Preparation and Characterization of Electrodeposited CuxBi2Te3 Thermoelectric Films

2014 ◽  
Vol 787 ◽  
pp. 205-209
Author(s):  
Yue Chao Hu ◽  
Zhi Gang Zou ◽  
Ke Feng Cai
Keyword(s):  
Electrical Conductivity ◽  
Seebeck Coefficient ◽  
Indium Tin Oxide ◽  
Photoelectron Spectroscopy ◽  
X Ray Diffraction ◽  
Electro Deposition ◽  
X Ray ◽  
Glass Substrates ◽  
Higher Power

CuxBi2Te3films were prepared by chronopotentiometry electro-deposition on indium tin oxide (ITO)-coated glass substrates from an aqueous acidic electrolyte at room temperature. The films were deposited at the same current density but in electrolyte with different Cu2+concentrations: 0.1, 0.25, 0.5, 0.75 or 1mM. The phase composition and morphology of the films were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and field emission scanning electron microscope, respectively. The electrical conductivity and Seebeck coefficient of the CuxBi2Te3films were measured after being transferred onto a non-conductive rubberized fabric support. All the films showed n-type conduction with Seebeck coefficient in the range of-63 to-84μV/K, and the electrical conductivity in the range of 90 to 185S/cm. The film deposited from an electrolyte with 0.5mM Cu2+showed higher power factor ~130 μW/K-2m-1.

The Role of Sputter Pressure in Influencing Electrical and Optical Properties of ITO on Glass

2010 ◽  
Vol 1256 ◽  
Author(s):  
Shereen Elhalawaty ◽  
Karthik Sivaramakrishnan ◽  
Theodore David ◽  
Terry L Alford
Keyword(s):  
Indium Tin Oxide ◽  
Photoelectron Spectroscopy ◽  
Visible Spectrum ◽  
Rf Magnetron Sputtering ◽  
Thin Layers ◽  
X Ray Diffraction ◽  
X Ray ◽  
Glass Substrates ◽  
Hall Effect Measurements

AbstractThin layers of indium tin oxide (ITO) were deposited onto glass substrates by RF magnetron sputtering with the pressure varying from 6 mTorr to 15 mTorr. The films were annealed in a reducing atmosphere at 500 °C for 30 minutes. Sheet resistance was determined by four-point-probe measurement. Resistivity, mobility, and carrier concentration were obtained by Hall effect measurements. Transmission of the films in the visible spectrum was determined by photospectrometry. The structure of the films was characterized by X-ray diffraction. X-ray photoelectron spectroscopy was used to determine the oxidation state of Sn, which was used to determine the fraction of active tin clusters. The effect of additional anneals was investigated. The results reveal that the lowest resistivity obtained was 1.69×10-4 -cm at 9 mTorr and the highest transmittance of 90% was obtained after a second anneal. However, the second anneal decreased the mobility and conductivity for high sputter pressures.

Electrodeposition of Cu2O Particles by Using Electrolyte Solution Containing Glucopone as Surfactant

2009 ◽  
Vol 1 (2) ◽  
pp. 18-20
Author(s):  
Dahyunir Dahlan
Keyword(s):  
Indium Tin Oxide ◽  
Pulse Current ◽  
Platinum Electrode ◽  
Saturated Calomel Electrode ◽  
X Ray Diffraction ◽  
X Ray ◽  
Glass Substrates ◽  
Continuous Current ◽  
Oxide Particles ◽  
Cupric Sulphate

Copper oxide particles were electrodeposited onto indium tin oxide (ITO) coated glass substrates. Electrodeposition was carried out in the electrolyte containing cupric sulphate, boric acid and glucopone. Both continuous and pulse currents methods were used in the process with platinum electrode, saturated calomel electrode (SCE) and ITO electrode as the counter, reference and working electrode respectively. The deposited particles were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). It was found that, using continuous current deposition, the deposited particles were mixture of Cu2O and CuO particles. By adding glucopone in the electrolyte, particles with spherical shapes were produced. Electrodeposition by using pulse current, uniform cubical shaped Cu2O particles were produced

scholarly journals Reactive Dual Magnetron Sputtering: A Fast Method for Preparing Stoichiometric Microcrystalline ZnWO4 Thin Films

Surfaces ◽  
2021 ◽  
Vol 4 (2) ◽  
pp. 106-114
Author(s):  
Yannick Hermans ◽  
Faraz Mehmood ◽  
Kerstin Lakus-Wollny ◽  
Jan P. Hofmann ◽  
Thomas Mayer ◽  
...  
Keyword(s):  
Thin Films ◽  
Magnetron Sputtering ◽  
Photoelectron Spectroscopy ◽  
Fast Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Glass Substrates ◽  
Post Annealing ◽  
Rf Signal ◽  
First Time

