Research on Miniature Thermoplastic Processing of Polyvinyl Alcohol Based Nanocomposites

2013 ◽  
Vol 380-384 ◽  
pp. 4224-4227
Author(s):  
Ming Fang Xie ◽  
Sheng Qiang
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Polyvinyl Alcohol ◽  
Raw Materials ◽  
Great Influence ◽  
Theoretical Method ◽  
Process Conditions ◽  
Processing Conditions ◽  
Elongation At Break ◽  
Preparation Conditions

This paper discusses the synthesis and preparation of polyvinyl alcohol based nanocomposites through the use of miniature thermoplastics processing technology. It studies the influence of different process conditions, the amount of raw materials and water on the processing performance, tensile strength and elongation at break of polyvinyl alcohol based nanocomposites. Studies have shown that using two miniature thermoplastic processes does not have much influence on the mechanical properties of polyvinyl alcohol based nanocomposites, different amount of polyvinyl alcohol will lead to enhancement of the tensile strength of the polyvinyl alcohol based nanocomposites system by the increasing amount of glycerin, and the water content has a great influence on the performance of polyvinyl alcohol based nanocomposites. To this end, according to the analysis of experimental results, it can obtain preparation conditions and influencing factors of polyvinyl alcohol based nanocomposites with the miniature thermoplastic processing conditions, and provide a new theoretical method and means for nanocomposites.

The effect of large area graphene oxide (LAGO) nanosheets on the mechanical properties of polyvinyl alcohol

2016 ◽  
Vol 36 (4) ◽  
pp. 399-405 ◽  
Author(s):  
Khalid Nawaz ◽  
Muhammad Ayub ◽  
Noaman Ul-Haq ◽  
M.B. Khan ◽  
Muhammad Bilal Khan Niazi ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Graphene Oxide ◽  
Polyvinyl Alcohol ◽  
Molecular Level ◽  
Large Area ◽  
Graphene Oxides ◽  
Elongation At Break ◽  
Graphene Oxide Sheets ◽  
Excellent Improvement

Abstract Large area graphene oxide sheets were synthesized, dispersed in water and used as nanofiller for mechanical improvement in terms of Young’s modulus and ultimate tensile strength (UTS) of polyvinyl alcohol (PVA) at low loading. The molecular level dispersion and interfacial interactions between the graphene oxides and polymeric matrix PVA were the real challenges. An excellent improvement in mechanical properties at 0.35 wt% loading was observed. Modulus improved from 1.58 GPa to 2.72 GPa (~71% improvement), UTS improved from 120 MPa to 197 MPa (~65% improvement), and in spite of these improvements, interestingly, there was no fall in elongation at break at this loading.

Superior Mechanical Properties of Ultrasonically Recycled EPDM Rubber

2003 ◽  
Vol 76 (1) ◽  
pp. 253-270 ◽  
Author(s):  
Jushik Yun ◽  
A. I. Isayev
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Power Consumption ◽  
Crosslink Density ◽  
Dynamic Properties ◽  
Extensive Study ◽  
Processing Conditions ◽  
Elongation At Break ◽  
Epdm Rubber ◽  
Superior Mechanical Properties

Abstract This paper describes the results of an extensive study involving the continuous ultrasonic devulcanization of unfilled EPDM rubber. Die pressure and ultrasound power consumption were measured as a function of processing conditions. The mechanical properties of aged and fresh revulcanized EPDM rubber were measured. Gel fraction, crosslink density, and dynamic properties were also determined for the virgin vulcanizate, the ultrasonically devulcanized rubber, and the revulcanized rubber. Additionally, the cure behavior of virgin and devulcanized EPDM rubber was investigated. The tensile strength of revulcanized EPDM rubber was found to be much higher than that of the virgin vulcanizate with the elongation at break being practically intact. A mechanism explaining the increase in mechanical properties of revulcanized rubbers was proposed.

Superior Mechanical Properties of Reclaimed SBR with Bimodal Network

1997 ◽  
Vol 70 (2) ◽  
pp. 194-201 ◽  
Author(s):  
A. I. Isayev ◽  
S. H. Kim ◽  
V. Yu Levin
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Crosslink Density ◽  
Processing Conditions ◽  
Elongation At Break ◽  
Gel Fraction ◽  
Superior Mechanical Properties

Abstract The correlation between the mechanical properties of revulcanized SBR, total and polysulfidic crosslink density, gel fraction of original vulcanizate, ultrasonically devulcanized, and revulcanized rubber is described. Under some processing conditions the tensile strength of revulcanized SBR is found to be much higher than that of the original vulcanizate with elongation at break being practically intact. A model explaining the increase in mechanical properties of revulcanized rubber is proposed.

