scholarly journals Surface roughness and wettability of surface densified heat-treated Norway spruce (Picea abies L. Karst.)

2019 ◽  
Vol 70 (4) ◽  
pp. 377-382
Author(s):  
Nadir Ayrilmis ◽  
Mirko Kariz ◽  
Jin Heon Kwon ◽  
Manja Kitek Kuzman
Keyword(s):  
Heat Treatment ◽  
Surface Roughness ◽  
Picea Abies ◽  
Cold Water ◽  
Longitudinal Direction ◽  
Tangential Direction ◽  
Treatment Temperature ◽  
Densified Wood ◽  
Surface Densification ◽  
Heat Treated

Surface roughness and wettability of the heat-treated and then surface densified spruce (Picea abies L. Karst.) wood were measured to determine the effect of densification and heat-treatment on wood surface properties. The process of heat-treatment with an initial vacuum was performed in a vacuum chamber on oven dried lamellas with dimensions of 630 mm (longitudinal direction) x 45 mm (tangential direction) x 25 mm (radial direction). The lamellas were heat-treated at four different temperatures which were 170 °C, 190 °C, 210 °C and 230 °C. Control specimens were not exposed to heat-treatment. The lamellas were first heated to 100 °C, the creation of a vacuum taking 30 min at this temperature, and then heated to the desired temperature, and treated at this constant temperature for 3 h. The lamellas were then cooled down by using coils with cold water inside the chamber. Surface densification of lamellas with compression from 22 mm to 15 mm thickness was made by press platens heated at 150 °C and held in that position for 60 s. After the 1 min, the heated platen was cooled to 90 °C, whilst the specimen remained under compression to minimize immediate spring back. The total time of compression was 2 min (30 s closing, 60 s pressing and approx. 30 s cooling). In the treatment groups, the optimum treatment temperature on the one-side densified wood specimens was found to be 170 °C based on the surface roughness and wettability values. Surface densification significantly decreased the surface roughness of the wood specimens. The surface quality of wood can be improved when the wood is exposed to the heat-treatment and then surface densification.

INFLUENCE THE QUENCHING AND TEMPERING ON THE MICROSTRUCTURE, MECHANICAL PROPERTIES AND SURFACE ROUGHNESS, OF MEDIUM CARBON STEEL

2018 ◽  
Vol 18 (1) ◽  
pp. 125-135
Author(s):  
Sattar H A Alfatlawi
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Surface Roughness ◽  
Carbon Steel ◽  
Cold Water ◽  
Medium Carbon Steel ◽  
Medium Carbon ◽  
Heating And Cooling ◽  
Treatment Processes ◽  
Quenching And Tempering

One of ways to improve properties of materials without changing the product shape toobtain the desired engineering applications is heating and cooling under effect of controlledsequence of heat treatment. The main aim of this study was to investigate the effect ofheating and cooling on the surface roughness, microstructure and some selected propertiessuch as the hardness and impact strength of Medium Carbon Steel which treated at differenttypes of heat treatment processes. Heat treatment achieved in this work was respectively,heating, quenching and tempering. The specimens were heated to 850°C and left for 45minutes inside the furnace as a holding time at that temperature, then quenching process wasperformed in four types of quenching media (still air, cold water (2°C), oil and polymersolution), respectively. Thereafter, the samples were tempered at 200°C, 400°C, and 600°Cwith one hour as a soaking time for each temperature, then were all cooled by still air. Whenthe heat treatment process was completed, the surface roughness, hardness, impact strengthand microstructure tests were performed. The results showed a change and clearimprovement of surface roughness, mechanical properties and microstructure afterquenching was achieved, as well as the change that took place due to the increasingtoughness and ductility by reducing of brittleness of samples.

scholarly journals Enhancing Graphene Retention and Electrical Conductivity of Plasma-Sprayed Alumina/Graphene Nanoplatelets Coating by Powder Heat Treatment

Coatings ◽  
2021 ◽  
Vol 11 (6) ◽  
pp. 643
Author(s):  
Xiaoyu Wu ◽  
Shufeng Xie ◽  
Kangwei Xu ◽  
Lei Huang ◽  
Daling Wei ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Electrical Conductivity ◽  
Structural Integrity ◽  
Ceramic Coatings ◽  
Treatment Temperature ◽  
Graphene Nanoplatelets ◽  
Structural Defects ◽  
Temperature Plasma ◽  
Heat Treated ◽  
Plasma Sprayed

