Polymer Crystallization History and Resultant Properties

1969 ◽  
Vol 42 (3) ◽  
pp. 769-779 ◽  
Author(s):  
John R. Collier
Keyword(s):  
Mechanical Properties ◽  
Glassy State ◽  
Polymeric Materials ◽  
Neck Formation ◽  
Rapid Crystallization ◽  
Platelet Morphology ◽  
Treatment Conditions ◽  
Crystallizing Polymers ◽  
Small Platelet ◽  
Crystallization From The Melt

Abstract Mechanical properties of semicrystalline polymeric materials are strongly influenced by the morphology into which these materials crystallize. In addition the morphology can be altered by changes in crystallization temperature and regime, crystallization pressure, melt treatment conditions, shear history, and probably other processing conditions. The mechanical properties reflect the changes in morphology not only in the initial moduli values but also the overall stress-strain relationships, including the fracture mechanism. A strong influence is noted, at least in the polymers cited, even when slight changes occur in average spherulite size, spherulitic fine structure, and in the nature of interlamellar ties. Smaller, finer textured spherulites with higher interconnections arc apparently more susceptible to yielding by neck formation and elongation to high values than are the larger, coarser textured spherulites than tend to fail by random brittle failure mechanisms at low elongations. In addition, if the chlorinated polyether (Penton) is typical of slowly crystallizing polymers, the change from spherulitic morphology obtained during crystallization from the melt to the small platelet morphology obtained during slow crystallization from quenched glassy state has a complex effect on mechanical properties. The specimens slowly crystallized from the glass exhibit initial shear and tensile moduli values higher than those exhibited for rapid crystallization from the melt and rapid crystallization from the glass, but lower than the corresponding values for slow crystallization from the melt. In addition, the only specimens of this chlorinated polyether that exhibited the ability to draw to high degrees of elongation (as a result of yielding by a necking phenomenon) were those crystallized slowly from the quenched glassy state.

Study of the character and causes of destruction of the cardan shaft of the propeller engine

2019 ◽  
Vol 85 (12) ◽  
pp. 43-50
Author(s):  
D. A. Movenko ◽  
L. V. Morozova ◽  
S. V. Shurtakov
Keyword(s):  
Mechanical Properties ◽  
Chemical Composition ◽  
Yield Point ◽  
Protective Coating ◽  
Fracture Pattern ◽  
Corrosion Cracking ◽  
Tempered Martensite ◽  
Neck Formation ◽  
Static Mechanism ◽  
Shaft Surface

The results of studying operational destruction of a high-loaded cardan shaft of the propeller engine made of steel 38KhN3MFA are presented to elucidate the cause of damage and develop a set of recommendations and measures aimed at elimination of adverse factors. Methods of scanning electron and optical microscopy, as well as X-ray spectral microanalysis are used to determine the mechanical properties, chemical composition, microstructure, and fracture pattern of cardan shaft fragments. It is shown that the mechanical properties and chemical composition of the material correspond to the requirements of the regulatory documentation, defects of metallurgical origin both in the shaft metal and in the fractures are absent. The microstructure of the studied shaft fragments is tempered martensite. Fractographic analysis revealed that the destruction of cardan shaft occurred by a static mechanism. The fracture surface is coated with corrosion products. The revealed cracks developed by the mechanism of corrosion cracking due to violation of the protective coating on the shaft. The results of the study showed that the destruction of the cardan shaft of a propeller engine made of steel 38Kh3MFA occurred due to formation and development of spiral cracks by the mechanism of stress corrosion cracking under loads below the yield point of steel. The reason for «neck» formation upon destruction of the shaft fragment is attributed to the yield point of steel attained during operation. Regular preventive inspections are recommended to assess the safety of the protective coating on the shaft surface to exclude formation and development of corrosion cracks.

Possibilities of using biodegradable polymeric materials in the agricultural sector

2020 ◽  
Vol 67 (2) ◽  
pp. 115-120
Author(s):  
Raisa A. Alekhina ◽  
Victoriya E. Slavkina ◽  
Yuliya A. Lopatina
Keyword(s):  
Mechanical Properties ◽  
Biodegradable Polymers ◽  
Biodegradable Polymer ◽  
Agricultural Sector ◽  
Polymeric Materials ◽  
Polymer Materials ◽  
Limiting Factors ◽  
Research Purpose ◽  
Biodegradable Materials ◽  
Advantages And Disadvantages

