Experimental Evidence of Density and Mechanical Properties Enhancement of Binary Alloys by Solidification Subject to Vibrations

2009 ◽  
Author(s):  
J. Vadasz ◽  
J. P. Meyer ◽  
S. Govender ◽  
M. Andrick ◽  
W. Carter ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Binary Alloys ◽  
Preliminary Evidence ◽  
Boundary Effects ◽  
Infinite Length ◽  
Vibration Source ◽  
Sound Waves

Preliminary evidence of density and mechanical properties enhancement of binary alloys by solidification subject to vibrations is presented. The frequency of vibrations was increased from 0 to 100 Hz by using sound waves as the vibration source. The latter shows that the solidified microstructure, the ultimate tensile strength, and the hardness improve as the frequency increases. The chosen alloy for this study was Pb-Sb 4.4% (lead antimony 4.4%) and was selected because of its low melting temperature. The cast chosen was of a rod shape having a diameter of 10mm and a length 500mm. This choice is consistent with assuming an infinite length and therefore ignoring boundary effects in a planned theoretical follow-up analysis. Also due to the geometry of the mould it can be assumed that the cast was cooled due to conduction alone.

Experimental Evidence of Density and Mechanical Properties Enhancements of Binary Alloys by Soldification Subject to Vibrations

2008 ◽  
Author(s):  
J. Vadasz ◽  
J. P. Meyer ◽  
S. Govender ◽  
M. Andrick ◽  
W. Carter ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Binary Alloys ◽  
Preliminary Evidence ◽  
Boundary Effects ◽  
Infinite Length ◽  
Vibration Source ◽  
Sound Waves

Preliminary evidence of density and mechanical properties enhancement of binary alloys by solidification subject to vibrations is presented. The frequency of vibrations was increased from 0 to 100 Hz by using sound waves as the vibration source. The latter shows that the solidified microstructure, the ultimate tensile strength, and the hardness improve as the frequency increases. The chosen alloy for this study was Pb-Sb 4.4% (lead antimony 4.4%) and was selected because of its low melting temperature. The cast chosen was of a rod shape having a diameter of 10mm and a length 500mm. This choice is consistent with assuming an infinite length and therefore ignoring boundary effects in a planned theoretical follow-up analysis. Also due to the geometry of the mould it can be assumed that the cast was cooled due to conduction alone.

Vibratory weld conditioning during gas tungsten arc welding of al 5052 alloy on the mechanical and micro-structural behavior

2020 ◽  
Vol 17 (6) ◽  
pp. 831-836
Author(s):  
M. Vykunta Rao ◽  
Srinivasa Rao P. ◽  
B. Surendra Babu
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Welded Joints ◽  
Great Influence ◽  
Welding Process ◽  
Microstructural Characterization ◽  
Content Type ◽  
Average Grain Size

Purpose Vibratory weld conditioning parameters have a great influence on the improvement of mechanical properties of weld connections. The purpose of this paper is to understand the influence of vibratory weld conditioning on the mechanical and microstructural characterization of aluminum 5052 alloy weldments. An attempt is made to understand the effect of the vibratory tungsten inert gas (TIG) welding process parameters on the hardness, ultimate tensile strength and microstructure of Al 5052-H32 alloy weldments. Design/methodology/approach Aluminum 5052 H32 specimens are welded at different combinations of vibromotor voltage inputs and time of vibrations. Voltage input is varied from 50 to 230 V at an interval of 10 V. At each voltage input to the vibromotor, there are three levels of time of vibration, i.e. 80, 90 and 100 s. The vibratory TIG-welded specimens are tested for their mechanical and microstructural properties. Findings The results indicate that the mechanical properties of aluminum alloy weld connections improved by increasing voltage input up to 160 V. Also, it has been observed that by increasing vibromotor voltage input beyond 160 V, mechanical properties were reduced significantly. It is also found that vibration time has less influence on the mechanical properties of weld connections. Improvement in hardness and ultimate tensile strength of vibratory welded joints is 16 and 14%, respectively, when compared without vibration, i.e. normal weld conditions. Average grain size is measured as per ASTM E 112–96. Average grain size is in the case of 0, 120, 160 and 230 is 20.709, 17.99, 16.57 and 20.8086 µm, respectively. Originality/value Novel vibratory TIG welded joints are prepared. Mechanical and micro-structural properties are tested.

