Mechanical Properties of Oxidized Zr-1Nb-0.7Sn-0.1Fe Alloy Nuclear Cladding Tubes at High Temperatures

2012 ◽  
Vol 557-559 ◽  
pp. 1157-1160
Author(s):  
Eun Kyu Lee ◽  
Sun Ig Hong
Keyword(s):  
Mechanical Properties ◽  
Brittle Fracture ◽  
Oxide Layer ◽  
Oxidation Rate ◽  
Volume Fraction ◽  
Ductility Loss ◽  
Drastic Increase ◽  
Porous Oxide ◽  
Tin Content ◽  
Oxidation Behaviors

The ductility loss and the failure of cladding tubes due to oxidation are considered as a threat to the safety of the nuclear. In this study, oxidation behaviors and the effect of oxide layer on the mechanical properties of Zr-1Nb-0.7Sn-0.1Fe alloy cladding tubes with a lower tin content (<1 wt. %) were investigated. The drastic increase of the oxidation rate at 700oC suggests the change in the nature of the oxide layer with increase of temperature. The acceleration of the oxidation rate for Zr-1Nb-0.7Sn-0.1Fe alloy tubes at 700oC suggests the increased volume fraction of less protective porous oxide, supported by the presence of oxide cracks even before mechanical testing. The ductility increased after oxidation at 600oC, suggesting softening due to recovery and recrystallization is predominant over the ductility loss caused by oxidation. The ductility began to decrease significantly after oxidation at 700oC and cladding tubes exhibited the brittle fracture.

scholarly journals IMCs Microstructure Evolution Dependence of Mechanical Properties for Ni/Sn/Ni Micro Solder-Joints

Materials ◽  
2020 ◽  
Vol 13 (1) ◽  
pp. 252 ◽  
Author(s):  
Ning Ren ◽  
Heng Fang ◽  
Dong Wang ◽  
Chenyi Hou ◽  
Yatao Zhao ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Brittle Fracture ◽  
Ductile Fracture ◽  
Solder Joints ◽  
Volume Fraction ◽  
Tensile Tests ◽  
Stress Concentrations ◽  
Element Analysis ◽  
Scale Down ◽  
Long Rod

The current miniaturization trend of microelectronic devices drives the size of solder joints to continually scale down. The miniaturized joints considerably increase intermetallic compounds (IMCs) volume fraction to trigger mechanical reliability issues. This study investigated precise relationships between varying IMC volumes and mechanical properties of Ni/Sn(20μm)/Ni micro-joints. A designed method that followed the IMC volume as the only variable was used to prepare micro-joint samples with different IMC volumes. The continuously thickened Ni3Sn4 IMCs exhibited a noticeable morphology evolution from rod-like to chunky shape. The subsequent tensile tests showed unexpected tensile strength responses as increasing Ni3Sn4 volume, which was strongly associated with the Ni3Sn4 morphological evolutions. Fractographic analysis displayed that the ductile fracture dominates the 20%–40% IMC micro-joints, whereas the brittle fracture governs the 40%–80% IMC micro-joints. For the ductile fracture-dominated joints, an abnormal reduction in strength occurred as increasing IMCs volume from 20% to 40%. This is primarily due to severe stress concentrations caused by the transformed long rod-typed morphology of the Ni3Sn4. For the brittle fracture-dominated joints, the strength appeared a monotonous increase as the Ni3Sn4 volume increased. This may be attributed to the increased crack resistance resulting from continuous coarsening of the chunky Ni3Sn4 without any voids. Moreover, the finite element analysis was provided to further understand the joint failure mechanisms.

Mechanical Properties of SiCp/Cu Composites Prepared by Electric Conduction Sintering

2007 ◽  
Vol 353-358 ◽  
pp. 1402-1405 ◽  
Author(s):  
Chun Hua Wang ◽  
Shao Kang Guan ◽  
Shou Shan Li ◽  
Rui Zhang
Keyword(s):  
Mechanical Properties ◽  
Brittle Fracture ◽  
Flexural Strength ◽  
Ductile Fracture ◽  
Fracture Behavior ◽  
Volume Fraction ◽  
Electric Conduction

SiCp/Cu composites were fabricated at 700 oC and under 40MPa for 10min in vacuum by electric conduction sintering. The mechanical properties and microstructure of the composites were studied. The porosity of the composites increases when the volume fraction of SiCp exceeds 35%. The flexural strength of the composites decreases with increasing fraction of SiCp. The composites with 10 vol.% SiCp exhibited ductile fracture behavior, while composites with the volume fraction of SiCp in the range of 20–65% exhibited brittle fracture behavior. The composites with 35 vol.% SiCp showed the highest hardness.

