Discharge ◽  
Nickel Layer ◽  
Good Adhesion ◽  
Polyethylene Surface

AbstractSurface modification of the carbon included polyethylene (semi-conductive PE) surface for metallizing using a low pressure RF discharge plasma has been carried out. The contact angle was used as a measure of the wettability of the PE surface. The roughness and the chemical bondings in PE surface layer were analized by DFM and XPS, respectively. Typical results show that the contact angle decreases from approximately 94° to below 10° after several minutes' treatment and recovers to a saturation value when it was put open to the air after treatment. The saturation value of the contact angle is smaller as the gas pressure for treatment is higher and the treatment time is longer but all are below approximately 60° which is still smaller than that of untreated. DFM and XPS results show that the surface roughness and the bondings C-O and C=O in the PE surface layer also increase with increasing the treatment time and seem to be responsible for improving the hydrophilic property of PE. After pretreatment process, nickel was coated on the PE sheet by electrodeposition method and a good adhesion between the nickel layer and the PE surface compared with that of untreated was obtained.

Enhancement of tribological properties and characteristic of polymer matrix composite (UHMWPE reinforced with short fibres of polyester) for Total Disc Replacement (TDR)

2020 ◽  
Vol 2 (102) ◽  
pp. 55-65
Author(s):  
M.N. Obaid ◽  
S.H. Radhi
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Wear Resistance ◽  
Composite Material ◽  
Thermal Properties ◽  
Coefficient Of Friction ◽  
Tribological Properties ◽  
Total Disc Replacement ◽  
Short Fibres ◽  
The Matrix

Purpose: The number of people suffering from Degenerative Disc Disease (DDD) is increasing. The disease causes heavy pain and restrict a number of day-to-day life activities. In extreme cases, the degraded disc is removed under total disc replacement which is usually made up of Ultra-High Molecular Weight Polyethylene (UHMWPE). The material has astounding biocompatible characteristics mechanical properties and wear resistance. However, these characteristics are insufficient in arthroplasty application. Therefore, research investigations are ongoing to improve tribological properties through reinforcement that may result in a composite material of UHMWPE. Thus the current study is aimed at reinforcing UHMWPE with short fibres of polyesters to enhance the tribological properties and surface characteristic so as to improve wear resistance and nourish the fibroblast cells on synthetic disc. Design/methodology/approach: The researcher prepared UHMWPE composite material, reinforced with different weight fractions of short polyester fibres (2, 4, 6, 8 and 10% following hot press method. Further pin-on-disc device was used to study the tribological properties (coefficient of friction and volume of wear). The study tested surface roughness and surface characteristics by atomic force microscopy (AFM) device, hardness by shore D device, contact angle to study the effect of polyester short fibres on wettability of UHMWPE surface and tested the thermal properties and crystalline degree using Differential Scanning Calorimetry measurement (DSC) device. Findings: The results infer that the wear resistance got improved when using 2% w.t polyester though it got decreased initially. However, the value was still more than neat UHMWPE. There was a decrease observed in coefficient of friction, but after 4 w.t% polyester, the coefficient of friction got increased due to increasing percentage of fibres which make it harder and stiff compared to UHMWPE. There was a decline observed in surface roughness due to alignment of the fibres with smooth surface. The contact angle got increased in a moderate range while the roughness enhanced the growth of fibroblast cell. The hardness of composite material got increased, because the fibres turned stiffer and harder than the matrix. DSC results infer the improvements in thermal stability due to high thermal properties of polyester fibres compared to UHMWPE. The degree of crystallinity got increased which in turn enhanced wear resistance, especially at 6 w.t % polyester fibres. There was a mild increase observed in density since the density of polyester is higher than polymer. Research limitations/implications: The major challenge was the dispersion of fibres. Uniform distribution of fibres within the matrix (UHMWPE) was achieved through two steps of mixing processes such as mechanical mixture and twin extruder. In future studies, fatigue tests must be conducted to study the behaviour of prepared composite materials under fatigue cycle. Practical implications: A significant objective is how to connect among different properties to obtain good improvement in tribological and surface properties so as to enhance wear resistance and growth of fibrolase cells. Originality/value: In this study, polymeric short fibres were used as reinforcement with polymeric matrix to enhance the wettability of fibres with matrix. In this way, the bonding among them got increased which supports the tribological, surface, and crystalline behaviour.

