Structural Evolution of Cold Rolled Multi-Layers in the Al-Cu-Fe Ternary System

2003 ◽  
Vol 805 ◽  
Author(s):  
J. S. Park ◽  
E. Fleury ◽  
J. H. Kim ◽  
H. J. Chang ◽  
W. T. Kim ◽  
...  
Keyword(s):  
Ternary System ◽  
Cold Rolling ◽  
Thermal Analyses ◽  
Structural Evolution ◽  
Target Composition ◽  
Cold Rolled

ABSTRACTSamples with a target composition of Al62.5Cu25Fe12.5 (at.%) have been produced from the repeated cold rolling and folding (R&F) process of Al, Cu and Fe elemental foils. Upon early increments of the R&F cycle, the mechanically-induced process led to the fragmentation of the initial foils, which resulted in the dispersion of elemental Fe layers through the refined Al and Cu layers. After 40 R&F cycles the Al2Cu phase was detected, while Fe did not contribute to the formation of compounds. Thermal analyses suggested that the formation and dissolution of the Al2Cu and Al7Cu2Fe phases are critical steps for the synthesis of the i-phase during post-R&F treatment. Annealing between 650° and 750°C enabled the formation of the stable i-phase and resulted in high values of the microhardness.

Rolling and Recrystallization Textures in High Purity Al Cold Rolled to Very High Rolling Reductions

2005 ◽  
Vol 495-497 ◽  
pp. 603-608 ◽  
Author(s):  
Atsushi Todayama ◽  
Hirosuke Inagaki
Keyword(s):  
Cold Rolling ◽  
High Purity ◽  
Work Hardening ◽  
Dynamic Recovery ◽  
The Other ◽  
Rolling Reduction ◽  
Theoretical Investigations ◽  
Theoretical Predictions ◽  
Cold Rolled ◽  
Very High

On the basis of Taylor-Bishop-Hill’s theory, many previous theoretical investigations have predicted that, at high rolling reductions, most of orientations should rotate along theβfiber from {110}<112> to {123}<634> and finally into the {112}<111> stable end orientations. Although some exceptions exist, experimental observations have shown, on the other hand, that the maximum on the β fiber is located still at about {123}<634> even after 97 % cold rolling. In the present paper, high purity Al containing 50 ppm Cu was cold rolled up to 99.4 % reduction in thickness and examined whether {112}<111> stable end orientation could be achieved experimentally. It was found that, with increasing rolling reduction above 98 %, {110}<112> decreased, while orientations in the range between {123}<634> and {112}<111> increased, suggesting that crystal rotation along the βfiber from {110}<112> toward {123}<634> and {112}<111> in fact took place. At higher rolling reductions, however, further rotation of this peak toward {112}<111> was extremely sluggish, and even at the highest rolling reduction, it could not arrive at {112}<111>. Such discrepancies between theoretical predictions and experimental observations should be ascribed to the development of dislocation substructures, which were formed by concurrent work hardening and dynamic recovery. Since such development of dislocation substructures are not taken into account in Taylor-Bishop-Hill’s theory, it seems that they can not correctly predict the development of rolling textures at very high rolling reductions, i. e. stable end orientations. On annealing specimens rolled above 98 % reduction in thickness, cube textures were very weak, suggesting that cube bands were almost completely rotated into other orientations during cold rolling. {325}<496>, which lay at an intermediate position between {123}<634> and {112}<111> along theβfiber, developed strongly in the recrystallization textures.

Effects of Cold-Rolling Reduction on Microstructure and Mechanical Properties of Ti50Zr30Nb10Ta10 Alloy

2016 ◽  
Vol 849 ◽  
pp. 376-381
Author(s):  
Ming Long Li ◽  
Yu Jie Geng ◽  
Chen Chen ◽  
Shu Jie Pang ◽  
Tao Zhang
Keyword(s):  
Mechanical Properties ◽  
Titanium Alloy ◽  
Plastic Strain ◽  
Cold Rolling ◽  
Reduction Ratio ◽  
High Fracture ◽  
Dendrite Structure ◽  
Microstructure And Mechanical Properties ◽  
Cold Rolling Reduction ◽  
Cold Rolled