Burning loss of graphene in the high-temperature plasma-spraying process is a critical issue, significantly limiting the remarkable performance improvement in graphene reinforced ceramic coatings. Here, we reported an effective approach to enhance the graphene retention, and thus improve the performance of plasma-sprayed alumina/graphene nanoplatelets (Al2O3/GNPs) coatings by heat treatment of agglomerated Al2O3/GNPs powders. The effect of powder heat treatment on the microstructure, GNPs retention, and electrical conductivity of Al2O3/GNPs coatings were systematically investigated. The results indicated that, with the increase in the powder heat treatment temperature, the plasma-sprayed Al2O3/GNPs coatings exhibited decreased porosity and improved adhesive strength. Thermogravimetric analysis and Raman spectra results indicated that increased GNPs retention from 12.9% to 28.4%, and further to 37.4%, as well as decreased structural defects, were obtained for the AG, AG850, and AG1280 coatings, respectively, which were fabricated by using AG powders without heat treatment, powders heat-treated at 850 °C, and powders heat-treated at 1280 °C. Moreover, the electrical conductivities of AG, AG850, and AG1280 coatings exhibited 3 orders, 4 orders, and 7 orders of magnitude higher than that of Al2O3 coating, respectively. Powder heat treatment is considered to increase the melting degree of agglomerated alumina particles, eventually leaving less thermal energy for GNPs to burn; thus, a high retention amount and structural integrity of GNPs and significantly enhanced electrical conductivity were achieved for the plasma-sprayed Al2O3/GNPs coatings.

scholarly journals Water Resistance and Creep Behavior of Heat-Treated Moso Bamboo Determined by the Stepped Isostress Method

Polymers ◽  
2021 ◽  
Vol 13 (8) ◽  
pp. 1264
Author(s):  
Teng-Chun Yang ◽  
Tung-Lin Wu ◽  
Chin-Hao Yeh
Keyword(s):  
Heat Treatment ◽  
Water Absorption ◽  
Creep Behavior ◽  
Heat Treatment Temperature ◽  
Water Resistance ◽  
Absorption Efficiency ◽  
Treatment Temperature ◽  
Moso Bamboo ◽  
Phyllostachys Pubescens ◽  
Heat Treated

The influence of heat treatment on the physico-mechanical properties, water resistance, and creep behavior of moso bamboo (Phyllostachys pubescens) was determined in this study. The results revealed that the density, moisture content, and flexural properties showed negative relationships with the heat treatment temperature, while an improvement in the dimensional stability (anti-swelling efficiency and anti-water absorption efficiency) of heat-treated samples was observed during water absorption tests. Additionally, the creep master curves of the untreated and heat-treated samples were successfully constructed using the stepped isostress method (SSM) at a series of elevated stresses. Furthermore, the SSM-predicted creep compliance curves fit well with the 90-day full-scale experimental data. When the heat treatment temperature increased to 180 °C, the degradation ratio of the creep resistance (rd) significantly increased over all periods. However, the rd of the tested bamboo decreased as the heat treatment temperature increased up to 220 °C.

Effect of Heat Treatment on the Microstructure and Property of TiAl Alloys Prepared by Gas Atomization Powders

2013 ◽  
Vol 747-748 ◽  
pp. 497-501
Author(s):  
Na Liu ◽  
Zhou Li ◽  
Guo Qing Zhang ◽  
Hua Yuan ◽  
Wen Yong Xu ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Heat Treatment Temperature ◽  
Tial Alloy ◽  
Lamellar Microstructure ◽  
Treatment Temperature ◽  
Gas Atomization ◽  
Thermally Induced ◽  
Heat Treated ◽  
Fine Duplex ◽  
Step Heat Treatment

Powder metallurgical TiAl alloy was fabricated by gas atomization powders, and the effect of heat treatment temperature on the microstructure evolution and room tensile properties of PM TiAl alloy was investigated. The uniform fine duplex microstructure was formed in PM TiAl based alloy after being heat treated at 1250/2h followed by furnace cooling (FC)+ 900/6h (FC). When the first step heat treatment temperature was improved to 1360/1h, the near lamellar microstructure was achieved. The ductility of the alloy after heat treatment improved markedly to 1.2% and 0.6%, but the tensile strength decreased to 570MPa and 600MPa compared to 655MPa of as-HIP TiAl alloy. Post heat treatment at the higher temperature in the alpha plus gamma field would regenerate thermally induced porosity (TIP).

Mechanical and Superelastic Properties of Au-51Ti-18Co Biomedical Shape Memory Alloy Heat-Treated at 1173 K to 1373 K

2016 ◽  
Vol 97 ◽  
pp. 141-146 ◽  
Author(s):  
Taywin Buasri ◽  
Hyunbo Shim ◽  
Masaki Tahara ◽  
Tomonari Inamura ◽  
Kenji Goto ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Heat Treatment Temperature ◽  
Critical Stress ◽  
Biomedical Applications ◽  
Shape Recovery ◽  
Treatment Temperature ◽  
Recovery Ratio ◽  
Recovery Strain ◽  
Heat Treated ◽  
Alloy Heat

The effect of heat treatment temperature from 1173 K to 1373 K for 3.6 ks on mechanical and superelastic properties of an Ni-free Au-51Ti-18Co alloy (mol%) was investigated. The stress for inducing martensitic transformation (SIMT) and the critical stress for slip deformation (CSS) slightly decrease with increasing the heat–treatment temperature. Regardless of heat–treatment temperature, good superelasticity was definitely recognized with the maximum shape recovery ratio up to 95 % and 4 % superelastic shape recovery strain. As the mentioned reasons, the Au-51Ti-18Co alloy is promising for practical biomedical applications.