Thin films of ZnWO4, a promising photocatalytic and scintillator material, were deposited for the first time using a reactive dual magnetron sputtering procedure. A ZnO target was operated using an RF signal, and a W target was operated using a DC signal. The power on the ZnO target was changed so that it would match the sputtering rate of the W target operated at 25 W. The effects of the process parameters were characterized using optical spectroscopy, X-ray diffraction, and scanning electron microscopy, including energy dispersive X-ray spectroscopy as well as X-ray photoelectron spectroscopy. It was found that stoichiometric microcrystalline ZnWO4 thin films could be obtained, by operating the ZnO target during the sputtering procedure at a power of 55 W and by post-annealing the resulting thin films for at least 10 h at 600 °C. As FTO coated glass substrates were used, annealing led as well to the incorporation of Na, resulting in n+ doped ZnWO4 thin films.

scholarly journals Fabrication and Characterization of Al/NiO Energetic Nanomultilayers

2015 ◽  
Vol 2015 ◽  
pp. 1-6 ◽  
Author(s):  
YiChao Yan ◽  
Wei Shi ◽  
HongChuan Jiang ◽  
Jie Xiong ◽  
WanLi Zhang ◽  
...  
Keyword(s):  
Photoelectron Spectroscopy ◽  
Total Thickness ◽  
X Ray Diffraction ◽  
Dc Magnetron Sputtering ◽  
Metallic Oxide ◽  
Promising Candidate ◽  
X Ray ◽  
Thermal Boundary Conductance ◽  
Fabrication And Characterization

The redox reaction between Al and metallic oxide has its advantage compared with intermetallic reaction and Al/NiO nanomutlilayers are a promising candidate for enhancing the performance of energetic igniter. Al/NiO nanomutlilayers with different modulation periods are prepared on alumina substrate by direct current (DC) magnetron sputtering. The thicknesses of each period are 250 nm, 500 nm, 750 nm, 1000 nm, and 1500 nm, respectively, and the total thickness is 3 μm. The X-ray diffraction (XRD) and scanning electron microscope (SEM) results of the as-deposited Al/NiO nanomutlilayers show that the NiO films are amorphous and the layered structures are clearly distinguished. The X-ray photoelectron spectroscopy (XPS) demonstrates that the thickness of Al2O3increases on the side of Al monolayer after annealing at 450°C. The thermal diffusion time becomes greater significantly as the amount of thermal boundary conductance across the interfaces increases with relatively smaller modulation period. Differential scanning calorimeter (DSC) curve suggests that the energy release per unit mass is below the theoretical heat of the reaction due to the nonstoichiometric ratio between Al and NiO and the presence of impurities.

Preparation and Characterization of γ-Fe2O3-ZnFe2O4 Composite Nanoparticles

2013 ◽  
Vol 873 ◽  
pp. 152-157
Author(s):  
Long Long Chen ◽  
Jun Ming Li ◽  
Xiao Min Gong ◽  
Jian Li
Keyword(s):  
Photoelectron Spectroscopy ◽  
Chemical Species ◽  
Composite Nanoparticles ◽  
X Ray Diffraction ◽  
Ferrite Core ◽  
Phase Synthesis ◽  
X Ray ◽  
Transmission Electron ◽  
Chemically Induced

Using a chemically induced transition in an FeCl2 solution, γ-Fe2O3 nanoparticles can be prepared from an amorphous precursor composed of FeOOH and Mg (OH)2. Surface modification by adding ZnCl2 during liquid-phase synthesis was attempted. The magnetization, morphology, crystal structure, and chemical species of as-prepared samples were characterized by vibrating sample magnetometer (VSM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray energy-dispersive spectroscopy (EDX), and X-ray photoelectron spectroscopy (XPS). The experimental results showed that the surface of the γ-Fe2O3 nanoparticles can be modified by adding ZnCl2 to form composite nanoparticles with a γ-Fe2O3/ZnFe2O4 ferrite core coated with Zn (OH)2 and absorbed FeCl36H2O; this modification can be enhanced by additional NaOH.

Effect of Substrate Temperature on the Electrochromic Properties of Cobalt Hydroxide Thin Films Prepared by Reactive Sputtering

2011 ◽  
Vol 1328 ◽  
Author(s):  
KyoungMoo Lee ◽  
Yoshio Abe ◽  
Midori Kawamura ◽  
Hidenobu Itoh
Keyword(s):  
Thin Films ◽  
Substrate Temperature ◽  
Indium Tin Oxide ◽  
Large Change ◽  
Amorphous Structure ◽  
Cobalt Hydroxide ◽  
X Ray Diffraction ◽  
X Ray ◽  
Glass Substrates ◽  
Substrate Temperatures

ABSTRACTCobalt hydroxide thin films with a thickness of 100 nm were deposited onto glass, Si and indium tin oxide (ITO)-coated glass substrates by reactively sputtering a Co target in H2O gas. The substrate temperature was varied from -20 to +200°C. The EC performance of the films was investigated in 0.1 M KOH aqueous solution. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy of the samples indicated that Co3O4 films were formed at substrate temperatures above 100°C, and amorphous CoOOH films were deposited in the range from 10 to -20°C. A large change in transmittance of approximately 26% and high EC coloration efficiency of 47 cm2/C were obtained at a wavelength of 600 nm for the CoOOH thin film deposited at -20°C. The good EC performance of the CoOOH films is attributed to the low film density and amorphous structure.