scholarly journals Effects of Substitution of Y with Yb and Ce on the Microstructures and Mechanical Properties of Mg88.5Zn5Y6.5

Metals ◽  
2020 ◽  
Vol 11 (1) ◽  
pp. 31
Author(s):  
Hongxin Liao ◽  
Taekyung Lee ◽  
Jiangfeng Song ◽  
Jonghyun Kim ◽  
Fusheng Pan
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Creep Resistance ◽  
Room Temperature ◽  
High Thermal Stability ◽  
Long Period ◽  
Microstructures And Mechanical Properties

The microstructures and mechanical properties of the Mg88.5Zn5Y6.5-XREX (RE = Yb and Ce, X = 0, 1.5, 3.0, and 4.5) (wt.%) alloys were investigated in the present study. Mg88.5Zn5Y6.5 is composed of three phases, namely, α-Mg, long-period stacking ordered (LPSO) phases, and intermetallic compounds. The content of the LPSO phases decreased with the addition of Ce and Yb, and no LPSO phases were detected in Mg88.5Zn5Y2.0Yb4.5. The alloys containing the LPSO phases possessed a stratified microstructure and exhibited excellent mechanical properties. Mg88.5Zn5Y5.0Ce1.5 exhibited the highest creep resistance and mechanical strength at both room temperature and 200 °C, owing to its suitable microstructure and high thermal stability. The yield strength of Mg88.5Zn5Y5.0Ce1.5 at room temperature was 358 MPa. The ultimate tensile strength of Mg88.5Zn5Y5.0Ce1.5 at room temperature and 200 °C was 453 MPa and 360 MPa, respectively.

scholarly journals Microstructure and Mechanical Properties of Dissimilar Friction Welding Ti-6Al-4V Alloy to Nitinol

Metals ◽  
2021 ◽  
Vol 11 (1) ◽  
pp. 109
Author(s):  
Ateekh Ur Rehman ◽  
Nagumothu Kishore Babu ◽  
Mahesh Kumar Talari ◽  
Yusuf Siraj Usmani ◽  
Hisham Al-Khalefah
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Flow Stress ◽  
Intermetallic Compound ◽  
Ultimate Tensile Strength ◽  
Friction Welding ◽  
Welding Process ◽  
Weld Interface ◽  
Dissimilar Joints ◽  
Dissimilar Alloys

In the present study, a friction welding process was adopted to join dissimilar alloys of Ti-Al-4V to Nitinol. The effect of friction welding on the evolution of welded macro and microstructures and their hardnesses and tensile properties were studied and discussed in detail. The macrostructure of Ti-6Al-4V and Nitinol dissimilar joints revealed flash formation on the Ti-6Al-4V side due to a reduction in flow stress at high temperatures during friction welding. The optical microstructures revealed fine grains near the Ti-6Al-4V interface due to dynamic recrystallization and strain hardening effects. In contrast, the area nearer to the nitinol interface did not show any grain refinement. This study reveals that the formation of an intermetallic compound (Ti2Ni) at the weld interface resulted in poor ultimate tensile strength (UTS) and elongation values. All tensile specimens failed at the weld interface due to the formation of intermetallic compounds.

scholarly journals The Effect of Water Concentration in Ethyl Alcohol on the Environmentally Assisted Embrittlement of Austempered Ductile Irons

Metals ◽  
2021 ◽  
Vol 11 (1) ◽  
pp. 94
Author(s):  
Petar Janjatovic ◽  
Olivera Eric Cekic ◽  
Leposava Sidjanin ◽  
Sebastian Balos ◽  
Miroslav Dramicanin ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Cast Iron ◽  
Ultimate Tensile Strength ◽  
Ethyl Alcohol ◽  
Water Concentration ◽  
Different Types ◽  
Influence Of Water ◽  
Iron Material ◽  
Proof Strength

Austempered ductile iron (ADI) is an advanced cast iron material that has a broad field of application and, among others, it is used in contact and for conveyance of fluids. However, it is noticed that in contact with some fluids, especially water, ADI material becomes brittle. The most significant decrease is established for the elongation. However, the influence of water and the cause of this phenomenon is still not fully understood. For that reason, in this paper, the influence of different water concentrations in ethyl alcohol on the mechanical properties of ADI materials was studied. The test was performed on two different types of ADI materials in 0.2, 4, 10, and 100 vol.% water concentration environments, and in dry condition. It was found that even the smallest concentration of water (0.2 vol.%) causes formation of the embrittled zone at fracture surface. However, not all mechanical properties were affected equally and not all water concentrations have been critical. The highest deterioration was established in the elongation, followed by the ultimate tensile strength, while the proof strength was affected least.