Ultra-precision grinding of 4H-SiC wafer by PAV/PF composite sol-gel diamond wheel

2021 ◽  
Vol 13 (9) ◽  
pp. 168781402110449
Author(s):  
Kaiping Feng ◽  
Tianchen Zhao ◽  
Binghai Lyu ◽  
Zhaozhong Zhou
Keyword(s):  
Surface Roughness ◽  
Low Temperature ◽  
Polyvinyl Alcohol ◽  
Feed Rate ◽  
Hot Pressing ◽  
Phenolic Resin ◽  
Sol Gel ◽  
Diamond Wheel ◽  
Sic Wafer ◽  
Better Than

To eliminate the deep scratches on the 4H-SiC wafer surface in the grinding process, a PVA/PF composite sol-gel diamond wheel was proposed. Diamond and fillers are sheared and dispersed in the polyvinyl alcohol-phenolic resin composite sol glue, repeatedly frozen at a low temperature of −20°C to gel, then 180°C sintering to obtain the diamond wheel. Study shows that the molecular chain of polyvinyl alcohol-phenolic resin is physically cross-linked to form gel under low-temperature conditions. Tested by mechanical property testing machines, microhardness tester, and SEM. The results show that micromorphology is more uniform, the strength of the sol-gel diamond wheel is higher, the hardness uniformity is better than that of the hot pressing diamond wheel. Grinding experiments of 4H-SiC wafer were carried out with the prepared sol-gel diamond wheel. The influence of grinding speed, feed rate, and grinding depth on the surface roughness was investigated. The results showed that by using the sol-gel diamond wheel, the surface quality of 4H-SiC wafer with an average surface roughness Ra 6.42 nm was obtained under grinding wheel speed 7000 r/min, grinding feed rate 6 µm/min, and grinding depth 15 µm, the surface quality was better than that of using hot pressing diamond wheel.

Capillary Forces Described by Effective Contact Angle Distributions via Simulations of the Centrifuge Technique

MRS Advances ◽  
2016 ◽  
Vol 1 (31) ◽  
pp. 2237-2245
Author(s):  
Myles Thomas ◽  
Elizabeth Krenek ◽  
Stephen Beaudoin
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Smooth Surface ◽  
Adhesion Force ◽  
Capillary Forces ◽  
Angle Distribution ◽  
Particle Adhesion ◽  
Multiple Factors ◽  
Effective Contact ◽  
Condensed Moisture

ABSTRACTUnderstanding particle adhesion is vital to any industry where particulate systems are involved. There are multiple factors that affect the strength of the adhesion force, including the physical properties of the interacting materials and the system conditions. Surface roughness on the particles and the surfaces to which they adhere, including roughness at the nanoscale, is critically important to the adhesion force. The focus of this work is on the capillary force that dominates the adhesion whenever condensed moisture is present. Theoretical capillary forces were calculated for smooth particles adhered to smooth and rough surfaces. Simulations of the classical centrifuge technique used to describe particle adhesion to surfaces were performed based on these forces. A model was developed to describe the adhesion of the particles to the rough surface in terms of the adhesion to a smooth surface and an ‘effective’ contact angle distribution.

scholarly journals Study on the Preparation and Properties of Impervious and Breathable Sand Based on Hydrophobic Theory

Materials ◽  
2021 ◽  
Vol 14 (19) ◽  
pp. 5613
Author(s):  
Xiao Li ◽  
Xiong Zhang ◽  
Hao Ren
Keyword(s):  
Contact Angle ◽  
Hydrostatic Pressure ◽  
Air Permeability ◽  
Coating Material ◽  
Raw Material ◽  
Sustainable Utilization ◽  
Land Resources ◽  
Nano Structure ◽  
Material Content ◽  
Pressure Resistance

Land desertification, a severe global ecological and environmental problem, brings challenges to the sustainable utilization of land resources in the world. The purpose of this research is to use hydrophobic theory to prepare impervious and breathable sand, and to solve the problems of sandy soil that seeps easily and makes it difficult for vegetation to survive in desertified areas. The influences of coating material content, first-level and second-level rough structure on the impermeability and air permeability of impervious and breathable sand were studied. The research showed that, with the increase in coating material content, the impervious performance of the sample increased firstly and then decreased, and the air permeability rose continuously. The hydrostatic pressure resistance of the sample can reach an extreme value of 53 mm. The first-level rough structure of micron structure can greatly improve the hydrophobic performance, thus improving the impervious performance. The addition of micron calcium carbonate would improve the hydrostatic pressure resistance height of the sample to 190 mm. The sample would reach a superhydrophobic state in the condition of a first-level rough structure of a nano structure built by nano silica, and the contact angle was up to 152.0°, so that the hydrostatic pressure resistance height can rise to 205 mm. The best performance would be achieved under the condition of relatively less raw material with a second-level rough structure of micro–nano. At this point, the contact angle of the sample reached 152.8° and the hydrostatic pressure resistance height was up to 205 mm. At the same time, the air permeability index of the above four kinds of impervious and breathable sand met all planting requirements. The sample prepared can satisfy the demands of different degrees of impermeability and air permeability, and can be widely used in desertification control.