Effect of Corn Straw Addition on Mechanical Properties of Polyvinyl Alcohol Hydrogel

2021 ◽  
Vol 904 ◽  
pp. 250-254
Author(s):  
Shuang Chen ◽  
Jui Chin Chen ◽  
Chi Hui Tsou ◽  
Peng Cheng Yang ◽  
Chun Fen Jia ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Polyvinyl Alcohol ◽  
The Other ◽  
Corn Straw ◽  
Freezing And Thawing ◽  
Elongation At Break ◽  
Composite Hydrogels ◽  
Freeze Dried ◽  
Freezing And Thawing Cycles

In this study, PVA/CS composite hydrogels were prepared by means of freezing and thawing cycles of agricultural wastes, corn straw (CS) and polyvinyl alcohol (PVA). The mechanical properties of the composite hydrogels were analyzed by universal tensile device. The effects of CS on tensile strength and elongation at break of PVA/CS composite hydrogels were analyzed. On the other hand, PVA and PVA/CS composite hydrogels were also freeze-dried to investigate the mechanical properties of all hydrogels after drying.

Effect of Compatilizers on Morphology and Properties of Natural Rubber/Polyvinyl Alcohol (NR/PVA) Blends

2014 ◽  
Vol 960-961 ◽  
pp. 262-269
Author(s):  
Ke Chen ◽  
Rui Wang
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Thermal Decomposition ◽  
Tensile Strength ◽  
Polyvinyl Alcohol ◽  
Natural Rubber ◽  
Graft Copolymerization ◽  
Elongation At Break ◽  
Latex Compounding ◽  
Thermal Stability Of

The natural rubber/polyvinyl alcohol (NR/PVA) blends containing various compatilizers grafted from NR were prepared using latex compounding techniques. The effects of various compatilizers on the morphology, mechanical properties and thermal behaviors were studied. The interface compatible performance of the blends were greatly improved with the presence of the compatilizers, and the phase dispertion of the blends achieved the best effect under the action of epoxidized natural rubber (ENR). The onset temperature of the thermal decomposition of ENR and graft copolymerization of methyl methacrylate (MMA) onto NR (NR-g-PMMA) increased obviously, but the maleic anhydride grafted onto NR (NR-g-MAH) drop obviously comparing to that of NR. The thermal stability of the blends were inferior to NR. With the presence of ENR, the tensile strength and elongation at break obtained great value which was ascribed the presence of the best phase dispertion, while the tear strength and shore A hardness obtained great value due to the addition of MAH-g-NR.

scholarly journals The Structure and Mechanical Properties of Hemp Fibers-Reinforced Poly(ε-Caprolactone) Composites Modified by Electron Beam Irradiation

2021 ◽  
Vol 11 (12) ◽  
pp. 5317
Author(s):  
Rafał Malinowski ◽  
Aneta Raszkowska-Kaczor ◽  
Krzysztof Moraczewski ◽  
Wojciech Głuszewski ◽  
Volodymyr Krasinskyi ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Electron Beam ◽  
Impact Strength ◽  
Flexural Modulus ◽  
Natural Fibers ◽  
High Energy ◽  
Electron Radiation ◽  
Elongation At Break ◽  
Hemp Fibers

The need for the development of new biodegradable materials and modification of the properties the current ones possess has essentially increased in recent years. The aim of this study was the comparison of changes occurring in poly(ε-caprolactone) (PCL) due to its modification by high-energy electron beam derived from a linear electron accelerator, as well as the addition of natural fibers in the form of cut hemp fibers. Changes to the fibers structure in the obtained composites and the geometrical surface structure of sample fractures with the use of scanning electron microscopy were investigated. Moreover, the mechanical properties were examined, including tensile strength, elongation at break, flexural modulus and impact strength of the modified PCL. It was found that PCL, modified with hemp fibers and/or electron radiation, exhibited enhanced flexural modulus but the elongation at break and impact strength decreased. Depending on the electron radiation dose and the hemp fibers content, tensile strength decreased or increased. It was also found that hemp fibers caused greater changes to the mechanical properties of PCL than electron radiation. The prepared composites exhibited uniform distribution of the dispersed phase in the polymer matrix and adequate adhesion at the interface between the two components.

scholarly journals Effect of Moisture Content on the Processing and Mechanical Properties of a Biodegradable Polyester

Polymers ◽  
2021 ◽  
Vol 13 (10) ◽  
pp. 1616
Author(s):  
Vincenzo Titone ◽  
Antonio Correnti ◽  
Francesco Paolo La Mantia
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Moisture Content ◽  
Mechanical Testing ◽  
Hydrolytic Degradation ◽  
Slight Reduction ◽  
Biodegradable Polyester ◽  
Molding Process ◽  
Elongation At Break ◽  
Effect Of Moisture

This work is focused on the influence of moisture content on the processing and mechanical properties of a biodegradable polyester used for applications in injection molding. The pellets of the biodegradable polyester were exposed under different relative humidity conditions at a constant temperature before being compression molded. The compression-molded specimens were again placed under the above conditions before the mechanical testing. With all these samples, it is possible to determine the effect of moisture content on the processing and mechanical properties separately, as well as the combined effect of moisture content on the mechanical properties. The results obtained showed that the amount of absorbed water—both before processing and before mechanical testing—causes an increase in elongation at break and a slight reduction of the elastic modulus and tensile strength. These changes have been associated with possible hydrolytic degradation during the compression molding process and, in particular, with the plasticizing action of the moisture absorbed by the specimens.