scholarly journals Achievement of High Strength and Ductility in Al–Si–Cu–Mg Alloys by Intermediate Phase Optimization in As-Cast and Heat Treatment Conditions

Materials ◽  
2020 ◽  
Vol 13 (3) ◽  
pp. 647 ◽  
Author(s):  
Bingrong Zhang ◽  
Lingkun Zhang ◽  
Zhiming Wang ◽  
Anjiang Gao
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Intermediate Phase ◽  
High Strength ◽  
Mg Alloys ◽  
Artificial Ageing ◽  
Treatment Conditions ◽  
Eutectic Si

In order to obtain high-strength and high-ductility Al–Si–Cu–Mg alloys, the present research is focused on optimizing the composition of soluble phases, the structure and morphology of insoluble phases, and artificial ageing processes. The results show that the best matches, 0.4 wt% Mg and 1.2 wt% Cu in the Al–9Si alloy, avoided the toxic effect of the blocky Al2Cu on the mechanical properties of the alloy. The addition of 0.6 wt% Zn modified the morphology of eutectic Si from coarse particles to fine fibrous particles and the texture of Fe-rich phases from acicular β-Fe to blocky π-Fe in the Al–9Si–1.2Cu–0.4Mg-based alloy. With the optimization of the heat treatment parameters, the spherical eutectic Si and the fully fused β-Fe dramatically improved the ultimate tensile strength and elongation to fracture. Compared with the Al–9Si–1.2Cu–0.4Mg-based alloy, the 0.6 wt% Zn modified alloy not only increased the ultimate tensile strength and elongation to fracture of peak ageing but also reduced the time of peak ageing. The following improved combination of higher tensile strength and higher elongation was achieved for 0.6 wt% Zn modified alloy by double-stage ageing: 100 °C × 3 h + 180 °C × 7 h, with mechanical properties of ultimate tensile strength (UTS) of ~371 MPa, yield strength (YS) of ~291 MPa, and elongation to fracture (E%) of ~5.6%.

scholarly journals Mechanical Response of Al-1.09Mg2Si Alloy under Varying Mould and Thermal Ageing Conditions

2012 ◽  
Vol 2012 ◽  
pp. 1-7
Author(s):  
O. I. Sekunowo ◽  
G. I. Lawal ◽  
S. O. Adeosun
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Ambient Temperature ◽  
Mechanical Response ◽  
Ageing Time ◽  
Thermal Ageing ◽  
Alloy Ingot ◽  
Solution Treated ◽  
Crucible Furnace

Samples of the 6063 (Al-1.09Mg2Si) alloy ingot were melted in a crucible furnace and cast in metal and sand moulds, respectively. Standard tensile, hardness, and microstructural test specimens were prepared from cast samples, solution treated at 520∘C, soaked for 6 hrs, and immediately quenched at ambient temperature in a trough containing water to assume a supersaturated structure. The quenched specimens were then thermally aged at 175∘C for 3–7 hrs. Results show that at different ageing time, varied fractions of precipitates and intermetallics evolved in the specimens’ matrices which affect the resulting mechanical properties. The metal mould specimens aged for four hours (MTA-4) exhibited superior ultimate tensile strength of 247.8 MPa; microhardness, 68.5 HV; elongation, 28.2% . It is concluded that the extent of improvement in mechanical properties depends on the fractions, coherence, and distribution of precipitates along with the type of intermetallics developed in the alloy during ageing process.