Addition of Cellulose Nanofibers to Control Surface Roughness for Hydrophobic Ceramic Coatings

2021 ◽  
Vol 21 (8) ◽  
pp. 4492-4497
Author(s):  
Eun Ae Shin ◽  
Gye Hyeon Kim ◽  
Jeyoung Jung ◽  
Sang Bong Lee ◽  
Chang Kee Lee
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Surface Energy ◽  
Water Contact Angle ◽  
Ceramic Coating ◽  
Cellulose Nanofibers ◽  
Ceramic Coatings ◽  
Coating Material ◽  
Textured Surface ◽  
Water Contact

Hydrophobic ceramic coatings are used for a variety of applications. Generally, hydrophobic coating surfaces are obtained by reducing the surface energy of the coating material or by forming a highly textured surface. Reducing the surface energy of the coating material requires additional costs and processing and changes the surface properties of the ceramic coating. In this study, we introduce a simple method to improve the hydrophobicity of ceramic coatings by implementing a textured surface without chemical modification of the surface. The ceramic coating solution was first prepared by adding cellulose nanofibers (CNFs) and then applied to a polypropylene (PP) substrate. The surface roughness increased as the amount of added CNFs increased, increasing the water contact angle of the surface. When the amount of CNFs added was corresponding to 10% of the solid content, the surface roughness average of the area was 43.8 μm. This is an increase of approximately 140% from 3.1 μm (the value of the surface roughness of the surface without added CNFs). In addition, the water contact angle of the coating with added CNF increased to 145.0°, which was 46% higher than that without the CNFs. The hydrophobicity of ceramic coatings with added CNFs was better because of changes in the surface topography. After coating and drying, the CNFs randomly accumulated inside the ceramic coating layer, forming a textured surface. Thus, hydrophobicity was improved by implementing a rugged ceramic surface without revealing the surface of the CNFs inside the ceramic layer.

scholarly journals Polyimide Surface Modification Using He-H2O Atmospheric Pressure Plasma Jet-Discharge Power Effect

Coatings ◽  
2020 ◽  
Vol 10 (7) ◽  
pp. 662
Author(s):  
Essam Abdel–Fattah ◽  
Mazen Alshaer
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Plasma Treatment ◽  
Atmospheric Pressure ◽  
Atmospheric Pressure Plasma ◽  
Plasma Jet ◽  
Discharge Power ◽  
Force Microscopy ◽  
Before And After ◽  
Power Effect

The atmospheric pressure He- H 2 O plasma jet has been analyzed and its effects on the Kapton polyimide surface have been investigated in terms of discharge power effect. The polyimide surfaces before and after plasma treatment were characterized using atomic force microscopy (AFM), X-ray photoelectrons spectroscopy (XPS) and contact angle. The results showed that, increasing the discharge power induces remarkable changes on the emission intensity, rotational and vibrational temperatures of He- H 2 O plasma jet. At the low discharge power ≤5.2 W, the contact angle analysis of the polyimide surface remarkably decrease owing to the abundant hydrophilic polar C=O and N–C=O groups as well as increase of surface roughness. Yet, plasma treatment at high discharge power ≥5.2 W results in a slight decrease of the surface wettability together with a reduction in the surface roughness and polar groups concentrations.

Preparation of Hydrophobic Nylon Fabric

2016 ◽  
Vol 11 (1) ◽  
pp. 155892501601100
Author(s):  
Jinmei Du ◽  
Lulu Zhang ◽  
Jing Dong ◽  
Ying Li ◽  
Changhai Xu ◽  
...  
Keyword(s):  
Surface Roughness ◽  
Contact Angle ◽  
Surface Energy ◽  
Water Contact Angle ◽  
Sem Images ◽  
Water Contact ◽  
Carboxyl Content ◽  
Factors Affecting ◽  
Nylon Fabric ◽  
Butanetetracarboxylic Acid

Surface roughness and surface energy are two important factors affecting the hydrophobicity of nylon fabric. In this study, nylon fabric was treated for hydrophobicity with tetrabutyltitanate (TBT) and octadecylamine (OA) which were respectively responsible for increasing surface roughness and reducing surface energy. In order to enhance the hydrophobicity, In order to further enhance hydrophobicity by increasing available reactive sites, 1,2,3,4–butanetetracarboxylic acid (BTCA) was applied as a pretreatment to the nylon fabric It was found that the carboxyl content of nylon was increased by the BTCA pretreatment. SEM images showed that the TBT treatment produced small particles on nylon fabric which made surface rough. The water contact angle of nylon fabric treated with BTCA, TBT and OA was measured to be 134°, which was much greater than the water contact angle of nylon fabric treated only with OA. This indicated that the surface roughness resulting from the TBT treatment played an important role in improving hydrophobicity of the treated nylon fabric. The resistance to water penetration and the repellency of water spray of nylon fabric treated with BTCA, TBT and OA were respectively measured to be 27.64 mbar and 85 out of 100.

Sign in / Sign up

Export Citation Format

Share Document