scholarly journals Lead sorption from aqueous solutions by kaolinite: laboratory experiments

2021 ◽  
Vol 2 (1) ◽  
pp. 1-8
Author(s):  
Salih Awadh ◽  
Ayad A Yousif
Keyword(s):  
Ion Exchange ◽  
Active Sites ◽  
Laboratory Experiments ◽  
Laboratory Simulation ◽  
Natural Sorbent ◽  
X Ray ◽  
Aqueous Environments ◽  
Pure Phase ◽  
Sorption From Aqueous Solutions ◽  
Solid Liquid

The lead has adverse effects in contamination the aquatic environment, for this reason, a laboratory simulation was conducted using kaolinite collected from the Ga’ara Formation at western Iraq to be considered as a natural sorbent material that can be addressed Pb2+ from the aqueous environments. The Energy-Dispersive X-ray Spectroscopy and atomic absorption spectroscopy clarifying very fine grains and pure phase with a very little quantity of quartz and has a number of active sites for adsorption. The sorption of kaolinite for the Pb2+ has been carefully tested by several designed laboratory experiments. Five lead solutions of different concentrations (25, 50, 75, 100 and 125 ppm) were tested under different values of pH (1.3-9). The best sorption has been recorded at pH 9, with an equilibrium reaction time 40 m and the solid-liquid ration 1.25 gm:50 ml. The sorption reaction is endothermic with two main mechanisms were identified, the rapid ion exchange which gets at the beginning of the reaction during the first 10 m, and ion exchange, which gets slow later due to form ionic complexes  

scholarly journals Properties of Iron-Modified-by-Silver Supported on Mordenite as Catalysts for NOx Reduction

Catalysts ◽  
2020 ◽  
Vol 10 (10) ◽  
pp. 1156 ◽  
Author(s):  
Perla Sánchez-López ◽  
Yulia Kotolevich ◽  
Evgeny Khramov ◽  
Ramesh Kumar Chowdari ◽  
Miguel Angel Estrada ◽  
...  
Keyword(s):  
Ion Exchange ◽  
Bimetallic Catalysts ◽  
Active Sites ◽  
Nox Reduction ◽  
The State ◽  
Edge Structure ◽  
X Ray ◽  
Disordered Phase ◽  
Activity Test ◽  
X Ray Absorption

A series of mono and bimetallic catalysts based on a Fe-Ag mixture deposited on mordenite was prepared by ion-exchange and evaluated in the catalytic activity test of the de-NOx reaction in the presence of CO/C3H6. The activity results showed that the most active samples were the Fe-containing ones, and at high temperatures, a co-promoter effect of Ag on the activity of Fe catalysts was also observed. The influence of the order of cation deposition on catalysts formation and their physicochemical properties was studied by FTIR (Fourier Transform Infrared Spectroscopy) of adsorbed NO, XANES (X-ray Absorption Near-Edge Structure), and EXAFS (Extended X-ray Absorption Fine Structure) and discussed in terms of the state of iron. Results of Fe K-edge XANES oscillations showed that, in FeMOR catalysts, iron was present in a disordered state as Fe3+ and Fe2+. In FeAgMOR, the prevailing species was Fe3+, while in the AgFeMOR catalyst, the state of iron was intermediate or mixed between FeMOR and FeAgMOR. The Fe K-edge EXAFS results were characteristic of a disordered phase, the first coordination sphere being asymmetric with two different Fe-O distances. In FeAgMOR and AgFeMOR, coordination of Fe-O was similar to Fe2O3 with a few amount of Fe2+ species. We may conclude that, in the bimetallic FeAgMOR and AgFeMOR samples, a certain amount of tetrahedral Al3+ ions in the mordenite framework is replaced by Fe3+ ions, confirming the previous reports that these species are active sites for the de-NOx reaction. Based on the thermodynamic analysis and experimental data, also, it was confirmed that the order of deposition of the components influenced the mechanism of active sites’ formation during the two steps ion-exchange synthesis.

scholarly journals Nanostructured faujasite zeolite as metal ion adsorbent: kinetics, equilibrium adsorption and metal recovery studies

2020 ◽  
Author(s):  
Mariana B. Goncalves ◽  
Djanyna V. C. Schmidt ◽  
Fabiana S. dos Santos ◽  
Daniel F. Cipriano ◽  
Gustavo R. Gonçalves ◽  
...  
Keyword(s):  
Ion Exchange ◽  
Metal Ions ◽  
Metal Ion ◽  
Active Sites ◽  
Metal Removal ◽  
High Surface ◽  
High Surface Area ◽  
Kinetic Studies ◽  
Crystallization Time ◽  
X Ray