Dependence of Microstructures and Mechanical Properties on the Growth Rate and Composition in Directionally Solidified Mg-Gd Alloys

2022 ◽  
Vol 327 ◽  
pp. 82-97
Author(s):  
He Qin ◽  
Guang Yu Yang ◽  
Shi Feng Luo ◽  
Tong Bai ◽  
Wan Qi Jie
Keyword(s):  
Mechanical Properties ◽  
Growth Rate ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Dendritic Structure ◽  
Directionally Solidified ◽  
Dendrite Morphology ◽  
Microstructural Parameters ◽  
Wide Range ◽  
Microstructures And Mechanical Properties

Microstructures and mechanical properties of directionally solidified Mg-xGd (5.21, 7.96 and 9.58 wt.%) alloys were investigated at a wide range of growth rates (V = 10-200 μm/s) under the constant temperature gradient (G = 30 K/mm). The results showed that when the growth rate was 10 μm/s, different interface morphologies were observed in three tested alloys: cellular morphology for Mg-5.21Gd alloy, a mixed morphology of cellular structure and dendritic structure for Mg-7.96Gd alloy and dendrite morphology for Mg-9.58Gd alloy, respectively. Upon further increasing the growth rate, only dendrite morphology was exhibited in all experimental alloys. The microstructural parameters (λ1, λ2) decreased with increasing the growth rate for all the experimental alloy, and the measured λ1 and λ2 values were in good agreement with Trivedi model and Kattamis-Flemings model, respectively. Vickers hardness and the ultimate tensile strength increased with the increase of the growth rate and Gd content, while the elongation decreased gradually. Furthermore, the relationships between the hardness, ultimate tensile strength, the growth rate and the microstructural parameters were discussed and compared with the previous experimental results.

scholarly journals Effects of Gd, Y Content on the Microstructure and Mechanical Properties of Mg-Gd-Y-Nd-Zr Alloy

Metals ◽  
2018 ◽  
Vol 8 (10) ◽  
pp. 790 ◽  
Author(s):  
Changping Tang ◽  
Kai Wu ◽  
Wenhui Liu ◽  
Di Feng ◽  
Xuezhao Wang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Solution Treatment ◽  
Age Hardening ◽  
Uniaxial Tensile ◽  
Microstructure And Mechanical Properties ◽  
Shaped Particle ◽  
Zr Alloy ◽  
Non Equilibrium

The effects of Gd, Y content on the microstructure and mechanical properties of Mg-Gd-Y-Nd-Zr alloy were investigated using hardness measurements, X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), and uniaxial tensile testing. The results indicate that the alloys in as-cast condition mainly consist of α-Mg matrix and non-equilibrium eutectic Mg5.05RE (RE = Gd, Y, Nd). After solution treatment, the non-equilibrium eutectics dissolved into the matrix but some block shaped RE-rich particles were left at the grain boundaries and within grains. These particles are especially Y-rich and deteriorate the mechanical properties of the alloys. Both the compositions of the eutectic and the block shaped particle were independent of the total Gd, Y content of the alloys, but the number of the particles increases as the total Gd, Y content increases. The ultimate tensile strength increases as the total Gd, Y content decreases. A Mg-5.56Gd-3.38Y-1.11Nd-0.48Zr alloy with the highest ultimate tensile strength of 280 MPa and an elongation of 1.3% was fabricated. The high strength is attributed to the age hardening behavior and the decrease in block shaped particles.

Strength of Commercial Aluminum Alloys after Equal Channel Angular Pressing and Post-ECAP Processing

2006 ◽  
Vol 114 ◽  
pp. 91-96 ◽  
Author(s):  
Maxim Yu. Murashkin ◽  
M.V. Markushev ◽  
Julia Ivanisenko ◽  
Ruslan Valiev
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Aluminum Alloys ◽  
Ultimate Tensile Strength ◽  
Equal Channel Angular Pressing ◽  
Room Temperature ◽  
Solution Treatment ◽  
Ecap Processing ◽  
Angular Pressing

The effects of equal channel angular pressing (ECAP), further heat treatment and rolling on the structure and room temperature mechanical properties of the commercial aluminum alloys 6061 (Al-0.9Mg-0.7Si) and 1560 (Al-6.5Mg-0.6Mn) were investigated. It has been shown that the strength of the alloys after ECAP is higher than that achieved after conventional processing. Prior ECAP solution treatment and post-ECAP ageing can additionally increase the strength of the 6061 alloy. Under optimal ageing conditions a yield strength (YS) of 434 MPa and am ultimate tensile strength (UTS) of 470 MPa were obtained for the alloy. Additional cold rolling leads to a YS and UTS of 475 and 500 MPa with 8% elongation. It was found that the post-ECAP isothermal rolling of the 1560 alloy resulted in the formation of a nano-fibred structure and a tensile strength (YS = 540 MPa and UTS = 635 MPa) that has never previously been observed in commercial non-heat treatable alloys.