Investigation of Heat Treated Electrodeposited CoNiFe on Microstructure and Hardness

2015 ◽  
Vol 1113 ◽  
pp. 56-61
Author(s):  
Nor Azrina Resali ◽  
Koay Mei Hyie ◽  
M.N. Berhan ◽  
C.M. Mardziah
Keyword(s):  
Heat Treatment ◽  
Heat Treatment Temperature ◽  
Treatment Temperature ◽  
Crystallographic Structure ◽  
Face Centered Cubic ◽  
Heat Treated ◽  
Hardness Property ◽  
Finishing Process ◽  
The Face ◽  
Face Centered

In this research, heat treatment is the final finishing process applied on nanocrystalline CoNiFe to improve microstructure for good hardness property. Nanocrystalline CoNiFe has been synthesized using the electrodeposition method. This study investigated the effect of heat treatment at 500°C, 600°C, 700°C and 800°C on electrodeposited nanocrystalline CoNiFe. The heat treatment process was performed in the tube furnace with flowing Argon gas. By changing the heat treatment temperature, physical properties such as phase and crystallographic structure, surface morphology, grain size and hardness of nanocrystalline CoNiFe was studied. The nanocrystalline CoNiFe phase revealed the Face Centered Cubic (FCC) and Body Centered Cubic (BCC) crystal structure. FESEM micrographs showed that the grain sizes of the coatings were in the range of 78.76 nm to 132 nm. Dendrite shape was found in the microstructure of nanocrystalline CoNiFe. The nanocrystalline CoNiFe prepared in heat treatment temperature of 700°C, achieved the highest hardness of 449 HVN. The surface roughness of nanocrystalline CoNiFe heated at 700°C was found to be smaller than other temperatures.

scholarly journals Tribological Behavior and Analysis on Surface Roughness of CNC Milled Dual Heat Treated Al6061 Composites

2021 ◽  
Vol 2021 ◽  
pp. 1-14
Author(s):  
A. Bovas Herbert Bejaxhin ◽  
G.M. Balamurugan ◽  
S.M. Sivagami ◽  
K. Ramkumar ◽  
V. Vijayan ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Surface Roughness ◽  
Lower Surface ◽  
Cnc Machining ◽  
Depth Of Cut ◽  
Good Surface ◽  
Heat Treated ◽  
Good Surface Finish ◽  
Artificial Neural Network Ann ◽  
Machining Properties

Dual heat treatment (DHT) effect is analyzed using the machining of Al6061-T6 alloy, a readily available material for quickly finding the machining properties. The heat treatments are conducted twice over the specimen by the furnace heating before processing through CNC machining. The HSS and WC milling cutters are preferred for the diameter of 10 mm for the reviewed rotational speeds of 2000 rpm and 4000 rpm, and the constant depth of cut of 0.5 mm is chosen based on various reviews. Worthy roughness could be provided mostly by the influence of feed rates preferred here as 0.05 mm/rev and 0.1 mm/rev. The influencing factors are identified by the Taguchi, genetic algorithm (GA), and Artificial Neural Network (ANN) techniques and compared within it. The simulation finding also helps to clarify the relationship between influenced machining constraints and roughness outcomes of this project. The average values of heat treated and nonheat treated Al6061-T6 are compared and it is to be evaluated that 41% improvement is obtained with the lower surface roughness of 1.78975 µm and it shows good surface finish with the help of dual heat treatment process.

Effects of Heat-Treatment Temperature on the Properties of Negative CTE Eucryptite Ceramics

2010 ◽  
Vol 105-106 ◽  
pp. 123-125 ◽  
Author(s):  
Yong Li ◽  
Qi Hong Wei ◽  
Ling Li ◽  
Chong Hai Wang ◽  
Xiao Li Zhang ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Thermal Expansion ◽  
Thermal Expansion Coefficient ◽  
Expansion Coefficient ◽  
Heat Treatment Temperature ◽  
Bending Strength ◽  
Sol Gel ◽  
Negative Thermal Expansion ◽  
Treatment Temperature ◽  
Heat Treated