The effects of cold-rolling with different reduction ratios of 70%-90% on the microstructure and mechanical properties of Ti50Zr30Nb10Ta10 alloy were investigated. It was found that the β-Ti phase in this alloy was stable under cold-rolling. With the increase in reduction ratio from 70% to 90%, the microstructure of the alloys evolved from deformed dendrite structure to fiber-like structure. The alloy cold-rolled with the reduction ratio of 70% exhibited optimum mechanical properties of combined high fracture strength of 1012 MPa and plastic strain of 10.1%, which are closely correlated with the dendrite structure of the alloy. It is indicated that the proper cold-rolling is an effective way to improve the mechanical properties of the titanium alloy.

Evaluation of Blister Behavior for U10Mo Mini Fuel Plates With Cold Rolled Foils

2012 ◽  
Author(s):  
Hakan Ozaltun ◽  
Samuel J. Miller
Keyword(s):  
Cold Rolling ◽  
Thermal Cycling ◽  
Cold Work ◽  
Rolling Process ◽  
Foil Thickness ◽  
Rolled Plate ◽  
Stress Profile ◽  
Wide Range ◽  
Threshold Temperatures ◽  
Cold Rolled

This article aims to provide possible mechanical causes for the lowered blister temperatures of RERTR-12 and AFIP-4 fuel plates. Recent experimental investigations to determine the blister threshold temperatures have indicated lower thresholds for similar plates with comparable burn-up histories. Measured blister temperatures of roughly 100 °C lower compared to the previously tested plates may not be satisfactory for some plates. The primary differences between recent experiments and previous tests are: (1) An aggressive cold work process involving large thickness reduction ratios without normalization or full annealing (2) Subjecting the plates to a thermal cycling process prior to irradiation, and finally (3) A primarily frontal neutron flux as opposed to a transverse flux profile. It is believed that the stress field has implications to blister behavior. To investigate this claim, the stress-strain states for the fabrication procedure were evaluated. First, the residual stress profile caused by the cold rolling process was calculated. Modeling of the cold rolling process has shown confirmation of residual stresses of considerable magnitude and the existence of stress gradients with respect to foil thickness prior to the HIP process. Once calculated, these stress profiles were used as an initial condition for the fabrication process. Due to the variation in stress fields depending on location at which a foil is cut from the cold rolled plate, three representative regions were selected and implemented in the HIP simulation. Variation in stresses, depending on location of the cold rolled plate as well and variation in the through-thickness, results in a wide range of mechanical stress states. This suggests that inhomogeneous irradiation and thermal cycling behavior will result from the use of cold rolled foils. Additionally, these results suggest that there will be fundamental differences in fuel plate behavior observed between plates fabricated with cold rolled foils versus hot rolled and fully annealed foils.

scholarly journals Morphological and Structural Evolution of Chemically Deposited Epitaxially LaNiO3 Thin Films

Coatings ◽  
2021 ◽  
Vol 11 (11) ◽  
pp. 1376
Author(s):  
Mircea Nasui ◽  
Ramona Bianca Sonher ◽  
Ecaterina Ware ◽  
Andrada Daniel ◽  
Traian Petrisor ◽  
...  
Keyword(s):  
Thin Films ◽  
Thermal Analyses ◽  
Structural Evolution ◽  
Precursor Solution ◽  
Solution Deposition ◽  
Chemical Solution Deposition Method ◽  
Out Of Plane ◽  
Optimal Surface ◽  
Decomposition Behavior ◽  
Surface Morphologies

We report the preparation and characterization of epitaxial LaNiO3 (LNO) thin films by chemical solution deposition method using lanthanum and nickel acetylacetonates as starting reagents dissolved in propionic acid. In order to obtain further information regarding the decomposition behavior of the film, the precursor solution was dried to obtain the precursor powder, which was investigated by thermal analyses and X-ray diffraction measurements (XRD). The LNO perovskite thin films were deposited by spin coating on SrTiO3(100) single crystal substrates. A detailed study with different crystallization temperatures (600–900 °C) at two different heating ramps (5 and 10 °C/min) was performed. Oriented LaNiO3 thin films with good out-of-plane textures were obtained with optimal surface morphologies.