Macroprobe Mode for the Study of Segregation in Steels

1990 ◽  
Vol 48 (2) ◽  
pp. 260-261
Author(s):  
Auclair Gilles ◽  
Benoit Danièle
Keyword(s):  
Mechanical Properties ◽  
Spatial Distribution ◽  
High Performance ◽  
Volume Fraction ◽  
Sheet Steel ◽  
Acquisition Time ◽  
Chemical Information ◽  
X Ray ◽  
Accurate Quantitative Analysis ◽  
Optical Micrographs

During these last 10 years, high performance correction procedures have been developed for classical EPMA, and it is nowadays possible to obtain accurate quantitative analysis even for soft X-ray radiations. It is also possible to perform EPMA by adapting this accurate quantitative procedures to unusual applications such as the measurement of the segregation on wide areas in as-cast and sheet steel products.The main objection for analysis of segregation in steel by means of a line-scan mode is that it requires a very heavy sampling plan to make sure that the most significant points are analyzed. Moreover only local chemical information is obtained whereas mechanical properties are also dependant on the volume fraction and the spatial distribution of highly segregated zones. For these reasons we have chosen to systematically acquire X-ray calibrated mappings which give pictures similar to optical micrographs. Although mapping requires lengthy acquisition time there is a corresponding increase in the information given by image anlysis.

ffect of Na2WO4 in electrolyte on mechanical properties of oxide layer on Al alloy via plasma electrolytic oxidation

2015 ◽  
Vol 53 (8) ◽  
pp. 535-540 ◽  
Author(s):  
Young Gun Ko ◽  
Dong Hyuk Shin ◽  
Hae Woong Yang ◽  
Yeon Sung Kim ◽  
Joo Hyun Park ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Oxide Layer ◽  
Plasma Electrolytic Oxidation ◽  
Al Alloy ◽  
Electrolytic Oxidation ◽  
Plasma Electrolytic

A Study of Some Mechanical and Physical Properties for Palm Fiber/Polyester Composite

2020 ◽  
Vol 38 (3B) ◽  
pp. 104-114
Author(s):  
Samah M. Hussein
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Dielectric Constant ◽  
Date Palm ◽  
Volume Fraction ◽  
Unsaturated Polyester ◽  
Dielectric Strength ◽  
Palm Fiber ◽  
Mechanical And Physical Properties ◽  
Polyester Composite

This research has been done by reinforcing the matrix (unsaturated polyester) resin with natural material (date palm fiber (DPF)). The fibers were exposure to alkali treatment before reinforcement. The samples have been prepared by using hand lay-up technique with fiber volume fraction of (10%, 20% and 30%). After preparation of the mechanical and physical properties have been studied such as, compression, flexural, impact strength, thermal conductivity, Dielectric constant and dielectric strength. The polyester composite reinforced with date palm fiber at volume fraction (10% and 20%) has good mechanical properties rather than pure unsaturated polyester material, while the composite reinforced with 30% Vf present poor mechanical properties. Thermal conductivity results indicated insulator composite behavior. The effect of present fiber polar group induces of decreasing in dielectric strength, and increasing dielectric constant. The reinforcement composite 20% Vf showed the best results in mechanical, thermal and electrical properties.