In this paper, negative thermal expansion coefficient eucryptite powders were prepared by sol-gel method using silica-sol as starting material. The raw blocks were obtained by dry pressing process after the powder was synthesized, and then the raw blocks were heat-treated at 600º, 1150º, 1280º, 1380º, 1420º and 1450°C, respectively. Variations of density, porosity and thermal expansion coefficient at different heat treatment temperatures were investigated. Phase transformation and fracture surface morphology of eucryptite heat-treated at different temperatures, respectively, were observed by XRD and SEM. The results indicate that, with the increasing heat- treatment temperature, the grain size and the bending strength increased, porosity decreased, thermal expansion coefficient decreased continuously. Negative thermal expansion coefficient of -5.3162×10-6~-7.4413×10-6 (0~800°C) was obtained. But when the heat-treatment temperature was more than 1420°C, porosity began to increase, bending strength began to decrease, which were the symbols of over-burning, while the main crystal phase didn’t change.

scholarly journals Effect of Heat Treatment Temperature on Martensitic Transformation and Superelasticity of the Ti49Ni51 Shape Memory Alloy

Materials ◽  
2019 ◽  
Vol 12 (16) ◽  
pp. 2539 ◽  
Author(s):  
Peiyou Li ◽  
Yongshan Wang ◽  
Fanying Meng ◽  
Le Cao ◽  
Zhirong He
Keyword(s):  
Heat Treatment ◽  
Martensitic Transformation ◽  
Shape Memory Alloy ◽  
Shape Memory ◽  
Thermal Hysteresis ◽  
Treatment Temperature ◽  
Heat Treated ◽  
Different Temperatures ◽  
Tini Phase ◽  
Rapidly Solidified

The martensitic transformation and superelasticity of Ti49Ni51 shape memory alloy heat-treatment at different temperatures were investigated. The experimental results show that the microstructures of as-cast and heat-treated (723 K) Ni-rich Ti49Ni51 samples prepared by rapidly-solidified technology are composed of B2 TiNi phase, and Ti3Ni4 and Ti2Ni phases; the microstructures of heat-treated Ti49Ni51 samples at 773 and 823 K are composed of B2 TiNi phase, and of B2 TiNi and Ti2Ni phases, respectively. The martensitic transformation of as-cast Ti49Ni51 alloy is three-stage, A→R→M1 and R→M2 transformation during cooling, and two-stage, M→R→A transformation during heating. The transformations of the heat-treated Ti49Ni51 samples at 723 and 823 K are the A↔R↔M/A↔M transformation during cooling/heating, respectively. For the heat-treated alloy at 773 K, the transformations are the A→R/M→R→A during cooling/heating, respectively. For the heat-treated alloy at 773 K, only a small thermal hysteresis is suitable for sensor devices. The stable σmax values of 723 and 773 K heat-treated samples with a large Wd value exhibit high safety in application. The 773 and 823 K heat-treated samples have large stable strain–energy densities, and are a good superelastic alloy. The experimental data obtained provide a valuable reference for the industrial application of rapidly-solidified casting and heat-treated Ti49Ni51 alloy.

Effect of Heat Treatment on the Combustion Characteristics of a Lignite

2019 ◽  
Vol 141 (7) ◽  
Author(s):  
Zhezi Zhang ◽  
Mingming Zhu ◽  
Jianbo Li ◽  
Kai Zhang ◽  
Guoqing Shen ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Ignition Delay ◽  
Delay Time ◽  
Heat Treatment Temperature ◽  
Ignition Delay Time ◽  
Treatment Temperature ◽  
Ftir Analysis ◽  
Single Particles ◽  
Heat Treated ◽  
Ignition And Combustion

In this study, the ignition and combustion behavior of raw and heat-treated single particles of lignite were experimentally investigated, with a focus on the effect of heat treatment temperatures. The lignite particles were heat treated to various final temperatures (473, 623 and 773 K) in nitrogen and characterized using proximate, ultimate, and Fourier transform infrared spectroscopy (FTIR) analysis. A single lignite particle of 2 or 3 mm in diameter was suspended on a silicon carbide fiber and burned in air in a horizontal tube furnace operating at 1123 K. The ignition and combustion process of the particle was record using a color CCD camera at 25 fps. The ignition mechanism, ignition delay time, volatile flame duration, and burnout time of the single particles were examined by processing the recorded images. The proximate and ultimate analysis results indicated that the volatile matter and oxygen contents decreased, while the carbon content increased with increasing temperature of heat treatment. This trend was consistent with observations in the FTIR analysis, in which the intensity of oxygen-containing functional groups decreased with increasing the heat treatment temperature. The ignition of raw and heat treated lignite particles followed a joint hetero-homogeneous mechanism under all conditions studied. The ignition delay time, volatile flame extinction time, and the total combustion time decreased with increasing heat treatment temperature up to 623 K. A further increase in the heat treatment temperature to 773 K resulted in prolonged key ignition and combustion characteristic times.

Sign in / Sign up

Export Citation Format

Share Document