scholarly journals Tensile Properties and Damping Capacity of Cold-Rolled Fe-20Mn-12Cr-3Ni-3Si Damping Alloy

Materials ◽  
2021 ◽  
Vol 14 (20) ◽  
pp. 5975
Author(s):  
Jae-Hwan Kim ◽  
Jong-Min Jung ◽  
Hyunbo Shim
Keyword(s):  
Tensile Strength ◽  
Cold Rolling ◽  
Tensile Properties ◽  
Volume Fraction ◽  
High Strength ◽  
Damping Capacity ◽  
Austenite Stability ◽  
Ε Martensite ◽  
Cold Rolled ◽  
The Relationship

The tensile properties and damping capacity of cold-rolled Fe–20Mn–12Cr–3Ni–3Si alloys were investigated. The martensitic transformation was identified, including surface relief with a specific orientation and partial intersection. Besides, as the cold rolling degree increased, the volume fraction of ε-martensite increased, whereas α’-martensite started to form at the cold rolling degree of 15% and slightly increased to 6% at the maximum cold rolling degree. This difference may be caused by high austenite stability by adding alloying elements (Mn and Ni). As the cold rolling degree increased, the tensile strength linearly increased, and the elongation decreased due to the fractional increment in the volume of martensite. However, the damping capacity increased until a 30% cold rolling degree was approached, and then decreased. The irregular tendency of the damping capacity was confirmed, depicting that it increased to a specific degree and then decreased as the tensile strength and elongation increased. Concerning the relationship between the tensile properties and the damping capacity, the damping capacity increased and culminated, and then decreased as the tensile properties and elongation increased. The damping capacity in the high-strength area tended to decrease because it is difficult to dissipate vibration energy into thermal energy in alloys with high strength. In the low-strength area, on the other hand, the damping capacity increased as the strength increased since the increased volume fraction of ε-martensite is attributed to the increase in the damping source.

scholarly journals Anneal hardening effect in sintered copper alloys

2002 ◽  
Vol 34 (2) ◽  
pp. 169-174 ◽  
Author(s):  
Svetlana Nestorovic ◽  
Boran Milicevic ◽  
Desimir Markovic
Keyword(s):  
Electrical Conductivity ◽  
Cold Rolling ◽  
Copper Alloys ◽  
Recrystallization Temperature ◽  
Temperature Range ◽  
Hardening Effect ◽  
Sintered Copper ◽  
Anneal Hardening ◽  
Cold Rolled

Samples of copper and copper alloys CuNi and CuNiAl were prepared by a powder metallurgical method and were then subjected to cold rolling with different degrees of deformation. Copper and copper alloys in the cold-rolled state were isochronally annealed up to the recrystallization temperature during which hardness and electrical conductivity were measured. This investigation shows that the anneal hardening effect occurs in a temperature range of 450 - 650 K, followed with an increase in hardness of alloys.

The Stability of γ ’-Co3(Al,W) Phase in Co-Al-W Ternary System

2010 ◽  
Vol 654-656 ◽  
pp. 448-451 ◽  
Author(s):  
Yuki Tsukamoto ◽  
Satoru Kobayashi ◽  
Takayuki Takasugi
Keyword(s):  
Heat Treatment ◽  
Ternary System ◽  
Microstructural Evolution ◽  
Treatment Time ◽  
Bulk Alloy ◽  
Epma Analysis ◽  
Heat Treated ◽  
Cold Rolled ◽  
The Stability ◽  
Couple Method

The thermodynamic stability ’- Co3(Al,W) phase (L12) in the Co-Al-W ternary system at 900 °C was investigated through microstructure and EPMA analysis on a heat-treated bulk alloy. To promote microstructural evolution, the bulk alloy was cold rolled before heat treatment. By heating at 900 °C, the ’ phase was formed discontinuously in contact with the -Co (A1) phase. With increasing heat treatment time, however, the fraction of ’ phase decreased while that of , CoAl (B2) and Co3W (D019) phases increased. These results are consistent with our previous work with a diffusion-couple method, indicating that the ’ phase is metastable, and the three phases of, CoAl and Co3W are thermodynamically stable at 900 °C.