scholarly journals Copper Containing Glass-Based Bone Adhesives for Orthopaedic Applications: Glass Characterization and Advanced Mechanical Evaluation

2020 ◽  
Author(s):  
Sahar. Mokhtari ◽  
Anthony.W. Wren
Keyword(s):  
Mechanical Properties ◽  
Photoelectron Spectroscopy ◽  
Structural Changes ◽  
Viscoelastic Behavior ◽  
Polymer Chains ◽  
Nano Particles ◽  
X Ray Diffraction ◽  
X Ray ◽  
Compression Data

AbstractThis study addresses issues with currently used bone adhesives, by producing novel glass based skeletal adhesives through modification of the base glass composition to include copper (Cu) and by characterizing each glass with respect to structural changes. Bioactive glasses have found applications in fields such as orthopedics and dentistry, where they have been utilized for the restoration of bone and teeth. The present work outlines the formation of flexible organic-inorganic polyacrylic acid (PAA) – glass hybrids, commercial forms are known as glass ionomer cements (GICs). Initial stages of this research will involve characterization of the Cu-glasses, significant to evaluate the properties of the resulting adhesives. Scanning electron microscopy (SEM) of annealed Cu glasses indicates the presence of partial crystallization in the glass. The structural analysis of the glass using Raman suggests the formation of CuO nanocrystals on the surface. X-ray diffraction (XRD) pattern and X-ray photoelectron spectroscopy (XPS) further confirmed the formation of crystalline CuO phases on the surface of the annealed Cu-glass. The setting reaction was studied using Fourier transform infrared spectroscopy (ATR-FTIR). The mechanical properties of the Cu containing adhesives exhibited gel viscoelastic behavior and enhanced mechanical properties when compared to the control composition. Compression data indicated the Cu glass adhesives were efficient at energy dissipation due to the reversible interactions between CuO nano particles and PAA polymer chains.

Synthesis and characterization of homogeneous lead-substituted tin oxide with the (110) face of rutile structure

2000 ◽  
Vol 15 (10) ◽  
pp. 2076-2079
Author(s):  
Chika Nozaki ◽  
Takashi Yamada ◽  
Kenji Tabata ◽  
Eiji Suzuki
Keyword(s):  
Electron Microscopy ◽  
Tin Oxide ◽  
Photoelectron Spectroscopy ◽  
Synthesis And Characterization ◽  
X Ray Diffraction ◽  
Rutile Structure ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

Synthesis of a rutile-type lead-substituted tin oxide with (110) face was investigated. The characterization was performed by x-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive x-ray spectroscopy, infrared spectroscopy, x-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller surface area measurements. The homogeneous rutile-type lead-substituted tin oxide was obtained until 4.1 mol% of tin was substituted with lead. The surface of obtained oxide had a homogeneously lead-substituted (110) face.

scholarly journals Synthesis, Crystal Structures, and Spectroscopic Characterization of Bis-aldehyde Monomers and Their Electrically Conductive Pristine Polyazomethines

Polymers ◽  
2019 ◽  
Vol 11 (9) ◽  
pp. 1498 ◽  
Author(s):  
Abdul Hafeez ◽  
Zareen Akhter ◽  
John F. Gallagher ◽  
Nawazish Ali Khan ◽  
Asghari Gul ◽  
...  
Keyword(s):  
Electrical Conductivity ◽  
Spectroscopic Characterization ◽  
Spectroscopic Techniques ◽  
Conductivity Measurements ◽  
X Ray Diffraction ◽  
Electrically Conductive ◽  
X Ray ◽  
Vis Spectroscopy ◽  
Ft Ir

Bis-aldehyde monomers 4-(4′-formyl-phenoxy)benzaldehyde (3a), 3-methoxy-4-(4′-formyl-phenoxy)benzaldehyde (3b), and 3-ethoxy-4-(4′-formyl-phenoxy)benzaldehyde (3c) were synthesized by etherification of 4-fluorobenzaldehyde (1) with 4-hydroxybenzaldehyde (2a), 3-methoxy-4-hydroxybenzaldehyde (2b), and 3-ethoxy-4-hydroxybenzaldehyde (2c), respectively. Each monomer was polymerized with p-phenylenediamine and 4,4′-diaminodiphenyl ether to yield six poly(azomethine)s. Single crystal X-ray diffraction structures of 3b and 3c were determined. The structural characterization of the monomers and poly(azomethine)s was performed by FT-IR and NMR spectroscopic techniques and elemental analysis. Physicochemical properties of polymers were investigated by powder X-ray diffraction, thermogravimetric analysis (TGA), viscometry, UV–vis, spectroscopy and photoluminescence. These polymers were subjected to electrical conductivity measurements by the four-probe method, and their conductivities were found to be in the range 4.0 × 10−5 to 6.4 × 10−5 Scm−1, which was significantly higher than the values reported so far.

Sign in / Sign up

Export Citation Format

Share Document