The article presents options for recycling polymers. The use of biodegradable materials is promising. This is a special class of polymers that can decompose under aerobic or anaerobic conditions under the action of microorganisms or enzymes forming natural products such as carbon dioxide, nitrogen, water, biomass, and inorganic salts. (Research purpose) The research purpose is in reviewing biodegradable materials that can be used for the manufacture of products used in agriculture. (Materials and methods) The study are based on open information sources containing information about biodegradable materials. Research methods are collecting, studying and comparative analysis of information. (Results and discussion) The article presents the advantages and disadvantages of biodegradable materials, mechanical properties of the main groups of biodegradable polymers. The article provides a summary list of agricultural products that can be made from biodegradable polymer materials. It was found that products from the general group are widely used in agriculture. Authors have found that products from a special group can only be made from biodegradable polymers with a controlled decomposition period in the soil, their use contributes to increasing the productivity of crops. (Conclusions) It was found that biodegradable polymer materials, along with environmental safety, have mechanical properties that allow them producing products that do not carry significant loads during operation. We have shown that the creation of responsible products (machine parts) from biodegradable polymers requires an increase in their strength properties, which is achievable by creating composites based on them. It was found that the technological complexity of their manufacture and high cost are the limiting factors for the widespread use of biodegradable polymers at this stage.

scholarly journals Anti-Inflammatory Properties of Injectable Betamethasone-Loaded Tyramine-Modified Gellan Gum/Silk Fibroin Hydrogels

Biomolecules ◽  
2020 ◽  
Vol 10 (10) ◽  
pp. 1456
Author(s):  
Isabel Matos Oliveira ◽  
Cristiana Gonçalves ◽  
Myeong Eun Shin ◽  
Sumi Lee ◽  
Rui Luis Reis ◽  
...  
Keyword(s):  
Rheumatoid Arthritis ◽  
Mechanical Properties ◽  
Silk Fibroin ◽  
Therapeutic Efficacy ◽  
Composite Structures ◽  
Gelation Time ◽  
Polymeric Materials ◽  
Gellan Gum ◽  
Traditional Use

Rheumatoid arthritis is a rheumatic disease for which a healing treatment does not presently exist. Silk fibroin has been extensively studied for use in drug delivery systems due to its uniqueness, versatility and strong clinical track record in medicine. However, in general, natural polymeric materials are not mechanically stable enough, and have high rates of biodegradation. Thus, synthetic materials such as gellan gum can be used to produce composite structures with biological signals to promote tissue-specific interactions while providing the desired mechanical properties. In this work, we aimed to produce hydrogels of tyramine-modified gellan gum with silk fibroin (Ty–GG/SF) via horseradish peroxidase (HRP), with encapsulated betamethasone, to improve the biocompatibility and mechanical properties, and further increase therapeutic efficacy to treat rheumatoid arthritis (RA). The Ty–GG/SF hydrogels presented a β-sheet secondary structure, with gelation time around 2–5 min, good resistance to enzymatic degradation, a suitable injectability profile, viscoelastic capacity with a significant solid component and a betamethasone-controlled release profile over time. In vitro studies showed that Ty–GG/SF hydrogels did not produce a deleterious effect on cellular metabolic activity, morphology or proliferation. Furthermore, Ty–GG/SF hydrogels with encapsulated betamethasone revealed greater therapeutic efficacy than the drug applied alone. Therefore, this strategy can provide an improvement in therapeutic efficacy when compared to the traditional use of drugs for the treatment of rheumatoid arthritis.

scholarly journals Analysis of PLA Composite Filaments Reinforced with Lignin and Polymerised-Lignin-Treated NFC

Polymers ◽  
2021 ◽  
Vol 13 (13) ◽  
pp. 2174
Author(s):  
Diana Gregor-Svetec ◽  
Mirjam Leskovšek ◽  
Blaž Leskovar ◽  
Urška Stanković Elesini ◽  
Urška Vrabič-Brodnjak
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Scanning Electron Microscopy ◽  
Tensile Strength ◽  
Glassy State ◽  
Nanofibrillated Cellulose ◽  
Dynamic Mechanical Properties ◽  
Initial Modulus ◽  
Surface Modified ◽  
Scanning Electron

Polylactic acid (PLA) is one of the most suitable materials for 3D printing. Blending with nanoparticles improves some of its properties, broadening its application possibilities. The article presents a study of composite PLA matrix filaments with added unmodified and lignin/polymerised lignin surface-modified nanofibrillated cellulose (NFC). The influence of untreated and surface-modified NFC on morphological, mechanical, technological, infrared spectroscopic, and dynamic mechanical properties was evaluated for different groups of samples. As determined by the stereo and scanning electron microscopy, the unmodified and surface-modified NFCs with lignin and polymerised lignin were present in the form of plate-shaped agglomerates. The addition of NFC slightly reduced the filaments’ tensile strength, stretchability, and ability to absorb energy, while in contrast, the initial modulus slightly improved. By adding NFC to the PLA matrix, the bending storage modulus (E’) decreased slightly at lower temperatures, especially in the PLA samples with 3 wt% and 5 wt% NFC. When NFC was modified with lignin and polymerised lignin, an increase in E’ was noticed, especially in the glassy state.