Effect of Titanium Carbide Particles on Mechanical Properties of Aluminum Matrix Composites

2017 ◽  
Vol 5 (2) ◽  
pp. 20-30
Author(s):  
Zaman Khalil Ibrahim
Keyword(s):  
Mechanical Properties ◽  
Titanium Carbide ◽  
Compression Strength ◽  
Volume Fraction ◽  
Aluminum Matrix ◽  
Aluminum Matrix Composites ◽  
Matrix Composites ◽  
Powder Metallurgy Technique ◽  
Carbide Particles ◽  
Properties Of Composites

In this research aluminum matrix composites (AMCs) was reinforced by titanium carbide (TiC) particles and was produced. Powder metallurgy technique (PM) has been used to fabricate AMCs reinforced with various amounts (0%, 4%, 8%, 12%, 16% and 20% volume fraction) of TiC particles to study the effect of different volume fractions on mechanical properties of the Al-TiC composites. Measurements of compression strength and hardness showed that mechanical properties of composites increased with an increase in volume fraction of TiC Particles. Al-20 % vol. TiC composites exhibited the best properties with hardness value (97HRB) and compression strength value (275Mpa).

Monitoring of mechanical properties of prestressed glass fiber epoxy composites over 12 months after fabrication

2021 ◽  
pp. 002199832110047
Author(s):  
Mahmoud Mohamed ◽  
Siddhartha Brahma ◽  
Haibin Ning ◽  
Selvum Pillay
Keyword(s):  
Mechanical Properties ◽  
Residual Stress ◽  
Flexural Strength ◽  
Compressive Residual Stress ◽  
Fiber Volume Fraction ◽  
Volume Fraction ◽  
Epoxy Composites ◽  
Flexural Properties ◽  
Initial Increase ◽  
Fiber Volume

Fiber prestressing during matrix curing can significantly improve the mechanical properties of fiber-reinforced polymer composites. One primary reason behind this improvement is the generated compressive residual stress within the cured matrix, which impedes cracks initiation and propagation. However, the prestressing force might diminish progressively with time due to the creep of the compressed matrix and the relaxation of the tensioned fiber. As a result, the initial compressive residual stress and the acquired improvement in mechanical properties are prone to decline over time. Therefore, it is necessary to evaluate the mechanical properties of the prestressed composites as time proceeds. This study monitors the change in the tensile and flexural properties of unidirectional prestressed glass fiber reinforced epoxy composites over a period of 12 months after manufacturing. The composites were prepared using three different fiber volume fractions 25%, 30%, and 40%. The results of mechanical testing showed that the prestressed composites acquired an initial increase up to 29% in the tensile properties and up to 32% in the flexural properties compared to the non-prestressed counterparts. Throughout the 12 months of study, the initial increase in both tensile and flexural strength showed a progressive reduction. The loss ratio of the initial increase was observed to be inversely proportional to the fiber volume fraction. For the prestressed composites fabricated with 25%, 30%, and 40% fiber volume fraction, the initial increase in tensile and flexural strength dropped by 29%, 25%, and 17%, respectively and by 34%, 26%, and 21%, respectively at the end of the study. Approximately 50% of the total loss took place over the first month after the manufacture, while after the sixth month, the reduction in mechanical properties became insignificant. Tensile modulus started to show a very slight reduction after the fourth/sixth month, while the flexural modulus reduction was observed from the beginning. Although the prestressed composites displayed time-dependent losses, their long-term mechanical properties still outperformed the non-prestressed counterparts.

scholarly journals Heat Treatment Evaluation for the Camshafts Production of ADI Low Alloyed with Vanadium

Metals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 1036
Author(s):  
Eduardo Colin García ◽  
Alejandro Cruz Ramírez ◽  
Guillermo Reyes Castellanos ◽  
José Federico Chávez Alcalá ◽  
Jaime Téllez Ramírez ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Ductile Iron ◽  
Volume Fraction ◽  
Energy Impact ◽  
Treatment Conditions ◽  
Mold Casting ◽  
Grade 3 ◽  
Good Agreement