Abstract The hydrothermal synthesis of nano-faujasite has been successfully performed and the effects of some crystallization parameters were investigated, along with the use of this material as a heavy-metal ion adsorbent. X-ray diffraction patterns have shown that the structure of the nano-faujasite is strongly dependent on both the crystallization time and the alkalinity of the synthesis medium. According to N2 physisorption, X-ray fluorescence, SEM/EDS, and solid state 29Si and 27Al NMR data, the produced nano-faujasite consists of a solid with low molar Si/Al ratio (1.7), with high availability of ion exchange sites and high surface area/small particle size, allowing easy diffusion of metal ions to adsorbent active sites. As a consequence, an excellent performance on removal of Cd2+, Zn2+ and Cu2+ ions was found for this solid. The adsorption capacity followed the order Cd2+ (133 mg·g−1) > Zn2+ (115 mg·g−1) > Cu2+ (99 mg·g−1), which agrees with the order of increasing absolute values of the hydration energy of the metal ions. Kinetic studies and adsorption isotherms showed that the metal ion removal takes place by ion exchange on the monolayer surface of the nano-faujasite. The electrochemical recovery of copper in metallic form exhibited an efficiency of 80.2% after 120 min, which suggests that this process can be adequately implemented for full-scale metal removal.

Scanning luminescence x-ray microscopy: Progress toward selective staining using microspheres

1994 ◽  
Vol 52 ◽  
pp. 74-75
Author(s):  
C. Jacobsen ◽  
J. Fu ◽  
S. Mayer ◽  
Y. Wang ◽  
S. Williams
Keyword(s):  
Visible Light ◽  
Active Sites ◽  
Light Emission ◽  
Chinese Hamster ◽  
Polystyrene Spheres ◽  
Good Resistance ◽  
X Ray ◽  
Selective Staining ◽  
Visible Light Emission ◽  
Specific Labelling

In scanning luminescence x-ray microscopy (SLXM), a high resolution x-ray probe is used to excite visible light emission (see Figs. 1 and 2). The technique has been developed with a goal of localizing dye-tagged biochemically active sites and structures at 50 nm resolution in thick, hydrated biological specimens. Following our initial efforts, Moronne et al. have begun to develop probes based on biotinylated terbium; we report here our progress towards using microspheres for tagging.Our initial experiments with microspheres were based on commercially-available carboxyl latex spheres which emitted ~ 5 visible light photons per x-ray absorbed, and which showed good resistance to bleaching under x-ray irradiation. Other work (such as that by Guo et al.) has shown that such spheres can be used for a variety of specific labelling applications. Our first efforts have been aimed at labelling ƒ actin in Chinese hamster ovarian (CHO) cells. By using a detergent/fixative protocol to load spheres into cells with permeabilized membranes and preserved morphology, we have succeeded in using commercial dye-loaded, spreptavidin-coated 0.03μm polystyrene spheres linked to biotin phalloidon to label f actin (see Fig. 3).

Structural/Texture Evolution During Facile Substitution of Ni into ZSM-5 Nanostructure vs. its Impregnation Dispersion Used in Selective Transformation of Methanol to Ethylene and Propylene

2020 ◽  
Vol 23 ◽  
Author(s):  
Parisa Sadeghpour ◽  
Mohammad Haghighi ◽  
Mehrdad Esmaeili
Keyword(s):  
High Temperature ◽  
Physicochemical Properties ◽  
Active Sites ◽  
Catalytic Performance ◽  
Fixed Bed Reactor ◽  
Light Olefins ◽  
Isomorphous Substitution ◽  
Impregnation Method ◽  
Hydrothermal Temperature ◽  
X Ray

Aim and Objective: Effect of two different modification methods for introducing Ni into ZSM-5 framework was investigated under high temperature synthesis conditions. The nickel successfully introduced into the MFI structures at different crystallization conditions to enhance the physicochemical properties and catalytic performance. Materials and Methods: A series of impregnated Ni/ZSM-5 and isomorphous substituted NiZSM-5 nanostructure catalysts were prepared hydrothermally at different high temperatures and within short times. X-ray diffraction (XRD), Field emission scanning electron microscopy (FESEM), Energy dispersive X-ray (EDX), Brunner, Emmett and Teller-Barrett, Joyner and Halenda (BET-BJH), Fourier transform infrared (FTIR) and Temperature-programmed desorption of ammonia (TPDNH3) were applied to investigate the physicochemical properties. Results: Although all the catalysts showed pure silica MFI–type nanosheets and coffin-like morphology, using the isomorphous substitution for Ni incorporation into the ZSM-5 framework led to the formation of materials with lower crystallinity, higher pore volume and stronger acidity compared to using impregnation method. Moreover, it was found that raising the hydrothermal temperature increased the crystallinity and enhanced more uniform incorporation of Ni atoms in the crystalline structure of catalysts. TPD-NH3 analysis demonstrated that high crystallization temperature and short crystallization time of NiZSM-5(350-0.5) resulted in fewer weak acid sites and medium acid strength. The MTO catalytic performance was tested in a fixed bed reactor at 460ºC and GHSV=10500 cm3 /gcat.h. A slightly different reaction pathway was proposed for the production of light olefins over impregnated Ni/ZSM-5 catalysts based on the role of NiO species. The enhanced methanol conversion for isomorphous substituted NiZSM-5 catalysts could be related to the most accessible active sites located inside the pores. Conclusion: The impregnated Ni/ZSM-5 catalyst prepared at low hydrothermal temperature showed the best catalytic performance, while the isomorphous substituted NiZSM-5 prepared at high temperature was found to be the active molecular sieve regarding the stability performance.