scholarly journals Heat Treatment Evaluation for the Camshafts Production of ADI Low Alloyed with Vanadium

Metals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 1036
Author(s):  
Eduardo Colin García ◽  
Alejandro Cruz Ramírez ◽  
Guillermo Reyes Castellanos ◽  
José Federico Chávez Alcalá ◽  
Jaime Téllez Ramírez ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Ductile Iron ◽  
Volume Fraction ◽  
Energy Impact ◽  
Treatment Conditions ◽  
Mold Casting ◽  
Grade 3 ◽  
Good Agreement

Ductile iron camshafts low alloyed with 0.2 and 0.3 wt % vanadium were produced by one of the largest manufacturers of the ductile iron camshafts in México “ARBOMEX S.A de C.V” by a phenolic urethane no-bake sand mold casting method. During functioning, camshafts are subject to bending and torsional stresses, and the lobe surfaces are highly loaded. Thus, high toughness and wear resistance are essential for this component. In this work, two austempering ductile iron heat treatments were evaluated to increase the mechanical properties of tensile strength, hardness, and toughness of the ductile iron camshaft low alloyed with vanadium. The austempering process was held at 265 and 305 °C and austempering times of 30, 60, 90, and 120 min. The volume fraction of high-carbon austenite was determined for the heat treatment conditions by XRD measurements. The ausferritic matrix was determined in 90 min for both austempering temperatures, having a good agreement with the microstructural and hardness evolution as the austempering time increased. The mechanical properties of tensile strength, hardness, and toughness were evaluated from samples obtained from the camshaft and the standard Keel block. The highest mechanical properties were obtained for the austempering heat treatment of 265 °C for 90 min for the ADI containing 0.3 wt % V. The tensile and yield strength were 1200 and 1051 MPa, respectively, while the hardness and the energy impact values were of 47 HRC and 26 J; these values are in the range expected for an ADI grade 3.

scholarly journals Mechanical and Morphological Properties of Bio-Phenolic/Epoxy Polymer Blends

Molecules ◽  
2021 ◽  
Vol 26 (4) ◽  
pp. 773
Author(s):  
Ahmad Safwan Ismail ◽  
Mohammad Jawaid ◽  
Norul Hisham Hamid ◽  
Ridwan Yahaya ◽  
Azman Hassan
Keyword(s):  
Mechanical Properties ◽  
Phase Separation ◽  
Polymer Blends ◽  
Epoxy Polymer ◽  
Flexural Modulus ◽  
Polymeric Materials ◽  
Morphological Properties ◽  
Comparison Results ◽  
Unique Material ◽  
Different Types

Polymer blends is a well-established and suitable method to produced new polymeric materials as compared to synthesis of a new polymer. The combination of two different types of polymers will produce a new and unique material, which has the attribute of both polymers. The aim of this work is to analyze mechanical and morphological properties of bio-phenolic/epoxy polymer blends to find the best formulation for future study. Bio-phenolic/epoxy polymer blends were fabricated using the hand lay-up method at different loading of bio-phenolic (5 wt%, 10 wt%, 15 wt%, 20 wt%, and 25 wt%) in the epoxy matrix whereas neat bio-phenolic and epoxy samples were also fabricated for comparison. Results indicated that mechanical properties were improved for bio-phenolic/epoxy polymer blends compared to neat epoxy and phenolic. In addition, there is no sign of phase separation in polymer blends. The highest tensile, flexural, and impact strength was shown by P-20(biophenolic-20 wt% and Epoxy-80 wt%) whereas P-25 (biophenolic-25 wt% and Epoxy-75 wt%) has the highest tensile and flexural modulus. Based on the finding, it is concluded that P-20 shows better overall mechanical properties among the polymer blends. Based on this finding, the bio-phenolic/epoxy blend with 20 wt% will be used for further study on flax-reinforced bio-phenolic/epoxy polymer blends.

scholarly journals Achievement of High Strength and Ductility in Al–Si–Cu–Mg Alloys by Intermediate Phase Optimization in As-Cast and Heat Treatment Conditions

Materials ◽  
2020 ◽  
Vol 13 (3) ◽  
pp. 647 ◽  
Author(s):  
Bingrong Zhang ◽  
Lingkun Zhang ◽  
Zhiming Wang ◽  
Anjiang Gao
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Intermediate Phase ◽  
High Strength ◽  
Mg Alloys ◽  
Artificial Ageing ◽  
Treatment Conditions ◽  
Eutectic Si