Ductile iron camshafts low alloyed with 0.2 and 0.3 wt % vanadium were produced by one of the largest manufacturers of the ductile iron camshafts in México “ARBOMEX S.A de C.V” by a phenolic urethane no-bake sand mold casting method. During functioning, camshafts are subject to bending and torsional stresses, and the lobe surfaces are highly loaded. Thus, high toughness and wear resistance are essential for this component. In this work, two austempering ductile iron heat treatments were evaluated to increase the mechanical properties of tensile strength, hardness, and toughness of the ductile iron camshaft low alloyed with vanadium. The austempering process was held at 265 and 305 °C and austempering times of 30, 60, 90, and 120 min. The volume fraction of high-carbon austenite was determined for the heat treatment conditions by XRD measurements. The ausferritic matrix was determined in 90 min for both austempering temperatures, having a good agreement with the microstructural and hardness evolution as the austempering time increased. The mechanical properties of tensile strength, hardness, and toughness were evaluated from samples obtained from the camshaft and the standard Keel block. The highest mechanical properties were obtained for the austempering heat treatment of 265 °C for 90 min for the ADI containing 0.3 wt % V. The tensile and yield strength were 1200 and 1051 MPa, respectively, while the hardness and the energy impact values were of 47 HRC and 26 J; these values are in the range expected for an ADI grade 3.

Effect of fibre content on the mechanical properties of hemp fibre woven fabrics/polypropylene composite laminates

2021 ◽  
pp. 096739112110239
Author(s):  
Sheedev Antony ◽  
Abel Cherouat ◽  
Guillaume Montay
Keyword(s):  
Mechanical Properties ◽  
Polymer Matrix ◽  
Composite Laminates ◽  
Volume Fraction ◽  
Fibre Volume Fraction ◽  
Fibre Volume ◽  
Woven Fabrics ◽  
Fibre Content ◽  
Viscoelastic Behaviour ◽  
Hemp Fibre

Nowadays natural fibre composites have gained great significance as reinforcements in polymer matrix composites. Composite material based on a polymer matrix reinforced with natural fibres is extensively used in industry due to their biodegradability, recyclability, low density and high specific properties. A study has been carried out here to investigate the fibre volume fraction effect of hemp fibre woven fabrics/PolyPropylene (PP) composite laminates on the tensile properties and impact hammer impact test. Initially, composite sheets were fabricated by the thermal-compression process with desired number of fabric layers to obtain composite laminates with different fibre volume fraction. Uniaxial, shear and biaxial tensile tests were performed and mechanical properties were calculated. Impact hammer test was also carried out to estimate the frequency and damping parameters of stratified composite plates. Scanning Electron Microscope (SEM) analysis was performed to observe the matrix and fibre constituent defects. Hemp fabrics/PP composite laminates exhibits viscoelastic behaviour and as the fibre volume fraction increases, the viscoelastic behaviour decreases to elastic behaviour. Due to this, the tensile strength increases as the fibre content increases. On the other hand, the natural frequency increases and damping ratio decrease as the fibre volume fraction increases.

scholarly journals Microstructural Characterization and Mechanical Properties of Ti-6Al-4V Alloy Subjected to Dynamic Plastic Deformation Achieved by Multipass Hammer Forging with Different Forging Temperatures

2019 ◽  
Vol 2019 ◽  
pp. 1-12 ◽  
Author(s):  
Xiurong Fang ◽  
Jiang Wu ◽  
Xue Ou ◽  
Fuqiang Yang
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Volume Fraction ◽  
Microstructural Characterization ◽  
Optical Microscope ◽  
Strain Rates ◽  
Materials Properties ◽  
Forging Process ◽  
Hammer Forging ◽  
Dynamic Plastic Deformation

Dynamic plastic deformation (DPD) achieved by multipass hammer forging is one of the most important metal forming operations to create the excellent materials properties. By using the integrated approaches of optical microscope and scanning electron microscope, the forging temperature effects on the multipass hammer forging process and the forged properties of Ti-6Al-4V alloy were evaluated and the forging samples were controlled with a total height reduction of 50% by multipass strikes from 925°C to 1025°C. The results indicate that the forging temperature has a significant effect on morphology and the volume fraction of primary α phase, and the microstructural homogeneity is enhanced after multipass hammer forging. The alloy slip possibility and strain rates could be improved by multipass strikes, but the marginal efficiency decreases with the increased forging temperature. Besides, a forging process with an initial forging temperature a bit above β transformation and finishing the forging a little below the β transformation is suggested to balance the forging deformation resistance and forged mechanical properties.

Sign in / Sign up

Export Citation Format

Share Document