Role of the Structure and Electronic Properties of Fe2O3-MoO3 Catalyst on the Dehydration of Isopropyl Alcohol

1993 ◽  
Vol 58 (7) ◽  
pp. 1591-1599 ◽  
Author(s):  
Abd El-Aziz A. Said
Keyword(s):  
Active Sites ◽  
Isopropyl Alcohol ◽  
Oxide Catalyst ◽  
Flow System ◽  
Charge Carriers ◽  
X Ray Diffraction ◽  
X Ray ◽  
Catalyst Composition ◽  
Surface Active

Molybdenum oxide catalyst doped or mixed with (1 - 50) mole % Fe3+ ions were prepared. The structure of the original samples and the samples calcined at 400 °C were characterized using DTA, X-ray diffraction and IR spectra. Measurements of the electrical conductivity of calcined samples with and without isopropyl alcohol revealed that the conductance increases on increasing the content of Fe3+ ions up to 50 mole %. The activation energies of charge carriers were determined in presence and absence of the alcohol. The catalytic dehydration of isopropyl alcohol was carried out at 250 °C using a flow system. The results obtained showed that the doped or mixed catalysts are active and selective towards propene formation. However, the catalyst containing 40 mole % Fe3+ ions exhibited the highest activity and selectivity. Correlations were attempted to the catalyst composition with their electronic and catalytic properties. Probable mechanism for the dehydration process is proposed in terms of surface active sites.

Melting and Crystallization of Poly(oxyethylene) Mixtures

1995 ◽  
Vol 60 (11) ◽  
pp. 1855-1868 ◽  
Author(s):  
Ivo Lapeš ◽  
Josef Baldrian ◽  
Ján Biroš ◽  
Julius Pouchlý ◽  
Hanes Mio
Keyword(s):  
Melting Point ◽  
Lamellar Structure ◽  
Composition Dependence ◽  
Eutectic Phase ◽  
Eutectic Melting ◽  
Pure Polymer ◽  
X Ray ◽  
Long Period ◽  
Solid Liquid ◽  
Melting And Crystallization

Solid-liquid eutectic phase diagrams of mixtures of poly(oxyethylene) (M.w. 2 000) with hydroxy and methoxy endgroups, crystallizing in extended-chain macroconformation only, with glutaric acid, benzoic acid or 1,2-diphenylethane are given. The composition dependence of the melting temperature can be fitted by the Flory-Huggins equation. Interaction parameters X and interaction energy densities B evaluated from the diluent branch of the phase diagram are consistent with those obtained from the polymer branch provided the calorimetric value of enthalpy of polymer fusion is used in the latter computation. Measurements of small- and wide-angle X-ray scatterings showed a stacked lamellar structure of POE. Below the eutectic melting point, the long period of the polymer is almost independent of the diluent concentration. On raising temperature gradually from this melting point to the melting point of pure polymer, the increasing long period indicates the penetration of the diluent between the lamellae. As follows from SAXS measurements, the crystallinity of poly(oxyethylene) in the mixtures remains unchanged compared to that of the pure polymer.

Physicochemical and Catalytic Properties of Spinels Formed by Solid-Solid Interaction Between Fe2O3and V2O5

1996 ◽  
Vol 61 (8) ◽  
pp. 1131-1140 ◽  
Author(s):  
Abd El-Aziz Ahmed Said
Keyword(s):  
Vanadium Oxide ◽  
Active Sites ◽  
Catalyst Surface ◽  
Catalytic Properties ◽  
Flow System ◽  
Oxide Catalysts ◽  
X Ray Diffraction ◽  
Selective Catalyst ◽  
X Ray ◽  
Solid Catalysts

Vanadium oxide catalysts doped or mixed with 1-50 mole % Fe3+ ions were prepared. The structure of the original samples and those calcined from 200 up to 500 °C were characterized by TG, DTA, IR and X-ray diffraction. The SBET values and texture of the solid catalysts were investigated. The catalytic dehydration-dehydrogenation of isopropanol was carried out at 200 °C using a flow system. The results obtained showed an observable decrease in the activity of V2O5 on the addition of Fe3+ ions. Moreover, Fe2V4O13 is the more active and selective catalyst than FeVO4 spinels. The results were correlated with the active sites created on the catalyst surface.