In order to obtain high-strength and high-ductility Al–Si–Cu–Mg alloys, the present research is focused on optimizing the composition of soluble phases, the structure and morphology of insoluble phases, and artificial ageing processes. The results show that the best matches, 0.4 wt% Mg and 1.2 wt% Cu in the Al–9Si alloy, avoided the toxic effect of the blocky Al2Cu on the mechanical properties of the alloy. The addition of 0.6 wt% Zn modified the morphology of eutectic Si from coarse particles to fine fibrous particles and the texture of Fe-rich phases from acicular β-Fe to blocky π-Fe in the Al–9Si–1.2Cu–0.4Mg-based alloy. With the optimization of the heat treatment parameters, the spherical eutectic Si and the fully fused β-Fe dramatically improved the ultimate tensile strength and elongation to fracture. Compared with the Al–9Si–1.2Cu–0.4Mg-based alloy, the 0.6 wt% Zn modified alloy not only increased the ultimate tensile strength and elongation to fracture of peak ageing but also reduced the time of peak ageing. The following improved combination of higher tensile strength and higher elongation was achieved for 0.6 wt% Zn modified alloy by double-stage ageing: 100 °C × 3 h + 180 °C × 7 h, with mechanical properties of ultimate tensile strength (UTS) of ~371 MPa, yield strength (YS) of ~291 MPa, and elongation to fracture (E%) of ~5.6%.

Effects of Heat Treatment on Microstructure Parameters, Mechanical Properties and Cold Resistance of Sparingly Alloyed High-Strength Steel

2021 ◽  
Vol 410 ◽  
pp. 197-202
Author(s):  
Pavel P. Poleckov ◽  
Olga A. Nikitenko ◽  
Alla S. Kuznetsova
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Cold Resistance ◽  
Heating Temperature ◽  
High Strength ◽  
Steel Microstructure ◽  
Treatment Conditions ◽  
Microstructure Parameters ◽  
Temperature Impact ◽  
Low Temperature Impact Toughness

This study considers the influence of various heat treatment conditions on the change of steel microstructure parameters, mechanical properties and cold resistance at a temperature of-60 °C. The common behavior of these properties is considered depending on the heating temperature used for quenching and subsequent tempering. Based on the obtained results, heat treatment conditions are proposed that provide a combination of a guaranteed yield point σ0.2 ≥600 N/mm2 with a low-temperature impact toughness KCV-60 ≥50 J/cm2 and plasticity δ5 ≥17%. The obtained research results are intended for industrial use at the mill "5000" site of MMK PJSC.

Tribology study of hydroxyapatite (HAp) scaffold blended single based binder via rheology and mechanical properties

2017 ◽  
Vol 69 (3) ◽  
pp. 414-419
Author(s):  
Mimi Azlina Abu Bakar ◽  
Siti Norazlini Abd Aziz ◽  
Muhammad Hussain Ismail
Keyword(s):  
Mechanical Properties ◽  
Injection Molding ◽  
Palm Stearin ◽  
Polymeric Materials ◽  
High Energy ◽  
Single Step ◽  
Injection Molding Process ◽  
Plastic Behavior ◽  
Molding Process ◽  
Content Type

Purpose This paper aims to investigate the vital characteristic of an innovative ceramic injection molding (CIM) process for orthopedic application with controlled porosity and improved tribological and mechanical properties which were affected by complex tribological interactions, whether lubricated like hip implants and other artificial prostheses. The main objective is to maximize the usage of palm stearin as a single based binder as the function of flow properties during injection molding process. Design/methodology/approach The binder used in this present study consists of 100 per cent palm stearin manufactured by Kempas Oil Sdn Bhd and supplied by Vistec Technology Sdn Bhd. The feedstock was prepared by using a Z-blade mixer (Thermo Haake Rheomix OS) and Brabender mixer model R2400. The feedstock prepared was injection molded using a manually operated vertical benchtop machine with an average pressure of about 5-7 bars. The firing step included the temporary holds at intermediate temperatures to burn out organic binders. At this stage, the green molded specimen was de-bound using a single-step wick-debinding method. Findings The maximum content of ceramic material is applied to investigate the efficiencies of net formulation that can be achieved by ceramic materials. The longer the viscosity will change with shear rate, the higher the value of n obtained instead. From the slope of the curves obtained in Figure 3, the value of n for the feedstock was determined to be less than 1, which indicates a pseudoplastic behavior and suitability for the molding process. Moreover, high shear sensitivity is important in producing complex and intrinsic specimens which are leading products in the CIM industry. Originality/value The feedstock containing HAp powder and palm stearin binder was successfully prepared at very low temperature of 70°C, which promoting a required pseudo-plastic behavior during rheological test. The single binder palm stearin should be optimized in other research works carried out, as palm stearin is most preferred compared to other polymeric materials that provided high energy consumption when subjected to the sintering process. Besides the binder is widely available in Malaysia, low cost and harmless effect during debinding process.

Sign in / Sign up

Export Citation Format

Share Document