The Influence of Cold Rolling on Magnetocaloric Properties of Gd100-xYx (x = 0, 5, 10, 15) Alloys

2015 ◽  
Vol 233-234 ◽  
pp. 238-242 ◽  
Author(s):  
Sergey Taskaev ◽  
Konstantin Skokov ◽  
Dmitriy Karpenkov ◽  
Vladimir V. Khovaylo ◽  
Vasiliy D. Buchelnikov ◽  
...  
Keyword(s):  
Cold Rolling ◽  
Magnetocaloric Effect ◽  
High Temperature Heat Treatment ◽  
Magnetic Cooling ◽  
A Value ◽  
Magnetocaloric Properties ◽  
Cooling Devices ◽  
Cold Rolled ◽  
Magnetocaloric Materials ◽  
Temperature Heat Treatment

In this work we report the results of investigation of the magnetocaloric effect in Gd100-xYx (x= 0, 5, 10, 15) cold rolled ribbons. It is shown that the magnetocaloric effect exists within a wide temperature interval 258-295 K and it is comparable with the magnetocaloric effect observed in bulk samples of pure gadolinium. The value of the magnetocaloric effect in the rolled samples is reduced in comparison with the bulk samples and strongly depends on a degree of plastic deformation. High temperature heat treatment can restore a value of the magnetocaloric effect in the cold rolled ribbons up to initial ones. Thus, cold rolling is proposed to be a promising technique for producing thin forms of magnetocaloric materials for heat exchangers of magnetic cooling devices.

Effect of Hot-Rolled Microstructure on the Recrystallization Texture of Cold-Rolled Non-Oriented Electrical Steel

2011 ◽  
Vol 298 ◽  
pp. 203-208 ◽  
Author(s):  
Zi Li Jin ◽  
Wei Li ◽  
Yi Ming Li
Keyword(s):  
Cold Rolling ◽  
Electrical Steel ◽  
Texture Evolution ◽  
Steel Strip ◽  
Silicon Steel ◽  
Grain Structure ◽  
Recrystallization Annealing ◽  
Rolled Sheet ◽  
Cold Rolled ◽  
Hot Rolled

With the help of orientation distribution function (ODF) analysis, experiments of different hot band grain microstructure 0.33% silicon steel were cold-rolled and annealed in the laboratory，to study the effect of the microstructure hot-rolled steel strip for cold rolled non-oriented silicon steel microstructure and texture of recrystallization annealing. The results show that hot rolled microstructure on cold rolled Non-Oriented Electrical Steel cold-rolled sheet evolution of texture and recrystallization have important influence, the quiaxed grain structure of steel by cold rolling and recrystallization annealing, the recrystallization speed than the fiber grain-based mixed crystals recrystallization fast , With the equiaxed grains made of cold rolled silicon steel after annealing the {110}<UVW> texture components was enhanced and {100}<uwv> texture components weakened. Different microstructure condition prior to cold rolling in the recrystallization annealing process the texture evolution has the obvious difference, the equiaxial grain steel belt cold rolling and annealing, has the strong crystal orientation. This shows that the equiaxed grain when hot microstructure is detrimental to the magnetic properties of cold-rolled non-oriented silicon steel to improve and increase.

Effects of Solubility Limit and the Presence of Ultra-Fine Al6Fe on the Kinetics of Grain Growth in Dilute Al-Fe Alloys

2007 ◽  
Vol 550 ◽  
pp. 339-344 ◽  
Author(s):  
Shigeo Saimoto ◽  
Hai Ou Jin
Keyword(s):  
Grain Size ◽  
Cold Rolling ◽  
Grain Growth ◽  
Solubility Limit ◽  
Rolled Sheet ◽  
Migration Rates ◽  
Cold Rolled ◽  
Fe Alloys ◽  
Grain Growth Kinetics ◽  
Kinetics Of

A nominally pure Al slab was thermo-mechanically treated to result in a near random texture of 90 m grain size. Subsequent cold rolling with intermediate anneals at 230, 275, and 300°C reduced the Fe solute to near equilibrium compositions below 0.5 ppm atomic. The final cold rolled sheet continuously recrystallized; grain growth of this structure is reported. A grain-growth kinetics mapping was generated, correlating the parameters of Fe-in-Al solubility limit, Fe diffusivities in the grain boundaries and the Al lattice and the activation energies for migration rates.