scholarly journals Preparation and Characterization of the Sulfur-Impregnated Natural Zeolite Clinoptilolite for Hg(II) Removal from Aqueous Solutions

Processes ◽  
2021 ◽  
Vol 9 (2) ◽  
pp. 217
Author(s):  
Marin Ugrina ◽  
Martin Gaberšek ◽  
Aleksandra Daković ◽  
Ivona Nuić
Keyword(s):  
Chemical Modification ◽  
Aqueous Solutions ◽  
Specific Surface ◽  
Surface Area ◽  
Natural Zeolite ◽  
Contact Time ◽  
Liquid Ratio ◽  
X Ray ◽  
Solid Liquid

Sulfur-impregnated zeolite has been obtained from the natural zeolite clinoptilolite by chemical modification with Na2S at 150 °C. The purpose of zeolite impregnation was to enhance the sorption of Hg(II) from aqueous solutions. Chemical analysis, acid and basic properties determined by Bohem’s method, chemical behavior at different pHo values, zeta potential, cation-exchange capacity (CEC), specific surface area, X-ray powder diffraction (XRPD), scanning electron microscopy with energy-dispersive X-ray analysis (SEM-EDS), Fourier transform infrared spectroscopy (FTIR), as well as thermogravimetry with derivative thermogravimetry (TG-DTG) were used for detailed comparative mineralogical and physico-chemical characterization of natural and sulfur-impregnated zeolites. Results revealed that the surface of the natural zeolite was successfully impregnated with sulfur species in the form of FeS and CaS. Chemical modification caused an increase in basicity and the net negative surface charge due to an increase in oxygen-containing functional groups as well as a decrease in specific surface area and crystallinity due to the formation of sulfur-containing clusters at the zeolite surface. The sorption of Hg(II) species onto the sulfur-impregnated zeolite was affected by the pH, solid/liquid ratio, initial Hg(II) concentration, and contact time. The optimal sorption conditions were determined as pH 2, a solid/liquid ratio of 10 g/L, and a contact time of 800 min. The maximum obtained sorption capacity of the sulfur-impregnated zeolite toward Hg(II) was 1.02 mmol/g. The sorption mechanism of Hg(II) onto the sulfur-impregnated zeolite involves electrostatic attraction, ion exchange, and surface complexation, accompanied by co-precipitation of Hg(II) in the form of HgS. It was found that sulfur-impregnation enhanced the sorption of Hg(II) by 3.6 times compared to the natural zeolite. The leaching test indicated the retention of Hg(II) in the zeolite structure over a wide pH range, making this sulfur-impregnated sorbent a promising material for the remediation of a mercury-polluted environment.

scholarly journals Controlled Synthesis of CuS and Cu9S5 and Their Application in the Photocatalytic Mineralization of Tetracycline

Catalysts ◽  
2021 ◽  
Vol 11 (8) ◽  
pp. 899
Author(s):  
Murendeni P. Ravele ◽  
Opeyemi A. Oyewo ◽  
Damian C. Onwudiwe
Keyword(s):  
Electron Microscopy ◽  
Visible Light ◽  
Blue Shift ◽  
X Ray Diffraction ◽  
X Ray ◽  
Copper Sulfides ◽  
Transmission Electron ◽  
Single Source Precursor ◽  
Pure Phase ◽  
Pure Phases

Pure-phase Cu2−xS (x = 1, 0.2) nanoparticles have been synthesized by the thermal decomposition of copper(II) dithiocarbamate as a single-source precursor in oleylamine as a capping agent. The compositions of the Cu2−xS nanocrystals varied from CuS (covellite) through the mixture of phases (CuS and Cu7.2S4) to Cu9S5 (digenite) by simply varying the temperature of synthesis. The crystallinity and morphology of the copper sulfides were studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM), which showed pure phases at low (120 °C) and high (220 °C) temperatures and a mixture of phases at intermediate temperatures (150 and 180 °C). Covellite was of a spherical morphology, while digenite was rod shaped. The optical properties of these nanocrystals were characterized by UV−vis–NIR and photoluminescence spectroscopies. Both samples had very similar absorption spectra but distinguishable fluorescence properties and exhibited a blue shift in their band gap energies compared to bulk Cu2−xS. The pure phases were used as catalysts for the photocatalytic degradation of tetracycline (TC) under visible-light irradiation. The results demonstrated that the photocatalytic activity of the digenite phase exhibited higher catalytic degradation of 98.5% compared to the covellite phase, which showed 88% degradation within the 120 min reaction time using 80 mg of the catalysts. The higher degradation efficiency achieved with the digenite phase was attributed to its higher absorption of the visible light compared to covellite.

Sign in / Sign up

Export Citation Format

Share Document