Vibratory weld conditioning during gas tungsten arc welding of al 5052 alloy on the mechanical and micro-structural behavior

2020 ◽  
Vol 17 (6) ◽  
pp. 831-836
Author(s):  
M. Vykunta Rao ◽  
Srinivasa Rao P. ◽  
B. Surendra Babu
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Welded Joints ◽  
Great Influence ◽  
Welding Process ◽  
Microstructural Characterization ◽  
Content Type ◽  
Average Grain Size

Purpose Vibratory weld conditioning parameters have a great influence on the improvement of mechanical properties of weld connections. The purpose of this paper is to understand the influence of vibratory weld conditioning on the mechanical and microstructural characterization of aluminum 5052 alloy weldments. An attempt is made to understand the effect of the vibratory tungsten inert gas (TIG) welding process parameters on the hardness, ultimate tensile strength and microstructure of Al 5052-H32 alloy weldments. Design/methodology/approach Aluminum 5052 H32 specimens are welded at different combinations of vibromotor voltage inputs and time of vibrations. Voltage input is varied from 50 to 230 V at an interval of 10 V. At each voltage input to the vibromotor, there are three levels of time of vibration, i.e. 80, 90 and 100 s. The vibratory TIG-welded specimens are tested for their mechanical and microstructural properties. Findings The results indicate that the mechanical properties of aluminum alloy weld connections improved by increasing voltage input up to 160 V. Also, it has been observed that by increasing vibromotor voltage input beyond 160 V, mechanical properties were reduced significantly. It is also found that vibration time has less influence on the mechanical properties of weld connections. Improvement in hardness and ultimate tensile strength of vibratory welded joints is 16 and 14%, respectively, when compared without vibration, i.e. normal weld conditions. Average grain size is measured as per ASTM E 112–96. Average grain size is in the case of 0, 120, 160 and 230 is 20.709, 17.99, 16.57 and 20.8086 µm, respectively. Originality/value Novel vibratory TIG welded joints are prepared. Mechanical and micro-structural properties are tested.

Effect of Castor Oil Impregnation on the Physical and Mechanical Properties of Bacterial Cellulose

2012 ◽  
Vol 3 (1) ◽  
pp. 13-26
Author(s):  
Myrtha Karina ◽  
Lucia Indrarti ◽  
Rike Yudianti ◽  
Indriyati
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Bacterial Cellulose ◽  
Young’S Modulus ◽  
Castor Oil ◽  
Young's Modulus ◽  
Physical And Mechanical Properties ◽  
Scanning Electron Micrographs ◽  
Elongation At Break ◽  
Acetone Water

The effect of castor oil on the physical and mechanical properties of bacterial cellulose is described. Bacterial cellulose (BC) was impregnated with 0.5–2% (w/v) castor oil (CO) in acetone–water, providing BCCO films. Scanning electron micrographs revealed that the castor oil penetrated the pores of the bacterial cellulose, resulting in a smoother morphology and enhanced hydrophilicity. Castor oil caused a slight change in crystallinity indices and resulted in reduced tensile strength and Young's modulus but increased elongation at break. A significant reduction in tensile strength and Young's modulus was achieved in BCCO films with 2% castor oil, and there was an improvement in elongation at break and hydrophilicity. Impregnation with castor oil, a biodegradable and safe plasticiser, resulted in less rigid and more ductile composites.

Graphite/Bio-Based Epoxy Composites: The Mechanical Properties Interface

2015 ◽  
Vol 799-800 ◽  
pp. 115-119 ◽  
Author(s):  
Anika Zafiah M. Rus ◽  
Nur Munirah Abdullah ◽  
M.F.L. Abdullah ◽  
M. Izzul Faiz Idris
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Elastic Modulus ◽  
Filler Content ◽  
Weight Percent ◽  
Epoxy Composites ◽  
Elongation At Break ◽  
Graphite Content ◽  
Dispersion Condition ◽  
Strong Interfacial Bonding

Graphite reinforced bio-based epoxy composites with different particulate fractions of graphite were investigated for mechanical properties such as tensile strength, elastic modulus and elongation at break. The graphite content was varied from 5 wt.%, 10 wt.%, 15 wt.%, 20 wt.%, 25 wt.%, 30 wt.% by weight percent in the composites. The results showed that the mechanical properties of the composites mainly depend on dispersion condition of the treated graphite filler, aggregate structure and strong interfacial bonding between treated graphite in the bio-based epoxy matrix. The composites showed improved tensile strength and elastic modulus with increase treated graphite weight loading. This also revealed the composites with increasing filler content was decreasing the elongation at break.

Sign in / Sign up

Export Citation Format

Share Document